CN107869012A - Silk woven dacron base embroidery wall cloth and preparation method thereof - Google Patents
Silk woven dacron base embroidery wall cloth and preparation method thereof Download PDFInfo
- Publication number
- CN107869012A CN107869012A CN201710999505.7A CN201710999505A CN107869012A CN 107869012 A CN107869012 A CN 107869012A CN 201710999505 A CN201710999505 A CN 201710999505A CN 107869012 A CN107869012 A CN 107869012A
- Authority
- CN
- China
- Prior art keywords
- processing
- preparation
- silk
- woven dacron
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of silk woven dacron base embroidery wall cloth, the preparation method comprises the following steps：(1) adhesive is coated on to the surface of woven dacron, then silk is laid in the surface of adhesive, preliminarily dried is then carried out, obtains first product；(2) first product is subjected to the first processing, second processing, product after must handling successively；(3) the whole system of product surface after the processing is embroidered, then carries out compaction treatment；Wherein, the temperature of the first processing is higher than the temperature of second processing 35 55 DEG C.The silk woven dacron base embroidery wall cloth has the performance that preferable cold-and-heat resistent alternately changes, and particularly in actual use, can not be deformed after alternately changing by the four seasons in spring, summer, autumn, winter, warpage, greatly reduce wall paper and play drum, the phenomenon of warpage.The preparation method has process simple and the advantages of raw material is easy to get simultaneously.
Description
Technical field
The present invention relates to wall paper, in particular it relates to a kind of silk woven dacron base embroidery wall cloth and preparation method thereof.
Background technology
Wall paper or wallpaper are a kind of using quite extensive house decorative material.Because wall paper has, color is various, pattern
The incomparable spies of a variety of other house decorative materials such as abundant, luxurious style, safety and environmental protection, easy for construction, affordable
Point, therefore obtain considerable degree of popularization in developed countries and regions such as America and Europe, Southeast Asia, Japan.Because with certain intensity,
Appearance attractive in appearance and good clean-up performance, it is widely used in the interior decoration etc. of house, office, hotel.
People are conducted extensive research to wallpaper at present, and the patent application document that notification number is CN107189532A is announced
A kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method, this method include：(1) prepare except aldehyde coating or aqueous, environmental protective oil
Black wallpaper coating；(2) base material is subjected to the pre-heat treatment；(3) wallpaper coating is coated on the base material after preheated processing, and added
Graphene formaldehyde-removing wallpaper, wall paper is made in heat, embossing.It is of the invention compared with common wallpaper, wall paper, it is organic not contain formaldehyde, benzene etc.
Pollutant, and formaldehyde can be fundamentally removed, meanwhile, the addition of graphene can also improve the decomposing, purifying of harmful substance
The anti-wear performance of efficiency and wallpaper coating.
Notification number is that CN107022325A patent application document is related to a kind of advanced wallpaper wall paper adhesive.The adhesive
45-60 parts by weight are accounted for by major ingredient of aqueous polymer resin, auxiliary material has following component：Filler 30-50 parts by weight, thickener 0.2-
0.7 parts by weight, defoamer 0.1-0.3 parts by weight, wetting dispersing agent 0.1-0.3 parts by weight, plasticizer 0.1-0.4 parts by weight, surely
Determine agent 0.5-1.0 parts by weight, thixotropic agent 0.5-2.0 weight, preservative 0.1-0.5 parts by weight, deionized water 2-20 parts by weight；This
The binding agent that inventive technique scheme is provided realizes easy for construction, and good with ground adhesion, water-alkali resistance, persistence is good,
The advantages that health environment-friendly.Increase intensity, the weatherability of binding agent by Fillers selection and Gradation Optimization.By other auxiliary agents and match somebody with somebody
Fang Youhua improves the stability of adhesive.
Notification number is CN106968407A patent application document, is related to a kind of wall paper and preparation method thereof.Wall of the present invention
Cloth is made up of cotton, non-woven fibre paper and Environment-friendlyglue glue, it is characterised in that described Environment-friendlyglue glue is by following percentage by weight
Material composition：PU glue 50%-60%, be situated between agent 3%-6%.The present invention uses PU glue as adhesive, green, environmentally friendly and right
Non-woven fibre paper and cotton have excellent glueability, adhesion strength height；Wall paper preparation method technique of the present invention is simple, finished product
Rate is high, and whole production process will not cause damage without noxious gas emission to worker's health.
Research for wall paper at present relates generally to the bonding of wall paper, reduces the content of wall paper formaldehyde or the burst size of formaldehyde
Deng still, to how to prevent wall paper from deforming less for Journal of Sex Research.In fact, wall paper is in use, particularly in length
After time use, by the change to cold and heat succeed each other in spring, summer, autumn, winter, wall paper can be deformed, and bulge occur, and warpage is asked
Topic.For this problem of wall paper warpage, use is bonded more using the binding agent of cementation in reality, or is mended after warpage occurs
Binding agent is filled, and the increase of binder content can increase the probability of the release of formaldehyde, or cause wall paper to change colour, influence decoration
It is attractive in appearance.
Therefore, how a kind of preparation technology is provided, makes the wall paper of preparation in the change to cold and heat succeed each other by spring, summer, autumn, winter
After change, reduce wall paper size itself change, be only fundamentally solve wall paper deform in use, the pass of warpage
Key.
The content of the invention
It is an object of the invention to provide a kind of silk woven dacron base embroidery wall cloth and preparation method thereof, the preparation method obtains
Silk woven dacron base embroidery wall cloth in actual use, can by the spring, the summer, the autumn, the winter the four seasons alternately change after not
Deform, warpage, greatly reduce wall paper and play drum, the phenomenon of warpage.
To achieve these goals, it is described the invention provides a kind of preparation method of silk woven dacron base embroidery wall cloth
Preparation method comprises the following steps：(1) adhesive is coated on to the surface of woven dacron, then silk is laid in the table of adhesive
Face, preliminarily dried is then carried out, obtains first product；(2) first product is subjected to the first processing successively, second processing, produced after must handling
Product；(3) the whole system of product surface after the processing is embroidered, then carries out compaction treatment；Wherein, the temperature of the first processing is than second
The temperature of processing is high 35-55 DEG C.
The present invention also provides a kind of silk woven dacron base embroidery wall cloth being prepared according to previously described preparation method.
Pass through above-mentioned technical proposal, the present invention particularly carry out the by formulating the manufacture craft of wall paper successively to first product
One processing, second processing, first processing temperature it is higher than the temperature of second processing 35-55 DEG C, so as to get silk woven dacron base
Embroidery wall cloth has the performance of preferable cold-and-heat resistent alternately change, particularly in actual use, can by the spring, the summer, the autumn,
The four seasons in winter do not deform after alternately changing, warpage, greatly reduce wall paper and play drum, the phenomenon of warpage.The preparation side simultaneously
Method has process simple and the advantages of raw material is easy to get.
Other features and advantages of the present invention will be described in detail in subsequent specific embodiment part.
Embodiment
The embodiment of the present invention is described in detail below.It is it should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
The end points of disclosed scope and any value are not limited to the accurate scope or value herein, these scopes or
Value should be understood to comprising the value close to these scopes or value.For number range, between the endpoint value of each scope, respectively
It can be combined with each other between the endpoint value of individual scope and single point value, and individually between point value and obtain one or more
New number range, these number ranges should be considered as specific open herein.
The invention provides a kind of preparation method of silk woven dacron base embroidery wall cloth, the preparation method includes following step
Suddenly：(1) adhesive is coated on to the surface of woven dacron, then silk is laid in the surface of adhesive, then carries out preliminarily dried,
Obtain first product；(2) first product is subjected to the first processing, second processing, product after must handling successively；(3) will be produced after the processing
The whole system embroidery in product surface, then carries out compaction treatment；Wherein, the temperature of the first processing is higher than the temperature of second processing 35-55 DEG C.
Pass through above-mentioned technical proposal, the present invention particularly carry out the by formulating the manufacture craft of wall paper successively to first product
One processing, second processing, the temperature of the first processing is higher than the temperature of second processing 35-55 DEG C, obtained silk woven dacron base thorn
The performance that there is wall paper preferable cold-and-heat resistent alternately to change is embroidered, particularly in actual use, can be by spring, summer, autumn, winter
The four seasons alternately change after do not deform, warpage, greatly reduce wall paper rise drum, the phenomenon of warpage.The preparation method simultaneously
It is simple and the advantages of raw material is easy to get with process.
In the above-mentioned technical solutions, the temperature of the first processing can be adjusted in relative broad range, in order that wall paper, has
The performance that preferable cold-and-heat resistent alternately changes, particularly in actual use, it can replace in the four seasons by spring, summer, autumn, winter
Change after do not deform, warpage, greatly reduce wall paper rise drum, the phenomenon of warpage, it is preferable that first processing temperature be
35-45℃。
For the time of the first processing, those skilled in the art can be adjusted in relative broad range, in order that wall paper, tool
There is the performance that preferable cold-and-heat resistent replaces change, to reduce bulging, warpage the phenomenon occurred in use, it is preferable that at first
The reason time is 30-40min.
Further, in order that wall paper has the performance that preferable cold-and-heat resistent alternately changes, occur to reduce in use
Rise drum, the phenomenon of warpage, it is preferable that first processing process carried out under conditions of steam is smoked.
Steam pressure when being smoked for steam, those skilled in the art can be adjusted in relative broad range, in order that wall
Cloth, have preferable cold-and-heat resistent alternately change performance, with reduce occur in use rise drum, warpage phenomenon, it is preferable that steam
Steam pressure is 0.01-0.04MPa when vapour is smoked.
For the temperature of second processing, those skilled in the art can be adjusted in relative broad range, in order that wall paper has
There is the performance that preferable cold-and-heat resistent replaces change, to reduce bulging, warpage the phenomenon occurred in use, it is preferable that at second
The temperature of reason is (- 10) DEG C-(- 5) DEG C.
Certainly, for the second processing time, those skilled in the art can be adjusted in relative broad range, in order that wall
Cloth, there is the performance of preferable cold-and-heat resistent alternately change, with reduce occur in use rise drum, warpage phenomenon, it is preferable that the
The time of two processing is 10-20min.
In the present invention, the step of also including being cooled after the first processing.Wherein for the speed of cooling, this area
Technical staff can be adjusted in relative broad range, in order to improve treatment effect, make wall paper that there is preferable cold-and-heat resistent alternately to become
The performance of change, to reduce bulging, warpage the phenomenon occurred in use, it is preferable that the speed of cooling is 5-10 DEG C/min.
For the thickness of woven dacron, those skilled in the art can be adjusted in relative broad range, in order to improve wall paper
Mechanical performance, the performance for further making wall paper that there is preferable cold-and-heat resistent alternately to change, to reduce the drum occurred in use, stick up
Bent phenomenon, it is preferable that the thickness of woven dacron is 30-40 silks.
Wherein, silk is the thickness unit that those skilled in the art commonly use, wherein, 100 are equal to 1mm.
For the thickness of adhesive coating, those skilled in the art can be adjusted in relative broad range, in order to improve wall
The bonding effect of cloth, the performance for further making wall paper that there is preferable cold-and-heat resistent alternately to change, to reduce occurred in use
Drum, the phenomenon of warpage, it is preferable that the thickness of adhesive coating is 25-40 silks.
For the thickness for whole system of embroidering, those skilled in the art can be adjusted in relative broad range, in order that wall paper has
Have the performance of preferable cold-and-heat resistent alternately change, with reduce occur in use rise drum, warpage phenomenon, it is preferable that embroidery is whole
The thickness of system is 15-25 silks.
For the thickness of silk laying, those skilled in the art can be adjusted in relative broad range, in order to improve wall paper
Mechanical performance, further make wall paper that there is the performance of preferable cold-and-heat resistent alternately change, with reduce occur in use rise drum,
The phenomenon of warpage, it is preferable that the thickness of silk laying is 5-15 silks.
In above-mentioned silk woven dacron base embroidery wall cloth, the coverage density of silk can select in wide scope, in order to
The mechanical performance of wall paper is improved, the performance for further making wall paper that there is preferable cold-and-heat resistent alternately to change, to reduce in use
Existing plays drum, the phenomenon of warpage, it is preferable that the coverage density of silk is 70-80 areas %.
In above-mentioned silk woven dacron base embroidery wall cloth, the specific species of silk can select in wide scope, still
In order that wall paper has mechanical performance, the performance for further making wall paper that there is preferable cold-and-heat resistent alternately to change, used with reducing
Middle appearance plays drum, the phenomenon of warpage, it is preferable that silk is selected from mulberry silk and/or tussah silk.
In above-mentioned silk woven dacron base embroidery wall cloth, the specific species of woven dacron can select in wide scope, but
It is in order that wall paper has mechanical performance, further makes wall paper that there is the performance of preferable cold-and-heat resistent alternately change, made with reducing
Roused with rising for middle appearance, the phenomenon of warpage, it is preferable that woven dacron is worked out by warp and weft 1 to 1, the warp and institute
It is chemical-fibres filaments to state parallel.
In above-mentioned silk woven dacron base embroidery wall cloth, the specific species of adhesive can select in wide scope, but
It is to improve the bonding effect of wall paper, further makes wall paper that there is the performance of preferable cold-and-heat resistent alternating change, made with reducing
Roused with rising for middle appearance, the phenomenon of warpage, it is preferable that adhesive is gelatine, hide glue, fishbone glue, casein, blood glue, phenolic resin
One or more in glue, polyvinyl acetate resin adhesive, urea-formaldehyde resin adhesive and bean gum.It is highly preferred that adhesive is poly-vinegar acid second
Olefine resin glue.
In the above-mentioned technical solutions, the actual conditions of preliminarily dried can select in wide condition in step (1), still
In order that obtained wall paper has the performance that preferable cold-and-heat resistent alternately changes, it is preferable that preliminarily dried is at least full in step (1)
It is enough lower condition：Drying temperature is 50-70 DEG C, drying time 12-24h.
In the above-mentioned technical solutions, the actual conditions of compaction treatment can select in wide condition, but in order that system
Wall paper there is the performance of preferable cold-and-heat resistent alternately change, it is preferable that in step (3), compaction treatment at least meet with
Lower condition：Compaction pressure is 3-4.5MPa, and the compacting time is 8-12h.
The present invention also provides a kind of silk woven dacron base embroidery wall cloth being prepared according to previously described preparation method.
There is preferable cold-and-heat resistent alternately to change for Pass through above-mentioned technical proposal, silk woven dacron base embroidery wall cloth of the invention
Performance, particularly in actual use, can by the spring, the summer, the autumn, the winter the four seasons alternately change after not deform,
Warpage, greatly reduce wall paper and play drum, the phenomenon of warpage.The preparation method has process simple and the advantages of raw material is easy to get simultaneously.
The present invention will be described in detail by way of examples below.In the examples below, polyvinyl acetate resin adhesive,
Model HD-4600 is purchased from Dongguan City Heng Dong resins Co., Ltd；Other are conventional commercial products.
Embodiment 1
The preparation method of silk woven dacron base embroidery wall cloth, comprises the following steps：
(1) adhesive (polyvinyl acetate resin adhesive) is coated on to the surface of woven dacron (30), the thickness of coating is 25
Silk, then mulberry silk is laid in the surface of adhesive, the thickness of laying is 5, and laying density be 70 area %, then at the beginning of progress
Step is dried and (dries 50 DEG C, drying time 12h), obtains first product；
(2) first product is subjected to the first processing successively, the process of the first processing is carried out under 0.01MPa steam pressure
Steam is carried out under conditions of smoking, first processing temperature be 35 DEG C of times be 10min, being cooled to 0 DEG C afterwards with 5 DEG C/min enters
Row second processing, time of second processing are 10-20min, product after must handling；
(3) by the whole system embroidery of product surface after the processing (thickness is 15), compaction treatment (compaction pressure is then carried out
For 3MPa, the compacting time is 8h).
Embodiment 2
The preparation method of silk woven dacron base embroidery wall cloth, comprises the following steps：
(1) adhesive (polyvinyl acetate resin adhesive) is coated on to the surface of woven dacron (35), the thickness of coating is 30
Silk, then mulberry silk is laid in the surface of adhesive, the thickness of laying is 8, and laying density be 75 area %, then at the beginning of progress
Step is dried and (dries 60 DEG C, drying time 18h), obtains first product；
(2) first product is subjected to the first processing successively, the process of the first processing is carried out under 0.02MPa steam pressure
Steam is carried out under conditions of smoking, first processing temperature be 40 DEG C of times be 10-20min, afterwards with 5-10 DEG C/min cool
Second processing is carried out to (- 5) DEG C, and time of second processing is 15min, product after must handling；
(3) by the whole system embroidery of product surface after the processing (thickness is 20), compaction treatment (compaction pressure is then carried out
For 3.5MPa, the compacting time is 10h).
Embodiment 3
The preparation method of silk woven dacron base embroidery wall cloth, comprises the following steps：
(1) adhesive (polyvinyl acetate resin adhesive) is coated on to the surface of woven dacron (40), the thickness of coating is 40
Silk, then mulberry silk is laid in the surface of adhesive, the thickness of laying is 15, and laying density is 80 area %, is then carried out
Preliminarily dried (dries 70 DEG C, drying time 24h), obtains first product；
(2) first product is subjected to the first processing successively, the process of the first processing is carried out under 0.04MPa steam pressure
Steam is carried out under conditions of smoking, the temperature of the first processing be 45 DEG C of times be 20min, be cooled to afterwards with 10 DEG C/min (-
DEG C 10) second processing is carried out, time of second processing is 20min, product after must handling；
(3) by the whole system embroidery of product surface after the processing (thickness is 25), compaction treatment (compaction pressure is then carried out
For 4.5MPa, the compacting time is 12h).
Comparative example 1
Method according to embodiment 2 prepares silk woven dacron base embroidery wall cloth, unlike, the temperature of the first processing is 25
℃
Comparative example 2
Method according to embodiment 2 prepares silk woven dacron base embroidery wall cloth, unlike, the temperature of the first processing is 55
℃。
Comparative example 3
Silk woven dacron base embroidery wall cloth is prepared according to the method in embodiment 2, unlike, without in step (2)
The step of, step (1) directly carries out compaction treatment after terminating.
Detect example 1
By instron GP-6113 (Instrument Ltd. is surveyed in the high product examine in Suzhou City) detect embodiment 1-3 and
The tensile strength of wall paper in comparative example 1-3.
Detect example 2
The wall paper in 20 × 30cm embodiment 1-3 and comparative example 1-3 is taken, is first placed in the environment of (- 6) DEG C 30 days, then
It is placed in 35 DEG C of environment 30 days, so carries out two circulations, measures the change in size of wall paper, and according to the side of detection example 1
Method detects the tensile strength of these wall papers.
Find after testing, before the processing in detecting example 2, the tension of each wall paper in embodiment 1-3 and comparative example 1-3
Intensity is more or less the same, and the order of tensile strength from big to small is successively：It is embodiment 3, embodiment 2, comparative example 2, comparative example 1, right
Ratio 3, embodiment 1, wherein reaching 64MPa with the tensile strength in embodiment 3, the tensile strength of wall paper is in embodiment 1
58MPa。
After testing after the processing in example 2, the tensile strength change unobvious in embodiment 1-3, tensile strength is above-mentioned
The tensile strength of detection 94% and more than；The tensile strength of each wall paper in comparative example 1-3 is relatively original to be declined substantially, is existed
Originally less than the 71% of tensile strength values, the 54% of the worst wall paper in comparative example 3, only initial value.
After testing, after the processing in detecting example 2, the change in size unobvious of each wall paper in embodiment 1-3, change is most
Big is the wall paper in embodiment 3, and width increases 0.3mm；And the wall paper change in size in comparative example 1-3 is larger, comparative example 3
In the length of wall paper add 6mm, width adds 4mm；In comparative example 1-3, the change of comparative example 1 is minimum, but its
Length adds 4mm, and width adds 2mm.
Illustrate the performance that there is silk woven dacron base embroidery wall cloth prepared by the present invention preferable cold-and-heat resistent alternately to change, be
In actual use, it can be not susceptible to deform after by the four seasons in spring, summer, autumn, winter alternately changing, warpage, reduce wall
Cloth plays drum, the phenomenon of warpage.
The preferred embodiment of the present invention described in detail above, still, the present invention are not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, a variety of simple variants can be carried out to technical scheme, this
A little simple variants belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy no longer separately illustrates.
In addition, various embodiments of the present invention can be combined randomly, as long as it is without prejudice to originally
The thought of invention, it should equally be considered as content disclosed in this invention.
Claims (10)
1. a kind of preparation method of silk woven dacron base embroidery wall cloth, it is characterised in that the preparation method comprises the following steps：
(1) adhesive is coated on to the surface of woven dacron, then silk is laid in the surface of adhesive, is then tentatively done
It is dry, obtain first product；
(2) first product is subjected to the first processing, second processing, product after must handling successively；
(3) the whole system of product surface after the processing is embroidered, then carries out compaction treatment；
Wherein, the temperature of the first processing is higher than the temperature of second processing 35-55 DEG C.
2. preparation method according to claim 1, wherein, the temperature of the first processing is 35-45 DEG C；And/or first processing
Time is 30-40min.
3. described preparation method according to claim 1 or 2, wherein, the bar that the first process handled is smoked in steam
Carried out under part.
4. described preparation method according to claim 3, wherein, steam pressure is 0.01- when steam is smoked
0.04MPa。
5. preparation method according to claim 1 or 2, wherein, the temperature of second processing is (- 10) DEG C-(- 5) DEG C；With/
Or, the time of second processing is 10-20min.
6. preparation method according to claim 1 or 2, wherein, the step of also including being cooled after the first processing, its
In, the speed of cooling is 5-10 DEG C/min.
7. preparation method according to claim 1 or 2, wherein, the thickness of woven dacron is 30-40 silks；And/or
The thickness of adhesive coating is 25-40 silks；And/or the thickness for whole system of embroidering is 15-25 silks；
And/or the thickness of silk laying is 5-15 silks；Preferably, silk laying density is 70-80 areas %.
8. preparation method according to claim 1 or 2, wherein, silk is selected from mulberry silk and/or tussah silk；And/or
Woven dacron is worked out by warp and weft 1 to 1, and the warp and the parallel are chemical-fibres filaments；
And/or adhesive is gelatine, hide glue, fishbone glue, casein, blood glue, phenolic resin glue, polyvinyl acetate resin adhesive, ureaformaldehyde
One or more in resin glue and bean gum.
9. preparation method according to claim 1 or 2, wherein, preliminarily dried at least meets following condition in step (1)：
Drying temperature is 50-70 DEG C, drying time 12-24h；And/or
In step (3), compaction treatment at least meets following condition：Compaction pressure is 3-4.5MPa, and the compacting time is 8-12h.
10. the silk woven dacron base embroidery wall cloth that the preparation method according to claim any one of 1-9 is prepared.