CN107868864A - 一种淬火剂 - Google Patents

一种淬火剂 Download PDF

Info

Publication number
CN107868864A
CN107868864A CN201711449180.1A CN201711449180A CN107868864A CN 107868864 A CN107868864 A CN 107868864A CN 201711449180 A CN201711449180 A CN 201711449180A CN 107868864 A CN107868864 A CN 107868864A
Authority
CN
China
Prior art keywords
parts
quenching medium
quenching
defoamer
polyethers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711449180.1A
Other languages
English (en)
Inventor
贾留宽
贾若龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LUOYANG SHENJIA KILN CO Ltd
Original Assignee
LUOYANG SHENJIA KILN CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LUOYANG SHENJIA KILN CO Ltd filed Critical LUOYANG SHENJIA KILN CO Ltd
Priority to CN201711449180.1A priority Critical patent/CN107868864A/zh
Publication of CN107868864A publication Critical patent/CN107868864A/zh
Pending legal-status Critical Current

Abstract

一种淬火剂，由以下重量份的成分组成：聚醚15‑20份，苯甲酸钠1‑3份，异丙醇胺0.5‑1份，磺酸钙0.2‑0.5份，三乙醇胺1‑5份，消泡剂0.1‑0.3份，水10‑20份。本发明提出的一种淬火剂在低温条件下大大降低冷却速度，高温条件下具有足够的冷却速度，保证产品不淬裂的情况下又能有较好的淬火效果，提高钢材使用寿命和性能，成本低，实现条件简单，有利于市场推广。

Description

一种淬火剂
技术领域
本发明属于金属热处理领域，具体是一种淬火剂。
背景技术
为了改善例如钢材等金属材料的性能，需要对金属材质的工件进行热处理，常用的热处理工艺有淬火、回火、退火、正火等热处理方法。其中，淬火是指将例如加热至奥氏体状态的工件以临界冷却速度以上的速度快速冷却至形成马氏体等淬火组织，淬火处理后，可以提高工件的硬度。在淬火的过程中，工件的冷却过程一般分为三个阶段，即金属材料被淬火介质的蒸汽包围的第一阶段(蒸汽膜阶段)、蒸汽膜破裂沸腾的第二阶段(沸腾阶段)、金属材料的温度达到淬火介质的沸点以下通过对流夺取热量的第三阶段(对流阶段)，然后被冷却至室温。
传统的淬火介质有水性淬火剂和油性淬火剂，水性淬火剂的特点是在整个冷却过程中都具有很高的冷却速度，在高温冷却阶段高的冷却速度可以促使形成晶粒细小的工件，有利于提高工件最终的性能，但在低温阶段，过快的冷却速度使工件的内应力过大，因此容易导致工件开裂。与水性淬火剂相比，油性淬火剂的特点是整个冷却阶段的冷却速度慢，虽然可以防止工件在低温阶段由于内应力过大而导致开裂，但是由于高温阶段冷却速度较慢，因此容易导致工件晶粒较大，降低工件淬火后的性能。
发明内容
本发明的目的在于针对上述问题，提出一种淬火效果好，能延长使用寿命的淬火剂。
为了实现上述目的，本发明采用以下技术方案来实现。依据本发明提出的一种淬火剂，由以下重量份的成分组成：聚醚15-20份，苯甲酸钠1-3 份，异丙醇胺0.5-1份，磺酸钙0.2-0.5份，三乙醇胺1-5份，消泡剂0.1-0.3 份，水10-20份。
为了实现上述目的，本发明还采用以下技术措施来进一步实现。
进一步的，一种淬火剂，由以下重量份的成分组成：聚醚15份，苯甲酸钠1份，异丙醇胺0.5份，磺酸钙0.2份，三乙醇胺1份，消泡剂0.1 份，水10份。
进一步的，一种淬火剂，由以下重量份的成分组成：聚醚20份，苯甲酸钠3份，异丙醇胺1份，磺酸钙0.5份，三乙醇胺5份，消泡剂0.3份，水20份。
进一步的，所述的消泡剂为硅类消泡剂。
进一步的，所述的聚醚的分子量为50000-60000。
本发明提出的一种淬火剂在低温条件下大大降低冷却速度，高温条件下具有足够的冷却速度，保证产品不淬裂的情况下又能有较好的淬火效果，提高钢材使用寿命和性能，成本低，实现条件简单，有利于市场推广。
上述说明仅是本发明技术方案的概述，为了能更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为让本发明的上述和其他目的、特征和优点能够更明显易懂，以下特举较佳实施例，详细说明如下。
具体实施方式
下面通过具体实施例对本发明做进一步的详细描述。
一种淬火剂，由以下重量份的成分组成：聚醚15-20份，苯甲酸钠1-3 份，异丙醇胺0.5-1份，磺酸钙0.2-0.5份，三乙醇胺1-5份，消泡剂0.1-0.3 份，水10-20份。
作为优选的，一种淬火剂，由以下重量份的成分组成：聚醚15份，苯甲酸钠1份，异丙醇胺0.5份，磺酸钙0.2份，三乙醇胺1份，消泡剂0.1 份，水10份。
作为优选的，一种淬火剂，由以下重量份的成分组成：聚醚20份，苯甲酸钠3份，异丙醇胺1份，磺酸钙0.5份，三乙醇胺5份，消泡剂0.3 份，水20份。
作为优选的，所述的消泡剂为硅类消泡剂。
作为优选的，所述的聚醚的分子量为50000-60000。
以上结合具体实施例描述了本发明的技术原理。这些描述只是为了解释本发明的原理，而不能以任何方式解释为对本发明保护范围的限制。本领域技术人员在本发明的基础上做各种各样的修改或补充或采用类似的方式替代，只要不偏离本发明的结构或者超越本权利要求书所定义的范围，均应属于本发明的保护范畴。

Claims (5)

1.一种淬火剂，其特征在于由以下重量份的成分组成：聚醚15-20份，苯甲酸钠1-3份，异丙醇胺0.5-1份，磺酸钙0.2-0.5份，三乙醇胺1-5份，消泡剂0.1-0.3份，水10-20份。
2.根据权利要求1所述的一种淬火剂，其特征在于由以下重量份的成分组成：聚醚15份，苯甲酸钠1份，异丙醇胺0.5份，磺酸钙0.2份，三乙醇胺1份，消泡剂0.1份，水10份。
3.根据权利要求1所述的一种淬火剂，其特征在于由以下重量份的成分组成：聚醚20份，苯甲酸钠3份，异丙醇胺1份，磺酸钙0.5份，三乙醇胺5份，消泡剂0.3份，水20份。
4.根据权利要求1所述的一种淬火剂，其特征在于，所述的消泡剂为硅类消泡剂。
5.根据权利要求1所述的一种淬火剂，其特征在于，所述的聚醚的分子量为50000-60000。
CN201711449180.1A 2017-12-27 2017-12-27 一种淬火剂 Pending CN107868864A (zh)