CN107266804A - A kind of dumb light PS sheet materials and its manufacture method - Google Patents
A kind of dumb light PS sheet materials and its manufacture method Download PDFInfo
- Publication number
- CN107266804A CN107266804A CN201710660866.9A CN201710660866A CN107266804A CN 107266804 A CN107266804 A CN 107266804A CN 201710660866 A CN201710660866 A CN 201710660866A CN 107266804 A CN107266804 A CN 107266804A
- Authority
- CN
- China
- Prior art keywords
- type
- sheet materials
- dumb light
- toughener
- chromomere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to polymeric packaging material technical field, more particularly to a kind of dumb light PS sheet materials and its manufacture method are made up of the component of following weight/mass percentage composition：The 50wt% and 2wt% of chromomere 1 of 383 type polystyrene resin 48 50wt%, NSBC210 type K glue 48.Inventive formulation can but be fabricated to matt sheets using PS as primary raw material by mirror roller, manufacturing cost is low, it is to avoid time and the energy waste of format roll are changed in plant produced.
Description
Technical field
The present invention relates to polymeric packaging material technical field, more particularly to a kind of dumb light PS pieces that can be produced with mirror roller
Material and its manufacture method.
Background technology
The conventional material of plastic uptake sheet material has PS/PET/PP/ABS etc., is of wide application, and such as hardware, electronics, food are medical
Packaging, it is desirable to brightness it is also different, wherein some products of hardware electrical type need the sheet material of high dumb light to do pallet, carrier band.
Matt sheets are characterised by that display surface is non-shining surfaces.Matt sheets be usually after extrusion molding by sand roller into
Type, because sand roller rough surface, sheet surface can be made coarse, so can just produce matte effect.Relative to dumb light
Sheet material, polishing sheet material be exactly display surface be shining surfaces sheet material.Because polishing sheet material any surface finish, format roll is minute surface
Roller.
The equipment that both sheet materials melt use in the fabrication process is identical, and format roll tends not to share.In factory
During actual operation, matt sheets and polishing sheet material are often aperiodically manufactured with same extruding machine, then Jiu Yaogeng
Changing format roll could process, but replacing one-shot forming roller can be along with very complicated flow：Baking material --- carwash (machine barrel, runner,
Melt in getting to know is cleaned up) --- shutting down (at the end for the treatment of non-dumb light order production) --- cooling (typically drops to 80-100
Between DEG C, constant temperature is not degradable when general material is long less than 100 DEG C) --- dismantle format roll --- installation forming roller --- plus
Warm --- feeding intake --- start production.Once change and take up to more than 8 hours, can also produce substantial amounts of energy waste, quite not
Beneficial to cost control.
Therefore, it is necessary to provide a kind of new technology to solve problem above.
The content of the invention
The main object of the present invention is to provide for a kind of dumb light PS sheet materials that can be produced with mirror roller and its manufacture method.
The present invention is achieved through the following technical solutions above-mentioned purpose：
A kind of dumb light PS sheet materials, are made up of the component of following weight/mass percentage composition：476L type polystyrene resins 79-
88wt%, SF ABYX52C1 types filler 5-8wt%, chromomere 5-8wt% and toughener 2-5wt%.
Specifically, the chromomere uses CP-04 type chromomeres.
Specifically, the toughener uses 3546F type toughener.
A kind of dumb light PS sheet materials, are made up of the component of following weight/mass percentage composition：383 type polystyrene resins
49.7wt%, NSBC210 type K glue 48.9wt%, CP-04 chromomere 1.4wt%.
A kind of manufacture method of dumb light PS sheet materials, raw material by proportioning melt in extruding machine, and extrusion is arranged after being well mixed
It is useless, wait to guide between forming press-roller being pressed into sheet material after steady quality, wherein format roll is mirror roller.
Compared with prior art, the beneficial effect of a kind of dumb light PS sheet materials of the invention and its manufacture method is：
Inventive formulation can but be fabricated to matt sheets using PS as primary raw material by mirror roller, and manufacturing cost is low,
Avoid time and the energy waste that format roll is changed in plant produced.
Brief description of the drawings
Fig. 1 is the manufacturing process sketch of dumb light PS sheet materials.
Numeral is represented in figure：
1- extruding machines；
2- press-roller devices,
21- format rolls；
3- sheet materials.
Embodiment
A kind of dumb light PS sheet materials and its manufacture method, are made up of the component of following weight/mass percentage composition：476L type polyphenyl second
Olefine resin 79-88wt%, SF ABYX52C1 types filler 5-8wt%, chromomere 5-8wt% and toughener 2-5wt%.
Wherein 476L types polystyrene resin is provided by Zhenjiang Qi Mei plastics Co., Ltd, and NSBC210 type K glue is by Bai Likai
Rice composite plastic (Kunshan) Co., Ltd is provided, and chromomere is provided by Taishan Yun Peng Co., Ltds, and toughener is flourish by Huizhou Lee's length
Limited rubber company provides.
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
Embodiment 1:
By 476L type polystyrene resin 790g, SF ABYX52C1 type filler 80g, CP-04 chromomere 80g and 3546F types
Toughener 50g is melted in extruding machine 1, it is well mixed after extrude waste discharge, wait to guide between press-roller device 2 being pressed into after steady quality
Sheet material 3, wherein format roll 21 are mirror roller.Performance test is carried out after sheet material 3 is cooled down.
Embodiment 2:
By 476L type polystyrene resin 880g, SF ABYX52C1 type filler 50g, CP-04 chromomere 50g and 3546F types
Toughener 20g is melted in extruding machine 1, it is well mixed after extrude waste discharge, wait to guide between press-roller device 2 being pressed into after steady quality
Sheet material 3, wherein format roll 21 are mirror roller.Performance test is carried out after sheet material 3 is cooled down.
Embodiment 3:
By 476L type polystyrene resin 841g, SF ABYX52C1 type filler 64g, CP-04 chromomere 72g and 3546F types
Toughener 23g is melted in extruding machine 1, it is well mixed after extrude waste discharge, wait to guide between press-roller device 2 being pressed into after steady quality
Sheet material 3, wherein format roll 21 are mirror roller.Performance test is carried out after sheet material 3 is cooled down.
Reference examples：
Use 476L type polystyrene resin melting extrusions for PS sheet materials, performance test is carried out after cooling.
Embodiment 1-3 and reference examples resulting sheet are subjected to correlated performance test respectively,
Glossiness detection method：Glossiness detection is carried out to sheet material using MIT-60 vancometers.
Concrete outcome is shown in Table 1.
The sheet properties of table 1 are tested：
As shown in Table 1, embodiment 1-3 modification PS sheet materials add density by adding filler, save manufacturing cost.
But at the same time significantly reduce the glossiness of sheet material, although manufacture format roll used for mirror roller, but sheet material remains unchanged and can had
There is matte effect.This manufacture method avoid plant produced this product with polishing sheet material handoff procedure in change format roll when
Between and energy waste.
Above-described is only some embodiments of the present invention.For the person of ordinary skill of the art, not
On the premise of departing from the invention design, various modifications and improvements can be made, these belong to the protection model of the present invention
Enclose.
Claims (5)
1. a kind of dumb light PS sheet materials, it is characterised in that be made up of the component of following weight/mass percentage composition：476L type polystyrene trees
Fat 79-88wt%, SF ABYX52C1 types filler 5-8wt%, chromomere 5-8wt% and toughener 2-5wt%.
2. dumb light PS sheet materials according to claim 1, it is characterised in that：The chromomere uses CP-04 type chromomeres.
3. dumb light PS sheet materials according to claim 1, it is characterised in that：The toughener uses 3546F type toughener.
4. dumb light PS sheet materials according to claim 1, it is characterised in that be made up of the component of following weight/mass percentage composition：
476L type polystyrene resins 84.1wt%, SF ABYX52C1 type filler 6.4wt%, CP-04 type chromomere 7.2wt% and
3546F type toughener 2.3wt%.
5. a kind of manufacture method of dumb light PS sheet materials, it is characterised in that：Raw material melt in extruding machine by proportioning, it is well mixed
After extrude waste discharge, wait to guide between forming press-roller being pressed into sheet material after steady quality, wherein format roll is mirror roller.