CN107779065A - A kind of polyurea waterproof coating material and preparation method thereof - Google Patents

A kind of polyurea waterproof coating material and preparation method thereof Download PDF

Info

Publication number
CN107779065A
CN107779065A CN201711091424.3A CN201711091424A CN107779065A CN 107779065 A CN107779065 A CN 107779065A CN 201711091424 A CN201711091424 A CN 201711091424A CN 107779065 A CN107779065 A CN 107779065A
Authority
CN
China
Prior art keywords
silane
component
coating
parts
lithopone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711091424.3A
Other languages
Chinese (zh)
Inventor
魏亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ningbo Hi Tech Zone Xia Yuan Technology Co Ltd
Original Assignee
Ningbo Hi Tech Zone Xia Yuan Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Hi Tech Zone Xia Yuan Technology Co Ltd filed Critical Ningbo Hi Tech Zone Xia Yuan Technology Co Ltd
Priority to CN201711091424.3A priority Critical patent/CN107779065A/en
Publication of CN107779065A publication Critical patent/CN107779065A/en
Withdrawn legal-status Critical Current

Abstract

The invention provides a kind of polyurea waterproof coating material and preparation method thereof, including component A and B component, the component A includes:The dicyclohexyl methyl hydride diisocyanate of 3,3 dimethyl 4,4, PPG, solvent;B component includes:Amino-polyether, amine chain extender, plasticizer, silane-modified nanometer lithopone.The present invention is with 3,3 dimethyl 4,4 dicyclohexyl methyl hydride diisocyanates are raw material, improve the photostability and weatherability of polyurea waterproof coating material, overcome using aromatic compound as raw material dope it is easy to aging the problem of, ensure that coating has enough gels and hardening time, coating and base material infiltration combine preferable.The present invention uses silane-modified nanometer lithopone, improves the corrosion-resistant and ageing resistace of coating, effective to absorb the concurrent third contact of a total solar or lunar eclipse catalytic reaction of ultraviolet, assigns coating antibiosis performance, adds the durability against pollution of coating.

Description

A kind of polyurea waterproof coating material and preparation method thereof
The application is divisional application, original bill Patent No.:201510591712.X the applying date is September in 2015 12, hair It is bright entitled:A kind of polyurea waterproof coating material and preparation method thereof.
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of polyurea waterproof coating material and preparation method thereof.
Background technology
Spray Polyurea Elastomer Technology be it is external in the past 10 years, applied after high solid coating, water paint, radiation curing After the low stain application techniques such as material, powdery paints, to adapt to a kind of novel solvent-free, the nothing that ecological requirements are developed, developed The green construction technology of pollution, there is preferable application prospect in the engineering such as anti-corrosion and waterproof, wear-resisting.
Two component spray polyurea waterproof coating material is a kind of bullet using isocyanate component and aminated compounds reaction generation Property body material, isocyanates both can be aromatic or aliphatic.Applied for two component spray polyurea water-proof Material, first component therein are monomer, condensate, the derivative of isocyanates, prepolymer and semi-prepolymer, prepolymer and half pre-polymerization Thing is to be made by Amino End Group or terminal hydroxy group compound with isocyanates reaction, the terminal hydroxy group compound generally use oligomer Dihydric alcohol, trihydroxylic alcohol or between mixture;Second component is by Amino End Group resin, Amino End Group chain extender, pigment, filler and auxiliary agent etc. Composition.Two kinds of mixed reaction speeds of component be exceedingly fast, it is necessary to special equipment under certain temperature, pressure by shock mode Mixing, is sprayed or is poured into a mould to form SPUA.
In existing two-component polyurea waterproof coating material based on aromatic series Spray Polyurea Elastomer, i.e., with aromatic series isocyanic acid Ester (TDI, MDI, PAPI) is main Material synthesis Isocyanate prepolymers body or hemipolymer, using aromatic amine as chain extender.Due to virtue Fragrant compounds of group can decompose under action of ultraviolet radiation, have chemical instability so that coating ageing-resistant performance reduces.It is existing Have in technology, application publication number is that CN101531861A Chinese patent literature discloses a kind of two-component spraying polyurea water-proof painting Material, the ageing-resistant performance of coating products is improved using aliphatic spray polyurea elastomer is raw material, but do not solved fundamentally Certainly ultraviolet needs further to be improved to the aging action of carbamide paint, its ageing-resistant performance.
The content of the invention
Present invention solves the technical problem that being to provide a kind of polyurea waterproof coating material and preparation method thereof, the polyurea water-proof applies Material is with good corrosion-resistant, anti-aging and anti-microbial property.
In view of this, the invention provides a kind of polyurea waterproof coating material, including component A and B component, in terms of mass fraction, The component A includes:
50-65 parts 3,3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanates,
30-40 part PPGs,
5-10 part solvents;
The B component includes:
40-50 part amino-polyethers,
30-40 part amine chain extenders,
10-15 part plasticizer,
The silane-modified nanometer lithopone of 5-10 parts.
Preferably, the PPG is pentaerythrite polyethers.
Preferably, the amino-polyether is diaminodiphenyl ether.
Preferably, the amine chain extender is 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanol methylamines.
Preferably, the plasticizer is dipropylene glycol dibenzoate.
Preferably, the granularity of silane-modified nanometer lithopone meets D90Less than 50nm, whiteness is more than 90%, and the silane is Acryloxy cetyl diethoxy silane.
Preferably, the silane-modified nanometer lithopone is prepared as follows:
It is 1 to volume ratio:0.1M hydrochloric acid solution is added in 1 ethanol water, regulation pH value is mixed to 4.0 Solution;
Nanometer lithopone is added into the mixed solution, in 40 DEG C of water-bath under 500r/min rotating speed stirring, by Acryloxy cetyl diethoxy silane is added dropwise to, continues to stir 3h, filters, washing, is fully dried at 80 DEG C, powder Silane-modified lithopone is obtained after broken.
Accordingly, the present invention also provides a kind of preparation method of polyurea waterproof coating material, in terms of mass fraction, including following step Suddenly:
30-40 parts PPG and 5-10 part solvents are placed in the first reactor, are warming up to 125 DEG C under agitation, It is passed through nitrogen and carries out atmosphere protection, decompression dehydration 3h, be cooled to 80 DEG C, then adds 50-65 parts 3, the ring of 3- dimethyl -4,4- bis- Hexyl methane diisocyanate, 3h is reacted after stirring, obtains component A;
40-50 parts amino-polyether, 30-40 parts amine chain extender and 10-15 part plasticizer are placed in the second reactor, led to Enter nitrogen and carry out atmosphere protection, the decompression dehydration 3h at 120 DEG C, then by described in the silane-modified nanometer lithopone addition of 5-10 parts Second reactor high speed stirs, and obtains B component.
Preferably, the amine chain extender is 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanol methylamines.
Preferably, the silane-modified nanometer lithopone is prepared as follows:It is 1 to volume ratio:1 ethanol is water-soluble 0.1M hydrochloric acid solution is added in liquid, regulation pH value obtains mixed solution to 4.0;Nanometer is added into the mixed solution to stand Moral powder, in 40 DEG C of water-bath under 500r/min rotating speed stirring, acryloxy cetyl diethoxy silicon is added dropwise Alkane, continue to stir 3h, filter, washing, silane-modified lithopone is obtained after fully dry, pulverize at 80 DEG C.
The invention provides a kind of polyurea waterproof coating material and preparation method thereof, including component A and B component, with mass fraction Meter, the component A include:50-65 parts 3,3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanates, 30-40 part polyether polyols Alcohol, 5-10 part solvents;The B component includes:40-50 part amino-polyethers, 30-40 part amine chain extenders, 10-15 part plasticizer, The silane-modified nanometer lithopone of 5-10 parts.Compared with prior art, on the one hand, the present invention uses the ring of 3,3- dimethyl -4,4- bis- Hexyl methane diisocyanate is raw material, and it belongs to saturated fat hydro carbons compound, simultaneous with methyl chains, improves polyureas The photostability and weatherability of water-repellent paint, overcome using aromatic compound as raw material dope it is easy to aging the problem of, while really Friendly coating has enough gels and hardening time, and coating and base material infiltration combine preferable.On the other hand, the present invention uses silane Modified Nano lithopone is modified to coating, not only increases the corrosion-resistant and ageing resistace of coating, while nano-particle The concurrent third contact of a total solar or lunar eclipse catalytic reaction of ultraviolet can be effectively absorbed, assigns coating antibiosis performance, adds the durability against pollution of coating.
Embodiment
For a further understanding of the present invention, the preferred embodiment of the invention is described with reference to embodiment, still It should be appreciated that these descriptions are simply further explanation the features and advantages of the present invention, rather than to the claims in the present invention Limitation.
It is described in terms of mass fraction the embodiment of the invention discloses a kind of polyurea waterproof coating material, including component A and B component Component A includes:
50-65 parts 3,3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanates,
30-40 part PPGs,
5-10 part solvents;
The B component includes:
40-50 part amino-polyethers,
30-40 part amine chain extenders,
10-15 part plasticizer,
The silane-modified nanometer lithopone of 5-10 parts.
The present invention substitutes arene raw material using saturated fat hydro carbons compound, hexa-atomic with the cyclohexyl with methyl chains Ring isocyanates -3,3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanate is raw material, and the raw material belongs to saturated fat hydro carbons Compound, simultaneous with methyl chains so that screening raw material has excellent photostability and weatherability.Present invention selection tool There is the aliphatic spray polyurea elastomer 3 compared with low activity, 3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanate is raw material, Not only overcome using aromatic compound as raw material dope it is easy to aging the problem of, while ensure that coating has enough gels and solid Change the time so that coating and base material infiltration combine preferably.
Preferably, the PPG is pentaerythrite polyethers;The solvent is preferably the poly- diformazan of vinyl Radical siloxane.
In B component, the amino-polyether is preferably diaminodiphenyl ether;The amine chain extender is preferably 2,5- diaminos Base -1,3,3- 3-methyl cyclohexanol methylamines;The plasticizer is preferably dipropylene glycol dibenzoate.
The amido chain extender that the present invention uses is preferably 2,5- diaminostilbenes, and 3,3- 3-methyl cyclohexanol methylamines, it is a kind of New chain extender, containing three Amino End Group groups, there is excellent reactivity and chemical stability, further improve coating Durability.
Because in general surface of inorganic particles is hydrophilic, it is not easy to be well mixed with traditional polymer, therefore, the present invention Using silane-modified nanometer lithopone, its surface is hydrophobic, adds the compatibility of particle and inorganic polymer, improves silicon Dispersing uniformity of the alkane modified Nano lithopone in coating so that coating can uniformly wrap up particle, avoid because of generation office The bulky grain in portion and reduce the adhesive property of coating.
Preferably, the granularity of the silane-modified nanometer lithopone preferably meets D90Less than 50nm, whiteness is more than 90%, the silane is preferably acryloxy cetyl diethoxy silane.
Preferably, the silane-modified nanometer lithopone is prepared as follows:It is 1 to volume ratio:1 second 0.1M hydrochloric acid solution is added in alcohol solution, regulation pH value obtains mixed solution to 4.0;Added into the mixed solution Nanometer lithopone, in 40 DEG C of water-bath under 500r/min rotating speed stirring, acryloxy cetyl diethyl is added dropwise TMOS, continue to stir 3h, filter, washing, silane-modified lithopone is obtained after fully dry, pulverize at 80 DEG C.
The filler that the present invention uses not only increases the corrosion-resistant and ageing resistance of coating for silane-modified nanometer lithopone Can, it contains zinc sulfide nano photocatalytic particle, can effectively absorb ultraviolet and make so as to eliminate aging of the ultraviolet to coating With improving the weatherability of coating.Nano-particle issues third contact of a total solar or lunar eclipse catalytic reaction in action of ultraviolet radiation simultaneously, and assigning coating surface has The effect of sterilization, bacterium, mould can be effectively killed, keep the bright and clean of coating top layer, add the durability against pollution of coating.
Preferably, the present invention is adjusted to the parts by weight of each component, the hexamethylene of 3,3- dimethyl -4,4- bis- Dicyclohexylmethane diisocyanate is preferably 55-65 parts, more preferably 55-60 parts;PPG is preferably 33-40 parts, more preferably For 33-37 parts;The solvent is preferably 5-8 parts, more preferably 7-8 parts;The amino-polyether is preferably 43-50 parts, more preferably For 43-46 parts;The amine chain extender is preferably 30-37 parts, more preferably 34-37 parts;The plasticizer is preferably 12-15 Part, more preferably 12-13 parts;The silane-modified nanometer lithopone is preferably 5-8 parts, more preferably 7-8 parts.
Accordingly, the present invention also provides a kind of preparation method of polyurea waterproof coating material, in terms of mass fraction, including following step Suddenly:30-40 parts PPG and 5-10 part solvents are placed in the first reactor, 125 DEG C is warming up under agitation, is passed through nitrogen Gas carries out atmosphere protection, decompression dehydration 3h, is cooled to 80 DEG C, then adds 50-65 parts 3,3- dimethyl -4,4- dicyclohexyl first Alkane diisocyanate, 3h is reacted after stirring, obtains component A;By 40-50 parts amino-polyether, 30-40 parts amine chain extender, 10-15 part plasticizer are placed in the second reactor, are passed through nitrogen and are carried out atmosphere protection, the decompression dehydration 3h at 120 DEG C, then will The silane-modified nanometer lithopone of 5-10 parts adds the second reactor high speed and stirred, and obtains B component.
Preferably, the amine chain extender is 2,5- diaminostilbenes, and 3,3- 3-methyl cyclohexanol methylamines, it is a kind of New chain extender, containing three Amino End Group groups, there is more excellent reactivity and chemical stability, further improve The durability of coating.
The silane-modified nanometer lithopone is preferably prepared as follows:It is 1 to volume ratio:1 ethanol water Middle addition 0.1M hydrochloric acid solution, regulation pH value obtain mixed solution to 4.0;Nanometer is added into the mixed solution and founds moral Powder, in 40 DEG C of water-bath under 500r/min rotating speed stirring, acryloxy cetyl diethoxy silane is added dropwise, Continue to stir 3h, filter, washing, silane-modified lithopone inserts is obtained after fully dry, pulverize at 80 DEG C.
The granularity of the silane-modified nanometer lithopone preferably meets D90Less than 50nm, whiteness is more than 90%, the silane Preferably acryloxy cetyl diethoxy silane.
The silane-modified nanometer lithopone not only increases the corrosion-resistant and ageing resistace of coating, and it contains zinc sulphide Nano-photo catalytic particle, ultraviolet can be effectively absorbed so as to eliminate aging action of the ultraviolet to coating, improves the resistance to of coating Hou Xing.Nano-particle issues third contact of a total solar or lunar eclipse catalytic reaction in action of ultraviolet radiation simultaneously, and assigning coating surface has the function that to sterilize, can be with It is effective to kill bacterium, mould, the bright and clean of coating top layer is kept, adds the durability against pollution of coating.
Preferably, the present invention is adjusted to the parts by weight of each raw material, 3,3- dimethyl -4,4- dicyclohexyls Methane diisocyanate is preferably 55-65 parts, more preferably 55-60 parts;PPG is preferably 33-40 parts, more preferably 33-37 parts;Solvent is preferably 5-8 parts, more preferably 7-8 parts;Amino-polyether is preferably 43-50 parts, more preferably 43-46 parts; Amine chain extender is preferably 30-37 parts, more preferably 34-37 parts;Plasticizer is preferably 12-15 parts, more preferably 12-13 parts; Silane-modified nanometer lithopone is preferably 5-8 parts, more preferably 7-8 parts.
Accordingly, the present invention also provides a kind of construction method of the polyurea waterproof coating material of above-mentioned preparation, including:By above-mentioned system Standby component A and B component are according to volume ratio 1:1 is used cooperatively, and makes A and B component atomizing spraying film forming using high-pressure spray gun.
From above scheme as can be seen that 1, present invention employs cyclohexyl hexatomic ring isocyanates -3 with methyl chains, 3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanate is raw material, and the raw material belongs to saturated fat hydro carbons compound, while band There are methyl chains so that screening raw material has excellent photostability and weatherability.2nd, amido chain extender preferably uses 2,5- Diaminostilbene, 3,3- 3-methyl cyclohexanol methylamines, it contains three Amino End Group groups, has more excellent reactivity and chemistry Stability, further improve the durability of coating.3rd, selected filler is silane-modified nanometer lithopone, contains zinc sulfide nano light Catalyst particle, ultraviolet can be effectively absorbed so as to eliminate aging action of the ultraviolet to coating, improves the weatherability of coating.Together When nano-particle issue third contact of a total solar or lunar eclipse catalytic reaction in action of ultraviolet radiation, assigning coating surface has the function that to sterilize, can be effective Bacterium, mould are killed, keeps the bright and clean of coating top layer.
For a further understanding of the present invention, technical scheme provided by the invention is carried out specifically with reference to embodiment Bright, protection scope of the present invention is not limited by the following examples.
The raw material and chemical reagent that the embodiment of the present invention uses are purchased in market.
Embodiment 1
Dose volume ratio is 1 first:1 ethanol water, pH value is adjusted to 4.0 with 0.1M hydrochloric acid solution, by nanometer Lithopone is dispersed in above-mentioned solution, and in 40 DEG C of water-bath under 500r/min rotating speed stirring, acryloyl is added dropwise Epoxide cetyl diethoxy silane, after the completion of continue stir 3h, finally through suction filtration, washing, at 80 DEG C fully dry, Crush, obtain silane-modified lithopone, the granularmetric composition of the nanometer lithopone meets that D90 is less than 50nm, and whiteness is more than 90%.
Embodiment 2
(1), example in mass ratio, weigh 40 parts pentaerythrite polyethers and 10 parts of vinyldimethicones in reaction In kettle, temperature is raised under agitation to 125 DEG C, while is passed through nitrogen and carries out atmosphere protection, and above-mentioned substance is subjected to decompression dehydration 3h, after the completion of temperature is reduced to 80 DEG C, then add 50 parts of the isocyanic acid of 3,3- dimethyl -4,4- dicyclohexyl methyl hydride two Ester, reaction 3h is kept to obtain component A after stirring.
(2), according to mass ratio, 40 parts of diaminodiphenyl ethers, 40 parts of 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanols are weighed Methylamine, 10 parts of dipropylene glycol dibenzoates are passed through nitrogen protection decompression dehydration 3h at 120 DEG C, so in another reactor Silane-modified lithopone prepared by 10 parts of embodiments 1 is added afterwards to stir in reactor high speed, obtains B component.
(3), by component A and B component according to volume ratio 1:1 is used cooperatively, and A and B component is atomized spray using high-pressure spray gun Apply film forming.
Embodiment 3
(1), example in mass ratio, weigh 37 parts pentaerythrite polyethers and 8 parts of vinyldimethicones in reaction In kettle, temperature is raised under agitation to 125 DEG C, while is passed through nitrogen and carries out atmosphere protection, and above-mentioned substance is subjected to decompression dehydration 3h, after the completion of temperature is reduced to 80 DEG C, then add 55 parts of the isocyanic acid of 3,3- dimethyl -4,4- dicyclohexyl methyl hydride two Ester, reaction 3h is kept to obtain component A after stirring.
(2), according to mass ratio, 43 parts of diaminodiphenyl ethers, 37 parts of 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanols are weighed Methylamine, 12 parts of dipropylene glycol dibenzoates are passed through nitrogen protection decompression dehydration 3h at 120 DEG C, so in another reactor Silane-modified lithopone prepared by 8 parts of embodiments 1 is added afterwards to stir in reactor high speed, obtains B component.
(3), by component A and B component according to volume ratio 1:1 is used cooperatively, and A and B component is atomized spray using high-pressure spray gun Apply film forming.
Embodiment 4
(1), example in mass ratio, weigh 33 parts pentaerythrite polyethers and 7 parts of vinyldimethicones in reaction In kettle, temperature is raised under agitation to 125 DEG C, while is passed through nitrogen and carries out atmosphere protection, and above-mentioned substance is subjected to decompression dehydration 3h, after the completion of temperature is reduced to 80 DEG C, then add 60 parts of the isocyanic acid of 3,3- dimethyl -4,4- dicyclohexyl methyl hydride two Ester, reaction 3h is kept to obtain component A after stirring.
(2), according to mass ratio, 46 parts of diaminodiphenyl ethers, 34 parts of 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanols are weighed Methylamine, 13 parts of dipropylene glycol dibenzoates are passed through nitrogen protection decompression dehydration 3h at 120 DEG C, so in another reactor Silane-modified lithopone prepared by 7 parts of embodiments 1 is added afterwards to stir in reactor high speed, obtains B component.
(3), by component A and B component according to volume ratio 1:1 is used cooperatively, and A and B component is atomized spray using high-pressure spray gun Apply film forming.
Embodiment 5
(1), example in mass ratio, weigh 30 parts pentaerythrite polyethers and 5 parts of vinyldimethicones in reaction In kettle, temperature is raised under agitation to 125 DEG C, while is passed through nitrogen and carries out atmosphere protection, and above-mentioned substance is subjected to decompression dehydration 3h, after the completion of temperature is reduced to 80 DEG C, then add 65 parts of the isocyanic acid of 3,3- dimethyl -4,4- dicyclohexyl methyl hydride two Ester, reaction 3h is kept to obtain component A after stirring.
(2), according to mass ratio, 50 parts of diaminodiphenyl ethers, 30 parts of 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanols are weighed Methylamine, 15 parts of dipropylene glycol dibenzoates are passed through nitrogen protection decompression dehydration 3h at 120 DEG C, so in another reactor Silane-modified lithopone prepared by 5 parts of embodiments 1 is added afterwards to stir in reactor high speed, obtains B component.
(3), by component A and B component according to volume ratio 1:1 is used cooperatively, and A and B component is atomized spray using high-pressure spray gun Apply film forming.
To 2-5 of the embodiment of the present invention prepare the polyurea waterproof coating material with anti-microbial property leading indicator according to GB/ T23446-2009 standards are detected, and its test result is as shown in table 1.As seen from table, water-repellent paint obtained by each embodiment Main performance index is satisfied by requirements of the national standard.
The main performance index of table 1, each embodiment water-repellent paint
The explanation of above example is only intended to help the method and its core concept for understanding the present invention.It should be pointed out that pair For those skilled in the art, under the premise without departing from the principles of the invention, the present invention can also be carried out Some improvement and modification, these are improved and modification is also fallen into the protection domain of the claims in the present invention.
The foregoing description of the disclosed embodiments, professional and technical personnel in the field are enable to realize or using the present invention. A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one The most wide scope caused.

Claims (1)

1. a kind of polyurea waterproof coating material, it is characterised in that including component A and B component, in terms of mass fraction, the component A bag Include:
50-65 parts 3,3- dimethyl -4,4- dicyclohexyl methyl hydride diisocyanates,
30-40 part PPGs, the PPG are pentaerythrite polyethers,
5-10 part solvents;
The B component includes:
40-50 part amino-polyethers, the amino-polyether are diaminodiphenyl ether,
30-40 part amine chain extenders, the amine chain extender are 2,5- diaminostilbenes, 3,3- 3-methyl cyclohexanol methylamines,
10-15 part plasticizer, the plasticizer are dipropylene glycol dibenzoate,
The silane-modified nanometer lithopone of 5-10 parts, the granularity of the silane-modified nanometer lithopone meet D90Less than 50nm, whiteness More than 90%, the silane is acryloxy cetyl diethoxy silane;
The silane-modified nanometer lithopone is prepared as follows:
It is 1 to volume ratio:0.1M hydrochloric acid solution is added in 1 ethanol water, regulation pH value obtains mixed solution to 4.0;
Nanometer lithopone is added into the mixed solution, in 40 DEG C of water-bath under 500r/min rotating speed stirring, is added dropwise Enter acryloxy cetyl diethoxy silane, continue to stir 3h, filter, washing, after fully dry, pulverize at 80 DEG C Obtain silane-modified lithopone.
CN201711091424.3A 2015-09-12 2015-09-12 A kind of polyurea waterproof coating material and preparation method thereof Withdrawn CN107779065A (en)