CN104389070A - Preparation method of insect-repellent textile fabric - Google Patents
Preparation method of insect-repellent textile fabric Download PDFInfo
- Publication number
- CN104389070A CN104389070A CN201410517677.2A CN201410517677A CN104389070A CN 104389070 A CN104389070 A CN 104389070A CN 201410517677 A CN201410517677 A CN 201410517677A CN 104389070 A CN104389070 A CN 104389070A
- Authority
- CN
- China
- Prior art keywords
- screen cloth
- complex root
- bamboo
- preparation
- carbon fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of an insect-repellent textile fabric. The method comprises the following steps: a, preparing flax threads, bamboo charcoal fibers, an active dye and a nano-silver antibacterial solution; b, boiling a plurality of flax threads with soap, and soaking the boiled flax threads into the active dye to allow the flax threads to absorb slowly; c, boiling a plurality of bamboo charcoal fibers with soap, and soaking the bamboo charcoal fibers into the nano-silver antibacterial solution added with a PVP (Polyvinyl Pyrrolidone) dispersing agent and a PDA dispersing agent; d, weaving the insect-repellent textile fabric comprising surface layer screen cloth and inner layer screen cloth according to a double-layer plain weave method by operating a shuttle loom, wherein warps of the inner layer screen cloth are dip-dyed flax threads, and wefts are soaked bamboo charcoal fibers and a plurality of acrylic fibers; warps and wefts of the surface layer screen cloth are a plurality of machine sewing threads. After being treated in the nano-silver antibacterial solution through a soaking process, the bamboo charcoal fibers have the effect of disinfecting, resisting bacteria and repelling insects.
Description
Technical field
The present invention relates to a kind of preparation method of weaving face fabric, more particularly, relate to a kind of preparation method of mosquito proof weaving face fabric.
Background technology
Fabric is mainly used for making house and spins and clothes or medical textile.Its kind is a lot.Along with the variation of the market demand, the functional of fabric is also more and more subject to people's attention.Along with living standard improves constantly, the functional requirement of people to garment material is more and more higher, except requiring clothes and having normal heat-preserving function, also will require to have the effect preventing bite by mosquitos, along with being be in hot summer, bite by mosquitos phenomenon has allowed child adult be caught unprepared.Light then red swelling of the skin after bite by mosquitos, heavy then communicate illness, has a strong impact on daily life.Thus developing a kind of weaving face fabric of bite by mosquitos that prevents is a kind of engineering having market and social benefit.
Chinese utility model patent (application number: 02217540.7, notification number: CN2540435), disclose a kind of Double-layer mosquito-proof material, comprise three layers that close and be woven in together, thickness is 0.3-1cm, middle thickness and flexible, can not relative motion and mutually keeping in check between each layer, and the softness of this fabric is poor, ventilation effect is poor, when using as close-fitting fabric, can leak and put mosquito because fitting bad with human body, not have mosquito-proof effect effectively.
Summary of the invention
The invention provides a kind of preparation method of mosquito proof weaving face fabric, its main purpose is that the meeting overcoming the existence of existing Double-layer mosquito-proof material causes wearer to feel sultry, uncomfortable defect.
For solving the problems of the technologies described above, the present invention adopts following technical scheme:
A preparation method for mosquito proof weaving face fabric, comprises following steps: a, prepare complex root linen thread, the bamboo-carbon fibre of complex root through arranging, a REACTIVE DYES and a nano-silver antiseptic solution; After linen thread described in b, soap boiling complex root, linen thread described in described complex root is immersed in described REACTIVE DYES, linen thread described in complex root is absorbed lentamente; After bamboo-carbon fibre described in c, soap boiling complex root, soak in bamboo-carbon fibre described in complex root and the nano-silver antiseptic solution having added a PVP dispersant and a PDA dispersant 50 to 100 minutes; D, operate a loom and knit out with pair of lamina plain weave method the mosquito proof weaving face fabric that comprises a top layer screen cloth and a nexine screen cloth, the warp of wherein said nexine screen cloth is the linen thread after contaminating, parallel be soak after bamboo-carbon fibre and complex root acryl fiber, warp, the parallel of described top layer screen cloth are complex root thread, described cover web hole size of arranging net is 80 ~ 120 meshes, and described nexine screen cloth mesh size is 60 ~ 80 meshes.
Preferably, the described warp thread of nexine screen cloth or the thickness of weft yarn are greater than the warp thread of described top layer screen cloth or the thickness of weft yarn.
Preferably, in described step b, the time of linen thread described in soap boiling complex root is 30 minutes.
Preferably, described step b is made up of substep: b1, when being immersed in described REACTIVE DYES by linen thread described in complex root, within every 10 minutes, add a certain amount of salt, totally four times; B2, within every 10 minutes, add a certain amount of sodium carbonate again, totally three times; B3, linen thread described in complex root to be picked up, afterwash, dehydration, and to dry in the shade.
Preferably, described step c also comprises following process, after having soaked bamboo-carbon fibre described in complex root, is picked up by bamboo-carbon fibre described in complex root, sequentially cleans, dewaters, and dry in the shade.
Compared to the prior art, the beneficial effect that the present invention produces is:
Bamboo-carbon fibre of the present invention is after soaking technology process in nano-silver antiseptic solution, make nanometer silver antimicrobial component distributing in the inside of conductive structure, because Nano Silver is a kind of anophelifuge activity composition efficiently, therefore, not only can make effect with disinfecting, antimicrobial, mosquito expelling of fabric lining, and make the present invention possess waterproof and perspiration functions simultaneously, there is range of application widely, and the Mechanical Contraction of the Electrostatic Absorption that can reduce on ready-made clothes and knitted fabric, wear more comfortable, outward appearance is also more attractive in appearance.
In addition, fabric structure of the present invention is by utilizing the first air-vent of top layer screen cloth to intercept mosquito contact skin, and coordinates the thickness of nexine screen cloth to penetrate on skin to stop mosquito lancet, thus can play the effect preventing bite by mosquitos well.In addition, be provided with the mesh-structured of air-vent because described top layer screen cloth and nexine screen cloth adopt, thus can improve the permeability of fabric widely, make to make the effect can when clothing is dressed with ventilation and heat.
Accompanying drawing explanation
Without accompanying drawing.
Detailed description of the invention
The invention discloses a kind of preparation method of mosquito proof weaving face fabric, those skilled in the art can use for reference present disclosure, and suitable improving technique parameter realizes.Special needs to be pointed out is, all similar replacements and change apparent to those skilled in the art, they are all deemed to be included in the present invention.Method of the present invention and application are described by preferred embodiment, related personnel obviously can not depart from content of the present invention, spirit and scope methods and applications as herein described are changed or suitably change with combination, realize and apply the technology of the present invention.
Embodiment one
Prevent a weaving face fabric for bite by mosquitos, comprise a top layer screen cloth and a nexine screen cloth, described top layer screen cloth has a plurality of first air-vents formed by warp thread and weft yarns, and the size of this first air-vent is 80 ~ 120 meshes; Described nexine screen cloth invests the one side of this top layer screen cloth, and there are a plurality of second air-vents formed by warp thread and weft yarns, the size of this first air-vent is 60 ~ 80 meshes, and the wherein said warp thread of nexine screen cloth or the thickness of weft yarn are greater than the Stylet length of mosquito.
Preferably, the described warp thread of nexine screen cloth or the thickness of weft yarn are greater than the warp thread of described top layer screen cloth or the thickness of weft yarn.
Preferably, described top layer screen cloth and nexine screen cloth are integrally weaved and are formed.
Preferably, the described warp thread of nexine screen cloth or the thickness of weft yarn are greater than 2.5 millimeters.
Preferably, described nexine screen cloth comprises the linen thread of complex root after reactive dyeing as warp, and complex root acrylic fiber and in nano-silver antiseptic solution soak after bamboo-carbon fibre as parallel, described top layer screen cloth comprises complex root thread as warp and parallel, and described top layer screen cloth and nexine screen cloth to be interweaved with pair of lamina plain weave method and to form by above-mentioned each warp and parallel.
Fabric structure of the present invention is by utilizing the first air-vent of top layer screen cloth to intercept mosquito contact skin, and coordinates the thickness of nexine screen cloth to penetrate on skin to stop mosquito lancet, thus can play the effect preventing bite by mosquitos well.In addition, be provided with the mesh-structured of air-vent because described top layer screen cloth and nexine screen cloth adopt, thus can improve the permeability of fabric widely, make to make the effect can when clothing is dressed with ventilation and heat.
Embodiment two
A preparation method for mosquito proof weaving face fabric, comprises following steps: a, prepare complex root linen thread, the bamboo-carbon fibre of complex root through arranging, a REACTIVE DYES and a nano-silver antiseptic solution; After linen thread described in b, soap boiling complex root, linen thread described in described complex root is immersed in described REACTIVE DYES, linen thread described in complex root is absorbed lentamente; After bamboo-carbon fibre described in c, soap boiling complex root, soak in bamboo-carbon fibre described in complex root and the nano-silver antiseptic solution having added a PVP dispersant and a PDA dispersant 50 to 100 minutes; D, operate a loom and knit out with pair of lamina plain weave method the mosquito proof weaving face fabric that comprises a top layer screen cloth and a nexine screen cloth, the warp of wherein said nexine screen cloth is the linen thread after contaminating, parallel be soak after bamboo-carbon fibre and complex root acryl fiber, warp, the parallel of described top layer screen cloth are complex root thread, described cover web hole size of arranging net is 80 ~ 120 meshes, and described nexine screen cloth mesh size is 60 ~ 80 meshes.
Preferably, the described warp thread of nexine screen cloth or the thickness of weft yarn are greater than the warp thread of described top layer screen cloth or the thickness of weft yarn.
Preferably, in described step b, the time of linen thread described in soap boiling complex root is 30 minutes.
Preferably, described step b is made up of substep: b1, when being immersed in described REACTIVE DYES by linen thread described in complex root, within every 10 minutes, add a certain amount of salt, totally four times; B2, within every 10 minutes, add a certain amount of sodium carbonate again, totally three times; B3, linen thread described in complex root to be picked up, afterwash, dehydration, and to dry in the shade.
Preferably, described step c also comprises following process, after having soaked bamboo-carbon fibre described in complex root, is picked up by bamboo-carbon fibre described in complex root, sequentially cleans, dewaters, and dry in the shade.
Bamboo-carbon fibre of the present invention is after soaking technology process in nano-silver antiseptic solution, make nanometer silver antimicrobial component distributing in the inside of conductive structure, because Nano Silver is a kind of anophelifuge activity composition efficiently, therefore, not only can make effect with disinfecting, antimicrobial, mosquito expelling of fabric lining, and make the present invention possess waterproof and perspiration functions simultaneously, there is range of application widely, and the Mechanical Contraction of the Electrostatic Absorption that can reduce on ready-made clothes and knitted fabric, wear more comfortable, outward appearance is also more attractive in appearance.
Above the preparation method of a kind of mosquito proof weaving face fabric provided by the present invention is described in detail.Apply specific case herein to set forth principle of the present invention and embodiment, the explanation of above embodiment just understands method of the present invention and core concept thereof for helping.It should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention, can also carry out some improvement and modification to the present invention, these improve and modify and also fall in the protection domain of the claims in the present invention.
Claims (5)
1. a preparation method for mosquito proof weaving face fabric, is characterized in that: comprise following steps: a, prepare complex root linen thread, the bamboo-carbon fibre of complex root through arranging, a REACTIVE DYES and a nano-silver antiseptic solution; After linen thread described in b, soap boiling complex root, linen thread described in described complex root is immersed in described REACTIVE DYES, linen thread described in complex root is absorbed lentamente; After bamboo-carbon fibre described in c, soap boiling complex root, soak in bamboo-carbon fibre described in complex root and the nano-silver antiseptic solution having added a PVP dispersant and a PDA dispersant 50 to 100 minutes; D, operate a loom and knit out with pair of lamina plain weave method the mosquito proof weaving face fabric that comprises a top layer screen cloth and a nexine screen cloth, the warp of wherein said nexine screen cloth is the linen thread after contaminating, parallel be soak after bamboo-carbon fibre and complex root acryl fiber, warp, the parallel of described top layer screen cloth are complex root thread, described cover web hole size of arranging net is 80 ~ 120 meshes, and described nexine screen cloth mesh size is 60 ~ 80 meshes.
2. the preparation method of a kind of mosquito proof weaving face fabric as claimed in claim 1, is characterized in that: the described warp thread of nexine screen cloth or the thickness of weft yarn are greater than the warp thread of described top layer screen cloth or the thickness of weft yarn.
3. the preparation method of a kind of mosquito proof weaving face fabric as claimed in claim 2, it is characterized in that: in described step b, the time of linen thread described in soap boiling complex root is 30 minutes.
4. the preparation method of a kind of mosquito proof weaving face fabric as claimed in claim 3, is characterized in that: described step b is made up of substep: b1, when being immersed in described REACTIVE DYES by linen thread described in complex root, within every 10 minutes, add a certain amount of salt, totally four times; B2, within every 10 minutes, add a certain amount of sodium carbonate again, totally three times; B3, linen thread described in complex root to be picked up, afterwash, dehydration, and to dry in the shade.
5. the preparation method of a kind of mosquito proof weaving face fabric as claimed in claim 4, is characterized in that: described step c also comprises following process, after having soaked bamboo-carbon fibre described in complex root, is picked up by bamboo-carbon fibre described in complex root, sequentially cleans, dehydration, and dries in the shade.