CN107868514A - 一种适用于干擦的闪光墨水及其制备方法 - Google Patents
一种适用于干擦的闪光墨水及其制备方法 Download PDFInfo
- Publication number
- CN107868514A CN107868514A CN201711221656.6A CN201711221656A CN107868514A CN 107868514 A CN107868514 A CN 107868514A CN 201711221656 A CN201711221656 A CN 201711221656A CN 107868514 A CN107868514 A CN 107868514A
- Authority
- CN
- China
- Prior art keywords
- xerotripsis
- agent
- shiny
- water
- shiny inks
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本法发明提供了一种适用于干擦的闪光墨水及其制备方法。所述墨水组分按重量百分比计:水性铝银浆2.5‑5%,水性染料0.5‑1%,树脂15‑25%,成助膜剂0.5‑3%,润湿剂2.5‑4%,流平剂1.5‑2.5%,渗透剂0.075‑0.15%,防腐剂0.075‑0.15%,蒸馏水余量。本发明的闪光墨水,描绘出的作品闪闪发光、成膜光滑平整、涂写流畅、快干易擦、安全环保。本发明的闪光墨水生产工艺简单,安全环保,可作为儿童书写绘画练习用的墨水。
Description
技术领域
本发明涉及文具用品,具体是一种适用于干擦的闪光墨水及其制备方法。
背景技术
传统的墨水流畅透明、色彩亮丽,易储存,分散良好,但是制备工艺繁琐,覆盖性较差,使用之前还得速溶,风干速度较慢,给使用者带来了诸多不便。特别是有的场合需要一种具有渲染效果的适于干擦的闪光墨水。但是,根据国内外专利与非专利文献查询,目前还没有适于干擦的闪光墨水的报道。
发明内容
本发明的目的在于提供一种适用于干擦的闪光墨水及其制备方法,所述闪光墨水应具有分散性、覆盖性好的特点,被覆盖的地方闪闪发光,能给人以眼前一亮的美感。
为了解决以上技术问题,本发明提供的技术方案如下:
一种适用于干擦的闪光墨水,组分按重量百分比计为:
水性铝银浆2.5-5%
水性染料0.5-1%
树脂15-25%
成膜助剂0.5-3%
润湿剂2.5-4%
流平剂1.5-2.5%
渗透剂0.075-0.15%
防腐剂0.075-0.15%
蒸馏水余量
如上所述的成膜助剂为醇酯类成膜剂,优选醇酯十二。
如上所述组分中还可以含有适量香精。
所述的树脂为丙烯酸乳液,优选常州广树化工生产的丙烯酸乳液(GS-220A)。
所述的润湿剂为甘油。
一种适用于干擦的闪光墨水的制备方法,包括如下步骤:
(1)按照上述闪光墨水的配方称取各原料;
(2)将水性染料溶于蒸馏水中;
(3)依次加入树脂、成膜助剂,搅拌10min;
(4)再加入润湿剂、流平剂、渗透剂、防腐剂,300r/min搅拌20min;
(5)转速不变,加入水性铝银浆不断搅拌,直至体系均匀。
与现有墨水相比本发明的有益效果:本发明闪光墨水中所用的水性铝银浆能在墨水涂层表面有闪光的效果,再辅以亮丽的颜色,特别容易吸人眼球,给人以美感。本发明树脂和成膜剂的选择解决了水性铝银浆在墨水中均匀、稳定分散的问题。本发明闪光墨水覆盖性好、涂写流畅、色彩亮丽、绿色环保、易于擦洗。而且风干速度快,有利于后续书写与擦除。本发明闪光墨水制备工艺简单,操作方便,易于工业化生产。
具体实施方式
以下是具体实施例,用于详细说明本发明。
实施例1
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液12g
醇酯十二0.4g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水19.88g
制备方法:
(1)按照上述闪光墨水的配方称取各原料;
(2)将水性染料溶于蒸馏水中;
(3)依次加入树脂、成膜助剂,搅拌10min;
(4)再加入润湿剂、流平剂、渗透剂、防腐剂,300r/min搅拌20min;
(5)转速不变,加入水性铝银浆不断搅拌,直至体系均匀。
实施例2
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.4g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
实施例3
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液20g
醇酯十二0.4g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水11.88g
制备方法同实施例1。
实施例4
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.8g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
实施例5
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.12g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
实施例6
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.16g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
实施例7
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.20g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
实施例8
水性铝银浆4g
水性染料0.4g
GS-220A丙烯酸乳液16g
醇酯十二0.20g
甘油2g
流平剂1.2g
渗透剂0.06g
防腐剂0.06g
蒸馏水15.88g
制备方法同实施例1。
以上实施例仅对本发明进行说明,但本发明不限于上述具体实施例。凡基于本发明做的任何改动或变形均属于本发明要求保护的范围。
Claims (5)
1.一种适用于干擦的闪光墨水,其特征在于,组分按重量百分比计为:
水性铝银浆2.5-5%
水性染料0.5-1%
树脂15-25%
成膜助剂0.5-3%
润湿剂2.5-4%
流平剂1.5-2.5%
渗透剂0.075-0.15%
防腐剂0.075-0.15%
蒸馏水 余量
所述的成膜助剂为:醇酯类成膜剂。
2.如权利要求1所述的一种适用于干擦的闪光墨水,其特征在于,所述的树脂为:丙烯酸乳液。
3.如权利要求1所述的一种适用于干擦的闪光墨水,其特征在于,所述的润湿剂为:甘油。
4.如权利要求1所述的一种适用于干擦的闪光墨水,其特征在于,所述的组分中可含有适量香精。
5.如权利要求1所述的一种适用于干擦的闪光墨水的制备方法,其特征在于,包括如下步骤:
(1)按权利要求1所述墨水组分配比称取各原料;
(2)将水性染料溶于蒸馏水中;
(3)依次加入树脂、成膜助剂,搅拌10min;
(4)再加入润湿剂、流平剂、渗透剂、防腐剂,300r/min搅拌20min;
(5)转速不变,加入水性铝银浆不断搅拌,直至体系均匀。