CN107805344A - A kind of novel plastic woven bag - Google Patents
A kind of novel plastic woven bag Download PDFInfo
- Publication number
- CN107805344A CN107805344A CN201711049191.0A CN201711049191A CN107805344A CN 107805344 A CN107805344 A CN 107805344A CN 201711049191 A CN201711049191 A CN 201711049191A CN 107805344 A CN107805344 A CN 107805344A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven bag
- bag
- novel plastic
- plastic woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of novel plastic woven bag, including 5 parts 100 parts of polypropylene, 50 parts of LLDPE, 22 parts of phenolic resin, 20 parts of polyoxymethylenes, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, 1 part of butyl tin oxide, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch.
Description
Technical field
The present invention relates to a kind of novel plastic woven bag.
Background technology
Polywoven Bag be using polypropylene as primary raw material, by extrusion, wire drawing, then through weaving, weaving, bag forms.
PP is formed into the primary raw material of woven bag.The use range of Polywoven Bag is very wide.With regard at present for, Polywoven Bag it is main
For agricultural product packaging, bag of cement packaging, packaging for foodstuff, Geotechnical Engineering, tourism traffic, flood fighting goods and materials etc..It is deposited in storehouse
It is easy to be broken by insect bite and caused content to spill, easy aging, peeling, fracture, powder under summer high temperature and ultraviolet irradiation
Broken, easily infiltration is entered in a humid environment, not only influences the article in polybag, is also affected Polywoven Bag and is used effect
Fruit.
The content of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of novel plastic woven bag, it is above-mentioned to solve
The problem of being proposed in background technology.
The present invention solves its technical problem and is achieved through the following technical solutions：
A kind of novel plastic woven bag, including 100 parts of polypropylene, 50 parts of LLDPE, 22 parts of phenolic resin,
20 parts of polyoxymethylenes, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, deca-BDE 0.5
5 parts part, 1 part of butyl tin oxide, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch.
The preparation method of the Anti-moth-eating Polywoven Bag is specific as follows：
1. by 100 parts of polypropylene polypropylene, 50 parts of LLDPE, 22 parts of phenolic resin, polyoxymethylenes 20
Part, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, butyl tin oxide 1
5 parts part, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch are sequentially added in mixer, are 33 in temperature
It is well mixed at DEG C, obtains mixture；
Extruded 2. mixture is added in extruder with 120kg/min charging rate, be then cooled and shaped, i.e.,
Obtain producing the coating woven cloth of woven bag；
3. first by the preheating temperature of preheating roller tube to 89 DEG C, the temperature of cooling stick is adjusted to 31 DEG C, then with membrana oralis to life
The coating woven cloth for the production woven bag that step II obtains is put into screw rod for 120mm and squeezed by the coating woven cloth gap of production woven bag
Go out in machine and extruded, obtain the flat filament of woven bag coated cloth；
4. the flat filament for the woven bag coated cloth that step III obtains is woven using flat die technique using cylindrical knitting machine,
Then in turn through cutting, severing and sewing, that is, obtain Polywoven Bag.
The present invention has the beneficial effect that：
The present invention extends the service life of woven bag and improves tensile property, and woven bag is non-aging, service life length, draws
Stretch is high so that the article of loading is not likely to produce putrid and deteriorated, not cracky, extends the service life of woven bag and improves and stretches
Performance.
Embodiment
The present invention will be described in detail below.
Embodiment：
A kind of novel plastic woven bag, including 100 parts of polypropylene, 50 parts of LLDPE, 22 parts of phenolic resin,
20 parts of polyoxymethylenes, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, deca-BDE 0.5
5 parts part, 1 part of butyl tin oxide, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch.
The preparation method of the Anti-moth-eating Polywoven Bag is specific as follows：
1. by 100 parts of polypropylene polypropylene, 50 parts of LLDPE, 22 parts of phenolic resin, polyoxymethylenes 20
Part, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, butyl tin oxide 1
5 parts part, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch are sequentially added in mixer, are 33 in temperature
It is well mixed at DEG C, obtains mixture；
Extruded 2. mixture is added in extruder with 120kg/min charging rate, be then cooled and shaped, i.e.,
Obtain producing the coating woven cloth of woven bag；
3. first by the preheating temperature of preheating roller tube to 89 DEG C, the temperature of cooling stick is adjusted to 31 DEG C, then with membrana oralis to life
The coating woven cloth for the production woven bag that step II obtains is put into screw rod for 120mm and squeezed by the coating woven cloth gap of production woven bag
Go out in machine and extruded, obtain the flat filament of woven bag coated cloth；
4. the flat filament for the woven bag coated cloth that step III obtains is woven using flat die technique using cylindrical knitting machine,
Then in turn through cutting, severing and sewing, that is, obtain Polywoven Bag.
Although disclosing embodiments of the invention for the purpose of illustration, it will be appreciated by those skilled in the art that：Not
Depart from the present invention and spirit and scope of the appended claims in, it is various replace, change and modifications all be it is possible, therefore, this
The scope of invention is not limited to embodiment disclosure of that.
Claims (1)
1. a kind of novel plastic woven bag, it is characterised in that including 100 parts of polypropylene, 50 parts of LLDPE, phenolic aldehyde
22 parts of resin, 20 parts of polyoxymethylenes, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, ten bromines two
5 parts 0.5 part of phenylate, 1 part of butyl tin oxide, 4.3 parts of acrylate, 1 part of ferrocene, addition of masterbatch.