CN107869066A - A kind of dyeing and finishing technology of high-grade people's cotton face fabric - Google Patents
A kind of dyeing and finishing technology of high-grade people's cotton face fabric Download PDFInfo
- Publication number
- CN107869066A CN107869066A CN201711272798.5A CN201711272798A CN107869066A CN 107869066 A CN107869066 A CN 107869066A CN 201711272798 A CN201711272798 A CN 201711272798A CN 107869066 A CN107869066 A CN 107869066A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- agent
- people
- finishing
- face fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of dyeing and finishing technology of high-grade people's cotton face fabric, including to the described high-grade woven people's cotton face fabric dyeing pretreatment of primary, antistatic and anti-crease finishing, boiling is subjected to dyestuff with the high-grade woven people's cotton face fabric of primary after sizing and pulls out print, immerse in dyeing liquor, described dyeing liquor includes 1ml/L coloring agent, 1ml/L chelating agent；It is warming up to 40 50 DEG C, 20 30min are steamed in the rapid steamer gas that steam pressure is 2kg, curve rises to 50 60 DEG C, is incubated 10min, adds salt and soda ash, salt is equal with the quality of soda ash, it is to be warming up to 60 70 DEG C for 3 5g/L, then curve, is incubated 10min, color fixing agent is being added, is then being post-processed.The present invention method obtain pull out printing and dyeing dyeing defect third dimension it is strong, dyestuff is firm, and moisture permeable anti-ultraviolet effect reaches satisfied degree, and Color is good.
Description
Technical field
The present invention relates to fabric finishing technical field, more particularly to a kind of dyeing and finishing technology of high-grade people's cotton face fabric.
Background technology
Pursued in modern textile and develop excellent regeneration natural plant fibre fabric, improved natural plant fibre and knit
The einnehmen function of thing, for meeting the needs of market, and people's cotton fabrics have special advantage, and spun rayon piece goods is dyed and met
The bigger market demand.The dyeing of spun rayon piece goods dyeing and finishing method is insecure in the prior art, especially middle deep colour dyeing skill deficiency,
Staining procedure is complicated.Moisture permeable anti-ultraviolet effect does not reach satisfied degree for another example, consumer to the feature of garment material,
Comfortableness, health, the feature of environmental protection and health have higher requirement, and penetrability, the uvioresistant of clothes have become people's purchase
Buy the preferred factor of clothes.And traditional dress fabric function is single, class is not high, and comfort level is poor, and its added value is not also high, it is impossible to
Meets the needs of people are to clothes.In addition, existing spun rayon piece goods dyeing and finishing method, is to use reactive dye direct printing mostly,
Small design of scattered small flowers and plants type market can receive, but encounter dark bottom, and light little Hua flower pattern, printing effect Fuzzy and Rough, third dimension is poor,
Market reaction is very undesirable.
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of flower pattern for allowing dark bottom light color flower and obtains very strong solid
The spun rayon piece goods of sense pulls out the dyeing and finishing method of print, reaches feature, comfortableness, health, the feature of environmental protection and the health of garment material
Requirement, it is and good with moisture permeable anti-ultraviolet effect, and middle deep colour dyeing is firm.
Concrete scheme is as follows：A kind of dyeing and finishing technology of high-grade people's cotton face fabric, comprises the following steps：(1) using dacron thread with
Spun rayon yarn twists compound twist yarn into line, forms primary high-grade woven people's cotton face fabric, the weight ratio of wherein dacron thread and spun rayon yarn is
3-5:10；(2) to the described high-grade woven people's cotton face fabric dyeing pretreatment of primary：By the described high-grade woven people's cotton face fabric of primary
Boiling in dyeing preprocessing solution is placed on, the temperature of described dyeing pretreatment is 50 DEG C -60 DEG C, and the solution includes defoaming
Agent 0.15-0.20g/L, dispersant 4-5g/L, bleeding agent 4-6g/L, sulfuric acid 0.10-0.20g/L, bleaching powder 0.10-0.20g/L,
Sodium carbonate 1-3g/L, hydrogen peroxide 3-10g/L, glacial acetic acid 0.20-0.40g/L, sodium phosphate 0.15-0.25g/L, turkey red oil 0.15-
0.25g/L, the time of described dyeing pretreatment is 10-50min；People's cotton fabrics semi-finished product after boiling are imported into overflow machine
In and cold wash export, and shape；(3) antistatic and anti-crease finishing：Fabric after shaping in step (2) is added into 10-15g/L to resist
Antistatic finish and 1.3-1.7g/L softness crease-shedding finishing agents, mangle handles 50-60m/min at 60-90 DEG C；(4) by boiling
Dyestuff is carried out with the high-grade woven people's cotton face fabric of primary after sizing and pulls out print, that is, is immersed in dyeing liquor, described dyeing liquor includes
1ml/L coloring agent, 1ml/L chelating agent；40-50 DEG C is warming up to, steams 20- in the rapid steamer gas that steam pressure is 2kg
30min, curve rise to 50-60 DEG C, are incubated 10min, add salt and soda ash, and salt is equal with the quality of soda ash, be for
3-5g/L, then curve are warming up to 60-70 DEG C, are incubated 10min, are adding color fixing agent, the color fixing agent 2-5g/L, then curve heating
To 70-80 DEG C, 10min is incubated, the Boratex that concentration is 8-10g/L is added and carries out reduction washing, dry；(5) post-process：Through
Cross high-grade woven people's cotton face fabric that step (4) dyestuff is pulled out after printing and be put into 1g/L romote antiquity oil solution and soften 25-30h, in institute
The soda ash that 3-5ml/L is added in romote antiquity oil solution is stated, is then taken out and is cleaned and dry, that is, obtains high-grade woven people's cotton face fabric.
Further, the defoamer is OPEO.
Further, described coloring agent is intellectual circle and rongalite batch mixing dyestuff, the quality of the rongalite and intellectual circle it
Than for 1:1.
Further, dispersant is alkyl alcohol ether mono sulfosuccinates.
It is preferred that described bleeding agent is sulfated castor oil.
It is preferred that main component is calcium hypochlorite in described bleaching powder, the bleaching powder available chlorine content is 20-28
(wt) %.
It is preferred that antistatic finishing agent is triethanolamine.
It is preferred that described chelating agent is chelating agent GD-108 or hydroxycarboxylic acid.
It is preferred that it is that amino silicone modified organic silicon copolymer emulsion or softness are crease-resistant that soft crease-shedding finishing agent, which is antistatic finishing agent,
Finishing agent JPBC.
Further, main component is calcium hypochlorite in described bleaching powder, and the bleaching powder available chlorine content is 25
(wt) %.
Described color fixing agent is brocide.
Further, step (1) twists compound twist yarn into line using dacron thread and spun rayon yarn, forms primary high-grade woven people
The weight ratio of cotton face fabric, wherein dacron thread and spun rayon yarn is 2:5.The temperature of dyeing pretreatment described in step (2) is 55 DEG C,
The solution includes defoamer 0.15g/L, dispersant 5g/L, bleeding agent 5g/L, sulfuric acid 0.20g/L, bleaching powder 0.10g/L, carbon
Sour sodium 3g/L, hydrogen peroxide 8g/L, glacial acetic acid 0.40g/L, sodium phosphate 0.15g/L, turkey red oil 0.15g/L, described dyeing are located in advance
The time of reason is 20min, and step (3) is antistatic and anti-crease finishing：Fabric addition 15g/L after being shaped in step (2) resists quiet
Electric finishing agent and 1.3g/L softness crease-shedding finishing agent, mangle handles 60m/min at 60 DEG C, and step (5) passes through step (4) dyestuff
Pull out high-grade woven people's cotton face fabric after print and be put into 1g/L romote antiquity oil solution and soften 28h, in the romote antiquity oil solution
4ml/L soda ash is added, boiling is carried out dyestuff with the high-grade woven people's cotton face fabric of primary after sizing and pull out print, that is, soaked by step (4)
Enter in dyeing liquor, described dyeing liquor includes 1ml/L coloring agent, 1ml/L chelating agent；50 DEG C are warming up to, in steam pressure
30min is steamed for 2kg rapid steamer gas, curve rises to 50 DEG C, is incubated 10min, adds the matter of salt and soda ash, salt and soda ash
Measure equal, be for 5g/L, then curve is warming up to 70 DEG C, is incubated 10min, is adding color fixing agent, the color fixing agent 3g/L, then bent
Line is warming up to 80 DEG C, is incubated 10min, adds the Boratex that concentration is 8g/L and carries out reduction washing, dries, described chelating agent
For hydroxycarboxylic acid, described soft crease-shedding finishing agent is amino silicone modified organic silicon copolymer emulsion.
Beneficial effects of the present invention are：The present invention is antistatic finishing agent using soft crease-shedding finishing agent, reaches increase color
The turgor in pool, makes gloss simple and honest, increases the feel of fabric, the effect for more having imitative hair.The present invention is using dacron thread and people cotton
The compound twist yarn of yarn twisting forms primary high-grade woven people's cotton face fabric, moisture permeable anti-ultraviolet effect reaches satisfied degree, energy into line
Meet requirement of the consumer to the feature of garment material, comfortableness, health, the feature of environmental protection and health.At dyeing and fixation
Reason, reaches that Color is good, and dyestuff is firm, good permeability, it is ensured that and it is clearly firm to pull out the lines of the decorative pattern of the printing of print technique,
Reduce defective product, feel is good, greatly meets the needs of client.
Embodiment
The present invention is further described in detail with reference to specific embodiment.
Embodiment 1
A kind of dyeing and finishing technology of high-grade people's cotton face fabric, comprises the following steps：(1) twisted using dacron thread with spun rayon yarn compound
Twist yarn forms primary high-grade woven people's cotton face fabric, the wherein weight ratio of dacron thread and spun rayon yarn is 5 into line:10；(2) to described
The high-grade woven people's cotton face fabric dyeing pretreatment of primary：The described high-grade woven people's cotton face fabric of primary is placed on dyeing pretreatment
Boiling in solution, the temperature of described dyeing pretreatment is 60 DEG C, and the solution includes defoamer 0.20g/L, the defoamer
For OPEO, dispersant is alkyl alcohol ether mono sulfosuccinates 5g/L, and bleeding agent is sulphation castor
Main component is calcium hypochlorite in sesame oil 6g/L, sulfuric acid 0.20g/L, bleaching powder 0.20g/L, bleaching powder, and the bleaching powder is effective
Chlorinity is 28 (wt) %., sodium carbonate 3g/L, hydrogen peroxide 10g/L, glacial acetic acid 0.40g/L, sodium phosphate 0.25g/L, turkey red oil
0.25g/L, the time of described dyeing pretreatment is 50min；People's cotton fabrics semi-finished product after boiling are imported in overflow machine
And cold wash exports, and shape；(3) antistatic and anti-crease finishing：It is antistatic that fabric after being shaped in step (2) is added into 15g/L
Finishing agent and 1.7g/L softness crease-shedding finishing agents, antistatic finishing agent are triethanolamine, and soft crease-shedding finishing agent changes for amino silicone
Property organosilicon copolymer emulsion, at 90 DEG C mangle handle 60m/min；(4) by boiling and the high-grade woven people cotton of primary after sizing
Fabric carries out dyestuff and pulls out print, that is, immerses in dyeing liquor, and described dyeing liquor includes 1ml/L coloring agent, coloring agent for intellectual circle with
The mass ratio of rongalite batch mixing dyestuff, the rongalite and intellectual circle are 1:1,1ml/L chelating agent, chelating agent are hydroxyl carboxylic
Acid, 50 DEG C are warming up to, steam 30min in the rapid steamer gas that steam pressure is 2kg, curve rises to 60 DEG C, is incubated 10min, adds
Salt and soda ash, salt is equal with the quality of soda ash, is 5g/L, then curve is warming up to 70 DEG C, is incubated 10min, solid adding
Toner brocide, the color fixing agent 5g/L, then curve are warming up to 80 DEG C, are incubated 10min, adding concentration is
10g/L Boratex carries out reduction washing, drying；(5) post-process：High-grade woven people cotton after step (4) dyestuff pulls out print
Fabric, which is put into 1g/L romote antiquity oil solution, softens 30h, 5ml/L soda ash is added in the romote antiquity oil solution, then
Take out and clean and dry, that is, obtain high-grade woven people's cotton face fabric.
Embodiment 2
A kind of dyeing and finishing technology of high-grade people's cotton face fabric, comprises the following steps：(1) twisted using dacron thread with spun rayon yarn compound
Twist yarn forms primary high-grade woven people's cotton face fabric, the wherein weight ratio of dacron thread and spun rayon yarn is 3 into line:10；(2) to described
The high-grade woven people's cotton face fabric dyeing pretreatment of primary：The described high-grade woven people's cotton face fabric of primary is placed on dyeing pretreatment
Boiling in solution, the temperature of described dyeing pretreatment is 50 DEG C, and the solution includes defoamer 0.15g/L, the defoamer
For OPEO, dispersant 4g/L, dispersant are alkyl alcohol ether mono sulfosuccinates, bleeding agent 4g/
L, bleeding agent is sulfated castor oil, and main component is calcium hypochlorite in sulfuric acid 0.10g/L, bleaching powder 0.10g/L, bleaching powder,
The bleaching powder available chlorine content is 20 (wt) %., sodium carbonate 1g/L, hydrogen peroxide 3g/L, glacial acetic acid 0.20g/L, sodium phosphate
0.15g/L, turkey red oil 0.15g/L, the time of described dyeing pretreatment is 10min；By people's cotton fabrics after boiling half into
Product import in overflow machine and cold wash export, and shape；(3) antistatic and anti-crease finishing：Fabric after being shaped in step (2) is added
Enter 10-15g/L antistatic finishing agents and 1.3g/L softness crease-shedding finishing agents, antistatic finishing agent is triethanolamine, soft crease-resistant
Finishing agent is amino silicone modified organic silicon copolymer emulsion, and mangle handles 50m/min at 60 DEG C；(4) by after boiling and sizing
Primary high-grade woven people's cotton face fabric carries out dyestuff and pulls out print, that is, immerses in dyeing liquor, described dyeing liquor includes 1ml/L dyeing
Agent, coloring agent are intellectual circle and rongalite batch mixing dyestuff, and the mass ratio of the rongalite and intellectual circle are 1:1,1ml/L chelating
Agent, chelating agent are hydroxycarboxylic acid；40 DEG C are warming up to, steams 30min in the rapid steamer gas that steam pressure is 2kg, curve rises to 50 DEG C,
10min is incubated, adds salt and soda ash, salt is equal with the quality of soda ash, is 4g/L, then curve is warming up to 60 DEG C, protects
Warm 10min, 70 DEG C are warming up to adding color fixing agent brocide, the color fixing agent 2g/L, then curve, insulation
10min, add the Boratex that concentration is 8g/L and carry out reduction washing, dry；(5) height after step (4) dyestuff pulls out print
The woven people's cotton face fabric of shelves, which is put into 1g/L romote antiquity oil solution, softens 25h, adds 3ml/L's in the romote antiquity oil solution
Soda ash, then take out and clean and dry, that is, obtain high-grade woven people's cotton face fabric.
| Embodiment 1 | Embodiment 2 | |
| Radially strength, N | 1090 | 1120 |
| Broadwise strength, N | 1140 | 1205 |
| Dyestuff pulls out print firmness | Firmness is excellent | Firmness is excellent |
| Colour fasteness to rubbing | Color fastness is excellent | Color fastness is excellent |
Embodiment above is only the preferred embodiment of this creation, all in this wound not to limit this creation
Any modification, equivalent substitution and improvements for being done etc. within the spirit and principle of work, should be included in this creation protection domain it
It is interior.
Claims (9)
1. a kind of dyeing and finishing technology of high-grade people's cotton face fabric, it is characterised in that comprise the following steps：(1) using dacron thread and people cotton
The compound twist yarn of yarn twisting forms primary high-grade woven people's cotton face fabric, the weight ratio of wherein dacron thread and spun rayon yarn is 3-5 into line:
10；(2) to the described high-grade woven people's cotton face fabric dyeing pretreatment of primary：The described high-grade woven people's cotton face fabric of primary is placed
The boiling in preprocessing solution is dyed, the temperature of described dyeing pretreatment is 50 DEG C -60 DEG C, and the solution includes defoamer
0.15-0.20g/L, dispersant 4-5g/L, bleeding agent 4-6g/L, sulfuric acid 0.10-0.20g/L, bleaching powder 0.10-0.20g/L, carbon
Sour sodium 1-3g/L, hydrogen peroxide 3-10g/L, glacial acetic acid 0.20-0.40g/L, sodium phosphate 0.15-0.25g/L, turkey red oil 0.15-
0.25g/L, the time of described dyeing pretreatment is 10-50min；People's cotton fabrics semi-finished product after boiling are imported into overflow machine
In and cold wash export, and shape.(3) antistatic and anti-crease finishing：Fabric after shaping in step (2) is added into 10-15g/L to resist
Antistatic finish and 1.3-1.7g/L softness crease-shedding finishing agents, mangle handles 50-60m/min at 60-90 DEG C.(4) by boiling
Dyestuff is carried out with the high-grade woven people's cotton face fabric of primary after sizing and pulls out print, that is, is immersed in dyeing liquor, described dyeing liquor includes
1ml/L coloring agent, 1ml/L chelating agent；40-50 DEG C is warming up to, steams 20- in the rapid steamer gas that steam pressure is 2kg
30min, curve rise to 50-60 DEG C, are incubated 10min, add salt and soda ash, salt is equal with the quality of soda ash, is 3-
5g/L, then curve are warming up to 60-70 DEG C, are incubated 10min, are warming up to adding color fixing agent, the color fixing agent 2-5g/L, then curve
70-80 DEG C, 10min is incubated, the Boratex that concentration is 8-10g/L is added and carries out reduction washing, dry.(5) post-process：By
High-grade woven people's cotton face fabric that step (4) dyestuff is pulled out after printing, which is put into 1g/L romote antiquity oil solution, softens 25-30h, described
3-5ml/L soda ash is added in romote antiquity oil solution, is then taken out and is cleaned and dry, that is, obtains high-grade woven people's cotton face fabric.
2. dyeing and finishing technology as claimed in claim 1, it is characterised in that：The defoamer is OPEO；It is described
Coloring agent be intellectual circle and rongalite batch mixing dyestuff, the mass ratio of the rongalite and intellectual circle are 1:1；Described dispersant is
Alkyl alcohol ether mono sulfosuccinates；Described bleeding agent is sulfated castor oil；In described bleaching powder mainly into
It is divided into calcium hypochlorite, the bleaching powder available chlorine content is 20-28 (wt) %.；Antistatic finishing agent is triethanolamine；Described
Chelating agent is chelating agent GD-108 or hydroxycarboxylic acid；Described soft crease-shedding finishing agent is amino silicone modified organic silicon copolymer emulsion
Or soft crease-shedding finishing agent JPBC；Described color fixing agent is brocide.
3. dyeing and finishing technology as claimed in claim 2, it is characterised in that：The bleaching powder available chlorine content is 25 (wt) %.
4. dyeing and finishing technology as claimed in claim 1, it is characterised in that：Step (1) is twisted compound using dacron thread with spun rayon yarn
Twist yarn forms primary high-grade woven people's cotton face fabric, the wherein weight ratio of dacron thread and spun rayon yarn is 2 into line:5.
5. dyeing and finishing technology as claimed in claim 1, it is characterised in that：Described in step (2) dyeing pretreatment temperature be
55 DEG C, the solution includes defoamer 0.15g/L, dispersant 5g/L, bleeding agent 5g/L, sulfuric acid 0.20g/L, bleaching powder 0.10g/
L, sodium carbonate 3g/L, hydrogen peroxide 8g/L, glacial acetic acid 0.40g/L, sodium phosphate 0.15g/L, turkey red oil 0.15g/L, described dyeing
The time of pretreatment is 20min.
6. dyeing and finishing technology as claimed in claim 1, it is characterised in that：Step (3) is antistatic and anti-crease finishing：By step (2)
Fabric after middle sizing adds 15g/L antistatic finishing agents and 1.3g/L softness crease-shedding finishing agents, and mangle is handled at 60 DEG C
60m/min。
7. dyeing and finishing technology as claimed in claim 1, it is characterised in that：Top grade of the step (5) after step (4) dyestuff pulls out print
Woven people's cotton face fabric, which is put into 1g/L romote antiquity oil solution, softens 28h, and the pure of 4ml/L is added in the romote antiquity oil solution
Alkali.
8. dyeing and finishing technology as claimed in claim 1, it is characterised in that：Step (4) by boiling with sizing after primary high-grade machine
Knit people's cotton face fabric progress dyestuff and pull out print, that is, immerse in dyeing liquor, described dyeing liquor includes 1ml/L coloring agent, 1ml/L chela
Mixture；50 DEG C are warming up to, steams 30min in the rapid steamer gas that steam pressure is 2kg, curve rises to 50 DEG C, is incubated 10min, then add
Enter salt and soda ash, salt is equal with the quality of soda ash, is to be warming up to 70 DEG C for 5g/L, then curve, is incubated 10min, is adding
Enter color fixing agent, the color fixing agent 3g/L, then curve and be warming up to 80 DEG C, be incubated 10min, add the Boratex that concentration is 8g/L and enter
Row reduction washing, drying.
9. dyeing and finishing technology as claimed in claim 2, it is characterised in that：Described chelating agent is hydroxycarboxylic acid, described softness
Crease-shedding finishing agent is amino silicone modified organic silicon copolymer emulsion.