CN1078449A - Utilize flyash to make light weight glazed tile production technique and product - Google Patents
Utilize flyash to make light weight glazed tile production technique and product Download PDFInfo
- Publication number
- CN1078449A CN1078449A CN93110129A CN93110129A CN1078449A CN 1078449 A CN1078449 A CN 1078449A CN 93110129 A CN93110129 A CN 93110129A CN 93110129 A CN93110129 A CN 93110129A CN 1078449 A CN1078449 A CN 1078449A
- Authority
- CN
- China
- Prior art keywords
- flyash
- production technique
- light weight
- product
- tile production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Utilize flyash to make light weight glazed tile production technique and product, flyash is pulverized the back mix, form three layers of stock cloth, just make Ben Wa through typing with magnesium oxide, magnesium chloride, glass fibre alkali cloth, hydrochloric acid etc.Ben Wa is bellows-shaped, pressure-proof and snap-resistent intensity height, and acid and alkali-resistance, freeze proof heat-resisting, water-intake rate is low, utilization of waste material, escapable cost about 50% is applicable to various buildingss.
Description
The present invention relates to a kind of flyash that utilizes and make light weight glazed tile production technique and product, this product can be widely used on the various buildingss.
Produce a large amount of tankage flyash when producing in heat power plant at present, these tankage all are taken as waste product and throw away, and cause a large amount of wastes, and produce the serious environmental pollution.
Purpose of the present invention is exactly that a kind of heat power plant's flyash leftover bits and pieces light weight glazed tile production technique and product of utilizing is provided in order to overcome the deficiencies in the prior art.
Purpose of the present invention can realize by following measure:
This watt prescription comprises magnesium oxide, magnesium chloride, flyash, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, six meta-acid sodium.
Purpose of the present invention can also realize by following measure:
This watt by three layered materials, and two-layer cloth is formed.
This watt concrete manufacture craft is as follows:
Batching
It is standby at first the magnesium chloride water to be dissolved into Be24 ° of-28 ° of liquid of Baume concentration.Get 100 parts of magnesium oxide weight, getting magnesium chloride liquid, flyash, hydrochloric acid, Precondensed UreaFormaldehyde Resin, tertiary sodium phosphate, Sodium hexametaphosphate 99 by proportioning stirred 15-20 minute with magnesium oxide, add tributyl phosphate again, stirred 5-10 minute again, slurry is accomplished fluently even back and is taken out standby.
The system watt
Mould is placed level attitude, mylar is taped against on the case, it is floating with trowel that the batching of accomplishing fluently slurry is poured on the film last layer, spread the layer of glass neutral-alkaline cloth then, the batching of falling one deck is floating with trowel again, and dead cloth mesh fan, repave the layer of glass neutral-alkaline cloth then, the batching of falling one deck is floating with trowel again, repaves one deck mylar then, above the scraping thin film, till the steam bubble in the interlayer being scraped the back.The work in-process of picking up moulding then are put on the mould, pick up above another piece mould is buckled in batching heating voluntarily at this moment again, cooling naturally after slaking 2-2.5 hour, temperature drops to 60-80 ℃, and molding goes out finished product, finalizes the design 15-20 days (20-30 days winter) after cutting.
Press magnesium oxide (content is more than 87%) weight ratio, get its content of magnesium chloride liquid 80-95%(more than 45%), flyash 20-60%, hydrochloric acid 450-550 milliliter, Precondensed UreaFormaldehyde Resin 4-6 ‰, tertiary sodium phosphate 1.7-2.2 ‰, Sodium hexametaphosphate 99 2-5 ‰, tbp 2-4 ‰.
Flyash is through pulverizing more than 120 orders hydrochloric acid (industrial concentration 36-38%).
Glass fibre neutral-alkaline cloth 2.5 * 2.5 * 0.2.
The present invention is a bellows-shaped, and thickness is at 4-6mm.
This product approval temperature is more than 0 ℃.
This formed product mould is the swage tool.
The making in winter of this product adds oxalic acid (molecular weight 162.07) 2-5 ‰, adds sodium silicate waterproofer 4-5 ‰ summer.
The tankage that with chlorine oxygen magnesium are the terra-cotta of major ingredient production are reached more than 120 orders through pulverizing, with flyash, magnesium oxide, magnesium chloride, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, be mixed in proportion again, prepare burden earlier and afterwards make watt.
The proportioning of various compositions and manufacture craft are pressed the magnesium oxide weight ratio with claim 2,3,4,5,6,7,8 identical.Add tankage 10-30%.
The present invention has following advantage:
1, resistance to compression, folding strength height.
2, acid and alkali-resistance, freeze proof heat-resisting, water-intake rate is low.
3, utilization of waste material saves material, and reduces cost about 50%.
4, in light weight, be convenient to processing and transportation.
Embodiment 1
Batching
It is standby at first the magnesium chloride water to be dissolved into B ' e24 ° of-28 ° of liquid of ripple concentration, and the flyash material is pulverized more than 120 orders.Get magnesium oxide 50kg, magnesium chloride liquid 45kg, flyash 20kg, 500 milliliters of hydrochloric acid (industrial concentration 36-38%), Precondensed UreaFormaldehyde Resin accounts for 2 ‰ of magnesium oxide weight, tertiary sodium phosphate accounts for 1.7 ‰, Sodium hexametaphosphate 99 accounts for 5 ‰, stirs after 15 minutes in stirrer simultaneously, adds tbp again and accounts for 4 ‰, restir 5 minutes is accomplished fluently the taking-up of slurry back and is transported to system watt worktable.
The system watt
The swage tool is placed level attitude, mylar is taped against on the case, the batching of accomplishing fluently slurry is poured on the film last layer, floating with trowel, spread one deck 2.5 * 5.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, the batching of falling one deck again, floating with trowel, and dead the hole pattern fan, repave one deck 2.5 * 2.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, the batching of falling one deck is floating with trowel again.The work in-process of picking up moulding then are put on the swage tool, pick up again above a swage tool is anchored to, at this moment the heating that in half an hour, reacts of preparing burden, curing time 2-2.5 hour, temperature reached between 100 ℃-300 ℃, after heat release is finished, naturally cooling, when temperature dropped to 60 ℃-80 ℃, molding went out finished product, finished product is finalized the design 15-20 days (20-30 days winter) at the typing storehouse after buck cuts, and realizes tile of finished product at last.In batching, add oxalic acid (molecular weight 162.07) 4 ‰ when produce winter, in batching, add sodium silicate waterproofer 5 ‰ when produce summer.
Embodiment 2
Batching
It is standby at first the magnesium chloride water to be dissolved into B ' e24 ° of-28 ° of liquid of Baume concentration, the flyash material is pulverized more than 120 orders, the tankage pulverizing that with chlorine oxygen magnesium is the terra-cotta of major ingredient production is reached more than 120 orders, get magnesium oxide 50kg, magnesium chloride liquid 45kg, flyash 20kg, tankage 20kg, 500 milliliters of hydrochloric acid (industrial concentration 36-38%), Precondensed UreaFormaldehyde Resin account for magnesium oxide heavy 2 ‰, tertiary sodium phosphate accounts for 1.7 ‰, Sodium hexametaphosphate 99 accounts for 5 ‰, stirs after 15 minutes in stirrer simultaneously, adds tbp again and accounts for 4 ‰, restir 5 minutes is accomplished fluently the taking-up of slurry back and is transported to system watt worktable.
The system watt
The swage tool is placed level attitude, mylar is taped against on the case, the batching of accomplishing fluently slurry is poured on the film last layer, floating with trowel, spread one deck 2.5 * 5.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, again the batching of falling one deck, floating with trowel, and dead the mesh fan, repave one deck 2.5 * 2.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, again the batching of falling one deck, floating with trowel, the work in-process of picking up moulding then are put on the swage tool, pick up above a mould is anchored to the heating that reacts in half an hour of at this moment preparing burden again, curing time 2-2.5 hour, temperature has reached between 100 ℃-300 ℃, after heat release is finished, and cooling naturally, when temperature drops to 60 ℃-80 ℃, molding goes out finished product, and finished product is finalized the design 15-20 days (20-30 days winter) at the typing storehouse after buck cuts, and realizes tile of finished product at last.In batching, add oxalic acid (molecular weight 162.07) 4 ‰ when produce winter, in batching, add sodium silicate waterproofer 5 ‰ when produce summer.
Claims (10)
1, utilize flyash to make light weight glazed tile production technique and product, it is characterized in that: this watt prescription comprises magnesium oxide, magnesium chloride, flyash, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, six meta-acid sodium.
2, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that: this watt by three layered materials, and two-layer cloth is formed.
3, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that:
Batching:
It is standby at first the magnesium chloride water to be dissolved into B ' e24 ° of-28 ° of liquid of Baume concentration, get 100 parts of magnesium chloride weight, get magnesium chloride liquid by proportioning, flyash, hydrochloric acid, Precondensed UreaFormaldehyde Resin, tertiary sodium phosphate, Sodium hexametaphosphate 99 stirred 15-20 minute with magnesium oxide, add tbp again, stirred 5-10 minute, slurry is accomplished fluently even back and is taken out standby again.
The system watt
Mould is placed level attitude, mylar is taped against on the case, it is floating with trowel that the batching of accomplishing fluently slurry is poured on the film last layer, spread the layer of glass neutral-alkaline cloth then, the batching of falling one deck again, floating with trowel, and dead cloth mesh fan, repave the layer of glass neutral-alkaline cloth then, the batching of falling one deck again, floating with trowel, spread one deck mylar then, above the scraping thin film, till the steam bubble in the interlayer is scraped away, the work in-process of picking up moulding then are put on the mould, pick up above another piece mould is buckled in batching heating voluntarily at this moment again, cooling naturally after slaking 2-2.5 hour, temperature drops to 60-80 ℃, and molding goes out finished product, finalizes the design 15-20 days (20-30 days winter) after cutting.
4, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that: press magnesium oxide (content is more than 87%) weight ratio, get magnesium chloride liquid 80-95%, (its content is more than 45%), flyash 20-60%, hydrochloric acid 450-550 milliliter, Precondensed UreaFormaldehyde Resin 4-6 ‰, tertiary sodium phosphate 1.7-2.2 ‰, Sodium hexametaphosphate 99 2-5 ‰, tbp 2-4 ‰.
5, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that: flyash is through pulverizing more than 120 orders, hydrochloric acid (technology concentration 36-38%), and the glass fibre neutral-alkaline cloth is 2.5 * 2.5 * 0.2.
6, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that: this product is a bellows-shaped, and thickness is at 4-6mm.
7, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that; This formed product mould is the swage tool, and production and setting temperature are more than 0 ℃.
8, make light weight glazed tile production technique and product according to the said flyash that utilizes of claim 1, it is characterized in that: the making in winter of this product adds oxalic acid (molecular weight 162.07) 2-5 ‰, adds sodium silicate waterproofer 4-5 ‰ summer.
9, make novel terra-cotta production technique of matter gently and product according to the said flyash that utilizes of claim 1, it is characterized in that: the tankage that with chlorine oxygen magnesium are the terra-cotta of major ingredient production are reached more than 120 orders through pulverizing, again with flyash magnesium oxide, magnesium chloride, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, be mixed in proportion, prepare burden earlier and afterwards make watt.
10, make novel light glass tile production technique and product according to claim 1 and the 9 said flyash that utilize, it is characterized in that: the proportioning of various compositions and manufacture craft are with claim 2,3,4,5,6,7,8 identical, press the magnesium oxide weight ratio, add tankage 10-30%.