CN107827395A - A kind of cracking resistance artificial quartz stone plate - Google Patents
A kind of cracking resistance artificial quartz stone plate Download PDFInfo
- Publication number
- CN107827395A CN107827395A CN201711080533.5A CN201711080533A CN107827395A CN 107827395 A CN107827395 A CN 107827395A CN 201711080533 A CN201711080533 A CN 201711080533A CN 107827395 A CN107827395 A CN 107827395A
- Authority
- CN
- China
- Prior art keywords
- parts
- artificial quartz
- stone plate
- quartz stone
- cracking resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cracking resistance artificial quartz stone plate, and it is prepared by the raw material of following parts by weight：20 25 parts of quartz sand, 18 35 parts of silica flour, 0.2 0.3 parts of nano silicon, 26 parts of wood fibre, 8 10 parts of unsaturated polyester resin, 12 parts of curing agent, 0.2 3 parts of γ aminopropyl triethoxysilanes, 0.2 0.3 parts of pigment, its solid content >=72% of the unsaturated polyester resin, viscosity are 1.3 1.6Pas（25℃）, acid number is 18 20mgKOH/g.The artificial quartz stone plate of the present invention, which has, solves the problems such as artificial quartz in lump cracking, deformation.The artificial quartz stone plate of the present invention is unlikely to deform, ftractures, bubbles, fades, tarnished, low with production cost, good decorating effect, indeformable feature.
Description
Technical field
The present invention relates to building decoration technology field, more particularly to a kind of cracking resistance artificial quartz stone plate.
Background technology
Artificial quartz in lump（Or Buddha's warrior attendant/hard rock）Cradle is cried when entering Chinese within 2005 and matches sharp stone in Spain,
After artificial quartz in lump is approved by increasing consumer, China in 2006 starts someone and researches and develops artificial quartz in lump, 2007
Year successively has many producers to be proposed domestic artificial quartz in lump.Artificial quartz in lump is as new Artificial construction material, moistureproof, anti-
Acid, spelling property etc. have the advantages of lithotome is incomparable.In natural stone resource increasingly exhausted today, artificial stone
Diamond stone is its best substitute.Meanwhile artificial quartz in lump can make raw material using discarded glass, thus while environmental protection
Resource reutilization is realized, these advantages allow artificial quartz in lump to turn into the upstart of architectural decoration, therefore, are widely used in
The public buildings such as hotel, dining room, bank, hospital, exhibition, laboratory and kitchen countertop, commode, kitchen and bath's metope, dining table, tea
The house decoration such as several, windowsill, door pocket field.
However, artificial quartz in lump of the prior art also has the shortcomings that its is intrinsic, for example, it is easily cracking.
The content of the invention
The defects of in order to make up prior art, the present invention provide a kind of cracking resistance artificial quartz stone plate.
The technical problems to be solved by the invention are achieved by the following technical programs：
A kind of cracking resistance artificial quartz stone plate, it is prepared by the raw material of following parts by weight：Quartz sand 20-25 parts, silica flour
18-35 parts, nano silicon 0.2-0.3 parts, wood fibre 2-6 parts, unsaturated polyester resin 8-10 parts, curing agent 1-2 parts,
Gamma-aminopropyl-triethoxy-silane 0.2-3 parts, pigment 0.2-0.3 parts, its solid content >=72% of the unsaturated polyester resin, stick
Spend for 1.3-1.6Pas（25℃）, acid number 18-20mgKOH/g.
The nano silicon that the present invention uses is added in quartzite slate, can play a part of nano particle, can
Improve the toughness of quartzite slate.
Further, the curing agent is peroxidating（2 ethyl hexanoic acid）The tert-butyl ester, methyl ethyl ketone peroxide, benzoyl peroxide first
Combination more than one or both of tert-butyl acrylate or fat polyamine.
Further, the pigment is titanium white, iron oxide yellow, iron oxide red, barba hispanica, cadmium red, cadmium yellow, carbon black, iron oxide black, azophosphine, phthalein
One or more in dark green and phthalocyanine blue.
The present invention has the advantages that：
（1）The artificial quartz stone plate of the present invention, which has, solves the problems such as artificial quartz in lump cracking, deformation.
（2）The artificial quartz stone plate of the present invention is unlikely to deform, ftractures, bubbles, fades, tarnished, and has production
Cost is low, good decorating effect, indeformable feature.
Embodiment
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Embodiment 1
A kind of cracking resistance artificial quartz stone plate, it is prepared by the raw material of following parts by weight：22 parts of quartz sand, silica flour 25
Part, 0.2 part of nano silicon, 4 parts of wood fibre, 9 parts of unsaturated polyester resin, 1 part of curing agent, the ethoxy of γ-aminopropyl three
1.5 parts of base silane, 0.2 part of pigment, its solid content >=72% of the unsaturated polyester resin, viscosity 1.3-1.6Pas（25
℃）, acid number 18-20mgKOH/g；Wherein described curing agent is peroxidating（2 ethyl hexanoic acid）The tert-butyl ester；The pigment is titanium
In vain.
Embodiment 2
A kind of cracking resistance artificial quartz stone plate, it is prepared by the raw material of following parts by weight：20 parts of quartz sand, silica flour 35
Part, 0.2 part of nano silicon, 2 parts of wood fibre, 8 parts of unsaturated polyester resin, 1 part of curing agent, the ethoxy of γ-aminopropyl three
0.2 part of base silane, 0.2 part of pigment, its solid content >=72% of the unsaturated polyester resin, viscosity 1.3-1.6Pas（25
℃）, acid number 18-20mgKOH/g；Wherein described curing agent is methyl ethyl ketone peroxide；The pigment is cadmium red.
Embodiment 3
A kind of cracking resistance artificial quartz stone plate, it is prepared by the raw material of following parts by weight：25 parts of quartz sand, silica flour 18
Part, 0.3 part of nano silicon, 6 parts of wood fibre, 10 parts of unsaturated polyester resin, 2 parts of curing agent, the ethoxy of γ-aminopropyl three
3 parts of base silane, 0.3 part of pigment, its solid content >=72% of the unsaturated polyester resin, viscosity 1.3-1.6Pas（25℃）,
Acid number is 18-20mgKOH/g；Wherein described curing agent is combination more than one or both of fat polyamine；The face
Expect for azophosphine.
Embodiment described above only expresses embodiments of the present invention, and its description is more specific and detailed, but can not
Therefore the limitation to the scope of the claims of the present invention is interpreted as, as long as the skill obtained using the form of equivalent substitution or equivalent transformation
Art scheme, it all should fall within the scope and spirit of the invention.
Claims (3)
1. a kind of cracking resistance artificial quartz stone plate, it is characterised in that it is prepared by the raw material of following parts by weight：Quartz sand
20-25 parts, silica flour 18-35 parts, nano silicon 0.2-0.3 parts, wood fibre 2-6 parts, unsaturated polyester resin 8-10
Part, curing agent 1-2 parts, gamma-aminopropyl-triethoxy-silane 0.2-3 parts, pigment 0.2-0.3 parts, the unsaturated polyester resin
Its solid content >=72%, viscosity 1.3-1.6Pas（25℃）, acid number 18-20mgKOH/g.
2. cracking resistance artificial quartz stone plate as claimed in claim 1, it is characterised in that the curing agent is peroxidating（2- ethyls
Caproic acid）More than one or both of the tert-butyl ester, methyl ethyl ketone peroxide, peroxidized t-butyl perbenzoate or fat polyamine
Combination.
3. cracking resistance artificial quartz stone plate as claimed in claim 1, it is characterised in that the pigment be titanium white, iron oxide yellow, iron oxide red,
One or more in barba hispanica, cadmium red, cadmium yellow, carbon black, iron oxide black, azophosphine, dark green and phthalocyanine blue.