CN107903765A - Anti- UV epoxy self-levelings finishing coat - Google Patents
Anti- UV epoxy self-levelings finishing coat Download PDFInfo
- Publication number
- CN107903765A CN107903765A CN201711192733.XA CN201711192733A CN107903765A CN 107903765 A CN107903765 A CN 107903765A CN 201711192733 A CN201711192733 A CN 201711192733A CN 107903765 A CN107903765 A CN 107903765A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- halloysite nanotubes
- carbon black
- nano carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the preparation field of epoxy self-leveling coating, and in particular to a kind of anti-UV epoxy self-levelings finishing coat.The finishing coat is made of two component of A, B;Component A is composed of the following raw materials by weight:10 12 parts of 1 1.5 parts of halloysite nanotubes, 10 20 parts of 100 120 mesh quartz sand, 23 parts of trimethyl phosphate and mill base that 50 60 parts of epoxy resin, 10 20 parts of acrylic resin, 10 20 parts of iso-octyl glycidyl ether, 10 15 parts of phenyl glycidyl ether, 8 10 parts of barium sulfate, 5 10 parts of mica powder, nano carbon black load etc.;B component is composed of the following raw materials by weight:8 10 parts of 10 12 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.The epoxy finish of the present invention possesses the excellent performance of common epoxy self-leveling, while adds mould proof scratch resistance performance, it may have unique uv-resistance, is suitable for open air.
Description
Technical field
The invention belongs to the preparation field of epoxy self-leveling coating, and in particular to a kind of anti-UV epoxy self-levelings finishing coat.
Background technology
Epoxy self-leveling coating is using epoxy resin, special curing agent as main material, by adding various auxiliary agents, pigment, filling out
Material etc., is process through stringent proportioning, not only with chemical characteristics such as excellent water-fast, resistance to greasy dirt, chemicals-resistant corrosion, but also
With adhesive force is good, high mechanical strength, paint film shrinking percentage is low after curing, can once apply the advantages that dressing up thick film, therefore extensive
In covering with paint for modern industry terrace.But the use scope of epoxy self-leveling coating is limited only to interior, use outdoors
It is ineffective.
A kind of epoxy self-leveling coating that can be used for open air is developed, the problem of filling a hole in the market, be urgent need to resolve.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of anti-UV epoxy self-levelings finishing coat.The finishing coat
Except the excellent performance with common epoxy self-leveling coating, the characteristic for adding mould proof scratch resistance at the same time is gone back, it may have unique
Uv-resistance, problem outdoors, economic and practical, easy construction cannot be used by solving epoxy coating.
To achieve the above object, the present invention adopts the following technical scheme that:
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:50-60 parts of epoxy resin, 10-20 parts of acrylic resin, 10-20 parts of iso-octyl glycidyl ether, phenyl glycidyl ether
10-15 parts, 8-10 parts of barium sulfate, 5-10 parts of mica powder, nano carbon black load 1-1.5 parts of halloysite nanotubes, 100-120 mesh
10-20 parts of quartz sand, 0.8-1.5 parts of wetting dispersing agent, 1.0-1.2 parts of levelling agent, 1-1.5 parts of defoamer, trimethyl phosphate 2-3
Part, 10-12 parts of mill base;B component is made of following raw material by weight:10-12 parts of base polyurethane prepolymer for use as and polyamide 8-
10 parts;The weight ratio of component A and B component is 3:1.
Preferably, the anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A by it is following by weight
The raw material composition of part meter:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, phenyl glycidyl
12 parts of ether, 9 parts of barium sulfate, 8 parts of mica powder, 1.2 parts of halloysite nanotubes, the 100-120 mesh quartz sand 15 of nano carbon black load
Part, 1.0 parts of wetting dispersing agent, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component is by following
Raw material composition by weight:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 10-12h, excessively drying, 100-200 mesh sieves, are obtained short
Cut halloysite nanotubes;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 5 ~ 10g silane coupling agents, and stir
10min;Then 300-400g steps are added(1)Halloysite nanotubes after processing, and stirred with reinforcement electric mixer
15min, filters, and then dry 2 h at 120 DEG C, are made coupling modifier halloysite nanotubes;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 1-2h filters, and ethanol washing, then the dry 1-2 h at 120 DEG C, are made nano carbon black
The halloysite nanotubes of load.
Step(3)The weight ratio of middle nano carbon black and coupling modifier halloysite nanotubes is:1:10-50.
The levelling agent is BYK-354, and the defoamer is BYK-054, and the wetting dispersing agent is BYK-
310。
Nano carbon black is best ultra-violet stabilizer, can be used as UV absorbers.But in multicomponent matrix tree
In the co-mixing system that fat is formed with carbon black, since the polarity of different matrix is different, nano carbon black can produce segregation phenomena, influence face
Flow leveling, adhesive force and the weather resistance of paint.And nano carbon black disperses more difficult in resin system.Galapectite nanometer
Pipe is a kind of alumino-silicate, and strong adsorption, is high reserves energy storage material.
Nano carbon black load is scattered on coupling modifier halloysite nanotubes by the present invention, solves nano carbon black in resin
The problem of middle bad dispersibility, possess excellent UVResistant effect.
The beneficial effects of the present invention are:
1)Nano carbon black load is scattered on coupling modifier halloysite nanotubes by the present invention, since halloysite nanotubes surface has
Have amphipathic, solve the problems, such as bad dispersibility;Halloysite nanotubes have high energy storage at the same time, and a large amount of nano carbon blacks disperse to bear
It is loaded on halloysite nanotubes, has played excellent anti-UV effects;There is halloysite nanotubes certain sustained release-controlled release to make at the same time
With with the extension of epoxy self-leveling finishing coat usage time, nano carbon black can be sustained out, play anti-UV effects for a long time;
2)Addition of the halloysite nanotubes in finishing coat, due to the strong adsorptivity of halloysite nanotubes itself, surface compatibility, increases
The strong adhesive force with middle painting primary coat, can effectively prevent coating and cracks, scratch resistance is good;Halloysite nanotubes are to finishing coat at the same time
In steam also have stronger suction-operated, moistureproof and mildewproof performance is good;In addition tensile strength and hardness are high, and with good
Shock resistance, and noise can be absorbed.
Embodiment
The present invention further illustrates the present invention with the following example, but protection scope of the present invention is not limited to following reality
Apply example.
Embodiment 1
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:50 parts of epoxy resin, 20 parts of acrylic resin, 10 parts of iso-octyl glycidyl ether, 15 parts of phenyl glycidyl ether, barium sulfate
8 parts, 10 parts of mica powder, nano carbon black load 1 part of halloysite nanotubes, 20 parts of 100-120 mesh quartz sand, wetting dispersing agent
0.8 part, 1.2 parts of levelling agent, 1 part of defoamer, 3 parts of trimethyl phosphate, 10 parts of mill base;B component is by following original by weight
Material composition:10 parts of 10 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 10h, excessively drying, 200 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 5g silane coupling agents, and stir 10min;
Then 300g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, filter, then
Dry 2 h, are made coupling modifier halloysite nanotubes at 120 DEG C;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 1h filters, and ethanol washing, then dry 2 h at 120 DEG C, are made nano carbon black load
Halloysite nanotubes;The weight ratio of nano carbon black and coupling modifier halloysite nanotubes is:1:10.
Embodiment 2
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, 12 parts of phenyl glycidyl ether, barium sulfate
9 parts, 8 parts of mica powder, nano carbon black load 1.2 parts of halloysite nanotubes, 15 parts of 100-120 mesh quartz sand, wetting dispersing agent
1.0 parts, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component by it is following by weight
Raw material forms:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 11h, excessively drying, 100 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 8g silane coupling agents, and stir 10min;
Then 400g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, filter, then
Dry 2 h, are made coupling modifier halloysite nanotubes at 120 DEG C;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 2h filters, and ethanol washing, then dry 2 h at 120 DEG C, are made nano carbon black load
Halloysite nanotubes.
Step(3)The weight ratio of middle nano carbon black and coupling modifier halloysite nanotubes is:1:25.
Embodiment 3
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:60 parts of epoxy resin, 10 parts of acrylic resin, 20 parts of iso-octyl glycidyl ether, 10 parts of phenyl glycidyl ether, barium sulfate
10 parts, 5 parts of mica powder, nano carbon black load 1.5 parts of halloysite nanotubes, 10 parts of 100-120 mesh quartz sand, wetting dispersing agent
1.5 parts, 1.0 parts of levelling agent, 1.5 parts of defoamer, 2 parts of trimethyl phosphate, 12 parts of mill base;B component by it is following by weight
Raw material forms:10 parts of 10 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 12h, excessively drying, 100 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 10g silane coupling agents, and stir
10min;Then 300g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, take out
Filter, then dry 2 h at 120 DEG C, are made coupling modifier halloysite nanotubes;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 2h filters, and ethanol washing, then the dry 1h at 120 DEG C, is made nano carbon black load
Halloysite nanotubes;The weight ratio of nano carbon black and coupling modifier halloysite nanotubes is:1:30.
Embodiment 4
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, 12 parts of phenyl glycidyl ether, barium sulfate
9 parts, 8 parts of mica powder, nano carbon black load 1.2 parts of halloysite nanotubes, 15 parts of 100-120 mesh quartz sand, wetting dispersing agent
1.0 parts, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component by it is following by weight
Raw material forms:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 11h, excessively drying, 100 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 8g silane coupling agents, and stir 10min;
Then 400g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, filter, then
Dry 2 h, are made coupling modifier halloysite nanotubes at 120 DEG C;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 2h filters, and ethanol washing, then dry 2 h at 120 DEG C, are made nano carbon black load
Halloysite nanotubes.
Step(3)The weight ratio of middle nano carbon black and coupling modifier halloysite nanotubes is:1:40.
Embodiment 5
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, 12 parts of phenyl glycidyl ether, barium sulfate
9 parts, 8 parts of mica powder, nano carbon black load 1.2 parts of halloysite nanotubes, 15 parts of 100-120 mesh quartz sand, wetting dispersing agent
1.0 parts, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component by it is following by weight
Raw material forms:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 11h, excessively drying, 100 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 8g silane coupling agents, and stir 10min;
Then 400g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, filter, then
Dry 2 h, are made coupling modifier halloysite nanotubes at 120 DEG C;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 2h filters, and ethanol washing, then dry 2 h at 120 DEG C, are made nano carbon black load
Halloysite nanotubes.
Step(3)The weight ratio of middle nano carbon black and coupling modifier halloysite nanotubes is:1:50.
Embodiment 6
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, 12 parts of phenyl glycidyl ether, barium sulfate
9 parts, 8 parts of mica powder, nano carbon black load 1.2 parts of halloysite nanotubes, 15 parts of 100-120 mesh quartz sand, wetting dispersing agent
1.0 parts, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component by it is following by weight
Raw material forms:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
The preparation method of the halloysite nanotubes of the nano carbon black load, concretely comprises the following steps:
(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 11h, excessively drying, 100 mesh sieves, obtain angstrom Lip river that is chopped
Stone nanotube;
(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 8g silane coupling agents, and stir 10min;
Then 400g steps are added(1)Halloysite nanotubes after processing, and 15min is stirred with reinforcement electric mixer, filter, then
Dry 2 h, are made coupling modifier halloysite nanotubes at 120 DEG C;
(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes
Property halloysite nanotubes, ultrasonic disperse 2h filters, and ethanol washing, then dry 2 h at 120 DEG C, are made nano carbon black load
Halloysite nanotubes.
Step(3)The weight ratio of middle nano carbon black and coupling modifier halloysite nanotubes is:1:30.
Comparative example 1
A kind of anti-UV epoxy self-levelings finishing coat, is made of component A and B component;Component A is by following raw material group by weight
Into:55 parts of epoxy resin, 15 parts of acrylic resin, 15 parts of iso-octyl glycidyl ether, 12 parts of phenyl glycidyl ether, barium sulfate
9 parts, 8 parts of mica powder, 1.2 parts of nano carbon black, 15 parts of 100-120 mesh quartz sand, 1.0 parts of wetting dispersing agent, 1.1 parts of levelling agent,
1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component is made of following raw material by weight:Polyurethane prepolymer
9 parts of 11 parts of body and polyamide;The weight ratio of component A and B component is 3:1.
Performance detection is carried out to the coating of embodiment 2, comparative example 1, testing result is as shown in table 1.
The anti-UV epoxy self-levelings finishing coat performance data of table 1
Embodiment 1-6, the anti-UV epoxy self-levelings finishing coat of comparative example 1 are coated on reflection plate substrate, it is 150 μm to smear thickness, is treated
After its maturation, anti-UV xanthochromias test is carried out.
Anti- UV xanthochromias test:Using QUV Ageing machines [Q-Panel companies], set UVB 313nm fluorescent tubes energy as
0.8W/m2/ nm, at 60 DEG C, sets UVB 313nm fluorescent tubes energy as 0.8W/m in ASTM G154 methods respectively2/ nm sequentially according to
Penetrate sample to be tested 100,300,500 it is small when, then take out sample size with ASTM E313 methods measure yellow colour index YI numerical value, and
Calculate yellow colour index changing value(∆YI), test acquired results such as following table 2.
2 QUV of table(UVB 313nm)Irradiate yellowing index change
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent are with repairing
Decorations, should all belong to the covering scope of the present invention.
Claims (4)
- A kind of 1. anti-UV epoxy self-levelings finishing coat, it is characterised in that:It is made of component A and B component;Component A is made of following raw material by weight:50-60 parts of epoxy resin, 10-20 parts of acrylic resin, iso-octyl 10-20 parts of glycidol ether, 10-15 parts of phenyl glycidyl ether, 8-10 parts of barium sulfate, 5-10 parts of mica powder, nano carbon black are born 1-1.5 parts of halloysite nanotubes, 10-20 parts of 100-120 mesh quartz sands, 0.8-1.5 parts of wetting dispersing agent, the levelling agent 1.0- of load 1.2 parts, 1-1.5 parts of defoamer, 2-3 parts of trimethyl phosphate, 10-12 parts of mill base;B component is made of following raw material by weight:8-10 parts of 10-12 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
- 2. anti-UV epoxy self-levelings finishing coat according to claim 1, it is characterised in that:It is made of component A and B component;Component A is made of following raw material by weight:55 parts of epoxy resin, 15 parts of acrylic resin, iso-octyl shrink sweet Oily 15 parts of ether, 12 parts of phenyl glycidyl ether, 9 parts of barium sulfate, 8 parts of mica powder, the halloysite nanotubes 1.2 of nano carbon black load Part, 15 parts of 100-120 mesh quartz sand, 1.0 parts of wetting dispersing agent, 1.1 parts of levelling agent, 1.2 parts of defoamer, 2 parts of trimethyl phosphate, 11 parts of mill base;B component is made of following raw material by weight:9 parts of 11 parts of base polyurethane prepolymer for use as and polyamide;The weight ratio of component A and B component is 3:1.
- 3. anti-UV epoxy self-levelings finishing coat according to claim 1 or 2, it is characterised in that:The nano carbon black load Halloysite nanotubes preparation method, concretely comprise the following steps:(1)Halloysite nanotubes are taken, through mechanical crushing, ethanol wet grinding 10-12h, excessively drying, 100-200 mesh sieves, are obtained short Cut halloysite nanotubes;(2)600mL ethanol and 200mL distilled water are measured in 1000mL beakers, adds 5 ~ 10g silane coupling agents, and stir 10min;Then 300-400g steps are added(1)Halloysite nanotubes after processing, and stirred with reinforcement electric mixer 15min, filters, and then dry 2 h at 120 DEG C, are made coupling modifier halloysite nanotubes;(3)Nano carbon black is scattered in the ethanol solution that volume fraction is 30%, then adds step(2)Obtained coupling changes Property halloysite nanotubes, ultrasonic disperse 1-2h filters, and ethanol washing, then the dry 1-2 h at 120 DEG C, are made nano carbon black The halloysite nanotubes of load.
- 4. anti-UV epoxy self-levelings finishing coat according to claim 3, it is characterised in that:Step(3)Middle nano carbon black and idol The weight ratio of the modified halloysite nanotubes of connection is:1:10-50.