CN107881369A - 铝钙锑中间合金孕育剂及其制备方法 - Google Patents

铝钙锑中间合金孕育剂及其制备方法 Download PDF

Info

Publication number
CN107881369A
CN107881369A CN201711023599.0A CN201711023599A CN107881369A CN 107881369 A CN107881369 A CN 107881369A CN 201711023599 A CN201711023599 A CN 201711023599A CN 107881369 A CN107881369 A CN 107881369A
Authority
CN
China
Prior art keywords
antimony
aluminium
intermediate alloy
preparation
calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711023599.0A
Other languages
English (en)
Other versions
CN107881369B (zh
Inventor
于宏辰
宁玉恒
孙旭
尤洋
孙越
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Datang Northeast Electric Power Test and Research Institute Co Ltd
Original Assignee
Datang Northeast Electric Power Test and Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Datang Northeast Electric Power Test and Research Institute Co Ltd filed Critical Datang Northeast Electric Power Test and Research Institute Co Ltd
Priority to CN201711023599.0A priority Critical patent/CN107881369B/zh
Publication of CN107881369A publication Critical patent/CN107881369A/zh
Application granted granted Critical
Publication of CN107881369B publication Critical patent/CN107881369B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于细化铝‑镁‑硅合金中初生、共晶Mg2Si晶粒的中间合金孕育剂及其制备方法，铝钙锑中间合金孕育剂，各元素化学质量百分比为：铝60，钙10‑20，锑20‑30。其制备方法为：在二氧化碳气体的保护下，将一定量的纯铝700℃进行熔化，然后将铝钙合金(Al‑40Ca)和纯锑同时加入到熔体中，完全熔化后进行搅拌，随后浇铸成锭或挤压成线材。该中间合金具有制备方法简单、使用方便、变质效果稳定、具有长效性等优点。

Description

铝钙锑中间合金孕育剂及其制备方法
技术领域
本发明涉及金属材料领域，特别是涉及一种用于细化铝-镁-硅合金中初生、共晶Mg2Si晶粒的中间合金孕育剂及其制备方法。
背景技术
金属间化合物Mg2Si具有低密度、高熔点、高弹性模量和低热膨胀系数等优点而普遍作为铝合金材料的增强体。然而，在传统铸造的铝-镁-硅合金中，初生Mg2Si通常呈现为粗大的树枝晶，割裂基体、产生应力集中，严重损害了合金的力学性能，限制了其广泛应用。虽然中间合金变质剂的加入可以细化初生、共晶Mg2Si的晶粒，但其用量大、晶粒细化效果欠佳等缺点限制了该技术在工业生产上的应用。熔体中异质核心的存在，可以在形核阶段促进晶体核心的形成，从而有效细化晶粒。
因此，急需开发一种制备工艺简单、可靠且能够有效细化铝镁硅合金中初生、共晶Mg2Si晶粒的中间合金孕育剂。
发明内容
为解决上述技术问题，本发明的目的是提供一种制备工艺简单、可靠且能够有效细化铝-镁-硅合金中初生、共晶Mg2Si晶粒的铝-钙-锑中间合金孕育剂及其制备方法。
本发明的技术方案是：
铝钙锑中间合金孕育剂，其化学成分质量百分比为：铝60，钙10-20，锑20-30。
用于制备铝钙锑中间合金孕育剂的方法，其制备过程包括以下步骤：
首先，分别按质量百分比称取原材料：纯铝30-45％，铝钙合金(Al-40Ca)25-50％，纯锑20-30％；
其次，在二氧化碳气体保护下的熔炼炉中将纯铝熔化至700℃，然后将铝钙合金(Al-40Ca)、纯锑同时加入，待完全熔化后搅拌均匀；
最后，浇铸成锭或挤压成线材。
本发明与已有的技术相比具有以下特点：(1)钙、锑可以在熔体中形成初生Mg2Si异质核心，有效细化晶粒；(2)所制备合金易在熔化和分散，使用方便；(3)加入量少，在钙、锑加入量均小于0.3％的情况下，初生Mg2Si的晶粒尺寸从～300μm减小到～8μm；形貌由粗大的树枝晶转变为细小的切角八面体；共晶Mg2Si由粗大的汉字状转变为细小的短棒状；(4)变质效果稳定，具有长效性。
附图说明
图1是本发明未变质Al-20Mg2Si合金光镜组织；
图2是本发明0.5wt.％Al60Ca20Sb20合金变质后Al-20Mg2Si合金光镜组织；
图3是本发明0.5wt.％Al60Ca10Sb30合金变质后Al-20Mg2Si合金光镜组织；
图4是本发明0.5wt.％Al60Ca15Sb25合金变质后Al-20Mg2Si合金光镜组织。
具体实施方式
下面结合附图和实施例，对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例1
制备铝钙锑中间合金孕育剂的方法，其制备过程包括以下步骤：
(1)分别按质量百分比称取原材料为：纯铝30％，铝钙合金(Al-40Ca)50％，纯锑20％；
(2)在二氧化碳气体保护下的熔炼炉中将纯铝700℃熔化，然后将铝钙合金(Al-40Ca)、纯锑同时加入，待完全熔化后搅拌均匀；
(3)浇铸成锭制得Al60Ca20Sb20合金。
实施例2
用于制备铝钙锑中间合金孕育剂的方法，其制备过程包括以下步骤：
(1)分别按质量百分比称取原材料为：纯铝45％，铝钙合金(Al-40Ca)25％，纯锑30％；
(2)在二氧化碳气体保护下的熔炼炉中将纯铝700℃熔化，然后将铝钙合金(Al-40Ca)、纯锑同时加入，待完全熔化后搅拌均匀；
(3)浇铸成锭制得Al60Ca10Sb30合金。
实施例3
用于制备铝钙锑中间合金孕育剂的方法，其制备过程包括以下步骤：
(1)分别按质量百分比称取原材料为：纯铝37.5％，铝钙合金(Al-40Ca)37.5％，纯锑25％；
(2)在二氧化碳气体保护下的熔炼炉中将纯铝700℃熔化，然后将铝钙合金(Al-40Ca)、纯锑同时加入，待完全熔化后搅拌均匀；
(3)浇铸成锭后挤压成线材制得Al60Ca15Sb25合金。

Claims (2)

1.一种铝钙锑中间合金孕育剂，其特征在于，其化学成分质量百分比为：铝60份，钙10-20份，锑20-30份。
2.一种用于制备铝钙锑中间合金孕育剂的方法，其特征在于，制备过程包括以下步骤：
首先，分别按质量百分比称取原材料：纯铝30-45份，铝钙合金(A l-40Ca)25-50份，纯锑20-30份；
其次，在二氧化碳气体保护下的熔炼炉中将纯铝熔化至700oC，然后将铝钙合金(Al-40Ca)、纯锑同时加入，待完全熔化后搅拌均匀；
最后，浇铸成锭或挤压成线材。
CN201711023599.0A 2017-10-27 2017-10-27 铝钙锑中间合金孕育剂及其制备方法 Active CN107881369B (zh)