CN107794769A - A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric - Google Patents
A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric Download PDFInfo
- Publication number
- CN107794769A CN107794769A CN201710894185.9A CN201710894185A CN107794769A CN 107794769 A CN107794769 A CN 107794769A CN 201710894185 A CN201710894185 A CN 201710894185A CN 107794769 A CN107794769 A CN 107794769A
- Authority
- CN
- China
- Prior art keywords
- proof
- uvioresistant
- dyeing
- soda ash
- mosquito
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, it is characterized in comprising the following steps that：Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → → desizing → mercerising → mosquito proof, Water-proof and oil-proof one-step method arrange → of singing bake → preshrunk.It is an advantage of the invention that process simple and compact, efficiently, energy consumption is low, production cost is reduced, nanometer three-proof finishing agent can be in fiber surface film forming, along with the crosslinked action of acrylic resin, pyrethroid is coated in film, the loss of active ingredient after washing is reduced, washability is improved, especially particular for summer outdoor environment feature, fabric mosquito proof, Water-proof and oil-proof, the function of uvioresistant are assigned, is adapted to outdoor exercises dress.
Description
Technical field
The invention belongs to textile fabric dyeing technical field, more particularly to a kind of mosquito proof waterproof and oilproof uvioresistant color surface of second order
The dyeing and finishing technology of material.
Background technology
Present outdoor exercises enter into the popular visual field from a kind of professional motion, and increasing people is added to, outdoor
Turn into a kind of popular fashionable life mode in the ranks of motion.But summer wild environment is more complicated：One side ultraviolet is strong,
Skin is easily tanned severely, in some instances it may even be possible to induces cutaneum carcinoma；Secondly, summer rainwater is more, and vegetative growth is vigorous, carries out outdoor exercises and often can
Perplexed by bite by mosquitos, or even a variety of diseases can be triggered；Finally, summer weather is changeable, rain or shine indefinite, neglects one such as it
Field heavy rain can make the people of participation outdoor exercises be caught unprepared.With the continuous development of scientific technology, people's difference needs are met
Textile fabric emerge in an endless stream, more and more important effect is played in the outdoor exercises of people.It can carry in the market
What is supplied is that there is simple function either at most to possess the fabrics or clothes of function in 2-4 mostly, and can by uvioresistant, it is grease proofing,
Antifouling, waterproof, antibacterial and mosquito proof etc. are multi-functional while assign a kind of fabric, to solve showing for the actual demand of specific group
Having in technology has following color-woven fabric dyeing and finishing technology：
First, Chinese patent application, application number 201610692313.7, applying date 2016.08.19, application publication number CN
106319939 A, data of publication of application 2017.01.11, disclose a kind of " processing work of the color-woven fabric of antibacterial ultraviolet-resistannanofiber line
Skill ", by anti-ultraviolet radiation treatment technique, how far at carboxylic acid pre-treating technology, nanometered disposal liquor treating process and three-proof finishing agent
Four steps of science and engineering skill, complete the handling process to color-woven fabric；Comprise the following steps that：Anti-ultraviolet radiation treatment technique：From anti-
Uvioresistant padding liquid is prepared in ultraviolet pulvis, color-woven fabric is put in 90-95 DEG C of uvioresistant padding liquid and impregnated
4-5 hours, then roll one time, pick-up 70-74%, the addition of the uvioresistant pulvis is 10-12g/L, described anti-
The particle diameter of ultraviolet pulvis is 20-30mm, proportion 1.0-1.2g/m3；Polybasic carboxylic acid pre-treating technology：After processing
Color-woven fabric pad and bakee complete polybasic carboxylic acid pre-treating technology, 108-200 DEG C of the stoving temperature, it is described baking the time be
4-6min；Nanometered disposal liquor treating process：Fabric after processing is put into nanometered disposal liquid and padded so that color-woven fabric
The volume ratio of formation rough surface, the fabric and Nano Silver treatment fluid is 1：12, the nanometered disposal liquid is nano-powder point
Dispersion liquid；Three-proof finishing agent handling process：Color-woven fabric after the processing of nanometered disposal liquid is padded, the padding liquid is three proofings
Finishing agent, the amount of the three-proof finishing agent is 20-40g/L, and the jacquard yarn-dyed fabric after padding is dried under 100 DEG C of environment
It is dry, then baked, the baking temperature is 150 DEG C, and it is 3min to bake the time.
2nd, Chinese patent application, application number 201610826575.8, applying date 2017.09.18, application publication number CN
106400259 A, data of publication of application 2017.02.15, " a kind of production method of composite multifunction fabric ", production process：A, spin
Yarn is weaved cotton cloth；B, dyeing and UV resistance arrange；C, flame-proof treatment；D, the mosquito-proof processing of antibacterial；E, three proofings processing be grease proofing, waterproof, it is anti-
Dirt processing.
The technical scheme of above-mentioned two pieces patent application publication can assign fabric have fire-retardant, antistatic, UV resistance, it is grease proofing,
One or more functions in antifouling, waterproof, antibacterial and mosquito proof, substantially meet actual demand, for making for particular surroundings
User provides safe and reliable guarantee.Shortcoming is that above two technical scheme is all the opposite on the basis of completing to spin cotton and weave cloth
Material carries out uvioresistant, mosquito proof, the PROCESS FOR TREATMENT of Water-proof and oil-proof, complex procedures, high energy consumption, production cost height.
The content of the invention
For overcome the deficiencies in the prior art, it is an object of the invention to provide a kind of mosquito proof waterproof and oilproof uvioresistant color surface of second order
The dyeing and finishing technology of material, process simple and compact, efficiently, energy consumption is low, reduces production cost, particular for summer outdoor environment feature,
Assign fabric mosquito proof, Water-proof and oil-proof, the function of uvioresistant.
To achieve the above object, the present invention adopts the following technical scheme that：
A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, is characterized in comprising the following steps that：
Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → are singed → desizing → silk
Light → mosquito proof, Water-proof and oil-proof one-step method arrange → bakes → preshrunk；
Wherein, described dyeing, uvioresistant single bath process are arranged and comprised the following steps that：Dye liquor, 10- are added at normal temperatures
Glauber salt is added in 15min, then heats up and adds soda ash at twice, be warming up to 43-47 DEG C, add for the first time a part of pure
Alkali；It is continuously heating to 57-63 DEG C and keeps the temperature, remainder soda ash, 10- is added to second within 10min after 5min
Ultraviolet-resistant absorbent is added within 35min, 45-30 DEG C is cooled to after insulation 5-10min, carries out pickling, temperature is kept not
Become, pickling time 10min；Then washed, washing time is controlled in 10min or so；The total dosage of soda ash added twice
For 5-20g/L.
As currently preferred technical scheme, described mosquito proof, Water-proof and oil-proof one-step method arrange specific steps such as
Under：One 65-70% → 100-130 DEG C of immersing and rolling liquid carrying rate drying → 160-180 DEG C bakes 1-3min；Using mosquito proof, waterproof,
It grease proofing one-bath finishing, can both shorten process, the washability of mosquito proof effect can be improved again, nanometer three-proof finishing agent can be in fibre
Surface filming is tieed up, along with the crosslinked action of acrylic resin, pyrethroid is coated in film, is reduced after washing effectively
The loss of composition, washability are high.
As currently preferred technical scheme, the described soda ash step first time soda ash of addition at twice addition is pure
The 1/3 of the total dosage of alkali, second of soda ash addition are the 2/3 of the total dosage of soda ash.
As currently preferred technical scheme, described dyeing, uvioresistant single bath process arrange to be contaminated using reagent for activity
Material and ultraviolet-resistant absorbent dosage, described ultraviolet-resistant absorbent dosage is 1.5-4.5%owf.
As currently preferred technical scheme, it is conjunction that described mosquito proof, Water-proof and oil-proof one-step method, which are arranged using medicament,
Into pyrethrins, acrylic resin and nanometer three-proof finishing agent.
As currently preferred technical scheme, described mosquito proof, Water-proof and oil-proof arrange one-step method finishing agent and used
Measure and be：Pyrethroid 80-150g/L, acrylic resin 20-45g/L, nanometer three-proof finishing agent 50-80g/L.
Compared with prior art, it is an advantage of the invention that process simple and compact, efficiently, energy consumption is low, reduce production cost, receive
Rice three-proof finishing agent, along with the crosslinked action of acrylic resin, pyrethroid can be coated in fiber surface film forming
In film, the loss of active ingredient after washing is reduced, improves washability, especially particular for summer outdoor environment feature, assigns face
Expect mosquito proof, Water-proof and oil-proof, the function of uvioresistant, be adapted to outdoor exercises dress.
Brief description of the drawings
The invention will be further described below in conjunction with the accompanying drawings.
Fig. 1 is present invention dyeing, uvioresistant single bath finishing technology step schematic diagram.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
What the nanometer three-proof finishing agent that is used in the embodiment of the present invention was selected is three nanometers of NANO-TEX companies of the U.S. anti-
Finishing agent, other reagents referred in the embodiment of the present invention are commercially available, do not do particular/special requirement.
Embodiment 1
A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, is characterized in comprising the following steps that：
Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → are singed → desizing → silk
Light → mosquito proof, Water-proof and oil-proof one-step method arrange → bakes → preshrunk；
Wherein, dyeing, uvioresistant single bath process are arranged and comprised the following steps that：Dye liquor is added at normal temperatures, is added in 10-15min
Enter glauber salt, then heat up and add soda ash at twice, be warming up to 45 DEG C, add 1/3 soda ash for the first time；It is continuously heating to 60
DEG C and keep the temperature, to the soda ash for adding 2/3 for second within 10min after 5min, uvioresistant is added within 10-35min
Absorbent, insulation 5-10min are cooled to 45-30 DEG C afterwards, carry out pickling, and temperature keeps constant, pickling time 10min；So
Laggard water-filling is washed, and washing time is controlled in 10min or so；
Above-mentioned 1/3 soda ash and 2/3 soda ash are weighed with the total dosage of soda ash, and the total dosage of soda ash is 5-20g/L.
Mosquito proof, Water-proof and oil-proof one-step method are arranged and comprised the following steps that：One immersing and rolling liquid carrying rate 65-70% → 110 DEG C
Drying 2min → 170 DEG C bake 2min；It using mosquito proof, Water-proof and oil-proof one-bath finishing, can both shorten process, can carry again
The washability of high mosquito proof effect, nanometer three-proof finishing agent can be in fiber surface film forming, along with the crosslinking of acrylic resin is made
With pyrethroid is coated in film, reduces the loss of active ingredient after washing, washability is high.
It is reactive dye and ultraviolet-resistant absorbent dosage that dyeing, uvioresistant single bath process, which are arranged using reagent, and described is anti-
Ultra-violet absorber dosage is 4.0%owf.
It is pyrethroid 120g/L, acrylic resin 40g/ that mosquito proof, Water-proof and oil-proof one-step method, which are arranged using medicament,
L and nanometer three-proof finishing agent 70g/L.
Embodiment 2
A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, is characterized in comprising the following steps that：
Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → are singed → desizing → silk
Light → mosquito proof, Water-proof and oil-proof one-step method arrange → bakes → preshrunk；
Wherein, dyeing, uvioresistant single bath process are arranged and comprised the following steps that：Dye liquor is added at normal temperatures, is added in 10-15min
Enter glauber salt, then heat up and add soda ash at twice, be warming up to 46.5 DEG C, add a part of soda ash for the first time；Continue to heat up
To 63 DEG C and keep the temperature, add remainder soda ash to second within 10min after 5min, added within 10-35min anti-
Ultra-violet absorber, insulation 5-10min are cooled to 45-30 DEG C afterwards, carry out pickling, and temperature keeps constant, and pickling time is
10min；Then washed, washing time is controlled in 10min or so；The total dosage of soda ash added twice is 5-20g/L.
1/3 that soda ash step first time soda ash addition is the total dosage of soda ash, second of soda ash addition are added at twice
For the 2/3 of the total dosage of soda ash.
Mosquito proof, Water-proof and oil-proof one-step method are arranged and comprised the following steps that：One immersing and rolling liquid carrying rate 65-70% → 100 DEG C
Drying 2min → 180 DEG C bake 2min；It using mosquito proof, Water-proof and oil-proof one-bath finishing, can both shorten process, can carry again
The washability of high mosquito proof effect, nanometer three-proof finishing agent can be in fiber surface film forming, along with the crosslinking of acrylic resin is made
With pyrethroid is coated in film, reduces the loss of active ingredient after washing, washability is high.
It is reactive dye and ultraviolet-resistant absorbent dosage that dyeing, uvioresistant single bath process, which are arranged using reagent, and described is anti-
Ultra-violet absorber dosage is 1.5%owf.
It is pyrethroid 100g/L, acrylic resin 25g/ that mosquito proof, Water-proof and oil-proof one-step method, which are arranged using medicament,
L and nanometer three-proof finishing agent 60g/L.
Embodiment 3
A kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, is characterized in comprising the following steps that：
Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → are singed → desizing → silk
Light → mosquito proof, Water-proof and oil-proof one-step method arrange → bakes → preshrunk；
Wherein, dyeing, uvioresistant single bath process are arranged and comprised the following steps that：Dye liquor is added at normal temperatures, is added in 10-15min
Enter glauber salt, then heat up and add soda ash at twice, be warming up to 43.5 DEG C, add a part of soda ash for the first time；Continue to heat up
To 57 DEG C and keep the temperature, add remainder soda ash to second within 10min after 5min, added within 10-35min anti-
Ultra-violet absorber, insulation 5-10min are cooled to 45-30 DEG C afterwards, carry out pickling, and temperature keeps constant, and pickling time is
10min；Then washed, washing time is controlled in 10min or so；The total dosage of soda ash added twice is 5-20g/L.
1/3 that soda ash step first time soda ash addition is the total dosage of soda ash, second of soda ash addition are added at twice
For the 2/3 of the total dosage of soda ash.
Mosquito proof, Water-proof and oil-proof one-step method are arranged and comprised the following steps that：One immersing and rolling liquid carrying rate 65-70% → 130 DEG C
Drying 2min → 160 DEG C bake 2min；It using mosquito proof, Water-proof and oil-proof one-bath finishing, can both shorten process, can carry again
The washability of high mosquito proof effect, nanometer three-proof finishing agent can be in fiber surface film forming, along with the crosslinking of acrylic resin is made
With pyrethroid is coated in film, reduces the loss of active ingredient after washing, washability is high.
It is reactive dye and ultraviolet-resistant absorbent dosage that dyeing, uvioresistant single bath process, which are arranged using reagent, and described is anti-
Ultra-violet absorber dosage is 4.5%owf.
It is pyrethroid 145g/L, acrylic resin 38g/ that mosquito proof, Water-proof and oil-proof one-step method, which are arranged using medicament,
L and nanometer three-proof finishing agent 80g/L.
Embodiment 4
The fabric made using embodiment 1-3 is tested, test result is as shown in table 1：
Table 1
The color-woven fabric that technical solution of the present invention is produced as shown in Table 1 possesses mosquito proof, Water-proof and oil-proof, uvioresistant work(
Can, the actual demand of summer outdoor exercises can be met, enjoyment is brought for outdoor exercises.
The embodiment of the present invention is the foregoing is only, but protection scope of the present invention is not limited thereto, it is any
Those skilled in the art disclosed herein technical scope in, can without the change that creative work is expected or
Replace, should all cover within the protection of the present invention is divided into.Therefore, protection scope of the present invention should be limited with claims
Fixed protection domain is defined.
Claims (6)
- A kind of 1. dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric, it is characterised in that：Comprise the following steps that： Cylinder yarn pre-treatment → dyeing, uvioresistant single bath process arrangement → warping → sizing → weaving → fabric overhauls → are singed → desizing → silk Light → mosquito proof, Water-proof and oil-proof one-step method arrange → bakes → preshrunk；Wherein, described dyeing, uvioresistant single bath process are arranged and comprised the following steps that：Dye liquor is added at normal temperatures, in 10-15min Glauber salt is added, then heats up and adds soda ash at twice, be warming up to 43-47 DEG C, add a part of soda ash for the first time；Continue to rise Temperature is to 57-63 DEG C and keeps the temperature, to adding remainder soda ash for second within 10min after 5min, within 10-35min Ultraviolet-resistant absorbent is added, 45-30 DEG C is cooled to after insulation 5-10min, carries out pickling, temperature keeps constant, during pickling Between be 10min；Then washed, washing time is controlled in 10min or so；The total dosage of soda ash added twice is 5-20g/L.
- 2. a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric according to claim 1, its feature exist In：Described mosquito proof, Water-proof and oil-proof one-step method are arranged and comprised the following steps that：One immersing and rolling liquid carrying rate 65-70% → 100- 130 DEG C of drying → 160-180 DEG C bake 1-3min.
- 3. a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric according to claim 1, its feature exist In：The described addition of addition soda ash step first time soda ash at twice is the 1/3 of the total dosage of soda ash, second of soda ash addition For the 2/3 of the total dosage of soda ash.
- 4. a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric according to claim 1, its feature exist In：It is reactive dye and ultraviolet-resistant absorbent dosage that described dyeing, uvioresistant single bath process, which are arranged using reagent, uvioresistant Absorbent dosage is 1.5-4.5%owf.
- 5. a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric according to claim 1, its feature exist In：It is pyrethroid, acrylic resin and nanometer three that described mosquito proof, Water-proof and oil-proof one-step method, which are arranged using medicament, Anti- finishing agent.
- 6. a kind of dyeing and finishing technology of mosquito proof waterproof and oilproof uvioresistant color-woven fabric according to claim 1, its feature exist In：It is pyrethroid 80-150g/L that described mosquito proof, Water-proof and oil-proof, which arrange one-step method finishing agent usage amount, propylene Acid resin 20-45g/L, nanometer three-proof finishing agent 50-80g/L.