CN107868601A - A kind of indoor water-proof emulsion paint and preparation method thereof - Google Patents
A kind of indoor water-proof emulsion paint and preparation method thereof Download PDFInfo
- Publication number
- CN107868601A CN107868601A CN201711249161.4A CN201711249161A CN107868601A CN 107868601 A CN107868601 A CN 107868601A CN 201711249161 A CN201711249161 A CN 201711249161A CN 107868601 A CN107868601 A CN 107868601A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- preparation
- indoor water
- proof emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of indoor water-proof emulsion paint and preparation method thereof, it is related to paint field.It is prepared by following raw material：40 50 parts of polysiloxane polyurethane emulsions, 35 parts of celluloses, 30 40 parts of talcum powder, 8 16 parts of coalescents, 58 parts of polyvinyl alcohol, 35 parts of defoamers, 35 parts of vegetable proteins, 15 20 parts of hollow glass micro-balls, 10 15 parts of deionized waters, 40 50 parts of lotus leaves.The invention provides a kind of indoor water-proof emulsion paint and preparation method thereof, emulsion paint can be made to have stronger hydrophobicity, so as to reach waterproof effect.
Description
Technical field
The present invention relates to paint field, more particularly to a kind of indoor water-proof emulsion paint and preparation method thereof.
Background technology
Emulsion paint is being commonly called as latex paint, is born in the next period in nineteen seventies, and emulsion paint possesses and biography
System wall covering many merits, such as it is easy to brush, dries the features such as rapid, scrub resistance is good.If but existing emulsion paint
At for a long time in a humid environment, the easy mouldy nigrescence of emulsion paint lacquer painting, carrys out inconvenience, and can cause to paint to ornamental tape
Emaciated face falls, or even gives out harmful substance and niff.
The content of the invention
It is an object of the invention to provide a kind of indoor water-proof emulsion paint and preparation method thereof, asked with solving above-mentioned technology
Topic.
The present invention using following technical scheme in order to solve the above technical problems, realized：
A kind of indoor water-proof emulsion paint, it is characterised in that be prepared by following raw material：The poly- silica of 40-50 parts
Alkane-polyaminoester emulsion, 3-5 parts cellulose, 30-40 parts talcum powder, 8-16 parts coalescents, 5-8 parts polyvinyl alcohol, 3-5 parts disappear
Infusion, 3-5 parts vegetable protein, 15-20 parts hollow glass micro-ball, 10-15 parts deionized water, 40-50 part lotus leaves.
A kind of preparation method of indoor water-proof emulsion paint, it is characterised in that comprise the following steps：
A, polysilicone-polyurethanes emulsion, talcum powder, polyvinyl alcohol, hollow glass micro-ball, deionized water are put into reaction
In kettle, 75-85 DEG C is heated to, and uniform stirring is carried out under microwave radiation technology, produces base material；
B, crushed after lotus leaf is dried, and Lotus Leaf is put into ethanol solution, entered under ultrasonic vibration auxiliary
Row stirring, mixing time is 10-15 minutes, and 20-30 minutes are stood after stirring, and takes supernatant liquor, by gained supernatant with planting
Thing albumen, cellulose are uniformly mixed, and uniform stirring is carried out at 50-60 DEG C, produce Lotus Leafextract lotion；
C, gained base material, Lotus Leafextract lotion are mixed with defoamer, and carried out at a temperature of 80-90 DEG C
Uniform stirring, mixing time are 40-60 minutes, produce mixed material；
D, gained mixed material is mixed with coalescents and injects grinder, stirred 3-4 hours, produce emulsion paint.
Preferably, in described step A, microwave power 500-1500w.
Preferably, in described step B, described vegetable protein is soybean protein.
Preferably, in described step C, 80-90 DEG C is controlled by heating water bath.
Preferably, in described step D, grinder rotating speed 200-250r/min.
Lotus leaf has micron-nanometer dual structure in itself, has extremely strong hydrophobicity, and the present invention is prepared for lotus leaf extraction
Thing lotion, and Lotus Leafextract lotion is synthesized with base material, so as to strengthen the hydrophobicity of emulsion paint, if latex
Lacquer painting is painted for a long time in the larger environment of humidity, the hydrophobicity of emulsion paint in itself can make moisture be difficult to enter inside lacquer painting, from
And use effect of emulsion paint is effectively guaranteed, and extend usage time.
The beneficial effects of the invention are as follows：The invention provides a kind of indoor water-proof emulsion paint and preparation method thereof, can make
Emulsion paint has stronger hydrophobicity, so as to reach waterproof effect.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further, but following embodiments are only the preferred embodiments of the present invention, and it is not all.
Based on the embodiment in embodiment, those skilled in the art obtain other realities on the premise of creative work is not made
Example is applied, belongs to protection scope of the present invention.Experimental method in following embodiments, it is conventional method unless otherwise specified,
Material used, reagent etc., unless otherwise specified, are commercially obtained in following embodiments.
Embodiment 1
By 40 parts of polysilicone-polyurethanes emulsions, 30 parts of talcum powder, 5 parts of polyvinyl alcohol, 15 parts of hollow glass micro-balls, 10
Part deionized water is put into reactor, is heated to 75 DEG C, and carries out uniform stirring in the case where power is 500w microwave radiation technology, is produced
Base material；
Crushed after 40 parts of lotus leaves are dried, and Lotus Leaf is put into ethanol solution, under ultrasonic vibration auxiliary
It is stirred, mixing time is 10 minutes, and 20 minutes are stood after stirring, and takes supernatant liquor, by gained supernatant and 3 portions of soybean
Albumen, 3 parts of celluloses uniformly mix, and uniform stirring are carried out at 50 DEG C, produce Lotus Leafextract lotion；
Gained base material, Lotus Leafextract lotion are mixed with 3 parts of defoamers, and cross heating water bath at 80 DEG C
At a temperature of carry out uniform stirring, mixing time is 40 minutes, produces mixed material；
Gained mixed material is mixed with 8 parts of coalescents and injects grinder, rotating speed 200r/min, is stirred 3 hours,
Produce emulsion paint.
Embodiment 2
By 50 parts of polysilicone-polyurethanes emulsions, 40 parts of talcum powder, 8 parts of polyvinyl alcohol, 20 parts of hollow glass micro-balls, 15
Part deionized water is put into reactor, is heated to 85 DEG C, and carries out uniform stirring in the case where power is 1500w microwave radiation technology, i.e.,
Obtain base material；
Crushed after 50 parts of lotus leaves are dried, and Lotus Leaf is put into ethanol solution, under ultrasonic vibration auxiliary
It is stirred, mixing time is 15 minutes, and 30 minutes are stood after stirring, and takes supernatant liquor, by gained supernatant and 5 portions of soybean
Albumen, 5 parts of celluloses uniformly mix, and uniform stirring are carried out at 60 DEG C, produce Lotus Leafextract lotion；
Gained base material, Lotus Leafextract lotion are mixed with 5 parts of defoamers, and cross heating water bath at 90 DEG C
At a temperature of carry out uniform stirring, mixing time is 60 minutes, produces mixed material；
Gained mixed material is mixed with 16 parts of coalescents and injects grinder, rotating speed 250r/min, it is small to stir 4
When, produce emulsion paint.
Embodiment 3
By 45 parts of polysilicone-polyurethanes emulsions, 35 parts of talcum powder, 7 parts of polyvinyl alcohol, 18 parts of hollow glass micro-balls, 12
Part deionized water is put into reactor, is heated to 80 DEG C, and carries out uniform stirring in the case where power is 1000w microwave radiation technology, i.e.,
Obtain base material；
Crushed after 45 parts of lotus leaves are dried, and Lotus Leaf is put into ethanol solution, under ultrasonic vibration auxiliary
It is stirred, mixing time is 12 minutes, and 25 minutes are stood after stirring, and takes supernatant liquor, by gained supernatant and 4 portions of soybean
Albumen, 4 parts of celluloses uniformly mix, and uniform stirring are carried out at 55 DEG C, produce Lotus Leafextract lotion；
Gained base material, Lotus Leafextract lotion are mixed with 4 parts of defoamers, and cross heating water bath at 85 DEG C
At a temperature of carry out uniform stirring, mixing time is 50 minutes, produces mixed material；
Gained mixed material is mixed with 12 parts of coalescents and injects grinder, rotating speed 230r/min, it is small to stir 3.5
When, produce emulsion paint.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is only the present invention
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (6)
1. a kind of indoor water-proof emulsion paint, it is characterised in that be prepared by following raw material：40-50 parts polysiloxanes-
Polyaminoester emulsion, 3-5 parts cellulose, 30-40 parts talcum powder, 8-16 parts coalescents, 5-8 parts polyvinyl alcohol, the defoaming of 3-5 parts
Agent, 3-5 parts vegetable protein, 15-20 parts hollow glass micro-ball, 10-15 parts deionized water, 40-50 part lotus leaves.
2. a kind of preparation method of indoor water-proof emulsion paint, it is characterised in that comprise the following steps：
A, polysilicone-polyurethanes emulsion, talcum powder, polyvinyl alcohol, hollow glass micro-ball, deionized water are put into reactor
In, 75-85 DEG C is heated to, and uniform stirring is carried out under microwave radiation technology, produce base material；
B, crushed after lotus leaf is dried, and Lotus Leaf is put into ethanol solution, stirred under ultrasonic vibration auxiliary
Mix, mixing time is 10-15 minutes, and 20-30 minutes are stood after stirring, and takes supernatant liquor, by gained supernatant and plant egg
In vain, cellulose is uniformly mixed, and uniform stirring is carried out at 50-60 DEG C, produces Lotus Leafextract lotion；
C, gained base material, Lotus Leafextract lotion are mixed with defoamer, and carried out uniformly at a temperature of 80-90 DEG C
Stirring, mixing time is 40-60 minutes, produces mixed material；
D, gained mixed material is mixed with coalescents and injects grinder, stirred 3-4 hours, produce emulsion paint.
A kind of 3. preparation method of indoor water-proof emulsion paint according to claim 2, it is characterised in that described step A
In, microwave power 500-1500w.
A kind of 4. preparation method of indoor water-proof emulsion paint according to claim 2, it is characterised in that described step B
In, described vegetable protein is soybean protein.
A kind of 5. preparation method of indoor water-proof emulsion paint according to claim 2, it is characterised in that described step C
In, 80-90 DEG C is controlled by heating water bath.
A kind of 6. preparation method of indoor water-proof emulsion paint according to claim 2, it is characterised in that described step D
In, grinder rotating speed 200-250r/min.