CN108221461A - A kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage - Google Patents
A kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage Download PDFInfo
- Publication number
- CN108221461A CN108221461A CN201810006286.2A CN201810006286A CN108221461A CN 108221461 A CN108221461 A CN 108221461A CN 201810006286 A CN201810006286 A CN 201810006286A CN 108221461 A CN108221461 A CN 108221461A
- Authority
- CN
- China
- Prior art keywords
- paper
- preparation
- filter stick
- common filter
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to papermaking and tobacco business fields, are related to a kind of preparation method of common filter stick shaping paper.A kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage, this method include the following steps：Wood pulp size degradation, addition filler, discongest and be beaten, is with slurry, manufacturing paper with pulp, Top wire former, squeezing, the drying of preceding road, top sizing, rear road are dried, are batched, are cut and the processes such as packed.Product produced by the invention on grease proofing barrier performance is ensured, using with can natural degradation, food security raw material, assign the excellent degradability of the common filter stick shaping paper of antiseepage, food touch-safe.
Description
Technical field
The invention belongs to papermaking and tobacco business fields, are related to a kind of preparation method of common filter stick shaping paper.
Background technology
When the preparation method of filter stick shaping paper is processing filter stick for cigarettes, for rolling up the dedicated paper of packet filter material, applied to cigarette
Acetate silk is wrapped up in filter tip, in cigarette filter constructions in internal acetate silk core and outer layer cork paper it
Between.Mainly there are the preparation method of common filter stick shaping paper and the preparation method of high filter stick shaping paper thoroughly.It is not special to air permeability
It is required that filter stick shaping paper preparation method common filter stick shaping paper preparation method；There is the filter stick being distinctly claimed to air permeability
The preparation method of forming paper is the preparation method of high filter stick shaping paper thoroughly.
Cigarette microcapsule essence technology, with the development of low-coke tar cigarette, the fragrance of tobacco in itself is by filtering and dilutes,
Fragrance seems apparent deficiency that flavoring not only can overcome the disadvantages that these losses, but also not increase tar yield.The flavoring of cigarette product is formula
One important link of design is the effective means for improving cigarette product quality, is the particularly important means of cigarette industry, is volume
One of core technology of cigarette enterprise and its secrecy.The essence capsule of addition package unique perfume, is smoking in cigarette filter tip rod
Before pinch brokenly essence capsule, ooze out the oiliness essence in capsule, improve smoking when fragrance.But oiliness essence is easy to infiltration filter
The preparation method of stick forming paper, causes filter rod to pollute, while may make the preparation method of filter stick shaping paper again in package tow
Bonding place explosion.
In order to coordinate the demand of tobacco enterprise, the present invention develops a kind of common filter stick shaping paper of the antiseepage with oleophobic property
Preparation method, the preparation method of this filter stick shaping paper can effectively prevent the essential oil exudation filter stick surface in filter rod.
Application publication number：105887569 A of CN disclose a kind of grease proofing saturating forming paper of height；105862506 A of CN are disclosed
A kind of grease proofing forming paper production technology, the technique include：Wood pulp size degradation, mashing, it is with slurry, manufacture paper with pulp, be Top wire former, squeezing, preceding
Road drying, sprinkling auxiliary agent, table glue, the drying of rear road and coiling process.Above-mentioned technique shortcoming has：1st, sprinkling oil-proofing agent it is more difficult
It is sprayed uniformly on same paper, while sprinkling can only generally be sprayed at single side, another side is more difficult grease proofing effect；2nd, spray pattern
Oil-proofing agent is made to have larger loss, is unfavorable for cost-effective；3rd, spray pattern is unfavorable for controlling keeping for oil-proofing agent, cannot guarantee that
There are enough oil-proofing agent additive amounts；4th, sprinkling auxiliary agent can be destroyed paper appearance and planarization；5th, it touches and spills oil-proofing agent and table
Glue size-press starch combines and is extremely difficult to satisfied oleophobic property anti-seepage effect.
In view of above deficiency and difference, now provide a kind of preparation method of the new common filter stick shaping paper of oleophobic property antiseepage
And its a solution of production technology.
Invention content
In order to solve the technical issues of above-mentioned, the purpose of the present invention is to provide a kind of common filter rod formings of oleophobic property antiseepage
The preparation method of paper.
In order to realize above-mentioned purpose, present invention employs following technical solutions：
A kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage, this method include the following steps：
1) wood pulp size degradation：It is 80-20% bleaching needle-point leaf pulps by mass percentage, 20-80% bleached hardwood pulps, separately
Add the filler of the 0-20% of slurry total amount, carry out size degradation in hydrabrusher together；
2) it discongests and is beaten：Various wood pulps are discongested again after hydrabrusher mixing size degradation after being soaked for a period of time
And mashing, refining concentration are controlled in 3.0-6.0%, and machine chest is put into after the completion of discongesting and being beaten；
3) it is with slurry：Wood pulp by milled etc. is configured in proportion in mud pit, mixing, adds wet strength agent, and wet strength agent is used
Amount control is in 10-30kg/t paper；
4) it manufactures paper with pulp：The slurry prepared is extracted into and destroies forebay through fan pump Top wire former, squeezing, drying；
5) top sizing：By the surface size made pumping to surface sizing device during copy paper, dried by preceding road
Dry page enters surface sizing device and carries out top sizing, and surface size is totally submerged page, by top sizing roller
It uniformly squeezes, surface size is uniformly coated on page；The surface size of top sizing include PVA solution, water repellent agent and
Oil-proofing agent, a concentration of the 5~10% of the PVA solution, dosage is 10-30kg/t paper, and the water repellent agent dosage is 3-
15kg/t paper, the oil-proofing agent dosage are 3-15kg/t paper；
6) it dries, batch, cutting packaging.
Preferably, step 1) the paper-making fibre slurry includes 40-60% bleached softwoods wood by mass percentage
Slurry, 60-40% bleached hardwood pulps, another plus slurry total amount 10-15% filler.
Preferably, the beating degree that the step 2) is discongested and is beaten is controlled in 50-80 ° of SR, weight in wet base >=3g.
Preferably, the mass percent concentration of step 3) the paper-making fibre slurry is 0.5-2.5%.
Preferably, the mass percent concentration of the step 5) surface size is 1%-3%.
Preferably, the wet strength agent uses PAE or PPE.
Preferably, the oil-proofing agent uses fluorinated polymer or acrylic latex.
Beneficial effects of the present invention：The preparation method of the common filter stick shaping paper of antiseepage produced by the invention can effectively prevent filter
Oiliness essence in mouth stick is exuded to filter rod surface, and the formation of anti-seepage effect focuses on oil-proofing agent and water repellent agent, PVA is total to
With use；Oil-proofing agent, water repellent agent, PVA are adsorbed in top sizing in page fiber surface, in Drying Process, with
The evaporation of moisture and the raising of temperature in page, the polymer substance in solution, form close reticular membrane on page, this
Film has the surface energy less than oil, and oils is made to be difficult to soak page.Product produced by the invention on grease proofing barrier performance is ensured,
Using with can natural degradation, food security raw material, assign the common filter stick shaping paper of antiseepage preparation method it is excellent can
Degradability, food touch-safe.
Specific embodiment
The specific implementation of the present invention is described further, but implementation of the invention and protection domain are not below in conjunction with example
It is limited to this.
There are two types of the oil-proofing agents used in the embodiment of the present invention：One kind is You Nien (UNIDYNE) fluorine system water and oil repellent agent,
It is a kind of fluorinated polymer；Another kind is a kind of water and oil repellent agent of Tao Shi productions, and main component is acrylic latex.
A kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage, includes the following steps：Wood pulp size degradation, addition are filled out
Expect, discongest and be beaten, is with slurry, manufacturing paper with pulp, Top wire former, squeezing, the drying of preceding road, top sizing, rear road are dried, batched, cutting packet
The processes such as dress.
The preparation method of the common filter stick shaping paper of oleophobic property antiseepage produced by the invention can ensure to have it is excellent it is grease proofing,
Water resistance, additionally with biodegradable, food touch-safe.The common filter stick of oleophobic property antiseepage produced by the invention
The preparation method of forming paper measures the oil preventing performance of paper according to the method for TAPPI T 559cm-02.Oleophobic property produced by the invention
The preparation method of the common filter stick shaping paper of antiseepage measures the water resistance of paper according to 1540 paper of GB/T and the requirement of cardboard water imbibition.
Below by specific example, the present invention is described further.
Embodiment 1
Wet end furnish：Northern 80% bleaching needle-point leaf pulp of board, parrot board bleached hardwood pulp 20%；Separately add slurry total amount
20% fine particle calcium carbonate.
Two kinds of wood pulps add fine particle calcium carbonate to be discongested and be beaten again after impregnating 30 minutes after hydrabrusher size degradation, and defibrination is dense
Degree control is 4.0%.Beating degree control is put into machine chest after the completion of 50-58 ° of SR, weight in wet base >=4.5g, mashing.
It is with slurry：The wood pulp of milled in mud pit is configured by a certain percentage, mixes, adds wet strength agent PPE, dosage
10kg/t paper.2.5% concentration is all diluted to after mixing.
It manufactures paper with pulp：By the pulp dilution prepared to 1.0% concentration, it is extracted into and destroies forebay through fan pump Top wire former, squeezing, dry
It is dry.
Top sizing operates：PVAC polyvinylalcohol concentration of ordinary dissolution：3.5%, dosage is 15kg/t paper；PVAC polyvinylalcohol is molten
A kind of water repellent agent is added after solution is good, dosage is 4kg/t paper；You Nien (UNIDYNE) fluorine system water and oil repellent agent is eventually adding, is used
It measures as 5kg/t paper；
By drying after page surface sizing, drying temperature be 105 DEG C be 3-6% to moisture after batch, cut packet
Dress etc..
The grease proofing grade of preparation method of the common filter stick shaping paper of oleophobic property antiseepage of production is 6 grades of (TAPPI T 559cm-
02)。
Embodiment 2
Wet end furnish：Northern 50% bleaching needle-point leaf pulp of board, parrot board bleached hardwood pulp 50%；Separately add slurry total amount
15% fine particle calcium carbonate.
Two kinds of wood pulps add fine particle calcium carbonate to be discongested and be beaten again after forty minutes through impregnating after hydrabrusher size degradation, and defibrination is dense
Degree control is 4.5%.Beating degree is controlled in 58-65 ° of SR, weight in wet base >=4g, and machine chest is put into after the completion of discongesting and being beaten.
It is with slurry：The wood pulp of milled in mud pit is configured by a certain percentage, mixes, adds wet strength agent PPE, dosage
15kg/t paper.2.6% concentration is all diluted to after mixing.
It manufactures paper with pulp：By the pulp dilution prepared to 1.5% concentration, it is extracted into and destroies forebay through fan pump Top wire former, squeezing, dry
It is dry.
Top sizing operates：PVAC polyvinylalcohol concentration of ordinary dissolution：4%, dosage is 20kg/t paper；PVAC polyvinylalcohol dissolves
A kind of water repellent agent is added after good, dosage is 5kg/t paper；It is eventually adding You Nien (UNIDYNE) fluorine system water and oil repellent agent, dosage
For 6kg/t paper；
By drying after page surface sizing, drying temperature be 105 DEG C be 3-6% to moisture after batch, cut packet
Dress etc..
The grease proofing grade of preparation method of the high filter stick shaping paper thoroughly of the oleophobic property antiseepage of production is 6 grades of (TAPPI T 559cm-
02)。
Embodiment 3
Wet end furnish：Northern 20% bleaching needle-point leaf pulp of board, parrot board bleached hardwood pulp 80%；
Wood pulp is discongested and is beaten again after impregnating 15 minutes after hydrabrusher size degradation, and refining concentration control exists
5.0%.Beating degree is controlled in 72-80 ° of SR, weight in wet base >=3g, and machine chest is put into after the completion of discongesting and being beaten.
It is with slurry：The wood pulp of milled is put into mud pit, adds in wet strength agent PPE, dosage 25kg/t paper.It is all dilute after mixing
Release the concentration to 3%.
It manufactures paper with pulp：By the pulp dilution prepared to 2% concentration, it is extracted into and destroies forebay through fan pump Top wire former, squeezing, drying.
Top sizing operates：PVAC polyvinylalcohol concentration of ordinary dissolution：4.5%, dosage is 30kg/t paper；PVAC polyvinylalcohol is molten
A kind of water repellent agent is added after solution is good, dosage is 6kg/t paper；You Nien (UNIDYNE) fluorine system water and oil repellent agent is eventually adding, is used
It measures as 8kg/t paper；
By drying after page surface sizing, drying temperature be 105 DEG C be 3-6% to moisture after batch, cut packet
Dress etc..
The grease proofing grade of preparation method of the high filter stick shaping paper thoroughly of the oleophobic property antiseepage of production is 6 grades of (TAPPI T 559cm-
02)。
Embodiment 4
Wet end furnish：Northern 60% bleaching needle-point leaf pulp of board, parrot board bleached hardwood pulp 40%；Separately add slurry total amount
10% fine particle calcium carbonate.
Two kinds of wood pulps are discongested and are beaten again after twenty minutes through impregnating after hydrabrusher size degradation, refining concentration control
4.5%.Mashing mode is based on discongesting, and cut staple, beating degree are not controlled in 65-72 ° of SR, weight in wet base >=3.5g as far as possible,
Machine chest is put into after the completion of discongesting and being beaten.
It is with slurry：The wood pulp of milled in mud pit is configured by a certain percentage, mixes, adds wet strength agent PPE, dosage
25kg/t paper.3.2% concentration is all diluted to after mixing.
It manufactures paper with pulp：By the pulp dilution prepared to 1.5% concentration, it is extracted into and destroies forebay through fan pump Top wire former, squeezing, dry
It is dry.
Top sizing operates：PVAC polyvinylalcohol concentration of ordinary dissolution：3%, dosage is 35kg/t paper；PVAC polyvinylalcohol dissolves
A kind of water repellent agent is added after good, dosage is 15kg/t paper；A kind of water and oil repellent agent of Tao Shi productions is eventually adding, dosage is
15kg/t paper；
By drying after page surface sizing, drying temperature be 105 DEG C be 3-6% to moisture after batch, cut packet
Dress etc..
The grease proofing grade of preparation method of the common filter stick shaping paper of oleophobic property antiseepage of production is 5 grades of (TAPPI T 559cm-
02)。
The specific matter of the preparation method of the common filter stick shaping paper of oleophobic property antiseepage that the various embodiments described above of the present invention are produced
Figureofmerit is as follows：
Claims (7)
1. a kind of preparation method of the common filter stick shaping paper of oleophobic property antiseepage, it is characterised in that this method includes the following steps：
1) wood pulp size degradation：It is 80-20% bleaching needle-point leaf pulps by mass percentage, 20-80% bleached hardwood pulps, another plus slurry
Expect the filler of the 0-20% of total amount, carry out size degradation in hydrabrusher together；
2) it discongests and is beaten：Various wood pulps are discongested and are beaten again after being soaked for a period of time after hydrabrusher mixing size degradation
Slurry, refining concentration are controlled in 3.0-6.0%, and machine chest is put into after the completion of discongesting and being beaten；
3) it is with slurry：Wood pulp by milled etc. is configured in proportion in mud pit, and mixing adds wet strength agent, wet strengthening agent control
System is in 10-30kg/t paper；
4) it manufactures paper with pulp：The slurry prepared is extracted into and destroies forebay through fan pump Top wire former, squeezing, drying；
5) top sizing：By the surface size made pumping to surface sizing device during copy paper, dried by preceding road
Page enters surface sizing device and carries out top sizing, and surface size is totally submerged page, by the uniform of top sizing roller
It squeezes, surface size is uniformly coated on page；The surface size of top sizing includes PVA solution, water repellent agent and grease proofing
Agent, a concentration of the 5~10% of the PVA solution, dosage is 10-30kg/t paper, and the water repellent agent dosage is 3-15kg/t
Paper, the oil-proofing agent dosage are 3-15kg/t paper；
6) it dries, batch, cutting packaging.
A kind of 2. preparation method of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that step
Rapid 1) paper-making fibre slurry includes 40-60% bleaching needle-point leaf pulps, 60-40% bleached hardwood pulps, another by mass percentage
Add the filler of slurry total amount 10-15%.
A kind of 3. preparation method of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that step
The rapid beating degree 2) discongested and be beaten is controlled in 50-80 ° of SR, weight in wet base >=3g.
A kind of 4. preparation method of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that step
The mass percent concentration of rapid paper-making fibre slurry 3) with slurry is 0.5-2.5%.
A kind of 5. preparation method of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that step
The mass percent concentration of rapid 5) surface size is 1%-3%.
6. the preparation method of a kind of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that wet
Strong agent uses PAE or PPE.
7. the preparation method of a kind of common filter stick shaping paper of oleophobic property antiseepage according to claim 1, which is characterized in that anti-
Finish uses fluorinated polymer or acrylic latex.