CN107815868B - A kind of crease-resistant treatment process of POLO shirt - Google Patents
A kind of crease-resistant treatment process of POLO shirt Download PDFInfo
- Publication number
- CN107815868B CN107815868B CN201711140601.2A CN201711140601A CN107815868B CN 107815868 B CN107815868 B CN 107815868B CN 201711140601 A CN201711140601 A CN 201711140601A CN 107815868 B CN107815868 B CN 107815868B
- Authority
- CN
- China
- Prior art keywords
- polo shirt
- crease
- parts
- treatment process
- resistant treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of crease-resistant treatment process of POLO shirt, POLO shirt is made of at least pure cotton of 85% or more quality accounting and the terylene of 10% or more quality accounting, include the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time 1h, mixed liquor include 6-8 parts of MgCl26H2O, 7 parts of BTCA, 93-95 parts of acrylic resins, 2-4 parts of citric acids by mass fraction；2) the POLO shirt after immersion is padded, pick-up rate 75%；3) the POLO shirt after 2) is baked, stoving temperature 130-160, bakes 0.2h.This programme is more likely to pure cotton firstly for the raw material selection of POLO shirt, and for pure cotton amount 85%, whole dress is more comfortable, and by above-mentioned technique, crease-resistant processing is carried out, so that POLO shirt is provided simultaneously with good wrinkle resistance.
Description
Technical field
The present invention relates to the crease-resistant processing of clothes, in particular to a kind of crease-resistant treatment process of POLO shirt.
Background technique
Polo shirt is referred to as tennis shirt (tennis shirt) originally, the clothes worn when being noble's playing polo originally,
Because comfortable, they like the cotta clothes that dress has collar.Over time " polo shirt " (polo just is referred to as by people
Shirt), widely masses liked later, so evolving into general easy suit.
As the general patent disclosure for being CN206576313U such as notification number of the structure of POLO shirt, including garment body,
And it is set to the POLO shirt at the top of garment body；And it is set to the coat-sleeve of garment body top two sides.
Existing POLO shirt is generally mixed by pure cotton or pure cotton+terylene, and pure cotton content is more, and snugness of fit is got over
Good, the ratio of terylene is less susceptible to wrinkle more greatly, general proportion pure cotton: terylene=6:4.Present people increasingly pursues dress and relaxes
Adaptive, but the wrinkle resistance that so will cause POLO shirt dies down.
Summary of the invention
The object of the present invention is to provide a kind of crease-resistant treatment process of POLO shirt, and comfortable, wrinkle resistance after treatment is good.
Above-mentioned technical purpose of the invention has the technical scheme that a kind of crease-resistant processing work of POLO shirt
Skill, POLO shirt is made of at least pure cotton of 85% or more quality accounting and the terylene of 10% or more quality accounting, including is walked as follows
Rapid: 1) the POLO shirt that will be made, which is put into mixed liquor, to be impregnated, and soaking time 1h, mixed liquor includes 6-8 by mass fraction
Part MgCl26H2O, 7 parts of BTCA, 93-95 parts of acrylic resins, 2-4 parts of citric acids；2) the POLO shirt after immersion is soaked
It rolls, pick-up rate 75%；3) the POLO shirt after 2) is baked, stoving temperature 130-160, bakes 0.2h.
This programme is more likely to pure cotton firstly for the raw material selection of POLO shirt, and pure cotton amount is 85%, and whole dress is more
Comfortably, and by above-mentioned technique, crease-resistant processing is carried out, so that POLO shirt is provided simultaneously with good wrinkle resistance.
Further: mixed liquor further includes 4-6 parts of Fe2(SO4)3。
Research shows that Fe is added2(SO4)3.Whole anti-wrinkle effect is more preferably afterwards.
2) and 3) further, between into prebake, prebake temperature 60 C, baking time 30 seconds.
By prebake, certain preheating is carried out to POLO shirt, so that baking progress later is more gentle, which exists
It can a degree of promotion anti-wrinkle effect in actual test.
Further, pick-up rate 72%.
Further, pick-up rate 73%.
Further, pick-up rate 74%.
Further, pick-up rate 75%.
Further, 132 DEG C of stoving temperature.
Further, 147 DEG C of stoving temperature.
Further, 158 DEG C of stoving temperature.
In conclusion the invention has the following advantages: the POLO shirt after process is with easypro through the invention
It is suitable, crease-resistant, and study discovery addition and Fe is added in mixed liquor2(SO4)3It impregnates and carries out carrying out the pre-heat treatment after padding
The wrinkle resistance of POLO shirt can effectively be promoted.
Specific embodiment
Invention is further described in detail below.
This specific embodiment is only explanation of the invention, is not limitation of the present invention, those skilled in the art
Member can according to need the modification that not creative contribution is made to the present embodiment after reading this specification, but as long as at this
All by the protection of Patent Law in the scope of the claims of invention.
BTCA is 1,2,3,4- butane tetracarboxylic acid.
Embodiment 1: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 132 DEG C of stoving temperature,
Bake 3min.
Embodiment 2: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 136 DEG C of stoving temperature,
Bake 3min.
Embodiment 3: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 141 DEG C of stoving temperature,
Bake 3min.
Embodiment 4: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 145 DEG C of stoving temperature,
Bake 3min.
Embodiment 5: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 147 DEG C of stoving temperature,
Bake 3min.
Embodiment 6: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 153 DEG C of stoving temperature,
Bake 3min.
Embodiment 7: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 85% pure cotton and quality accounting
15% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 6 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 158 DEG C of stoving temperature,
Bake 3min.
Embodiment 8: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 90% pure cotton and quality accounting
10% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 7 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 95 parts of acrylic resins, 3 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 72%；3) the POLO shirt after 2) is baked, 155 DEG C of stoving temperature,
Bake 3min.
Embodiment 9: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 90% pure cotton and quality accounting
10% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 7 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 95 parts of acrylic resins, 3 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 73%；3) the POLO shirt after 2) is baked, 155 DEG C of stoving temperature,
Bake 3min.
Embodiment 10: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 90% pure cotton and quality accounting
10% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 7 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 95 parts of acrylic resins, 3 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 74%；3) the POLO shirt after 2) is baked, 155 DEG C of stoving temperature,
Bake 3min.
Embodiment 11: a kind of crease-resistant treatment process of POLO shirt, POLO shirt by quality accounting 90% pure cotton and quality accounting
10% terylene composition, includes the following steps: that 1) the POLO shirt made is put into mixed liquor and impregnates, soaking time
1h, mixed liquor include 7 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 95 parts of acrylic resins, 3 parts of citric acids；It 2) will leaching
POLO shirt after bubble is padded, pick-up rate 75%；3) the POLO shirt after 2) is baked, 155 DEG C of stoving temperature,
Bake 3min.
Embodiment 12: a kind of crease-resistant treatment process of POLO shirt, the difference from embodiment 1 is that, mixed liquor further includes 6 parts
Fe2(SO4)3。
Embodiment 13: a kind of crease-resistant treatment process of POLO shirt, the difference from embodiment 1 is that, mixed liquor further includes 4 parts
Fe2(SO4)3。
Embodiment 14: a kind of crease-resistant treatment process of POLO shirt, the difference from embodiment 1 is that, mixed liquor further includes 5 parts
Fe2(SO4)3。
Embodiment 15: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 8 are that mixed liquor further includes 6 parts
Fe2(SO4)3。
2) and 3) embodiment 16: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 12 be, into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
2) and 3) embodiment 17: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 13 be, into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
2) and 3) embodiment 18: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 14 be, into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
2) and 3) embodiment 19: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 15 be, into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
Embodiment 20: a kind of crease-resistant treatment process of POLO shirt, the difference from embodiment 1 is that, 2) and 3) into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
2) and 3) embodiment 21: a kind of crease-resistant treatment process of POLO shirt, the difference with embodiment 9 be, into pre- between
It bakes, prebake temperature 60 C, baking time 30 seconds.
Crease-resistant testing standard is according to GB/T3819-1997 " horn cupping is replied in the measurement of textile fabric wrinkle recovery property ".It is right
According to embodiment 1-21 scheme, treated that POLO shirt is test.Angle is bigger, and wrinkle resistance is more preferable.
By above-mentioned statistics indicate that: the immersion of Fe2 (SO4) 3 is added in mixed liquor can effectively promote wrinkle resistance, pad laggard
Row the pre-heat treatment can effectively promote wrinkle resistance.It is best that above-mentioned the two carries out wrinkle resistance simultaneously.
Claims (9)
1. a kind of crease-resistant treatment process of POLO shirt, POLO shirt by at least pure cotton of 85% or more quality accounting and quality accounting 10% with
On terylene composition, which comprises the steps of: 1) the POLO shirt made is put into mixed liquor and is impregnated,
Soaking time 1h, mixed liquor include 6-8 parts of MgCl by mass fraction2·6H2O, 7 parts of BTCA, 93-95 parts of acrylic resins, 2-4
Part citric acid；2) the POLO shirt after immersion is padded, pick-up rate 72-75%；3) the POLO shirt after 2) is dried
Roasting, bakes 3min by 130-160 DEG C of stoving temperature；Mixed liquor further includes 4-6 parts of Fe2(SO4)3。
2) and 3) 2. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: into preliminary drying between
Roasting, prebake temperature 60 C, baking time 30 seconds.
3. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: pick-up rate is 72%.
4. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: pick-up rate is 73%.
5. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: pick-up rate is 74%.
6. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: pick-up rate is 75%.
7. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: 132 DEG C of stoving temperature.
8. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: 147 DEG C of stoving temperature.
9. a kind of crease-resistant treatment process of POLO shirt according to claim 1, it is characterized in that: 158 DEG C of stoving temperature.