CN107747226A - A kind of preparation method of dress ornament antibacterial finish agent - Google Patents
A kind of preparation method of dress ornament antibacterial finish agent Download PDFInfo
- Publication number
- CN107747226A CN107747226A CN201711237398.0A CN201711237398A CN107747226A CN 107747226 A CN107747226 A CN 107747226A CN 201711237398 A CN201711237398 A CN 201711237398A CN 107747226 A CN107747226 A CN 107747226A
- Authority
- CN
- China
- Prior art keywords
- parts
- good
- preparation
- dress ornament
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method this application discloses dress ornament with antibacterial finish agent, weighs pure water, protease, colouring agent, azodicarbonamide, sodium acetate, sodium citrate, ammonium phosphate, polyacrylonitrile fibre, diphenylguanidine, dinitrophenol and amido silicon oil;Preparation method is simple, and anti-mold effect is good, mildewproof, and the 5MPa of tensile strength 3, resistance to moisture is excellent, makes dress ornament more soft, good hand touch;Skin-friendly is good, increases gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 250 450 times, dirt-removing power is strong;Antistatic property is good, and 80 90 acarids of water-wash resistance walk quickly and keep away rate 93 97%, and pliability 1mm, glossiness is good, and hydrophobic oil repellency is good;Hydrophilicity is good, extends embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 98 99%, can extensively produce and constantly replace current material.
Description
Technical field
The application belongs to dress material field, more particularly to a kind of dress ornament preparation method of antibacterial finish agent.
Background technology
During the application of antibacterial finishing agent originates from World War II, German army was due to wearing antibacterial military uniform and significantly at that time
Reduce the bacterium infection of the wounded.Antibacterial finishing agent can make clothing more comfortable, improve the hygiene and health of people's living environment
Deng.
Resin finishing agent is intended to prevent or improved contraction or the wrinkle phenomenon that fabric occurs in wearing process, in its printing and dyeing
Chemical finishing (being commonly called as resin finishing) is carried out with synthetic resin after processing, such as shrinkproof, wrinkle resistant resin arranges.Material used is referred to as
Resin finishing agent.
Textile finishing is to apply a kind of finishing agent on fabric, and it can change the surface property of fabric, so as to assign fabric
Special function.Such as it is to handle fabric with the finishing agent with low surface tension that hydrophobic and oil repellent, which arranges, changes the surface of fiber
Characteristic, fabric face is set to be not easy by water or glossy wet and sprawl, so as to reach the purpose of hydrophobic and oil repellent.Soil resistant finish and easy decontamination
Arrangement is the surface property or surface state by changing fiber, makes fabric be not easy to attach dirt under dress, use condition, or
The dirt attached is easy to wash to the processing technology of not recontamination.
Nano-silver antibacterial finishing agent is a kind of to should be primarily used to the whole of each kind fabric such as various textiles, non-woven fabrics, leather
Manage agent.
High-efficiency antimicrobial, it is mould proof, drive mite textile finshing agent be three-in-one polymer-function material, suitable for cotton, viscose glue,
The fabrics such as LYOCELL;Suitable for protein fibre fabrics such as wool, silks;Suitable for chemistry such as polyamide fibre, terylene, spandexs
Fabric;It is also applied for the blended fabric such as cellulose and terylene, polyamide fibre, spandex, PPT.Treated fabric, which has, to be held
Long, antibacterial, mildew-proof function and certain drive mite effect efficiently, stable.
With the improvement of living standards, people increasingly pay attention to the quality of life, it would be desirable to obtaining has the clothing of comfort,
And the living environment of hygiene and health.For various textiles require more and more higher, particularly safely, feel at ease, comfortably,
The formation of " green " ideas such as health, health, cleaning, the antibacterial of textile, mould proof, deodorization final finishing processing is set to be more exposed to people
Attention.
In life, people inevitably touch the microorganisms such as various bacteriums, fungi, and these microorganisms exist
It under suitable external condition, can rapidly breed, and be spread disease by the mode such as contacting, influence the health of people and normal
Work, studying and living.Fiber belongs to porous material, can form the polylayer forest in countless spaces after superposition braiding again, therefore
Fabric is easier to adsorb mushroom.Antibiotic finish is exactly fabric is had the function of suppressing fungus grown, maintains the clothing life of health
Environment living, ensures health.
The content of the invention
The technical problem of solution:
The application is directed to above-mentioned technical problem, there is provided a kind of preparation method of dress ornament antibacterial finish agent, solves existing dress ornament and uses
Antibacterial finish agent anti-mold effect is poor, anti-wrinkle effect difference and the technical problem such as fungistatic effect difference.
Technical scheme:
A kind of dress ornament preparation method of antibacterial finish agent, comprises the following steps:
The first step:100 parts of pure water, protease 25-45 parts, colouring agent 0.8-1.2 parts, azo two are weighed according to parts by weight proportioning
Formamide 15-35 parts, sodium acetate 0.1-2 parts, sodium citrate 5-25 parts, ammonium phosphate 20-40 parts, polyacrylonitrile fibre 15-25 parts,
Diphenylguanidine 1-5 parts, dinitrophenol 0.5-4.5 parts and amido silicon oil 1-5 parts;
Second step:By sodium citrate, polyacrylonitrile fibre and diphenylguanidine input with the anti-of thermometer, mixer and heater
Answer in kettle, open mixer mixing, be warming up to 50-60 DEG C, mixing velocity 250-350r/min, mix 1-3h;
3rd step:Sodium acetate, pure water and protease are sequentially added, is passed through nitrogen, regulation mixing velocity to 400- in a kettle
500 r/min, 60-100min is mixed, add surplus stock, be warming up to 90-100 DEG C, by well mixed production after dissolving completely
In thing input sand mill, 20-30min is sanded, after crossing cleaner liquid, is produced after standing 6-10h.
As a preferred technical solution of the present invention:In the first step dress ornament with the raw material of antibacterial finish agent by weight
Number proportioning is as follows:100 parts of pure water, 25 parts of protease, 0.8 part of colouring agent, 15 parts of azodicarbonamide, 0.1 part of sodium acetate, lemon
1 part of 5 parts of lemon acid sodium, 20 parts of ammonium phosphate, 15 parts of polyacrylonitrile fibre, 1 part of diphenylguanidine, 0.5 part of dinitrophenol and amido silicon oil.
As a preferred technical solution of the present invention:In the first step dress ornament with the raw material of antibacterial finish agent by weight
Number proportioning is as follows:100 parts of pure water, 45 parts of protease, 1.2 parts of colouring agent, 35 parts of azodicarbonamide, 2 parts of sodium acetate, lemon
5 parts of sour 25 parts of sodium, 40 parts of ammonium phosphate, 25 parts of polyacrylonitrile fibre, 5 parts of diphenylguanidine, 4.5 parts of dinitrophenol and amido silicon oil.
As a preferred technical solution of the present invention:In the first step dress ornament with the raw material of antibacterial finish agent by weight
Number proportioning is as follows:100 parts of pure water, 5 parts of protease 3,1 part of colouring agent, 25 parts of azodicarbonamide, 1 part of sodium acetate, citric acid
3 parts of 15 parts of sodium, 30 parts of ammonium phosphate, 20 parts of polyacrylonitrile fibre, 3 parts of diphenylguanidine, 2.5 parts of dinitrophenol and amido silicon oil.
As a preferred technical solution of the present invention:The colouring agent uses the bright red LC of rubber.
Beneficial effect:
A kind of dress ornament of the present invention uses above technical scheme compared with prior art with the preparation method of antibacterial finish agent, tool
There is following technique effect:1st, preparation method is simple, and anti-mold effect is good, mildewproof, and tensile strength 3-5MPa, resistance to moisture is excellent,
Make dress ornament more soft, good hand touch;2nd, skin-friendly is good, increases gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 250-
450 times, dirt-removing power is strong;3rd, antistatic property is good, and 80-90 acarid of water-wash resistance walks quickly and keeps away rate 93-97%, pliability 1mm, light
Damp degree is good, and hydrophobic oil repellency is good;4th, hydrophilicity is good, extends embroidery service life, fast drying, fire resistance is good, antibiotic property
Can be good, to Escherichia coli bacteriostasis rate 98-99%, it can extensively produce and constantly replace current material.
Embodiment
Embodiment 1:
100 parts of pure water, 25 parts of protease, the bright red LC0.8 parts of rubber, azodicarbonamide 15 are weighed according to parts by weight proportioning
Part, 0.1 part of sodium acetate, 5 parts of sodium citrate, 20 parts of ammonium phosphate, 15 parts of polyacrylonitrile fibre, 1 part of diphenylguanidine, dinitrophenol
0.5 part and 1 part of amido silicon oil.
By reaction of sodium citrate, polyacrylonitrile fibre and the diphenylguanidine input with thermometer, mixer and heater
In kettle, mixer mixing is opened, is warming up to 50 DEG C, mixing velocity 250r/min, mixes 1h.
Sodium acetate, pure water and protease are sequentially added, is passed through nitrogen, regulation mixing velocity to 400 r/ in a kettle
Min, mixing 60min, adds surplus stock, is warming up to 90 DEG C, puts into well mixed product in sand mill after dissolving completely,
20min is sanded, after crossing cleaner liquid, is produced after standing 6h.
Preparation method is simple, and anti-mold effect is good, mildewproof, and tensile strength 3MPa, resistance to moisture is excellent, makes dress ornament more soft
It is soft, good hand touch;Skin-friendly is good, increases gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 250 times, dirt-removing power is strong;It is anti-
Antistatic property is good, and 80-90 acarid of water-wash resistance walks quickly and keeps away rate 93%, and pliability 1mm, glossiness is good, and hydrophobic oil repellency is good;Parent
Water-based energy is good, extends embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, can to Escherichia coli bacteriostasis rate 98%
To produce extensively and constantly replace current material.
Embodiment 2:
100 parts of pure water, 45 parts of protease, the bright red LC1.2 parts of rubber, azodicarbonamide 35 are weighed according to parts by weight proportioning
Part, 2 parts of sodium acetate, 25 parts of sodium citrate, 40 parts of ammonium phosphate, 25 parts of polyacrylonitrile fibre, 5 parts of diphenylguanidine, dinitrophenol 4.5
5 parts of part and amido silicon oil.
By reaction of sodium citrate, polyacrylonitrile fibre and the diphenylguanidine input with thermometer, mixer and heater
In kettle, mixer mixing is opened, is warming up to 60 DEG C, mixing velocity 350r/min, mixes 3h.
Sodium acetate, pure water and protease are sequentially added, is passed through nitrogen, regulation mixing velocity to 500 r/ in a kettle
Min, 100min is mixed, add surplus stock, be warming up to 100 DEG C, well mixed product is put into sand mill after dissolving completely
In, 30min is sanded, after crossing cleaner liquid, is produced after standing 10h.
Preparation method is simple, and anti-mold effect is good, mildewproof, and tensile strength 4MPa, resistance to moisture is excellent, makes dress ornament more soft
It is soft, good hand touch;Skin-friendly is good, increases gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 300 times, dirt-removing power is strong;It is anti-
Antistatic property is good, and 85 acarids of water-wash resistance walk quickly and keep away rate 95%, and pliability 1mm, glossiness is good, and hydrophobic oil repellency is good;Hydrophily
Can be good, extend embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, can be with to Escherichia coli bacteriostasis rate 98.5%
Produce extensively and constantly replace current material.
Embodiment 3:
According to parts by weight proportioning weigh 100 parts of pure water, 5 parts of protease 3, the bright red LC1 parts of rubber, 25 parts of azodicarbonamide,
1 part of sodium acetate, 15 parts of sodium citrate, 30 parts of ammonium phosphate, 20 parts of polyacrylonitrile fibre, 3 parts of diphenylguanidine, 2.5 parts of dinitrophenol
With 3 parts of amido silicon oil.
By reaction of sodium citrate, polyacrylonitrile fibre and the diphenylguanidine input with thermometer, mixer and heater
In kettle, mixer mixing is opened, is warming up to 55 DEG C, mixing velocity 300r/min, mixes 2h.
Sodium acetate, pure water and protease are sequentially added, is passed through nitrogen, regulation mixing velocity to 450 r/ in a kettle
Min, mixing 80min, adds surplus stock, is warming up to 95 DEG C, puts into well mixed product in sand mill after dissolving completely,
25min is sanded, after crossing cleaner liquid, is produced after standing 8h.
Preparation method is simple, and anti-mold effect is good, mildewproof, and tensile strength 5MPa, resistance to moisture is excellent, makes dress ornament more soft
It is soft, good hand touch;Skin-friendly is good, increases gloss, adhesion 1 grade, good corrosion resistance, abrasion resistance 350 times, dirt-removing power is strong;It is anti-
Antistatic property is good, and 90 acarids of water-wash resistance walk quickly and keep away rate 97%, and pliability 1mm, glossiness is good, and hydrophobic oil repellency is good;Hydrophily
Can be good, extend embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 99%, Ke Yiguang
It is general to produce and constantly replace current material.
Composition all components in above example can be with commercially available.
The above embodiments are intended to illustrate the present invention, rather than limitation, therefore with the present invention's
Any change in claims suitable implication and scope, all it is considered as being included within the scope of the claims.
Claims (5)
1. a kind of dress ornament preparation method of antibacterial finish agent, it is characterised in that comprise the following steps:
The first step:100 parts of pure water, protease 25-45 parts, colouring agent 0.8-1.2 parts, azo two are weighed according to parts by weight proportioning
Formamide 15-35 parts, sodium acetate 0.1-2 parts, sodium citrate 5-25 parts, ammonium phosphate 20-40 parts, polyacrylonitrile fibre 15-25 parts,
Diphenylguanidine 1-5 parts, dinitrophenol 0.5-4.5 parts and amido silicon oil 1-5 parts;
Second step:By sodium citrate, polyacrylonitrile fibre and diphenylguanidine input with the anti-of thermometer, mixer and heater
Answer in kettle, open mixer mixing, be warming up to 50-60 DEG C, mixing velocity 250-350r/min, mix 1-3h;
3rd step:Sodium acetate, pure water and protease are sequentially added, is passed through nitrogen, regulation mixing velocity to 400- in a kettle
500 r/min, 60-100min is mixed, add surplus stock, be warming up to 90-100 DEG C, by well mixed production after dissolving completely
In thing input sand mill, 20-30min is sanded, after crossing cleaner liquid, is produced after standing 6-10h.
2. the dress ornament according to claim 1 preparation method of antibacterial finish agent, it is characterised in that:Taken in the first step
Decorations are as follows with the raw materials by weight portion proportioning of antibacterial finish agent:100 parts of pure water, 25 parts of protease, 0.8 part of colouring agent, azo
15 parts of diformamide, 0.1 part of sodium acetate, 5 parts of sodium citrate, 20 parts of ammonium phosphate, 15 parts of polyacrylonitrile fibre, 1 part of diphenylguanidine, two
1 part of 0.5 part of nitrophenol and amido silicon oil.
3. the dress ornament according to claim 1 preparation method of antibacterial finish agent, it is characterised in that:Taken in the first step
Decorations are as follows with the raw materials by weight portion proportioning of antibacterial finish agent:100 parts of pure water, 45 parts of protease, 1.2 parts of colouring agent, azo
35 parts of diformamide, 2 parts of sodium acetate, 25 parts of sodium citrate, 40 parts of ammonium phosphate, 25 parts of polyacrylonitrile fibre, 5 parts of diphenylguanidine, two
5 parts of 4.5 parts of nitrophenol and amido silicon oil.
4. the dress ornament according to claim 1 preparation method of antibacterial finish agent, it is characterised in that:Taken in the first step
Decorations are as follows with the raw materials by weight portion proportioning of antibacterial finish agent:100 parts of pure water, 5 parts of protease 3,1 part of colouring agent, azo two
25 parts of formamide, 1 part of sodium acetate, 15 parts of sodium citrate, 30 parts of ammonium phosphate, 20 parts of polyacrylonitrile fibre, 3 parts of diphenylguanidine, dinitro
3 parts of 2.5 parts of base phenol and amido silicon oil.
5. the dress ornament according to claim 1 preparation method of antibacterial finish agent, it is characterised in that:The colouring agent uses
The bright red LC of rubber.