CN1075113A - Light weight glazed tile production technique and product - Google Patents
Light weight glazed tile production technique and product Download PDFInfo
- Publication number
- CN1075113A CN1075113A CN 92109963 CN92109963A CN1075113A CN 1075113 A CN1075113 A CN 1075113A CN 92109963 CN92109963 CN 92109963 CN 92109963 A CN92109963 A CN 92109963A CN 1075113 A CN1075113 A CN 1075113A
- Authority
- CN
- China
- Prior art keywords
- product
- production technique
- light weight
- glazed tile
- tile production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of light weight glazed tile production technique and product, form by magnesium oxide, magnesium chloride, talcum powder, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, mill base etc., through batch mixing, spread three layers of stock cloth again through nature typing just make Ben Wa.Ben Wa is bellows-shaped, pressure-proof and snap-resistent intensity height, and acid and alkali-resistance, freeze proof heat-resisting, water-intake rate is low, and good looking appearance can be widely used on the various buildingss.
Description
The present invention relates to a kind of light weight glazed tile production technique and product, this product can be widely used on the various buildingss.
Existing magnesia watt is to be that main raw material adds an amount of magnesium chloride, glass fibre is made with magnesium oxide at present, and this watt shortcoming is the water-intake rate height, and easily deliquescence returns halogen, and pressure-proof and snap-resistent intensity is low, and the life-span is short.
Purpose of the present invention is exactly that a kind of light weight glazed tile production technique and product are provided in order to overcome the deficiencies in the prior art.
Purpose of the present invention can realize by following measure:
This terra-cotta are made up of three layers of stock cloth, and its prescription comprises magnesium oxide, magnesium chloride, talcum powder, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, mill base, and its production technique is first batching system watt then.
Batching
It is standby at first the magnesium chloride water to be dissolved into Be24 °～28 ° liquid of Baume concentration.Get 100 parts of magnesium oxide weight, getting magnesium chloride liquid, talcum powder, hydrochloric acid, Precondensed UreaFormaldehyde Resin, tertiary sodium phosphate, Sodium hexametaphosphate 99 in proportion stirred 15～20 minutes with magnesium oxide, add tbp again, mill base stirred 5～10 minutes, slurry is accomplished fluently even back and is taken out standby.
The system watt
Mould is placed level attitude, mylar is taped against on the case, it is floating with trowel that the batching of accomplishing fluently slurry is poured on the film last layer, spread the layer of glass neutral-alkaline cloth then, the batching of falling one deck again, floating with trowel, and dead cloth mesh fan, repave the layer of glass neutral-alkaline cloth then, the batching of falling one deck again, floating with trowel, spread one deck mylar then, above the scraping thin film, till the steam bubble in the interlayer is scraped away, the work in-process of picking up moulding then are put on the mould, pick up above another piece mould is buckled in batching heating voluntarily at this moment again, through slaking cooling naturally after 2～2.5 hours, temperature drops to 60 ℃～80 ℃, and molding goes out finished product, finalizes the design 15～20 days (20～30 days winters) after cutting.
Purpose of the present invention can also realize by following measure:
Press magnesium oxide (content is more than 87%) weight ratio, get its content of magnesium chloride liquid 80～95%(more than 45%), talcum powder 10～30%, 500 milliliters of hydrochloric acid, Precondensed UreaFormaldehyde Resin 2～5 ‰, tertiary sodium phosphate 1.7～2 ‰, Sodium hexametaphosphate 99 5～10 ‰, tbp 4～5 ‰.
The glass fibre neutral-alkaline cloth is 2.5 * 2.5 * 0.2.
Talcum powder more than 120 orders, hydrochloric acid (industrial concentration 36～38%).
This product is a bellows-shaped, and thickness is at 4～5mm.
Production and setting temperature are more than 0 ℃.
Mould is the swage tool.
Add oxalic acid (molecular weight 162.07) winter, add sodium silicate waterproofer 5～10 ‰ summer.
The present invention has following advantage:
1. resistance to compression, folding strength height.
2. acid and alkali-resistance, freeze proof heat-resisting, water-intake rate is low.
3. make simply, cost is low.
Embodiment
Batching
It is standby at first the magnesium chloride water to be dissolved into Be24 °～28 ° liquid of Baume concentration.Get magnesium oxide 50kg, magnesium chloride liquid 45kg, 120 purpose talcum powder 10kg, 500 milliliters of hydrochloric acid (industrial concentration 36～38%), Precondensed UreaFormaldehyde Resin accounts for 2 ‰ of magnesium oxide weight, tertiary sodium phosphate accounts for 1.7 ‰, and Sodium hexametaphosphate 99 accounts for 5 ‰, stirs after 15 minutes in stirrer simultaneously, add tbp again and account for 4 ‰, mill base is an amount of, and restir 5 minutes is accomplished fluently the taking-up of slurry back and transported to system watt worktable.
The system watt
The swage tool is placed level attitude, mylar is taped against on the case, the batching of accomplishing fluently slurry is poured on the film last layer, floating with trowel, spread one deck 2.5 * 2.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, again the batching of falling one deck, floating with trowel, and dead the mesh fan, repave one deck 2.5 * 2.5 * 0.2 glass fibre neutral-alkaline cloth 2 linear meter then, again the batching of falling one deck, floating with trowel, spread one deck mylar then, above the instrument scraping thin film, till the steam bubble in the interlayer scraped away.The work in-process of picking up moulding then are put on the swage tool, pick up again above a swage tool is anchored to, at this moment the heating that in half an hour, reacts of preparing burden, 2～2.5 hours curing times, temperature has reached between 100 ℃～300 ℃, after heat release is finished, naturally cooling, when temperature dropped to 60 ℃～80 ℃, molding went out finished product, finished product is finalized the design 15～20 days (20～30 days winters) at the typing storehouse after buck cuts, and realizes tile of finished product at last.In batching, add oxalic acid (molecular weight 162.07) 4 ‰ when produce winter, in batching, add sodium silicate waterproofer 5 ‰ when produce summer.
Claims (8)
1, a kind of light weight glazed tile production technique and product is characterized in that; This terra-cotta are by three layered materials, and two-layer cloth is formed, and its prescription comprises magnesium oxide, magnesium chloride, talcum powder, hydrochloric acid, Precondensed UreaFormaldehyde Resin, defoamer, tertiary sodium phosphate, glass fibre neutral-alkaline cloth, mill base, and its production technique is to prepare burden earlier afterwards to make watt,
Batching
It is standby at first the magnesium chloride water to be dissolved into Be24 °～28 ° liquid of Baume concentration, get 100 parts of magnesium oxide weight, getting magnesium chloride liquid, talcum powder, hydrochloric acid, Precondensed UreaFormaldehyde Resin, tertiary sodium phosphate, Sodium hexametaphosphate 99 by proportioning stirred 15～20 minutes with magnesium oxide, adding tbp, mill base again stirred 5～10 minutes again, slurry is accomplished fluently even back and is taken out standby
The system watt
Mould is placed level attitude, mylar is taped against on the case, it is floating with trowel that the batching of accomplishing fluently slurry is poured on the film last layer, spread the layer of glass neutral-alkaline cloth then, the batching of falling one deck again, floating with trowel, and dead cloth mesh fan, repave layer of glass cloth then, the batching of falling one deck again, floating with trowel, spread one deck mylar then, above the scraping thin film, till the steam bubble in the interlayer is scraped away, the work in-process of picking up moulding then are put on the mould, pick up above another piece mould is buckled in batching heating voluntarily at this moment again, through slaking cooling naturally after 2～2.5 hours, temperature drops to 60 ℃～80 ℃, and molding goes out finished product, finalizes the design after cutting 15～20 days (20～30 days winters).
2, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: press magnesium oxide (content is more than 87%) weight ratio, get its content of magnesium chloride liquid 80～95%(more than 45%), talcum powder 10～30%, 500 milliliters of hydrochloric acid, Precondensed UreaFormaldehyde Resin 2～5 ‰, tertiary sodium phosphate 1.7～2 ‰, Sodium hexametaphosphate 99 5～10 ‰, tbp 4～5 ‰.
3, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: the glass fibre neutral-alkaline cloth is 2.5 * 2.5 * 0.2.
4, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: talcum powder more than 120 orders, hydrochloric acid (industrial concentration 36～38).
5, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: this product is a bellows-shaped, and thickness is at 4～5mm.
6, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: production and setting temperature are more than 0 ℃.
7, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: mould is the swage tool.
8, according to said light weight glazed tile production technique of claim 1 and product, it is characterized in that: add oxalic acid 4～5 ‰ winter, add sodium silicate waterproofer 5～10 ‰ summer.