CN107841214A - A kind of construction technology of building external paint - Google Patents
A kind of construction technology of building external paint Download PDFInfo
- Publication number
- CN107841214A CN107841214A CN201711193169.3A CN201711193169A CN107841214A CN 107841214 A CN107841214 A CN 107841214A CN 201711193169 A CN201711193169 A CN 201711193169A CN 107841214 A CN107841214 A CN 107841214A
- Authority
- CN
- China
- Prior art keywords
- parts
- construction technology
- building external
- water
- external paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of construction technology of building external paint, is specially:To the building wall being surface-treated, use spray gun that paint slurry is sprayed on metope in a manner of spraying, thickness of coating layer is 5 8mm;The spray gun spraying air pressure is 3.2 3.5kg/cm2, spray tip is 20 25cm apart from the distance of metope, and angle of inclination is 72 80 degree.Coating application technique of the present invention is simple, used coating is environmentally safe, wherein adding the raw material coating such as far infrared nano powder, hollow beads, closed-cell expanded perlite, fire retardant by rational proportion not only has good reflective thermal-insulating heat-blocking action, while also has good fire resistance.
Description
Technical field
The invention belongs to building coating technical field, and in particular to a kind of construction technology of building external paint.
Background technology
There is building coating decoration functions, defencive function and livability to improve function.Proportion shared by various functions is because making
It is not quite similar with purpose difference.Decoration functions are to improve the function of its appearance value by the beautification of building.Mainly
Design design and the design of three-dimensional pattern design in terms of including plane color, pattern and gloss.But will be with building in itself
The size and shape of moulding and base material in itself is engaged, and just can fully play out.Defencive function refers to protect building not
Function that is protected from environmental and destroying.Different types of content for being required by protective defencive function is also different.Such as
It is indoor just very big with index difference that is reaching required by outdoor application.Some buildings are to mould proof, fire prevention, insulation, corrosion resistant
Erosion etc. has particular/special requirement.Livability improves function mainly for indoor application, just contributes to improve the work(of living environment
Can, such as sound-proofing, the effect of sound absorption properties coating and its classification, anti-condensation.
With the deep propulsion being becoming tight the day of the energy with country in terms of energy-conserving and environment-protective and sustainable development, reflective insulation
The application of coating is more and more extensive.Reflective heat-insulation paint is a kind of new energy-saving material developed in recent years, by effective
Ground reflection, barrier, the energy of radiation sunshine, can substantially reduce skin, roof and indoor temperature, so as to effectively reduce
The energy consumption of refrigeration plant such as air-conditioning under the high temperature conditions.Therefore, reflective heat-insulation paint can improve working environment, save again
The substantial amounts of energy.But though the reflective heat-insulation paint produced in the market does not have with certain reflective insulation effect
There is fire resistance, limit its application.
The content of the invention
For deficiency of the prior art, the invention provides a kind of building external paint with reflective insulation effect
Construction technology.
Specifically, the construction technology of building external paint of the present invention:To the building wall being surface-treated, adopt
Paint slurry is sprayed on metope in a manner of spraying with spray gun, thickness of coating layer 5-8mm;The spray gun spraying air pressure is
3.2-3.5kg/cm2, spray tip is 20-25cm apart from the distance of metope, and angle of inclination is 72-80 degree;The coating by with
The component of lower parts by weight is prepared:Water-based acrylic resin 200-300 parts, aqueous elastic resin 50-100 parts, deionization
Water 300-400 parts, titanium dioxide 80-120 parts, far infrared nano powder 30-50 parts, sepiolite powder 30-50 parts, hollow beads 30-50
Part, closed-cell expanded perlite 30-50 parts, nanometer calcium silicates 30-50 parts, fire retardant 3-5 parts, thickener 10-50 parts, dispersant 1-
3 parts, defoamer 1-3 parts, preservative 0.5-1 parts, coalescents 0.1-1 parts.
As the further explanation of the present invention, the coating is prepared using following steps successively:
(1)Water-based acrylic resin 200-300 parts, aqueous elastic resin 50-100 parts, deionized water 300-400 parts are mixed,
Obtain component A material;
(2)Component A material is put into container, adds the raw material of following parts by weight while stirring:Titanium dioxide 80-120 parts, far infrared
Nano powder 30-50 parts, sepiolite powder 30-50 parts, hollow beads 30-50 parts, closed-cell expanded perlite 30-50 parts, nanometer silicic acid
Calcium 30-50 parts, fire retardant 3-5 parts, dispersant 1-3 parts, defoamer 1-3 parts, preservative 0.5-1 parts, stir, obtain B component
Material;
(3)The raw material of following parts by weight is added in B component material:Thickener 10-50 parts, coalescents 0.1-1 parts, stirring are equal
It is even, you can.
Water-based acrylic resin includes emulsion acrylic resin, aqueous acrylic resin dispersion(Also known as water-dilutable propylene
Acid)And acrylic resin aqueous solution.Emulsion is mainly emulsified in water by oiliness vinyl monomer draws in water-based free radical initiator
Synthesis is given, and resin water dispersion is synthesized by the different technique of free radical solution polymerization or progressively polymerisation in solution etc.
's.Water soluble acrylic resin belongs to anionic more, in the monomer of copolymer resins from appropriate unsaturated carboxylic acid such as acrylic acid,
Methacrylic acid, maleic anhydride, methylene-succinic acid etc., make to carry carboxyl on side chain, then neutralized with organic amine or ammoniacal liquor
Water solubility is obtained into salt.In addition can also be by introducing-OH hydroxyls ,-CONH2 acyls from appropriate monomer on resin side chain
The hydrophilic radical such as amino or-O- ehter bonds and increase the water solubility of resin.Water, but its water can be dissolved in by neutralizing into the acrylic resin of salt
Dissolubility is simultaneously not bery strong, the liquid of milkiness shape or the solution that viscosity is very high is frequently formed, so must add in water-soluble resin
Enter a certain proportion of hydrophilic cosolvent to increase the water solubility of resin.
Nano inorganic far-infrared powder is with the refined compound far infrared health care of novel nano formed of special nanometer composite technology
Functional material.Detected through China National Measuring Science Research Inst., the infrared emittance under normal temperature in the μ m of wavelength 2-18 is up to
92%.Japan is in the leading level in the world in the research and development of normal temperature far-infrared technique, and according to Japan Patent introduction, far infrared is spun
The ceramic powder normal temperature radiance that fabric is selected is generally higher than 0.65, and preferably more than 0.75, best is more than 0.90.Now, far
The particle diameter of infrared nanometer powder can produce -80 nanometers of 1250 mesh.Nano composite inorganic far infrared health care material has and human body radiation
The farsighted infrared emittance of respective wavelength is absorbed, is good body-care far-infrared radiation material, there is uvioresistant, kill
Bacterium eliminates peculiar smell, the function such as prevent and cure diseases, and can effectively improve microcirculation in human body, promotes normal microcirculation blood flow increase by 2 ~ 3
Times, tissue oxygen supply is improved, improves metabolism, strengthen immunity.
Sepiolite has extremely strong absorption, decolourizes and the performance such as scattered, also there is a high heat endurance, and heat-resisting quantity is reachable
1500 ~ 1700 DEG C, formative nature, insulating properties, salt resistance degree are all very good.
The water-based acrylic resin selects anion-type water-thinned acrylic resin.
The aqueous elastic resin selects ultraviolet light self-crosslinking elastic pure acrylic acid resin.
The hollow beads are made up of glass hollow microballon and ceramic hollow microballon, and glass hollow microballon and ceramic hollow are micro-
The mass ratio of pearl is 3:1.
The particle diameter of the closed-cell expanded perlite is 1-1.5mm.
The fire retardant selects Firebrake ZB or aluminium hydroxide.
The thickener selects polyurethane thickener.
The dispersant selects inorganic silicic acid salt dispersant.
The defoamer is from this DF-7010 type defoamer of hamming.
The preservative selects isothiazoline -3- ketone preservatives.
The coalescents select the coalescents of alcohol ester 12.
Coating application technique of the present invention is simple, and used coating is environmentally safe, wherein being added by rational proportion
The raw materials such as far infrared nano powder, hollow beads, closed-cell expanded perlite, fire retardant cause coating that not only there is reflection well to protect
Warm heat-blocking action, while also there is good fire resistance.
Embodiment
The present invention is described in further detail below in conjunction with specific embodiment, the present embodiment is only more clear to present invention work
The explanation of Chu, rather than limitation of the present invention, made under other any Spirit Essences and principle without departing from the present invention
Change, modify, substitute, combine, simplify, should be equivalent substitute mode, be included within protection scope of the present invention.
Embodiment 1
A kind of construction technology of building external paint, it is specifically:To the building wall being surface-treated, spray gun is used to spray
Paint slurry is sprayed on metope by the mode of painting, thickness of coating layer 8mm;The spray gun spraying air pressure is 3.2kg/cm2, spray
The distance of rifle nozzle distance metope is 20cm, and angle of inclination is 80 degree;
Wherein, the preparation method of the coating is as follows:
(1)By anion-type water-thinned acrylic resin 300kg, ultraviolet light self-crosslinking elastic pure acrylic acid resin 80kg, deionization
Water 300kg is mixed, and obtains component A material;
(2)Component A material is put into container, adds the raw material of following weight while stirring:The kg of titanium dioxide 120, far infrared nano
The kg of powder 40, the kg of sepiolite powder 50, hollow beads(It is made up of glass hollow microballon and ceramic hollow microballon, wherein glass hollow
The mass ratio of microballon and ceramic hollow microballon is 3:1)40 kg, closed-cell expanded perlite(Particle diameter is 1-1.5mm)50 kg, nanometer
The kg of calcium silicates 40, aluminium hydroxide fire retardant 3kg, the kg of inorganic silicic acid salt dispersant 3, hamming this DF-7010 types defoamer 2
Kg, the kg of isothiazoline -3- ketones preservative 1, stir, obtain B component material;
(3)The raw material of following weight is added in B component material:The kg of polyurethane thickener 40, the coalescents 0.2 of alcohol ester 12
Kg, stir, you can.
Embodiment 2
A kind of construction technology of building external paint, it is specifically:To the building wall being surface-treated, spray gun is used to spray
Paint slurry is sprayed on metope by the mode of painting, thickness of coating layer 6mm;The spray gun spraying air pressure is 3.4kg/cm2, spray
The distance of rifle nozzle distance metope is 22cm, and angle of inclination is 70 degree;
Wherein, the preparation method of the coating is as follows:
(1)By anion-type water-thinned acrylic resin 240kg, ultraviolet light self-crosslinking elastic pure acrylic acid resin 100kg, deionization
Water 350kg is mixed, and obtains component A material;
(2)Component A material is put into container, adds the raw material of following weight while stirring:The kg of titanium dioxide 100, far infrared nano
The kg of powder 40, sepiolite powder 35kg, hollow beads(It is made up of glass hollow microballon and ceramic hollow microballon, wherein glass hollow is micro-
The mass ratio of pearl and ceramic hollow microballon is 3:1)35 kg, closed-cell expanded perlite(Particle diameter is 1-1.5mm)35 kg, nano-silicon
Sour calcium 40kg, zinc borate flame retardant 5kg, the kg of inorganic silicic acid salt dispersant 1, this DF-7010 type defoamer of hamming 2kg, different thiophene
The kg of oxazoline -3- ketones preservative 0.8, stirs, obtains B component material;
(3)The raw material of following weight is added in B component material:The kg of polyurethane thickener 15, the coalescents 0.3kg of alcohol ester 12,
Stir, you can.
Embodiment 3
A kind of construction technology of building external paint, it is specifically:To the building wall being surface-treated, spray gun is used to spray
Paint slurry is sprayed on metope by the mode of painting, thickness of coating layer 5-8mm;The spray gun spraying air pressure is 3.2-3.5kg/
Cm2, spray tip are 20-25cm apart from the distance of metope, and angle of inclination is 72-80 degree;
Wherein, the preparation method of the coating is as follows:
(1)By anion-type water-thinned acrylic resin 200kg, ultraviolet light self-crosslinking elastic pure acrylic acid resin 80kg, deionization
Water 350kg is mixed, and obtains component A material;
(2)Component A material is put into container, adds the raw material of following weight while stirring:The kg of titanium dioxide 100, far infrared nano
Powder 30kg, sepiolite powder 40kg, hollow beads(It is made up of glass hollow microballon and ceramic hollow microballon, wherein glass hollow is micro-
The mass ratio of pearl and ceramic hollow microballon is 3:1)40kg, closed-cell expanded perlite(Particle diameter is 1-1.5mm)50 kg, nano-silicon
The sour kg of calcium 35, the kg of aluminium hydroxide fire retardant 4, the kg of inorganic silicic acid salt dispersant 2, hamming this DF-7010 types defoamer 3
Kg, isothiazoline -3- ketone preservative 0.5kg, stir, obtain B component material;
(3)The raw material of following weight is added in B component material:The kg of polyurethane thickener 35, the coalescents 0.5kg of alcohol ester 12,
Stir, you can.
Embodiment 4
A kind of construction technology of building external paint, it is specifically:To the building wall being surface-treated, spray gun is used to spray
Paint slurry is sprayed on metope by the mode of painting, thickness of coating layer 7mm;The spray gun spraying air pressure is 3.4kg/cm2, spray
The distance of rifle nozzle distance metope is 24cm, and angle of inclination is 78 degree;
Wherein, the preparation method of the coating is as follows:
(1)By anion-type water-thinned acrylic resin 260kg, ultraviolet light self-crosslinking elastic pure acrylic acid resin 110kg, deionization
Water 320kg is mixed, and obtains component A material;
(2)Component A material is put into container, adds the raw material of following weight while stirring:The kg of titanium dioxide 80, far infrared nano
The kg of powder 35, sepiolite powder 40kg, hollow beads(It is made up of glass hollow microballon and ceramic hollow microballon, wherein glass hollow is micro-
The mass ratio of pearl and ceramic hollow microballon is 3:1)20kg, closed-cell expanded perlite(Particle diameter is 1-1.5mm)30kg, nanometer silicic acid
Calcium 25kg, zinc borate flame retardant 10kg, the kg of inorganic silicic acid salt dispersant 5, this DF-7010 type defoamer of hamming 3kg, different thiophene
Oxazoline -3- ketone preservative 1kg, stir, obtain B component material;
(3)The raw material of following weight is added in B component material:The kg of polyurethane thickener 20, the coalescents 0.8kg of alcohol ester 12,
Stir, you can.
Embodiment 5
A kind of construction technology of building external paint, it is specifically:To the building wall being surface-treated, spray gun is used to spray
Paint slurry is sprayed on metope by the mode of painting, thickness of coating layer 6mm;The spray gun spraying air pressure is 3.5kg/cm2, spray
The distance of rifle nozzle distance metope is 22cm, and angle of inclination is 75 degree;
Wherein, the preparation method of the coating is as follows:
(1)By anion-type water-thinned acrylic resin 250kg, ultraviolet light self-crosslinking elastic pure acrylic acid resin 100kg, deionization
Water 400kg is mixed, and obtains component A material;
(2)Component A material is put into container, adds the raw material of following weight while stirring:The kg of titanium dioxide 80, far infrared nano
The kg of powder 50, the kg of sepiolite powder 30, hollow beads(It is made up of glass hollow microballon and ceramic hollow microballon, wherein glass hollow
The mass ratio of microballon and ceramic hollow microballon is 3:1)50 kg, closed-cell expanded perlite(Particle diameter is 1-1.5mm)40 kg, nanometer
The kg of calcium silicates 40, the kg of zinc borate flame retardant 3, the kg of inorganic silicic acid salt dispersant 3, hamming this DF-7010 types defoamer 1
Kg, the kg of isothiazoline -3- ketones preservative 1, stir, obtain B component material;
(3)The raw material of following weight is added in B component material:The kg of polyurethane thickener 15, the coalescents 0.5 of alcohol ester 12
Kg, stir, you can.
Claims (7)
1. a kind of construction technology of building external paint, it is characterised in that to the building wall being surface-treated, using spray
Paint slurry is sprayed on metope by rifle in a manner of spraying, thickness of coating layer 5-8mm;The spray gun spraying air pressure is 3.2-
3.5kg/cm2, spray tip is 20-25cm apart from the distance of metope, and angle of inclination is 72-80 degree;The coating is by following heavy
The component of amount number is prepared:Water-based acrylic resin 200-300 parts, aqueous elastic resin 50-100 parts, deionized water
300-400 parts, titanium dioxide 80-120 parts, far infrared nano powder 30-50 parts, sepiolite powder 30-50 parts, hollow beads 30-50 parts,
Closed-cell expanded perlite 30-50 parts, nanometer calcium silicates 30-50 parts, fire retardant 3-5 parts, thickener 10-50 parts, dispersant 1-3
Part, defoamer 1-3 parts, preservative 0.5-1 parts, coalescents 0.1-1 parts.
2. the construction technology of building external paint according to claim 1, it is characterised in that the coating is successively using following
Step is prepared:
(1)The raw material of following parts by weight is mixed:Water-based acrylic resin 200-300 parts, aqueous elastic resin 50-100 parts, go
Ionized water 300-400 parts, obtain component A material;
(2)Component A material is put into container, adds the raw material of following parts by weight while stirring:Titanium dioxide 80-120 parts, far infrared
Nano powder 30-50 parts, sepiolite powder 30-50 parts, hollow beads 30-50 parts, closed-cell expanded perlite 30-50 parts, nanometer silicic acid
Calcium 30-50 parts, fire retardant 3-5 parts, dispersant 1-3 parts, defoamer 1-3 parts, preservative 0.5-1 parts, stir, obtain B component
Material;
(3)The raw material of following parts by weight is added in B component material:Thickener 10-50 parts, coalescents 0.1-1 parts, stirring are equal
It is even, you can.
3. the construction technology of building external paint according to claim 2, it is characterised in that the water-based acrylic resin choosing
With anion-type water-thinned acrylic resin.
4. the construction technology of building external paint according to claim 2, it is characterised in that the aqueous elastic resin is selected
Ultraviolet light self-crosslinking elastic pure acrylic acid resin.
5. the construction technology of building external paint according to claim 2, it is characterised in that the hollow beads are by glass
The mass ratio of empty microballon and ceramic hollow microballon composition, glass hollow microballon and ceramic hollow microballon is 3:1.
6. the construction technology of building external paint according to claim 2, it is characterised in that the closed-cell expanded perlite
Particle diameter is 1-1.5mm.
7. the construction technology of building external paint according to claim 2, it is characterised in that the fire retardant selects Firebrake ZB
Or aluminium hydroxide;The thickener selects polyurethane thickener;The dispersant selects inorganic silicic acid salt dispersant;It is described to disappear
Infusion is from this DF-7010 type defoamer of hamming;The preservative selects isothiazoline -3- ketone preservatives;The film forming helps
The coalescents of alcohol ester 12 are selected in agent.