CN107740276A - A kind of radiation proof softener and preparation method thereof - Google Patents
A kind of radiation proof softener and preparation method thereof Download PDFInfo
- Publication number
- CN107740276A CN107740276A CN201710897079.6A CN201710897079A CN107740276A CN 107740276 A CN107740276 A CN 107740276A CN 201710897079 A CN201710897079 A CN 201710897079A CN 107740276 A CN107740276 A CN 107740276A
- Authority
- CN
- China
- Prior art keywords
- parts
- softener
- radiation proof
- essential oil
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of radiation proof softener, the radiation proof softener includes the raw material of following parts by weight:10 20 parts of octamethylcy-clotetrasiloxane, 57 parts of polyether-modified nanometer silane, 5 10 parts of sodium acid carbonate, 5 10 parts of plants essential oil, 10 15 parts of odium stearate, 35 parts of acrylamide, 35 parts of calgon, 5 10 parts of nano silicon, 10 20 parts of ethanol, 5 10 parts of chitosan, 5 10 parts of metallic fiber powder, 5 10 parts of nanometer ferrite powder, 30 50 parts of deionized water.After the radiation proof softener application of the present invention, the stiffness decline of fabric is a lot, and shearing rigidity and bending stiffness all decline a lot, and creasy recovery angle increase is a lot, and compliance improves a lot, and shielding property improves more than 80% than source textile.The radiation proof softener manufacturing process of the present invention is simple to operation, and low in raw material price easily obtains, and nontoxic, human body is not stimulated, volatility is low.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relates to a kind of radiation proof softener and preparation method thereof.
Background technology
It is uniformly last layer diaphragm for fabric, fiber that the effect of softener, which just looks like, fiber surface due to
Softener is adsorbed, interfibrous coefficient of friction reduces, and mobility enhances, the intrinsic smooth, extension of fiber, compressibility
Can also it be recovered, so fabric becomes more soft, fluffy, flexible.
In daily life, electromagnetic radiation turns into the third-largest " stealthy killer " after pollution of waterhead, air pollution, to me
Health have a very big impact.Such as:Radiation can cause children's intelligence incomplete, and it is most likely to cause
One of the reason for virgin cases with leukemia;Radiation can induce cancer and accelerate the cancer cell multiplication of human body;Radiation can influence people
Cardiovascular system, show as palpitaition, hair loss, insomnia, some women disorder of menstrual cycle, bradycardia, heartbeat oligemia, Dou Xingxin
Rate is uneven, Neuroleptic Leukocytopenia, and immunologic function declines etc..
With the improvement of living standards, the enhancing of the awareness of environment protection and health, the requirement more and more higher to textile material, it is desirable to
Fabric has certain submissive wrinkle resistance, radiation resistance, and to the quality requirements of feature softener also more and more higher, this also promotees
The development of multi-functional softener is entered.
The content of the invention
It is an object of the invention to provide a kind of radiation proof softener and preparation method, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme:
A kind of radiation proof softener, according to parts by weight, including following components:Octamethylcy-clotetrasiloxane 10-20 parts, gather
Ether modified Nano silane 5-7 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, odium stearate 10-15 parts, acrylamide 3-5
Part, calgon 3-5 parts, nano silicon 5-10 parts, ethanol 10-20 parts, chitosan 5-10 parts, metallic fiber powder 5-
10 parts, nanometer ferrite powder 5-10 parts, deionized water 30-50 parts.
Preferably, the ethanol is absolute ethyl alcohol, and purity is pure to analyze.
Preferably, the plants essential oil is Lavender, Peppermint essential oil, lemon, jasmine essential oil, rhodamine toner
It is one or more than one kinds of in oil, yulan essential oil, cape jasmine flower essential oil, narcissus flower essential oil.
Preferably, the nanometer ferrite powder, metallic fiber powder, the particle diameter of nano silicon are 50-200nm.
Preferably, the metallic fiber powder is one kind in silver plated fiber, plating aluminum fiber, Cu coated fibre, nickel plating fiber
Or more than one.
Preferably, described radiation proof softener, according to parts by weight, including following components:Octamethylcy-clotetrasiloxane
10 parts, 5 parts of polyether-modified nanometer silane, 5 parts of sodium acid carbonate, 5 parts of plants essential oil, 10 parts of odium stearate, 3 parts of acrylamide, six
3 parts of sodium metaphosphate, 5 parts of nano silicon, 10 parts of ethanol, 5 parts of chitosan, 5 parts of metallic fiber powder, nanometer ferrite powder
5 parts, 30 parts of deionized water.
Preferably, described radiation proof softener, according to parts by weight, including following components:Octamethylcy-clotetrasiloxane
15 parts, 6 parts of polyether-modified nanometer silane, 8 parts of sodium acid carbonate, 8 parts of plants essential oil, 13 parts of odium stearate, 4 parts of acrylamide, six
4 parts of sodium metaphosphate, 8 parts of nano silicon, 15 parts of ethanol, 8 parts of chitosan, 8 parts of metallic fiber powder, nanometer ferrite powder
8 parts, 40 parts of deionized water.
Preferably, described radiation proof softener, according to parts by weight, including following components:Octamethylcy-clotetrasiloxane
20 parts, 7 parts of polyether-modified nanometer silane, 10 parts of sodium acid carbonate, 10 parts of plants essential oil, 15 parts of odium stearate, 5 parts of acrylamide,
5 parts of calgon, 10 parts of nano silicon, 20 parts of ethanol, 10 parts of chitosan, 10 parts of metallic fiber powder, Nanoscale Iron oxygen
10 parts of body powder, 50 parts of deionized water.
A kind of preparation method of radiation proof softener, is comprised the following steps that:
(1) octamethylcy-clotetrasiloxane 10-20 parts, deionized water 30-50 parts are added inside four-hole boiling flask, in oil bath pan
80-100 DEG C of heating, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly, and insertion flatly is equipped with 5-7 parts
The separatory funnel of polyether-modified nanometer silane, rate of addition 2-3mL/min, agitator, mixing speed 1000- is inserted flatly
2000 revs/min, reaction time 3-4h;
(2) first by calgon 3-5 parts, metallic fiber powder 5-10 parts, nanometer ferrite powder 5-10 parts, nanometer two
Silica 5-10 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic power 1000-2000W, obtain uniformly molten
Liquid;
(3) homogeneous solution of step (2) is added in the solution of step (1), 500-1000 revs/min, 20-30 points of stirring
Clock;
(4) temperature is reduced to 60-70 DEG C, addition odium stearate 10-15 parts, acrylamide 3-5 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
(5) 40-50 DEG C is cooled to, adds chitosan 5-10 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, 500-
1000 revs/min, stir 1-2 hours;
(6) 20-30 DEG C is cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows:
1st, after radiation proof softener of the invention application, the stiffness of fabric declines a lot, and shearing rigidity is firm with bending
Degree all decline is a lot, and creasy recovery angle increase is a lot, and compliance improves a lot, and the shielding property of fabric improves than source textile
More than 80%.
2nd, after radiation proof softener application fabric of the invention, fabric is not easy yellowing, and it is soft to assign fabric feeling radiation proof
It is suitable, smooth, plentiful, and there is good drapability and bulkiness.
3rd, after radiation proof softener application fabric of the invention, the excellent water imbibition of natural fabric and good can be kept
Good gas permeability, hydrophobic fiber type is set to obtain hygroscopicity.
4th, after radiation proof softener application fabric of the invention, fabric has good resilience, resistance to fold performance.
5th, radiation proof softener manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and nontoxic nothing
Evil, is not stimulated human body, volatility is low.
6th, mutual compatibility between various raw materials used in radiation proof softener of the invention, synergy, collectively constitutes performance
Excellent product.
7th, the addition of sodium acid carbonate improves the submissive performance of fabric, metallic fiber powder, nanometer ferrite powder plus
Enter to improve the shielding property of fabric.
8th, technique is simplified, safe operation is simple, is easy to industrialized production.
9th, radiation proof softener working solution of the invention is stable, is not demulsified, not floating oil
10th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of radiation proof softener, according to parts by weight, including following components:The silica of prestox ring four
Alkane 10-20 parts, polyether-modified nanometer silane 5-7 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, odium stearate 10-15
Part, acrylamide 3-5 parts, calgon 3-5 parts, nano silicon 5-10 parts, ethanol 10-20 parts, chitosan 5-10 parts,
Metallic fiber powder 5-10 parts, nanometer ferrite powder 5-10 parts, deionized water 30-50 parts.
Present invention also offers a kind of preparation method of radiation proof softener, comprise the following steps that:
(1) octamethylcy-clotetrasiloxane 10-20 parts, deionized water 30-50 parts are added inside four-hole boiling flask, in oil bath pan
80-100 DEG C of heating, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly, and insertion flatly is equipped with 5-7 parts
The separatory funnel of polyether-modified nanometer silane, rate of addition 2-3mL/min, agitator, mixing speed 1000- is inserted flatly
2000 revs/min, reaction time 3-4h;
(2) first by calgon 3-5 parts, metallic fiber powder 5-10 parts, nanometer ferrite powder 5-10 parts, nanometer two
Silica 5-10 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic power 1000-2000W, obtain uniformly molten
Liquid;
(3) homogeneous solution of step (2) is added in the solution of step (1), 500-1000 revs/min, 20-30 points of stirring
Clock;
(4) temperature is reduced to 60-70 DEG C, addition odium stearate 10-15 parts, acrylamide 3-5 parts, 500-1000 revs/min
Clock, stir 20-30 minutes;
(5) 40-50 DEG C is cooled to, adds chitosan 5-10 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, 500-
1000 revs/min, stir 1-2 hours;
(6) 20-30 DEG C is cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of radiation proof softener, according to parts by weight, including following components:The silica of prestox ring four
10 parts of alkane, 5 parts of polyether-modified nanometer silane, 5 parts of sodium acid carbonate, 5 parts of plants essential oil, 10 parts of odium stearate, 3 parts of acrylamide,
3 parts of calgon, 5 parts of nano silicon, 10 parts of ethanol, 5 parts of chitosan, 5 parts of metallic fiber powder, nanometer ferrite powder
Last 5 parts, 30 parts of deionized water.
Present invention also offers a kind of preparation method of radiation proof softener, comprise the following steps that:
(1) 10 parts of octamethylcy-clotetrasiloxane, 30 parts of deionized water are added inside four-hole boiling flask, 80 DEG C add in oil bath pan
Heat, nitrogen protection, the speed for being passed through nitrogen is 1L/min, keeps charging flatly, and insertion flatly is equipped with 5 parts of polyether-modified nano-silicons
The separatory funnel of alkane, rate of addition 2mL/min, agitator is inserted flatly, mixing speed is 1000 revs/min, the reaction time
For 3h;
(2) first by 3 parts of calgon, 5 parts of metallic fiber powder, 5 parts of nanometer ferrite powder, nano silicon 5
Part, 10 parts of ethanol, with ultrasonic disperse 10 minutes, ultrasonic power 1000W, obtain homogeneous solution;
(3) homogeneous solution of step (2) is added in the solution of step (1), 500 revs/min, stirred 20 minutes;
(4) temperature is reduced to 60 DEG C, is added 10 parts of odium stearate, 3 parts of acrylamide, 500 revs/min, is stirred 20 minutes;
(5) 40 DEG C are cooled to, 5 parts of chitosan, 5 parts of sodium acid carbonate, 5 parts of plants essential oil is added, 500 revs/min, stirs 1
Hour;
(6) 20 DEG C are cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of radiation proof softener, according to parts by weight, including following components:The silica of prestox ring four
15 parts of alkane, 6 parts of polyether-modified nanometer silane, 8 parts of sodium acid carbonate, 8 parts of plants essential oil, 13 parts of odium stearate, 4 parts of acrylamide,
4 parts of calgon, 8 parts of nano silicon, 15 parts of ethanol, 8 parts of chitosan, 8 parts of metallic fiber powder, nanometer ferrite powder
Last 8 parts, 40 parts of deionized water.
Present invention also offers a kind of preparation method of radiation proof softener, comprise the following steps that:
(1) 15 parts of octamethylcy-clotetrasiloxane, 40 parts of deionized water are added inside four-hole boiling flask, 90 DEG C add in oil bath pan
Heat, nitrogen protection, the speed for being passed through nitrogen is 2L/min, keeps charging flatly, and insertion flatly is equipped with 6 parts of polyether-modified nano-silicons
The separatory funnel of alkane, rate of addition 2mL/min, agitator is inserted flatly, mixing speed is 2000 revs/min, the reaction time
For 3h;
(2) first by 4 parts of calgon, 8 parts of metallic fiber powder, 8 parts of nanometer ferrite powder, nano silicon 8
Part, 15 parts of ethanol, with ultrasonic disperse 15 minutes, ultrasonic power 2000W, obtain homogeneous solution;
(3) homogeneous solution of step (2) is added in the solution of step (1), 900 revs/min, stirred 30 minutes;
(4) temperature is reduced to 65 DEG C, is added 13 parts of odium stearate, 4 parts of acrylamide, 800 revs/min, is stirred 25 minutes;
(5) 45 DEG C are cooled to, 8 parts of chitosan, 8 parts of sodium acid carbonate, 8 parts of plants essential oil is added, 900 revs/min, stirs 1
Hour;
(6) 25 DEG C are cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of radiation proof softener, according to parts by weight, including following components:The silica of prestox ring four
20 parts of alkane, 7 parts of polyether-modified nanometer silane, 10 parts of sodium acid carbonate, 10 parts of plants essential oil, 15 parts of odium stearate, acrylamide 5
Part, 5 parts of calgon, 10 parts of nano silicon, 20 parts of ethanol, 10 parts of chitosan, 10 parts of metallic fiber powder, Nanoscale Iron
10 parts of ferrite powder, 50 parts of deionized water.
Present invention also offers a kind of preparation method of radiation proof softener, comprise the following steps that:
(1) 20 parts of octamethylcy-clotetrasiloxane, 50 parts of deionized water are added inside four-hole boiling flask, in 100 DEG C of oil bath pan
Heating, nitrogen protection, the speed for being passed through nitrogen is 2L/min, keeps charging flatly, and insertion flatly is equipped with 7 parts of polyether-modified nanometers
The separatory funnel of silane, rate of addition 3mL/min, agitator is inserted flatly, mixing speed is 2000 revs/min, during reaction
Between be 4h;
(2) first by 5 parts of calgon, 10 parts of metallic fiber powder, 10 parts of nanometer ferrite powder, nano silicon
10 parts, 20 parts of ethanol, with ultrasonic disperse 20 minutes, ultrasonic power 2000W, obtain homogeneous solution;
(3) homogeneous solution of step (2) is added in the solution of step (1), 1000 revs/min, stirred 30 minutes;
(4) temperature is reduced to 70 DEG C, is added 15 parts of odium stearate, 5 parts of acrylamide, 1000 revs/min, is stirred 30 points
Clock;
(5) 50 DEG C are cooled to, 10 parts of chitosan, 10 parts of sodium acid carbonate, 10 parts of plants essential oil is added, 1000 revs/min, stirs
Mix 2 hours;
(6) 30 DEG C are cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of radiation proof softener, according to parts by weight, including following components:The silica of prestox ring four
20 parts of alkane, 7 parts of polyether-modified nanometer silane, 10 parts of sodium acid carbonate, 5 parts of plants essential oil, 10 parts of odium stearate, 3 parts of acrylamide,
5 parts of calgon, 5 parts of nano silicon, 10 parts of ethanol, 5 parts of chitosan, 5 parts of metallic fiber powder, nanometer ferrite powder
Last 10 parts, 30 parts of deionized water.
Present invention also offers a kind of preparation method of radiation proof softener, comprise the following steps that:
(1) 20 parts of octamethylcy-clotetrasiloxane, 30 parts of deionized water are added inside four-hole boiling flask, in 100 DEG C of oil bath pan
Heating, nitrogen protection, the speed for being passed through nitrogen is 2L/min, keeps charging flatly, and insertion flatly is equipped with 7 parts of polyether-modified nanometers
The separatory funnel of silane, rate of addition 3mL/min, agitator is inserted flatly, mixing speed is 2000 revs/min, the reaction time
For 4h;
(2) first by 5 parts of calgon, 5 parts of metallic fiber powder, 10 parts of nanometer ferrite powder, nano silicon 5
Part, 10 parts of ethanol, with ultrasonic disperse 10 minutes, ultrasonic power 2000W, obtain homogeneous solution;
(3) homogeneous solution of step (2) is added in the solution of step (1), 1000 revs/min, stirred 20 minutes;
(4) temperature is reduced to 70 DEG C, is added 10 parts of odium stearate, 3 parts of acrylamide, 500 revs/min, is stirred 30 minutes;
(5) 45 DEG C are cooled to, 5 parts of chitosan, 10 parts of sodium acid carbonate, 5 parts of plants essential oil is added, 900 revs/min, stirs 1
Hour;
(6) 20 DEG C are cooled to, closes down stirring, the liquid radiation proof softener prepared;
(7) stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.
Test case
The softener that embodiment 1,2,3,4 is respectively adopted in the fabric of four pieces of formed objects carries out submissive processing, test result
It is as follows:
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention includes appended claims and its equivalent limits.
Claims (9)
- A kind of 1. radiation proof softener, it is characterised in that:The radiation proof softener includes the raw material of following parts by weight:Eight first Basic ring tetrasiloxane 10-20 parts, polyether-modified nanometer silane 5-7 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, tristearin Sour sodium 10-15 parts, acrylamide 3-5 parts, calgon 3-5 parts, nano silicon 5-10 parts, ethanol 10-20 parts, shell gather Sugared 5-10 parts, metallic fiber powder 5-10 parts, nanometer ferrite powder 5-10 parts, deionized water 30-50 parts.
- 2. radiation proof softener according to claim 1, it is characterised in that:The ethanol is absolute ethyl alcohol, and purity is point Analyse pure.
- 3. radiation proof softener according to claim 1, it is characterised in that:The plants essential oil is Lavender, thin Lotus essential oil, lemon, jasmine essential oil, Rosa Damascana, yulan essential oil, cape jasmine flower essential oil, one kind in narcissus flower essential oil or Person more than one.
- 4. radiation proof softener according to claim 1, it is characterised in that:The metallic fiber powder, nanometer ferrite Powder, the particle diameter of nano silicon are 50-200nm.
- 5. radiation proof softener according to claim 1, it is characterised in that:The metallic fiber powder be silver plated fiber, Plate the one or more in aluminum fiber, Cu coated fibre, nickel plating fiber.
- 6. radiation proof softener according to claim 1, it is characterised in that:According to parts by weight, including following components:Eight 10 parts of methyl cyclotetrasiloxane, 5 parts of polyether-modified nanometer silane, 5 parts of sodium acid carbonate, 5 parts of plants essential oil, 10 parts of odium stearate, 3 parts of acrylamide, 3 parts of calgon, 5 parts of nano silicon, 10 parts of ethanol, 5 parts of chitosan, 5 parts of metallic fiber powder, 5 parts of nanometer ferrite powder, 30 parts of deionized water.
- 7. radiation proof softener according to claim 1, it is characterised in that:According to parts by weight, including following components:Eight 15 parts of methyl cyclotetrasiloxane, 6 parts of polyether-modified nanometer silane, 8 parts of sodium acid carbonate, 8 parts of plants essential oil, 13 parts of odium stearate, 4 parts of acrylamide, 4 parts of calgon, 8 parts of nano silicon, 15 parts of ethanol, 8 parts of chitosan, 8 parts of metallic fiber powder, 8 parts of nanometer ferrite powder, 40 parts of deionized water.
- 8. radiation proof softener according to claim 1, it is characterised in that:According to parts by weight, including following components:Eight 20 parts of methyl cyclotetrasiloxane, 7 parts of polyether-modified nanometer silane, 10 parts of sodium acid carbonate, 10 parts of plants essential oil, odium stearate 15 Part, 5 parts of acrylamide, 5 parts of calgon, 10 parts of nano silicon, 20 parts of ethanol, 10 parts of chitosan, metallic fiber powder 10 parts of end, 10 parts of nanometer ferrite powder, 50 parts of deionized water.
- A kind of 9. preparation method of any described radiation proof softener in 1-8 using the claims, it is characterised in that:Tool Body step is as follows:Step 1, octamethylcy-clotetrasiloxane 10-20 parts, deionized water 30-50 parts are added inside four-hole boiling flask, in oil bath pan 80-100 DEG C of heating, nitrogen protection, the speed for being passed through nitrogen is 1-2L/min, keeps charging flatly, and insertion flatly is equipped with 5-7 parts The separatory funnel of polyether-modified nanometer silane, rate of addition 2-3mL/min, agitator, mixing speed 1000- is inserted flatly 2000 revs/min, reaction time 3-4h;Step 2, first by calgon 3-5 parts, metallic fiber powder 5-10 parts, nanometer ferrite powder 5-10 parts, nanometer two Silica 5-10 parts, ethanol 10-20 parts, with ultrasonic disperse 10-20 minutes, ultrasonic power 1000-2000W, obtain uniformly molten Liquid;Step 3, the homogeneous solution of step 2 is added in the solution of step 1,500-1000 revs/min, stirs 20-30 minutes;Step 4, temperature is reduced to 60-70 DEG C, addition odium stearate 10-15 parts, acrylamide 3-5 parts, 500-1000 revs/min Clock, stir 20-30 minutes;Step 5,40-50 DEG C is cooled to, adds chitosan 5-10 parts, sodium acid carbonate 5-10 parts, plants essential oil 5-10 parts, 500- 1000 revs/min, stir 1-2 hours;Step 6,20-30 DEG C is cooled to, closes down stirring, the liquid radiation proof softener prepared;Step 7, stand and be cooled in four-hole boiling flask liquid radiation proof softener and be less than 20 DEG C, blowing encapsulation, finished product.