CN107724073A - A kind of fabric finishing agent and preparation method thereof - Google Patents

A kind of fabric finishing agent and preparation method thereof Download PDF

Info

Publication number
CN107724073A
CN107724073A CN201710896085.XA CN201710896085A CN107724073A CN 107724073 A CN107724073 A CN 107724073A CN 201710896085 A CN201710896085 A CN 201710896085A CN 107724073 A CN107724073 A CN 107724073A
Authority
CN
China
Prior art keywords
parts
finishing agent
fabric finishing
acid
diatomite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710896085.XA
Other languages
Chinese (zh)
Inventor
储平
徐有琦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu New Lucky Polytron Technologies Inc
Original Assignee
Jiangsu New Lucky Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu New Lucky Polytron Technologies Inc filed Critical Jiangsu New Lucky Polytron Technologies Inc
Priority to CN201710896085.XA priority Critical patent/CN107724073A/en
Publication of CN107724073A publication Critical patent/CN107724073A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of fabric finishing agent and preparation method thereof, the fabric finishing agent is made up of the raw material of following parts by weight：10 20 parts of butane tetracid, 35 parts of ammonium citrate, 35 parts of calgon, 57 parts of diatomite, 35 parts of aspartic acid, 35 parts of lignin sulfonic acid, 35 parts of malic acid, 57 parts of plant essence, 5 10 parts of hydroxymethyl cellulose, 10 15 parts of amido silicon oil, 20 30 parts of deionized water.After fabric finishing agent application the fabric of the present invention, fabric has good formative memory and washing fastness, and no free formaldehyde, crease and shrink resistance, outward appearance is well-pressed, good hand feeling softness, washable, wearability is good, not yellowing under high temperature, without colour-change phenomena.The fabric finishing agent manufacturing process of the present invention is simple to operation, and low in raw material price easily obtains, and toxicity is low, human body is not stimulated, volatility is low.

Description

A kind of fabric finishing agent and preparation method thereof
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relates to a kind of fabric finishing agent and preparation method thereof.
Background technology
Hi-tech development makes rapid progress, and people's living standard improves constantly, and is no longer limited to for the demand of textile The intrinsic characteristic of the fabrics such as cold-proof comfort, according to different industries, crowd, purposes, requirement of the people to textile is also increasingly It is more, clothes are proposed with the requirement such as comfortable, hygienic, attractive in appearance, health care, protection, the finishing technique of textile also continues to bring out.
Natural cotton has excellent performance, is preferable dress materials, but bafta needs to press after washing Scald, this just brings very big trouble to user.Although the protein fibres such as wool fibre, cocoon fiber in natural fiber are than fine Cellulose fiber is better, but wet elasticity and wrinkle resistance are all not as good as synthetic fibers.Therefore, it is required for pressing after this kind of clothes washing Scald.
In recent years, wash and wear finisher was popular, but traditional N- methylol amide class ironing and anti-crease finishing agents, crease-resistant Work well, but the fabric after it is handled can discharge harmful formaldehyde during processing, storage kimonos are used.
The content of the invention
It is an object of the invention to provide a kind of fabric finishing agent and preparation method thereof, to solve to carry in above-mentioned background technology The problem of going out.
To achieve the above object, the present invention provides following technical scheme：
A kind of fabric finishing agent, according to parts by weight, including following components：Butane tetracid 10-20 parts, ammonium citrate 3-5 Part, calgon 3-5 parts, diatomite 5-7 parts, aspartic acid 3-5 parts, lignin sulfonic acid 3-5 parts, malic acid 3-5 parts, plant Essence 5-7 parts, hydroxymethyl cellulose 5-10 parts, amido silicon oil 10-15 parts, deionized water 20-30 parts.
Preferably, described fabric finishing agent, according to parts by weight, including following components：10 parts of butane tetracid, citric acid 3 parts of ammonium, 3 parts of calgon, 5 parts of diatomite, 3 parts of aspartic acid, 3 parts of lignin sulfonic acid, 3 parts of malic acid, plant essence 5 Part, 5 parts of hydroxymethyl cellulose, 10 parts of amido silicon oil, 20 parts of deionized water.
Preferably, described fabric finishing agent, according to parts by weight, including following components：15 parts of butane tetracid, citric acid 4 parts of ammonium, 4 parts of calgon, 6 parts of diatomite, 4 parts of aspartic acid, 4 parts of lignin sulfonic acid, 4 parts of malic acid, plant essence 6 Part, 8 parts of hydroxymethyl cellulose, 13 parts of amido silicon oil, 25 parts of deionized water.
Preferably, described fabric finishing agent, according to parts by weight, including following components：20 parts of butane tetracid, citric acid 5 parts of ammonium, 5 parts of calgon, 7 parts of diatomite, 5 parts of aspartic acid, 5 parts of lignin sulfonic acid, 5 parts of malic acid, plant essence 7 Part, 10 parts of hydroxymethyl cellulose, 15 parts of amido silicon oil, 30 parts of deionized water.
A kind of preparation method of fabric finishing agent, is comprised the following steps that：
(1) butane tetracid 10-20 parts, ammonium citrate 3-5 parts, amido silicon oil 10-15 parts, deionization are added in a kettle Water 20-30 parts, 500-1000 revs/min, stir 20-30 minutes；
(2) addition calgon 3-5 parts, diatomite 5-7 parts, hydroxymethyl cellulose 5-10 parts, 500-1000 revs/min Clock, stir 20-30 minutes；
(3) aspartic acid 3-5 parts, lignin sulfonic acid 3-5 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(4) malic acid 3-5 parts, plant essence 5-7 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, after fabric finishing agent application fabric of the invention, fabric has good formative memory and washing fastness, nothing Free formaldehyde, crease and shrink resistance, outward appearance is well-pressed, and good hand feeling is soft, washable, wearability is good, not yellowing under high temperature, shows without discoloration As.
2nd, fabric finishing agent manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and toxicity is low, right Human body does not stimulate, and volatility is low.
3rd, mutual compatibility between various raw materials used in fabric finishing agent of the invention, synergy, it is excellent to collectively constitute performance Different product.
4th, technique is simplified, safe operation is simple, is easy to industrialized production.
5th, fabric finishing agent construction is simple of the invention, can by impregnating, spraying, roller coat etc. applied, production effect Rate improves.
6th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of fabric finishing agent, according to parts by weight, including following components：Butane tetracid 10-20 parts, Ammonium citrate 3-5 parts, calgon 3-5 parts, diatomite 5-7 parts, aspartic acid 3-5 parts, lignin sulfonic acid 3-5 parts, apple Sour 3-5 parts, plant essence 5-7 parts, hydroxymethyl cellulose 5-10 parts, amido silicon oil 10-15 parts, deionized water 20-30 parts.
Present invention also offers a kind of preparation method of fabric finishing agent, comprise the following steps that：
(1) butane tetracid 10-20 parts, ammonium citrate 3-5 parts, amido silicon oil 10-15 parts, deionization are added in a kettle Water 20-30 parts, 500-1000 revs/min, stir 20-30 minutes；
(2) addition calgon 3-5 parts, diatomite 5-7 parts, hydroxymethyl cellulose 5-10 parts, 500-1000 revs/min Clock, stir 20-30 minutes；
(3) aspartic acid 3-5 parts, lignin sulfonic acid 3-5 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(4) malic acid 3-5 parts, plant essence 5-7 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of fabric finishing agent, according to parts by weight, including following components：10 parts of butane tetracid, lemon 3 parts of lemon acid ammonium, 3 parts of calgon, 5 parts of diatomite, 3 parts of aspartic acid, 3 parts of lignin sulfonic acid, 3 parts of malic acid, plant are fragrant 5 parts of essence, 5 parts of hydroxymethyl cellulose, 10 parts of amido silicon oil, 20 parts of deionized water.
Present invention also offers a kind of preparation method of fabric finishing agent, comprise the following steps that：
(1) 10 parts of butane tetracid, 3 parts of ammonium citrate, 10 parts of amido silicon oil, 20 parts of deionized water are added in a kettle, 900 revs/min, stir 20 minutes；
(2) 3 parts of calgon, 5 parts of diatomite, 5 parts of hydroxymethyl cellulose are added, 500 revs/min, is stirred 30 minutes；
(3) 3 parts of aspartic acid, 3 parts of lignin sulfonic acid are added, 500 revs/min, is stirred 20 minutes；
(4) 3 parts of malic acid, 5 parts of plant essence are added, 500 revs/min, is stirred 20 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of fabric finishing agent, according to parts by weight, including following components：15 parts of butane tetracid, lemon 4 parts of lemon acid ammonium, 4 parts of calgon, 6 parts of diatomite, 4 parts of aspartic acid, 4 parts of lignin sulfonic acid, 4 parts of malic acid, plant are fragrant 6 parts of essence, 8 parts of hydroxymethyl cellulose, 13 parts of amido silicon oil, 25 parts of deionized water.
Present invention also offers a kind of preparation method of fabric finishing agent, comprise the following steps that：
(1) 15 parts of butane tetracid, 4 parts of ammonium citrate, 13 parts of amido silicon oil, 25 parts of deionized water are added in a kettle, 800 revs/min, stir 25 minutes；
(2) 4 parts of calgon, 6 parts of diatomite, 8 parts of hydroxymethyl cellulose are added, 800 revs/min, is stirred 25 minutes；
(3) 4 parts of aspartic acid, 4 parts of lignin sulfonic acid are added, 800 revs/min, is stirred 25 minutes；
(4) 4 parts of malic acid, 6 parts of plant essence are added, 800 revs/min, is stirred 25 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of fabric finishing agent, according to parts by weight, including following components：20 parts of butane tetracid, lemon 5 parts of lemon acid ammonium, 5 parts of calgon, 7 parts of diatomite, 5 parts of aspartic acid, 5 parts of lignin sulfonic acid, 5 parts of malic acid, plant are fragrant 7 parts of essence, 10 parts of hydroxymethyl cellulose, 15 parts of amido silicon oil, 30 parts of deionized water.
Present invention also offers a kind of preparation method of fabric finishing agent, comprise the following steps that：
(1) 20 parts of butane tetracid, 5 parts of ammonium citrate, 15 parts of amido silicon oil, 30 parts of deionized water are added in a kettle, 1000 revs/min, stir 30 minutes；
(2) 5 parts of calgon, 7 parts of diatomite, 10 parts of hydroxymethyl cellulose are added, 1000 revs/min, stirs 30 points Clock；
(3) 5 parts of aspartic acid, 5 parts of lignin sulfonic acid are added, 1000 revs/min, is stirred 30 minutes；
(4) 5 parts of malic acid, 7 parts of plant essence are added, 1000 revs/min, is stirred 30 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of fabric finishing agent, according to parts by weight, including following components：20 parts of butane tetracid, lemon 5 parts of lemon acid ammonium, 5 parts of calgon, 5 parts of diatomite, 3 parts of aspartic acid, 3 parts of lignin sulfonic acid, 3 parts of malic acid, plant are fragrant 7 parts of essence, 10 parts of hydroxymethyl cellulose, 15 parts of amido silicon oil, 20 parts of deionized water.
Present invention also offers a kind of preparation method of fabric finishing agent, comprise the following steps that：
(1) 20 parts of butane tetracid, 5 parts of ammonium citrate, 15 parts of amido silicon oil, 20 parts of deionized water are added in a kettle, 1000 revs/min, stir 20 minutes；
(2) 5 parts of calgon, 5 parts of diatomite, 10 parts of hydroxymethyl cellulose are added, 1000 revs/min, stirs 20 points Clock；
(3) 3 parts of aspartic acid, 3 parts of lignin sulfonic acid are added, 700 revs/min, is stirred 20 minutes；
(4) 3 parts of malic acid, 7 parts of plant essence are added, 800 revs/min, is stirred 25 minutes；
(5) stirring is closed down, the liquid fabric finishing agent prepared；
(6) stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
Test case
4 pieces of identical fabrics are put into the textile finishing agent solution of embodiment 1,2,3,4 and padded, are rolled by two leachings two, 80-100 DEG C of prebake is then heated to, then is dried at 120-140 DEG C, is then cleaned with 40-50 DEG C of hot water, is finally rushed with cold water Wash, dried after cleaning, 4 pieces of cloth with shrinkproof ironing-free performance can be obtained.Test result is as follows：
Embodiment Creasy recovery angle (°)
1 245
2 254
3 268
4 263
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding And modification, the scope of the present invention is defined by the appended.

Claims (5)

  1. A kind of 1. fabric finishing agent, it is characterised in that：The fabric finishing agent includes the raw material of following parts by weight：Butane tetracid 10-20 parts, ammonium citrate 3-5 parts, calgon 3-5 parts, diatomite 5-7 parts, aspartic acid 3-5 parts, lignin sulfonic acid 3-5 Part, malic acid 3-5 parts, plant essence 5-7 parts, hydroxymethyl cellulose 5-10 parts, amido silicon oil 10-15 parts, deionized water 20-30 Part.
  2. 2. fabric finishing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：Butane 10 parts of tetracid, 3 parts of ammonium citrate, 3 parts of calgon, 5 parts of diatomite, 3 parts of aspartic acid, 3 parts of lignin sulfonic acid, malic acid 3 parts, 5 parts of plant essence, 5 parts of hydroxymethyl cellulose, 10 parts of amido silicon oil, 20 parts of deionized water.
  3. 3. fabric finishing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：Butane 15 parts of tetracid, 4 parts of ammonium citrate, 4 parts of calgon, 6 parts of diatomite, 4 parts of aspartic acid, 4 parts of lignin sulfonic acid, malic acid 4 parts, 6 parts of plant essence, 8 parts of hydroxymethyl cellulose, 13 parts of amido silicon oil, 25 parts of deionized water.
  4. 4. fabric finishing agent according to claim 1, it is characterised in that：According to parts by weight, including following components：Butane 20 parts of tetracid, 5 parts of ammonium citrate, 5 parts of calgon, 7 parts of diatomite, 5 parts of aspartic acid, 5 parts of lignin sulfonic acid, malic acid 5 parts, 7 parts of plant essence, 10 parts of hydroxymethyl cellulose, 15 parts of amido silicon oil, 30 parts of deionized water.
  5. A kind of 5. preparation method using any described fabric finishing agents of claim 1-4, it is characterised in that：Specific steps are such as Under：
    Step 1, butane tetracid 10-20 parts, ammonium citrate 3-5 parts, amido silicon oil 10-15 parts, deionization are added in a kettle Water 20-30 parts, 500-1000 revs/min, stir 20-30 minutes；
    Step 2, addition calgon 3-5 parts, diatomite 5-7 parts, hydroxymethyl cellulose 5-10 parts, 500-1000 revs/min, Stir 20-30 minutes；
    Step 3, aspartic acid 3-5 parts, lignin sulfonic acid 3-5 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
    Step 4, malic acid 3-5 parts, plant essence 5-7 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
    Step 5, stirring is closed down, the liquid fabric finishing agent prepared；
    Step 6, stand and be cooled in stirred tank liquid fabric finishing agent and be less than 20 DEG C, blowing encapsulation, finished product.
CN201710896085.XA 2017-09-28 2017-09-28 A kind of fabric finishing agent and preparation method thereof Pending CN107724073A (en)