CN106752855A - A kind of furniture polyurethane Brilliant white paint - Google Patents
A kind of furniture polyurethane Brilliant white paint Download PDFInfo
- Publication number
- CN106752855A CN106752855A CN201611030942.XA CN201611030942A CN106752855A CN 106752855 A CN106752855 A CN 106752855A CN 201611030942 A CN201611030942 A CN 201611030942A CN 106752855 A CN106752855 A CN 106752855A
- Authority
- CN
- China
- Prior art keywords
- parts
- furniture
- brilliant white
- white paint
- butyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The embodiment of the invention discloses a kind of furniture polyurethane Brilliant white paint, the furniture includes host, curing agent and diluent with polyurethane Brilliant white paint, wherein, host includes synthctic fat acid resin, butyl acetate, defoamer, levelling agent, white slurry；White slurry includes synthctic fat acid resin, butyl acetate, dispersant, titanium dioxide, nanometer potassium aluminosilicate powder；Curing agent includes toluene diisocyanate trimer, hexamethylene diisocyanate trimer, butyl acetate；Diluent includes butyl acetate, dimethylbenzene, propylene glycol methyl ether acetate.Furniture polyurethane Brilliant white paint, by using nanometer potassium aluminosilicate powder, can improve the sand mark shielding ability and richness of paint film, and reach the purpose for reducing dark bubble, improving levelling effect.
Description
Technical field
The present invention relates to chemical technology field, more particularly to a kind of furniture polyurethane Brilliant white paint.
Background technology
With the raising of material and cultural life, requirement of the people to the taste and decorative effect of family's living furniture is more next
Higher, especially light is serial.And in the market is applied to the richness and levelling of the polyurethane Brilliant white paint in paint film of furniture
Etc. aspect be always difficult to reach preferably effect, in theory for, can be well by the filler systems changed in formulation for coating material
Improve problems, however, for partial filler system on the market, such as blanc fixe, due to itself easily heavy characteristic
And the limitation on formula system, corresponding polyurethane Brilliant white paint is produced many disadvantages, such as coating surface is easily produced
The particle of raw convex, influences the aesthetic property of paint film, is unfavorable for the development of polyurethane Brilliant white paint.
Therefore, it is necessary to the filler systems in improving formulation for coating material, to avoid that paint film can be effectively improved while disadvantage
The decorative effect such as richness, levelling.
The content of the invention
A kind of furniture polyurethane Brilliant white paint is the embodiment of the invention provides, by using nanometer potassium aluminosilicate powder,
The sand mark shielding ability and richness of paint film can be improved, and reaches the purpose for reducing dark bubble, improving levelling effect.
In view of this, first aspect present invention provides a kind of furniture polyurethane Brilliant white paint, the light fine flour
Paint may include：
Host, curing agent and diluent；
In terms of parts by weight, host includes：
Wherein, in terms of parts by weight, white slurry includes：
In terms of parts by weight, curing agent includes：
40 to 50 parts of toluene diisocyanate trimer；
20 to 30 parts of hexamethylene diisocyanate trimer；
20 to 30 parts of butyl acetate；
In terms of parts by weight, the diluent includes：
25 to 40 parts of butyl acetate；
25 to 30 parts of dimethylbenzene；
35 to 45 parts of propylene glycol methyl ether acetate.
With reference to the embodiment of the present invention in a first aspect, the first implementation method of the first aspect in the embodiment of the present invention
In, levelling agent is fluorin modified crylic acid ester solution.
With reference to the embodiment of the present invention in a first aspect, or the embodiment of the present invention first aspect the first implementation method,
In second implementation method of the first aspect of the embodiment of the present invention, defoamer is modified siloxane copolymer solution.
With reference to the embodiment of the present invention in a first aspect, the first implementation method or of the first aspect of the embodiment of the present invention
Two kinds of implementation methods, in the third implementation method of the first aspect of the embodiment of the present invention, in terms of parts by weight, host is 1
Part, curing agent is 0.8 to 1 part, and diluent is 0.3 to 0.4 part.
As can be seen from the above technical solutions, the embodiment of the present invention has advantages below：
In the embodiment of the present invention, it is main body to use synthctic fat acid resin, and titanium dioxide collocation nanometer potassium aluminosilicate powder is to fill out
Material system.Then because synthctic fat acid resin has more plentiful plate face effect in itself, such that it is able to improve the plentiful of paint film
Degree, and titanium dioxide and nanometer potassium aluminosilicate powder for paint film while whiteness is provided, it is possible to have preferable fillibility so that
The ability that paint film covers sand trace is greatly promoted, and because nanometer potassium aluminosilicate powder is the laminated structure of Nano grade, can be at this
Paint film is supported well in the work progress of furniture polyurethane light fine flour, hence it is evident that is reduced the disadvantages such as dark bubble, pin hole, is entered one
Step improves the levelling effect of paint film.Additionally, nanometer potassium aluminosilicate powder can be big due to its superpower weatherability, and titanium dioxide collocation
Amplitude strengthens the anti-yellowing property of paint film.
Specific embodiment
A kind of furniture polyurethane Brilliant white paint is the embodiment of the invention provides, is carried by using nanometer potassium aluminosilicate powder
The sand mark shielding ability and richness of paint film high, and reach the purpose for reducing dark bubble, improving levelling effect.
In order that those skilled in the art more fully understand the present invention program, below to the technology in the embodiment of the present invention
Scheme is clearly and completely described, it is clear that described embodiment is only the embodiment of a part of the invention, rather than
Whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creative work premise
Lower obtained every other embodiment, should all belong to the scope of protection of the invention.
The invention provides a kind of furniture polyurethane Brilliant white paint, the Brilliant white paint can include host, solidification
Agent and diluent；
In terms of parts by weight, host can include：
Wherein, in terms of parts by weight, white slurry includes：
In terms of parts by weight, curing agent includes：
40 to 50 parts of toluene diisocyanate trimer；
20 to 30 parts of hexamethylene diisocyanate trimer；
20 to 30 parts of butyl acetate；
In terms of parts by weight, the diluent includes：
25 to 40 parts of butyl acetate；
25 to 30 parts of dimethylbenzene；
35 to 45 parts of propylene glycol methyl ether acetate.
The furniture polyurethane Brilliant white paint that the present invention is provided can include host, curing agent and diluent, wherein, it is main
Agent can include synthctic fat acid resin, butyl acetate, defoamer, levelling agent and white slurry, the percentage of each component in host
Than sum be 100%, curing agent can include toluene diisocyanate trimer, hexamethylene diisocyanate trimer and
Butyl acetate, in curing agent the percentage sum of each component be 100%, diluent can include butyl acetate, dimethylbenzene with
And propylene glycol methyl ether acetate, the percentage sum of each component is 100% in diluent, and white slurry can include synthctic fat
Acid resin, butyl acetate, dispersant, titanium dioxide, the powder of resistance to potassium aluminosilicate, the percentage sum of each component is also in white slurry
100%.In actual applications, the furniture can prepare host, curing agent and diluent with polyurethane Brilliant white paint and carry out
After mixing, you can carry out application, simple and convenient, strong applicability.
In the present invention, synthctic fat acid resin is the key component of furniture polyurethane Brilliant white paint, for improving
The gloss of paint film, richness and pliability that furniture polyurethane Brilliant white paint is formed in construction, can be dissolved in vinegar
In acid butyl ester.Specifically such as：The Niu Peisi companies trade mark is 2848 product.
In the present invention, the effect of defoamer is to remove furniture polyurethane Brilliant white paint to produce in process of production
Bubble, and furniture polyurethane Brilliant white paint bubble for producing in construction can be suppressed.Preferably, carried in the present invention
In one embodiment of confession, defoamer can be used but be not limited to modified siloxane copolymer solution.Specifically such as：This moral of hamming is modest
The trade mark is 5300 product.
In the present invention, the effect of levelling agent is the surface tension for reducing furniture polyurethane Brilliant white paint so that
Furniture polyurethane Brilliant white paint after construction, can the Self-leveling after ground wetting more quickly, and will not produce
The morbid state phenomenon such as orange peel, shrinkage cavity.Preferably, in one embodiment that the present invention is provided, levelling agent can be used but is not limited to
Fluorin modified crylic acid ester solution, specifically such as：The EFKA company trade mark is the product of EFKA3600.
In the present invention, the effect of dispersant is when shortening the dispersion of white slurry in furniture polyurethane Brilliant white paint
Between, the gloss of the paint film that furniture polyurethane Brilliant white paint is formed in construction is improved, its tinting strength, tinting power and covering power are improved, change
It is apt to its color developing and toning property, prevents floating, prevents from flocculating and settle.Specifically such as：The Bi Ke companies trade mark is 110 product
Product.
In the present invention, titanium dioxide and nanometer potassium aluminosilicate powder are the filler systems of furniture polyurethane Brilliant white paint,
Also it is the key component of white slurry, in addition to incremental contribution, also with some property for improving furniture polyurethane Brilliant white paint
The effect of energy, such as controls rheological characteristic, improves adhesive force, control gloss, raising covering power, prevent from corroding and optimizing pigment product concentration
Deng, and because nanometer potassium aluminosilicate powder is the laminated structure of Nano grade, being capable of applying in the furniture polyurethane light fine flour
Paint film is supported during work well, and effectively reduces the generation of particulate material.Specifically such as：The trade mark of E.I.Du Pont Company is R-
900 product (titanium dioxide), the trade mark of Wan Tai companies is the product (nanometer potassium aluminosilicate powder) of FS08.
In the present invention, the effect of curing agent is the synthetic fatty acid with host in furniture polyurethane Brilliant white paint
Resin is crosslinked, and improves the gloss stability of the paint film that furniture polyurethane Brilliant white paint is formed in construction, specifically,
Toluene diisocyanate trimer and hexamethylene diisocyanate trimer can be dissolved in butyl acetate as curing agent.
In the present invention, the effect of diluent is that the host in furniture polyurethane Brilliant white paint is entered with curing agent
Row dilution reconciles, and further promotes dissolving of other components in diluent, can specifically include butyl acetate, dimethylbenzene with
And propylene glycol methyl ether acetate.
Further, on the basis of the explanation of above-mentioned each component, in order that obtain furniture polyurethane Brilliant white paint having
Preferable painting effect, in the present invention, it is preferred to, in terms of parts by weight, can prepare obtain furniture with following formula
Use polyurethane Brilliant white paint：Host is 1 part, and curing agent is 0.8 to 1 part, and diluent is 0.3 to 0.4 part.
Specifically, in actual applications, it is determined that after formula of the furniture with polyurethane Brilliant white paint, can use following
Preparation method is prepared：
1st, white slurry is made：It is determined that after container cleaning used is pollution-free, synthctic fat acid resin is first put into, and in stirring at low speed
Lower addition dispersant, then disperse 10 to 15 minutes fineness to mixture to be less than 15 microns mixture middling speed, in stirring at low speed
It is lower to add titanium dioxide and nanometer potassium aluminosilicate powder, then dispersion 10 to 15 minutes at a high speed, and butyl acetate is added under the low speed, will make
The white slurry for obtaining is by white slurry:Zirconium pearl=1:After 1.5 mass ratio mixing, the fineness of white slurry is ground to less than 15 microns, be filtrated to get
Final white slurry.
2nd, host is made：It is determined that after container cleaning used is pollution-free, synthctic fat acid resin is first put into, under stirring at low speed
Defoamer, levelling agent are sequentially added, middling speed disperses 10 to 15 minutes fineness to mixture to be less than 25 microns, under stirring at low speed
10 to 15 minutes fineness of dispersion are less than 25 microns at a high speed to add white slurry, and butyl acetate is added under low speed.
3rd, curing agent is made：By toluene diisocyanate trimer, hexamethylene diisocyanate trimer, butyl acetate
It is well mixed according to the first preset ratio.
4th, diluent is made：Butyl acetate, dimethylbenzene, propylene glycol methyl ether acetate are mixed equal according to the second preset ratio
It is even.
5th, the host of above-mentioned making, curing agent and diluent are stirred according to respective ratio and is mixed, obtained furniture and use poly-
Urethane Brilliant white paint.
In the present embodiment, after furniture is obtained with polyurethane Brilliant white paint, can be to furniture polyurethane Brilliant white paint
Spray plate observation is carried out on ground, corresponding paint film property is detected.
In the embodiment of the present invention, it is main body to use synthctic fat acid resin, and titanium dioxide collocation nanometer potassium aluminosilicate powder is to fill out
Material system.Then because synthctic fat acid resin has more plentiful plate face effect in itself, such that it is able to improve the plentiful of paint film
Degree, and titanium dioxide and nanometer potassium aluminosilicate powder for paint film while whiteness is provided, it is possible to have preferable fillibility so that
The ability that paint film covers sand trace is greatly promoted, and because nanometer potassium aluminosilicate powder is the laminated structure of Nano grade, can be at this
Paint film is supported well in the paint work progress of furniture polyurethane light fine flour, hence it is evident that is reduced the disadvantages such as dark bubble, pin hole, is entered
One step improves the levelling effect of paint film.Additionally, nanometer potassium aluminosilicate powder is due to its superpower weatherability, and titanium dioxide collocation energy
Significantly strengthen the anti-yellowing property of paint film.
For the sake of becoming apparent from, it is described in detail below by following examples, wherein, synthctic fat acid resin is purchased from knob
Pei Si companies, product grade is 2848；Levelling agent is purchased from EFKA company, and product grade is EFKA3600；Defoamer is purchased from sea
The modest companies of Ming Side, product grade is 5300；Purchased from Bi Ke chemistry, product grade is BYK110 to dispersant；Titanium dioxide is purchased from Du
Company of nation, product grade is R-900；Nanometer potassium aluminosilicate powder is purchased from Wan Tai companies, and product grade is FS08；Toluene diisocynate
Ester tripolymer, hexamethylene diisocyanate trimer are purchased from Beyer Co., Ltd；Butyl acetate, dimethylbenzene, propylene glycol monomethyl ether acetic acid
Ester is purchased from happy up to company.
Embodiment 1
Get the raw materials ready：The host of 100 weight portions, the curing agent of 80 weight portions, the diluent of 30 weight portions；
Wherein, host includes：The synthctic fat acid resin of 25 weight portions, the butyl acetate of 2 weight portions, 0.3 weight portion
Defoamer, the levelling agent of 0.2 weight portion, the white slurry of 72.5 weight portions；
White slurry includes：The synthctic fat acid resin of 35 weight portions, the butyl acetate of 4.2 weight portions, the dispersion of 0.8 weight portion
Agent, the titanium dioxide of 50 weight portions, the nanometer potassium aluminosilicate powder of 10 weight portions；
Curing agent includes：The toluene diisocyanate trimer of 40 weight portions, the isocyanic acid of hexa-methylene two of 30 weight portions
Ester tripolymer, the butyl acetate of 30 weight portions；
Diluent includes：The butyl acetate of 25 weight portions, the dimethylbenzene of 30 weight portions, the propylene glycol monomethyl ether vinegar of 45 weight portions
Acid esters.
Embodiment 2
Get the raw materials ready：The host of 100 weight portions, the curing agent of 80 weight portions, the diluent of 30 weight portions；
Wherein, host includes：The synthctic fat acid resin of 28.3 weight portions, the ethyl acetate of 4 weight portions, 0.1 weight portion
Defoamer, the levelling agent of 0.1 weight portion, the white slurry of 67.5 weight portions；
White slurry includes：The synthctic fat acid resin of 35 weight portions, the butyl acetate of 4.2 weight portions, the dispersion of 0.8 weight portion
Agent, the titanium dioxide of 55 weight portions, the nanometer potassium aluminosilicate powder of 5 weight portions；
Curing agent includes：The toluene diisocyanate trimer of 50 weight portions, the isocyanic acid of hexa-methylene two of 20 weight portions
Ester tripolymer, the butyl acetate of 30 weight portions；
Diluent includes：The butyl acetate of 40 weight portions, the dimethylbenzene of 25 weight portions, the propylene glycol monomethyl ether vinegar of 35 weight portions
Acid esters.
Embodiment 3
Get the raw materials ready：The host of 100 weight portions, the curing agent of 100 weight portions, the diluent of 40 weight portions；
Wherein, host includes：The synthctic fat acid resin of 30 weight portions, the ethyl acetate of 2.3 weight portions, 0.1 weight portion
Defoamer, the levelling agent of 0.1 weight portion, the white slurry of 67.5 weight portions；
White slurry includes：The synthctic fat acid resin of 40 weight portions, the butyl acetate of 4 weight portions, the dispersion of 0.9 weight portion
Agent, the titanium dioxide of 50 weight portions, the nanometer potassium aluminosilicate powder of 5.1 weight portions；
Curing agent includes：The toluene diisocyanate trimer of 50 weight portions, the isocyanic acid of hexa-methylene two of 30 weight portions
Ester tripolymer, the butyl acetate of 20 weight portions；
Diluent includes：The butyl acetate of 35 weight portions, the dimethylbenzene of 25 weight portions, the propylene glycol monomethyl ether vinegar of 40 weight portions
Acid esters.
The formula rate of above weight portion is respectively prepared furniture polyurethane light by above-mentioned provided preparation method
After white finish paint, can be constructed according to the mode of hand spray, it is possible to according to HG/T2454-200《Solvent borne polyurethane is applied
Material (bi-component)》And GB 18581-2001《Limits of harmful substances in indoor decorating and refurnishing materials solvent wood coatings》To applying
Work effect detection, measured data result is as follows：
Table 1
It is apparent to those skilled in the art that, in several embodiments provided herein, it should
It is understood that disclosed product and method, can realize by another way.Above example is only used to illustrate of the invention
Technical scheme, rather than its limitations；Although being described in detail to the present invention with reference to the foregoing embodiments, this area it is common
Technical staff should be understood：It can still modify to the technical scheme described in foregoing embodiments, or to wherein
Some technical characteristics carry out equivalent；And these modifications or replacement, the essence of appropriate technical solution is departed from this hair
The spirit and scope of bright each embodiment technical scheme.
Claims (4)
1. a kind of furniture polyurethane Brilliant white paint, the Brilliant white paint includes host, curing agent and diluent, its feature
It is,
In terms of parts by weight, the host includes：
Wherein, in terms of parts by weight, the white slurry includes：
In terms of parts by weight, the curing agent includes：
40 to 50 parts of toluene diisocyanate trimer；
20 to 30 parts of hexamethylene diisocyanate trimer；
20 to 30 parts of the butyl acetate；
In terms of parts by weight, the diluent includes：
25 to 40 parts of the butyl acetate；
25 to 30 parts of dimethylbenzene；
35 to 45 parts of propylene glycol methyl ether acetate.
2. furniture according to claim 1 polyurethane Brilliant white paint, it is characterised in that the levelling agent is fluorine richness
Acrylate solution.
3. furniture according to claim 1 polyurethane Brilliant white paint, it is characterised in that the defoamer is modified silicon
Siloxane copolymers solution.
4. furniture according to any one of claim 1 to 3 polyurethane Brilliant white paint, it is characterised in that with weight
Number meter, the host is 1 part, and the curing agent is 0.8 to 1 part, and the diluent is 0.3 to 0.4 part.