CN107900266A - A kind of forging technology of machinery forging - Google Patents
A kind of forging technology of machinery forging Download PDFInfo
- Publication number
- CN107900266A CN107900266A CN201711114281.3A CN201711114281A CN107900266A CN 107900266 A CN107900266 A CN 107900266A CN 201711114281 A CN201711114281 A CN 201711114281A CN 107900266 A CN107900266 A CN 107900266A
- Authority
- CN
- China
- Prior art keywords
- forging
- temperature
- accessory
- embryo material
- machinery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of forging technology of mechanical forging, it is characterised in that as follows including step:(1) sorting:Select embryo material;(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature are taken as 1000~1200 DEG C, pressure is applied to blank using metal forming machinery, produce plastic deformation so that its internal loose fine grain compacting, so that reaching the tool performance for improving accessory;(3) cool down:Cooldown rate is 45 50 DEG C/min;(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that the surfaces externally and internally of accessory all covers the zinc ion that can prevent surface oxidisation.The beneficial effects of the invention are as follows:The difficulty and equipment cost of processing are reduced, production efficiency is higher, good mechanical property, can meet the requirement of long-time service.
Description
Technical field
The invention belongs to field of mechanical technique, and in particular to a kind of forging technology of machinery forging.
Background technology
Forging can fast, easily make the blank part that is not much different with required part, with forge come blank part
Finish again, part production yields can be accelerated, be a kind of convenient and practical mode of production.
Forging technology is one of industrial important technology, is widely used in the fields such as Aeronautics and Astronautics, machinery, shipbuilding.
Forging technology is that one kind applies pressure using forging machinery to metal stock, it is produced plastic deformation to obtain with certain machine
The processing method of the forging parts of tool performance, definite shape and size.
But existing forging is after forging, there are the problem of surface smoothness is poor, finish is low, structural strength is insufficient, and
It is particularly important that heat treatment mode of forging influences the structural strength of forging.
The content of the invention
To solve the above-mentioned problems, the present invention provides a kind of forging technology of mechanical forging, and step is as follows:
(1) sorting:Select embryo material;
(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature
1000~1200 DEG C are taken as, pressure is applied to blank using metal forming machinery, produces plastic deformation so that it is internal loose thin
Crystal grain is compacted, so that reaching the tool performance for improving accessory;
(3) cool down:Cooldown rate is 45-50 DEG C/min;
(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that accessory
Surfaces externally and internally all covers the zinc ion that can prevent surface oxidisation.
Preferably, electric furnace temperature is 1200 DEG C in the step (2).
Preferably, cooldown rate is 45 DEG C/min in step (3).
The beneficial effects of the invention are as follows:The difficulty and equipment cost of processing are reduced, production efficiency is higher, mechanical performance
It is good, it can meet the requirement of long-time service.
Embodiment
A kind of forging technology of mechanical forging of the present invention is illustrated using embodiment below.
Embodiment 1:
A kind of forging technology of machinery forging, step are as follows:
(1) sorting:Select embryo material;
(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature
1200 DEG C are taken as, pressure is applied to blank using metal forming machinery, produces plastic deformation so that its internal loose fine grain pressure
It is real, so that reaching the tool performance for improving accessory;
(3) cool down:Cooldown rate is 45 DEG C/min;
(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that accessory
Surfaces externally and internally all covers the zinc ion that can prevent surface oxidisation.
Embodiment 2:
A kind of forging technology of machinery forging, step are as follows:
(1) sorting:Select embryo material;
(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature
1000 DEG C are taken as, pressure is applied to blank using metal forming machinery, produces plastic deformation so that its internal loose fine grain pressure
It is real, so that reaching the tool performance for improving accessory;
(3) cool down:Cooldown rate is 45 DEG C/min;
(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that accessory
Surfaces externally and internally all covers the zinc ion that can prevent surface oxidisation.
Embodiment 3:
A kind of forging technology of machinery forging, step are as follows:
(1) sorting:Select embryo material;
(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature
1200 DEG C are taken as, pressure is applied to blank using metal forming machinery, produces plastic deformation so that its internal loose fine grain pressure
It is real, so that reaching the tool performance for improving accessory;
(3) cool down:Cooldown rate is 50 DEG C/min;
(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that accessory
Surfaces externally and internally all covers the zinc ion that can prevent surface oxidisation.
The technical solution provided above the embodiment of the present invention is described in detail, specific case used herein
The principle and embodiment of the embodiment of the present invention are set forth, the explanation of above example is only applicable to help and understands this
The principle of inventive embodiments;Meanwhile for those of ordinary skill in the art, according to the embodiment of the present invention, in specific embodiment party
There will be changes in formula and application range, in conclusion this specification content should not be construed as limiting the invention.
Claims (3)
1. a kind of forging technology of machinery forging, it is characterised in that as follows including step:
(1) sorting:Select embryo material;
(2) heat:It is 1000~1500 DEG C that embryo material, which is sent into electric furnace to temperature, it is contemplated that temperature increasing by deformation, heating-up temperature are taken as
1000~1200 DEG C, pressure is applied to blank using metal forming machinery, produces plastic deformation so that its internal loose fine grain
Compacting, so that reaching the tool performance for improving accessory;
(3) cool down:Cooldown rate is 45-50 DEG C/min;
(4) it is surface-treated:The melting that forging after cooling is put into design temperature is had in the coating bath of zinc so that accessory it is inside and outside
Surface all covers the zinc ion that can prevent surface oxidisation.
2. the forging technology of a kind of mechanical forging according to claim 1, it is characterised in that electricity adds in the step (2)
Hot stove temperature is 1200 DEG C.
A kind of 3. forging technology of mechanical forging according to claim 1, it is characterised in that cooling in the step (3)
Speed is 45 DEG C/min.