CN107927898A - A kind of compounded mix for improving reconstituted tobacco surface friction property and its application - Google Patents
A kind of compounded mix for improving reconstituted tobacco surface friction property and its application Download PDFInfo
- Publication number
- CN107927898A CN107927898A CN201711089962.9A CN201711089962A CN107927898A CN 107927898 A CN107927898 A CN 107927898A CN 201711089962 A CN201711089962 A CN 201711089962A CN 107927898 A CN107927898 A CN 107927898A
- Authority
- CN
- China
- Prior art keywords
- reconstituted tobacco
- compounded mix
- surface friction
- friction property
- winnofil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of compounded mix for improving reconstituted tobacco surface friction property provided by the invention and its application, each component match as follows according to mass percent：Compounded mix is by calcium carbonate 65% 80%, magnesium carbonate 15% 30%, titanium dioxide 1% 5%；The calcium carbonate is winnofil, and the crystal habit of the winnofil is diamond shape, and the particle diameter of the winnofil is 800 mesh, 1200 mesh.Compounded mix solution is added to slurry neutralization as coating fluid and is sprayed on reconstituted tobacco surface, achievees the purpose that to improve reconstituted tobacco surface friction property.The present invention is by adding feature compounded mix, start with from reconstituted tobacco physical property is improved, be not required to increase filament cutter and relevant equipment, have the advantages that safe and simple, inexpensive and method feasibility is high, to improve the Cigarette processing performance of reconstituted tobacco, there is provided an effective method.
Description
Technical field
The present invention relates to cigarette producing field, and in particular to a kind of compounded mix for improving reconstituted tobacco surface friction property
And its application.
Background technology
Due to the process of papermaking-method reconstituted tobaccos, it is special can effectively to change its physical characteristic, chemical characteristic and sense organ
Property, different functional reconstructions tobacco leaves can be made into according to cigarette product demand, for cigarette product lowering harm and decreasing coking, prominent production
Product style and features, lifting cigarette quality have critical function.Therefore, lifted reconstituted tobacco cigarette application in processing quality and
The problem of using effect is always industry general concern.Show reconstituted tobacco with tobacco leaf in the process of chopping is mixed, commonly
There are have impact on the physical index of cigarette the problems such as piece is run in chopping, tobacco cut width is unqualified, one is caused to product sensory quality
It is fixing to ring.
Chinese patent CN104432478A discloses a kind of method for reducing papermaking-method reconstituted tobaccos smoothness, to reproduce cigarette
The problems such as leaf manufacturing enterprise and Cigarette processing enterprise solve higher smoothness, slide plate.It is that papermaking-method reconstituted tobaccos product tiles
In hot air drier, the tiling number of plies is one layer, by way of heated-air drying, is dried at 100 DEG C ± 1 DEG C to moisture content 7
~8%, that is, realize the smoothness for reducing papermaking-method reconstituted tobaccos.Chinese invention patent CN102008122A is disclosed using papermaking
Method reconstituted tobacco is the processing technology by reconstituted tobacco without high intensity, individually into the method and its equipment of silk manufacture cigarette
Mixed after chopping with pipe tobacco.Chinese patent CN101828762A discloses a kind of filament forming process for paper making method-based reconstituted tobacco and its sets
It is standby, it is that first cutting is in blocks, then cut into bar using cutting three times i.e., the method for finally cutting into silk carries out reconstituted tobacco into silk,
Reconstruction pipe tobacco after dry do directly is mixed according to cigarette composition design proportion and is matched somebody with somebody into tobacco shred production line, solves paper-making method reconstructed cigarette
The problem of leaf is difficult to individually into silk.
In conclusion there are many deficiencies and defect for the prior art：First, without press dewatering, and convection drying
Mode, will produce larger steam consumption, and increase manufacturing cost；Second, the special chopping equipment of reconstituted tobacco need to be increased,
The problems such as there are equipment investment and taking up a large area.
The content of the invention
The present invention from reconstituted tobacco physical property is improved in view of the deficienciess of the prior art, start with, in reconstituted tobacco
A kind of feature compounded mix is added in production process, using the function of crystal habit and the absorbing fats acid of compounded mix, is made
The frictional behaviour on reconstituted tobacco surface is improved；Using the absorption combination of compounded mix and pulp fiber, fiber is reduced
Between combination power, be reduced the shear strength of reconstituted tobacco；Reach and reduce reconstituted tobacco and tobacco leaf mixing chopping or independent
Race piece during chopping, the problems such as tobacco cut width is unqualified, improve processing quality of the reconstituted tobacco in cigarette application process.
To achieve the above object, a kind of compounded mix for improving reconstituted tobacco surface friction property provided by the invention, its
It is characterized in that：Each component matches as follows according to mass percent：Compounded mix is by calcium carbonate 65%-80%, magnesium carbonate 15%-
30%th, titanium dioxide 1%-5%；The calcium carbonate is winnofil, and the crystal habit of the winnofil is water chestnut
Shape, the particle diameter of the winnofil is -1200 mesh of 800 mesh.
The present invention also provides a kind of application of the compounded mix of above-mentioned raising reconstituted tobacco surface friction property, its feature exists
In：
(1) based on the compounded mix, water is added to stir, mixing speed 500-900r/min, is stirred 10-20 minutes
After add natural plant gum, be prepared into compounded mix solution, the natural plant gum of the addition is no more than the 0.01% of compounded mix weight, institute
The solid content for stating compounded mix solution is no more than 50%；
(2) compounded mix solution is added to slurry neutralization as coating fluid and is sprayed on reconstituted tobacco surface, make reconstruction cigarette
Leaf surface is covered by filler, achievees the purpose that to improve reconstituted tobacco surface friction property.
Preferably, the natural plant gum is cationic guar gum.
Preferably, compounded mix solution usage is addition 10%-20% (to oven dry stock amount), surface addition in slurry
1-5g/m2。
Cationic guar gum can interact with electronegative fiber, filler grain, and being added in slurry can improve carefully
The retention of small fiber and filler, has effects that retention and drainage；Addition sprays after being mixed with compounded mix in coating fluid
On reconstituted tobacco surface, mainly reinforcer and interfibrous combination power, the compounded mix for being sprayed on reconstituted tobacco surface is reduced
Dry linting phenomenon.
The advantage of the invention is that：Method by improving reconstituted tobacco surface friction property, come solve reconstituted tobacco with
The quality problems such as piece, tobacco cut width be unqualified are run in the chopping that occurs in tobacco leaf mixing chopping process, to improve reconstituted tobacco
Cigarette processing performance, there is provided an effective method；The present invention reproduces cigarette by adding feature compounded mix, from improving
Leaf physical property is started with, and is not required to increase filament cutter and relevant equipment, has safe and simple, inexpensive and method feasibility height etc.
Advantage.
Embodiment
Below in conjunction with specific embodiment, the technical solution in the present invention is clearly and completely described.
Embodiment one：
(1) calcium carbonate 65kg, magnesium carbonate 30kg, titanium dioxide 5kg are mixed as compounded mix, then adds 100kg water
Stirring, mixing speed 500r/min, stirring add cationic guar gum 0.01kg after 15 minutes, it is molten to be prepared into compounded mix
Liquid；
(2) deserve to be called and state compounded mix solution 10kg and be added in 100kg over dry slurries, stir evenly as coating fluid, lead to
Cross the processes such as the online of paper machine, shaping, coating and be prepared into the reconstituted tobacco that moisture is about 20% or so；
(3) above-mentioned coating fluid is sprayed into above-mentioned reconstituted tobacco surface, coating weight 2g/m by painting equipment2, pass through
The processes such as drying, section are prepared into reconstituted tobacco product.
Embodiment two：
(1) calcium carbonate 80kg, magnesium carbonate 18kg, titanium dioxide 2kg are mixed as compounded mix, then adds 100kg water
Stirring, mixing speed 800r/min, stirring add cationic guar gum 0.005kg after 12 minutes, are prepared into compounded mix
Solution；
(2) deserve to be called and state compounded mix solution 20kg and be added in 100kg over dry slurries, stir evenly as coating fluid, lead to
Cross the processes such as the online of paper machine, shaping, coating and be prepared into the reconstituted tobacco that moisture is about 20% or so；
(3) above-mentioned coating fluid is sprayed into above-mentioned reconstituted tobacco surface, coating weight 3g/m by painting equipment2, pass through
The processes such as drying, section are prepared into reconstituted tobacco product.
Embodiment three：
(1) calcium carbonate 75kg, magnesium carbonate 22kg, titanium dioxide 3kg are mixed as compounded mix, then adds 100kg water
Stirring, mixing speed 900r/min, stirring add cationic guar gum 0.008kg, are prepared into compounded mix after ten minutes
Solution；
(2) deserve to be called and state compounded mix solution 15kg and be added in 100kg over dry slurries, stir evenly as coating fluid, lead to
Cross the processes such as the online of paper machine, shaping, coating and be prepared into the reconstituted tobacco that moisture is about 20% or so；
(3) above-mentioned coating fluid is sprayed into above-mentioned reconstituted tobacco surface, coating weight 5g/m by painting equipment2, pass through
The processes such as drying, section are prepared into reconstituted tobacco product.
In above-described embodiment, the calcium carbonate is winnofil, and the crystal habit of the winnofil is water chestnut
Shape, the particle diameter of the winnofil is -1200 mesh of 800 mesh.
Refer to object detection method according to paper physical, physical index contrasting detection is carried out to sample, the results are shown in Table 1, detection
Method is as follows：
The paper of GB/T 22895-2008 and the static measure planar process with dynamic friction coefficient of cardboard
Reconstituted tobacco " vertical-vertical " friction coefficient：The movement of upper and lower two papermaking-method reconstituted tobaccos samples is along fiber orientation；
The measure of shear strength uses Texture instrument constant speed downpressure, Sample Width 15mm, shear rate 30mm/min,
Measure reconstituted tobacco vertical fibers move towards shear strength (abbreviation longitudinal shear intensity)；
Piece rate is run in chopping：Claim 100 grams of finished cut tobaccos, using the method for hand picking, Ti removes underproof pipe tobacco, unqualified
Pipe tobacco weight accounts for the percentage of finished cut tobacco total amount, is that piece rate is run in chopping.
1 sample physical index of table detects
Detection data show that after the technology of the present invention, the frictional behaviour on reconstituted tobacco surface is obviously improved above,
Particularly confficient of static friction has a distinct increment；Reconstituted tobacco shearing force also slightly reduces, and is conducive to improve the chopping of reconstituted tobacco
Quality；Finished cut tobacco chopping runs piece rate and is reduced to 3.17% by 5.1%, reduces 37.9%.
The above description is merely a specific embodiment, but protection scope of the present invention is not limited thereto, any
Belong to those skilled in the art the invention discloses technical scope in, the change or replacement that can readily occur in, all should
It is included within the scope of the present invention.Therefore, protection scope of the present invention should be subject to scope of the claims.
Claims (4)
1. a kind of compounded mix for improving reconstituted tobacco surface friction property, it is characterised in that each component is matched somebody with somebody according to mass percent
Than as follows：Compounded mix is by calcium carbonate 65%-80%, magnesium carbonate 15%-30%, titanium dioxide 1%-5%；The calcium carbonate
For winnofil, the crystal habit of the winnofil is diamond shape, the particle diameter of the winnofil for 800 mesh-
1200 mesh.
2. the application of the compounded mix of a kind of as claimed in claim 1 raising reconstituted tobacco surface friction property, its feature exist
In：
(1) based on the compounded mix, water is added to stir, mixing speed 500-900r/min, stirring adds after 10-20 minutes
Enter natural plant gum, be prepared into compounded mix solution, 0.01% of natural plant gum no more than compounded mix weight of the addition is described multiple
The solid content for closing filler solution is no more than 50%；
(2) compounded mix solution is added to slurry neutralization as coating fluid and is sprayed on reconstituted tobacco surface, make reconstituted tobacco table
Face is covered by filler, achievees the purpose that to improve reconstituted tobacco surface friction property.
3. the application of the compounded mix of reconstituted tobacco surface friction property is improved as claimed in claim 2：The natural plant gum is
Cationic guar gum.
4. the application of the compounded mix of reconstituted tobacco surface friction property is improved as claimed in claim 2：It is compound in slurry to fill out
Expect 10%-20%, surface addition 1-5g/m of the solution additive amount for absolute dry pulp weight2。