CN107780200A - A kind of wash and wear finisher and preparation method thereof - Google Patents
A kind of wash and wear finisher and preparation method thereof Download PDFInfo
- Publication number
- CN107780200A CN107780200A CN201710897076.2A CN201710897076A CN107780200A CN 107780200 A CN107780200 A CN 107780200A CN 201710897076 A CN201710897076 A CN 201710897076A CN 107780200 A CN107780200 A CN 107780200A
- Authority
- CN
- China
- Prior art keywords
- parts
- wash
- wear finisher
- ethanol
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wash and wear finisher and preparation method thereof, the wash and wear finisher is made up of the raw material of following parts by weight：35 parts of magnesium chloride, 35 parts of citric acid, 5 10 parts of sodium acid carbonate, 35 parts of borax, 35 parts of triethanolamine, 5 10 parts of hydroxymethyl cellulose, 5 10 parts of double amido organosilicon emulsions, 35 parts of AEO, 10 15 parts of ethanol, 37 parts of cactus powder, 10 20 parts of deionized water.After the wash and wear finisher application fabric of the present invention, fabric has excellent crease and shrink resistance performance, and outward appearance is well-pressed, is not required to press again after washing, line ball is kept for a long time；It is non-ignitable not quick-fried without free formaldehyde.The wash and wear finisher manufacturing process of the present invention is simple to operation, and low in raw material price is easily obtained, and nontoxic, and human body is not stimulated, and volatility is low, and the fabric after arrangement its toughness, intensity, feel are substantially unaffected.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, specifically relates to a kind of wash and wear finisher and preparation method thereof.
Background technology
Hi-tech development makes rapid progress, and people's living standard improves constantly, and is no longer limited to for the demand of textile
The intrinsic characteristic of the fabrics such as cold-proof comfort, according to different industries, crowd, purposes, requirement of the people to textile is also increasingly
It is more, clothes are proposed with the requirement such as comfortable, hygienic, attractive in appearance, health care, protection, the finishing technique of textile also continues to bring out.
Natural cotton has excellent performance, is preferable dress materials, but bafta needs to press after washing
Scald, this just brings very big trouble to user.Although the protein fibres such as wool fibre, cocoon fiber in natural fiber are than fine
Cellulose fiber is better, but wet elasticity and wrinkle resistance are all not as good as synthetic fibers.Therefore, it is required for pressing after this kind of clothes washing
Scald.
In recent years, wash and wear finisher was popular, but traditional N- methylol amide class wash and wear finishers, effect are good
It is good, but the fabric after it is handled can discharge harmful formaldehyde during processing, storage kimonos are used.
The content of the invention
It is an object of the invention to provide a kind of wash and wear finisher and preparation method, to solve to propose in above-mentioned background technology
The problem of.
To achieve the above object, the present invention provides following technical scheme：
A kind of wash and wear finisher, according to parts by weight, including following components：Magnesium chloride 3-5 parts, citric acid 3-5 parts, carbonic acid
Hydrogen sodium 5-10 parts, borax 3-5 parts, triethanolamine 3-5 parts, hydroxymethyl cellulose 5-10 parts, double amido organosilicon emulsion 5-10 parts,
AEO 3-5 parts, ethanol 10-15 parts, cactus powder 3-7 parts, deionized water 10-20 parts.
Preferably, the ethanol is absolute ethyl alcohol, and purity is pure to analyze.
Preferably, the cactus powder diameter is 1-200nm.
Preferably, the cactus powder is that grinding screening obtains after cactus high temperature is dried.
Preferably, described wash and wear finisher, according to parts by weight, including following components：3 parts of magnesium chloride, citric acid 3
Part, 5 parts of sodium acid carbonate, 3 parts of borax, 3 parts of triethanolamine, 5 parts of hydroxymethyl cellulose, 5 parts of double amido organosilicon emulsions, fatty alcohol
3 parts of APEO, 10 parts of ethanol, 3 parts of cactus powder, 10 parts of deionized water.
Preferably, described wash and wear finisher, according to parts by weight, including following components：4 parts of magnesium chloride, citric acid 4
Part, 8 parts of sodium acid carbonate, 4 parts of borax, 4 parts of triethanolamine, 8 parts of hydroxymethyl cellulose, 8 parts of double amido organosilicon emulsions, fatty alcohol
4 parts of APEO, 13 parts of ethanol, 5 parts of cactus powder, 15 parts of deionized water.
Preferably, described wash and wear finisher, according to parts by weight, including following components：5 parts of magnesium chloride, citric acid 5
Part, 10 parts of sodium acid carbonate, 5 parts of borax, 5 parts of triethanolamine, 10 parts of hydroxymethyl cellulose, 10 parts of double amido organosilicon emulsions, fat
5 parts of fat alcohol APEO, 15 parts of ethanol, 7 parts of cactus powder, 20 parts of deionized water.
A kind of preparation method of wash and wear finisher, is comprised the following steps that：
(1) citric acid 3-5 parts, hydroxymethyl cellulose 5-10 parts, double amido organosilicon emulsion 5-10 are added in a kettle
Part, AEO 3-5 parts, rise temperature stir 20-30 minutes to 60-70 DEG C, 500-1000 revs/min；
(2) it is by borax 3-5 parts, triethanolamine 3-5 parts, ethanol 10-15 part ultrasonic disperses, ultrasonic disperse power first
500-1000W, jitter time are 10-20 minutes；
(3) solution of step (2) is added in the solution of step (1), 500-1000 revs/min, stirs 20-30 minutes；
(4) temperature is reduced to 30-40 DEG C, addition magnesium chloride 3-5 parts, sodium acid carbonate 5-10 parts, 500-1000 revs/min,
Stir 10-20 minutes；
(5) cactus powder 3-7 parts, deionized water 10-20 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, after wash and wear finisher application fabric of the invention, fabric has excellent crease and shrink resistance performance, and outward appearance is well-pressed,
It is not required to press again after washing, line ball is kept for a long time；It is non-ignitable not quick-fried without free formaldehyde.
2nd, wash and wear finisher manufacturing process of the invention is simple to operation, and low in raw material price easily obtains, and nontoxic,
Human body is not stimulated, volatility is low, and the fabric after arrangement its toughness, intensity, feel are substantially unaffected.
3rd, mutual compatibility between various raw materials used in wash and wear finisher of the invention, synergy, it is excellent to collectively constitute performance
Different product.
4th, technique is simplified, safe operation is simple, is easy to industrialized production.
5th, wash and wear finisher construction is simple of the invention, can by impregnating, spraying, roller coat etc. applied, production effect
Rate improves.
6th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of wash and wear finisher, according to parts by weight, including following components：Magnesium chloride 3-5 parts, lemon
Sour 3-5 parts, sodium acid carbonate 5-10 parts, borax 3-5 parts, triethanolamine 3-5 parts, hydroxymethyl cellulose 5-10 parts, double amino are organic
Silicon emulsion 5-10 parts, AEO 3-5 parts, ethanol 10-15 parts, cactus powder 3-7 parts, deionized water 10-20
Part.
Present invention also offers a kind of preparation method of wash and wear finisher, comprise the following steps that：
(1) citric acid 3-5 parts, hydroxymethyl cellulose 5-10 parts, double amido organosilicon emulsion 5-10 are added in a kettle
Part, AEO 3-5 parts, rise temperature stir 20-30 minutes to 60-70 DEG C, 500-1000 revs/min；
(2) it is by borax 3-5 parts, triethanolamine 3-5 parts, ethanol 10-15 part ultrasonic disperses, ultrasonic disperse power first
500-1000W, jitter time are 10-20 minutes；
(3) solution of step (2) is added in the solution of step (1), 500-1000 revs/min, stirs 20-30 minutes；
(4) temperature is reduced to 30-40 DEG C, addition magnesium chloride 3-5 parts, sodium acid carbonate 5-10 parts, 500-1000 revs/min,
Stir 10-20 minutes；
(5) cactus powder 3-7 parts, deionized water 10-20 parts are added, 500-1000 revs/min, stirs 20-30 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 1
The invention discloses a kind of wash and wear finisher, according to parts by weight, including following components：3 parts of magnesium chloride, citric acid
3 parts, 5 parts of sodium acid carbonate, 3 parts of borax, 3 parts of triethanolamine, 5 parts of hydroxymethyl cellulose, 5 parts of double amido organosilicon emulsions, fat
3 parts of alcohol APEO, 10 parts of ethanol, 3 parts of cactus powder, 10 parts of deionized water.
Present invention also offers a kind of preparation method of wash and wear finisher, comprise the following steps that：
(1) 3 parts of citric acid, 5 parts of hydroxymethyl cellulose, 5 parts of double amido organosilicon emulsions, fatty alcohol are added in a kettle
3 parts of APEO, rise temperature stir 20 minutes to 60 DEG C, 500 revs/min；
(2) by 3 parts of borax, 3 parts of triethanolamine, 10 parts of ethanol with ultrasonic disperse, ultrasonic disperse power it is first 500W, disperses
Time is 10 minutes；
(3) solution of step (2) is added in the solution of step (1), 500 revs/min, is stirred 20 minutes；
(4) temperature is reduced to 30 DEG C, is added 3 parts of magnesium chloride, 5 parts of sodium acid carbonate, 500 revs/min, is stirred 10 minutes；
(5) 3 parts of cactus powder, 10 parts of deionized water are added, 500 revs/min, is stirred 20 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 2
The invention discloses a kind of wash and wear finisher, according to parts by weight, including following components：4 parts of magnesium chloride, citric acid
4 parts, 8 parts of sodium acid carbonate, 4 parts of borax, 4 parts of triethanolamine, 8 parts of hydroxymethyl cellulose, 8 parts of double amido organosilicon emulsions, fat
4 parts of alcohol APEO, 13 parts of ethanol, 5 parts of cactus powder, 15 parts of deionized water.
Present invention also offers a kind of preparation method of wash and wear finisher, comprise the following steps that：
(1) 4 parts of citric acid, 8 parts of hydroxymethyl cellulose, 8 parts of double amido organosilicon emulsions, fatty alcohol are added in a kettle
4 parts of APEO, rise temperature stir 25 minutes to 65 DEG C, 800 revs/min；
(2) by 4 parts of borax, 4 parts of triethanolamine, 13 parts of ethanol with ultrasonic disperse, ultrasonic disperse power it is first 800W, disperses
Time is 15 minutes；
(3) solution of step (2) is added in the solution of step (1), 800 revs/min, is stirred 25 minutes；
(4) temperature is reduced to 35 DEG C, is added 4 parts of magnesium chloride, 8 parts of sodium acid carbonate, 800 revs/min, is stirred 15 minutes；
(5) 5 parts of cactus powder, 15 parts of deionized water are added, 800 revs/min, is stirred 25 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 3
The invention discloses a kind of wash and wear finisher, according to parts by weight, including following components：5 parts of magnesium chloride, citric acid
5 parts, 10 parts of sodium acid carbonate, 5 parts of borax, 5 parts of triethanolamine, 10 parts of hydroxymethyl cellulose, 10 parts of double amido organosilicon emulsions, fat
5 parts of fat alcohol APEO, 15 parts of ethanol, 7 parts of cactus powder, 20 parts of deionized water.
Present invention also offers a kind of preparation method of wash and wear finisher, comprise the following steps that：
(1) 5 parts of citric acid, 10 parts of hydroxymethyl cellulose, 10 parts of double amido organosilicon emulsions, fat are added in a kettle
5 parts of alcohol APEO, rise temperature stir 30 minutes to 70 DEG C, 1000 revs/min；
(2) by 5 parts of borax, 5 parts of triethanolamine, 15 parts of ethanol with ultrasonic disperse, ultrasonic disperse power it is first 1000W, point
It is 20 minutes to dissipate the time；
(3) solution of step (2) is added in the solution of step (1), 1000 revs/min, is stirred 30 minutes；
(4) temperature is reduced to 40 DEG C, is added 5 parts of magnesium chloride, 10 parts of sodium acid carbonate, 1000 revs/min, is stirred 20 minutes；
(5) 7 parts of cactus powder, 20 parts of deionized water are added, 1000 revs/min, is stirred 30 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Embodiment 4
The invention discloses a kind of wash and wear finisher, according to parts by weight, including following components：3 parts of magnesium chloride, citric acid
3 parts, 5 parts of sodium acid carbonate, 5 parts of borax, 3 parts of triethanolamine, 10 parts of hydroxymethyl cellulose, 10 parts of double amido organosilicon emulsions, fat
3 parts of fat alcohol APEO, 10 parts of ethanol, 7 parts of cactus powder, 20 parts of deionized water.
Present invention also offers a kind of preparation method of wash and wear finisher, comprise the following steps that：
(1) 3 parts of citric acid, 10 parts of hydroxymethyl cellulose, 10 parts of double amido organosilicon emulsions, fat are added in a kettle
3 parts of alcohol APEO, rise temperature stir 20 minutes to 70 DEG C, 1000 revs/min；
(2) by 5 parts of borax, 3 parts of triethanolamine, 10 parts of ethanol with ultrasonic disperse, ultrasonic disperse power it is first 900W, disperses
Time is 14 minutes；
(3) solution of step (2) is added in the solution of step (1), 900 revs/min, is stirred 30 minutes；
(4) temperature is reduced to 35 DEG C, is added 5 parts of magnesium chloride, 5 parts of sodium acid carbonate, 1000 revs/min, is stirred 10 minutes；
(5) 7 parts of cactus powder, 20 parts of deionized water are added, 900 revs/min, is stirred 30 minutes；
(6) stirring is closed down, the liquid wash and wear finisher prepared；
(7) stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.
Test case
4 pieces of identical fabrics are put into the noniron finish agent solution of embodiment 1,2,3,4 and padded, are rolled by two leachings two,
80-100 DEG C of prebake is then heated to, then is dried at 120-140 DEG C, is then cleaned with 40-50 DEG C of hot water, is finally rushed with cold water
Wash, dried after cleaning, 4 pieces of cloth with ironing-free performance can be obtained.Test result is as follows：
| Embodiment | Creasy recovery angle (°) |
| 1 | 252 |
| 2 | 265 |
| 3 | 278 |
| 4 | 269 |
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
- A kind of 1. wash and wear finisher, it is characterised in that：The wash and wear finisher includes the raw material of following parts by weight：Magnesium chloride 3- 5 parts, it is citric acid 3-5 parts, sodium acid carbonate 5-10 parts, borax 3-5 parts, triethanolamine 3-5 parts, hydroxymethyl cellulose 5-10 parts, double Amido organosilicon emulsion 5-10 parts, AEO 3-5 parts, ethanol 10-15 parts, cactus powder 3-7 parts, deionization Water 10-20 parts.
- 2. wash and wear finisher according to claim 1, it is characterised in that：The ethanol is absolute ethyl alcohol, and purity is analysis It is pure.
- 3. wash and wear finisher according to claim 1, it is characterised in that：The cactus powder is dried for cactus high temperature Grinding screening afterwards obtains.
- 4. wash and wear finisher according to claim 1, it is characterised in that：The cactus powder diameter is 1-200nm.
- 5. wash and wear finisher according to claim 1, it is characterised in that：According to parts by weight, including following components：Chlorination 3 parts of magnesium, 3 parts of citric acid, 5 parts of sodium acid carbonate, 3 parts of borax, 3 parts of triethanolamine, 5 parts of hydroxymethyl cellulose, double amido organosilicons 5 parts of emulsion, 3 parts of AEO, 10 parts of ethanol, 3 parts of cactus powder, 10 parts of deionized water.
- 6. wash and wear finisher according to claim 1, it is characterised in that：According to parts by weight, including following components：Chlorination 4 parts of magnesium, 4 parts of citric acid, 8 parts of sodium acid carbonate, 4 parts of borax, 4 parts of triethanolamine, 8 parts of hydroxymethyl cellulose, double amido organosilicons 8 parts of emulsion, 4 parts of AEO, 13 parts of ethanol, 5 parts of cactus powder, 15 parts of deionized water.
- 7. wash and wear finisher according to claim 1, it is characterised in that：According to parts by weight, including following components：Chlorination 5 parts of magnesium, 5 parts of citric acid, 10 parts of sodium acid carbonate, 5 parts of borax, 5 parts of triethanolamine, 10 parts of hydroxymethyl cellulose, double amino are organic 10 parts of silicon emulsion, 5 parts of AEO, 15 parts of ethanol, 7 parts of cactus powder, 20 parts of deionized water.
- A kind of 8. preparation method of any described wash and wear finisher in 1-7 using the claims, it is characterised in that：Specifically Step is as follows：Step 1, citric acid 3-5 parts, hydroxymethyl cellulose 5-10 parts, double amido organosilicon emulsion 5-10 are added in a kettle Part, AEO 3-5 parts, rise temperature stir 20-30 minutes to 60-70 DEG C, 500-1000 revs/min；Step 2, it is by borax 3-5 parts, triethanolamine 3-5 parts, ethanol 10-15 part ultrasonic disperses, ultrasonic disperse power first 500-1000W, jitter time are 10-20 minutes；Step 3, the solution of step 2 is added in the solution of step 1,500-1000 revs/min, stirs 20-30 minutes；Step 4, temperature is reduced to 30-40 DEG C, is added magnesium chloride 3-5 parts, sodium acid carbonate 5-10 parts, 500-1000 revs/min, is stirred Mix 10-20 minutes；Step 5, cactus powder 3-7 parts, deionized water 10-20 parts are added, 500-1000 revs/min, stirs 20-30 minutes；Step 6, stirring is closed down, the liquid wash and wear finisher prepared；Step 7, stand and be cooled in stirred tank liquid wash and wear finisher and be less than 20 DEG C, blowing encapsulation, finished product.