CN107721377A - One kind receives tea sand device and its method for cooking - Google Patents
One kind receives tea sand device and its method for cooking Download PDFInfo
- Publication number
- CN107721377A CN107721377A CN201711109441.5A CN201711109441A CN107721377A CN 107721377 A CN107721377 A CN 107721377A CN 201711109441 A CN201711109441 A CN 201711109441A CN 107721377 A CN107721377 A CN 107721377A
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- sand device
- tea
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to one kind to receive tea sand device, includes each component of following parts by weight：Blue or green 30 80 parts of earthenware, 3 10 parts of bentonite, 29 parts of 20 35 parts of sand cash, 7 20 parts of feldspar and quartz.The present invention also provides a kind of method for cooking for receiving tea sand device, comprises the following steps：Dispensing, grinding, mud processed, rubs mud, is molded, and dries, and fires.The core that the present invention receives tea sand device is from blue or green earthenware, bentonite, sand cash, feldspar and quartz are used as raw material, collocation uses dispensing, grinds, mud processed, rub mud, shaping, drying, the technological process of firing, and the rational proportion and firing temperature of preferred pair above-mentioned raw materials, produce the receipts tea sand device that heat transfer is uniform, good permeability and heat endurance are high.Because sand utensil has good gas permeability, brewing rear remaining tealeaves will not go bad for a long time, and keep the business composition of original tealeaves, after being collected to remaining tealeaves, can recycle again.
Description
Technical field
The invention belongs to sand device firing field, and in particular to one kind receives tea sand device and its method for cooking.
Background technology
The tealeaves brewed remaining useless tea after having tea not only can apply eyes with beauty, and disappear livid ring around eye；Can be with
Pillow, improving eyesight sleeping are done after airing；, can Reusability and surplus tealeaves can also dry and put deodorization in refrigerator；In addition, surplus tealeaves
After boiling water boils, immersion can effectively treat heel breach；The advantages of fertilizers for potted flowers etc. is many can be.At present to remaining tealeaves
Processing method be directly tip rubbish cylinder, directly fall toilet, it is both unhygienic or not environmentally, be also easy to block pipeline.
The content of the invention
In consideration of it, it is an object of the invention to provide one kind to receive tea sand device and its method for cooking, it is intended to overcomes after brewing
The defects of remaining tea leaves are directly as garbage disposal.
In order to reach foregoing invention purpose, the technical scheme that the present invention takes is as follows：
One kind receives tea sand device, includes each component of following parts by weight：
Blue or green earthenware 30-80 parts, bentonite 3-10 parts, sand cash 20-35 parts, feldspar 7-20 parts and quartzy 2-9 parts.
The present invention also provides a kind of method for cooking for receiving tea sand device, comprises the following steps：
S1：Dispensing；Choose blue or green earthenware 30-80 parts, bentonite 3-10 parts, sand cash 20-35 parts, feldspar 7-20 parts and quartzy 2-9
Part is stand-by；
S2：Grinding；Each raw material that step S1 is chosen insert in ball mill be ground it is standby to 200 targeted fine powders；
S3：Mud processed；The fine powder that step S2 is ground is 1 according to weight ratio with water:3-6 proportioning is placed in clear mud sump rotten
Change 2 months to half a year, dried in the shade after mud-water separation, obtain the base mud that water content is 50-70%；
S4：Rub mud；Base mud prepared by step S3 is kneaded to form walk repeatedly, it is desirable to the surface of walk and inner homogeneous and
Free from admixture and stomata；
S5：Shaping；By the walk that step S4 is formed, the base substrate for receiving tea sand device is made in throwing on mud platform；
S6：Drying；To the base substrate for receiving tea sand device made of step S5 be dried to its surface temperature as 50-70 DEG C；
S7：Fire；The step S6 base substrates prepared are positioned in kiln, 18- is fired at a temperature of 1250-1300 DEG C
25h, normal temperature, kiln discharge are naturally cooled to, polishing, which is formed, receives tea sand device.
Beneficial effects of the present invention：The present invention receive tea sand device core be from blue or green earthenware, bentonite, sand cash, feldspar and
Quartz is used as raw material, and collocation uses dispensing, grinds, mud processed, rubs mud, is molded, drying, the technological process of firing, and in preferred pair
The rational proportion and firing temperature of raw material are stated, produces the receipts tea sand device that heat transfer is uniform, good permeability and heat endurance are high.Due to
Sand utensil has good gas permeability, and brewing rear remaining tealeaves will not go bad for a long time, and keep the business of original tealeaves
Composition, after being collected to remaining tealeaves, it can again recycle, such as beauty, such as be used as pillow, be alternatively arranged as deodorant for refregerator
Use etc..
Embodiment
It should be noted that in the case where not conflicting, the feature in embodiment and embodiment in the application can phase
Mutually combination.The present invention is described in detail below in conjunction with embodiment.
Embodiment described in the invention is only the embodiment of the application part, rather than whole embodiments.Base
Embodiment in the application, those of ordinary skill in the art obtained under the premise of creative work is not made it is all its
His embodiment, it should all belong to the scope of the application protection.
Embodiment 1
One kind receives tea sand device, includes each component of following parts by weight：
Blue or green 30 parts of earthenware, 3 parts of bentonite, 2 parts of 20 parts of sand cash, 7 parts of feldspar and quartz.
The present invention also provides a kind of method for cooking for receiving tea sand device, comprises the following steps：
S1：Dispensing；Blue or green 30 parts of earthenware is chosen, 3 parts of bentonite, 2 parts of 20 parts of sand cash, 7 parts of feldspar and quartz are stand-by；
S2：Grinding；Each raw material that step S1 is chosen insert in ball mill be ground it is standby to 200 targeted fine powders；
S3：Mud processed；The fine powder that step S2 is ground is 1 according to weight ratio with water:3 proportioning, which is placed in clear mud sump, degenerates
2 months, dry in the shade after mud-water separation, obtain the base mud that water content is 50%；
S4：Rub mud；Base mud prepared by step S3 is kneaded to form walk repeatedly, it is desirable to the surface of walk and inner homogeneous and
Free from admixture and stomata；
S5：Shaping；By the walk that step S4 is formed, the base substrate for receiving tea sand device is made in throwing on mud platform；
S6：Drying；The base substrate that tea sand device is received made of step S5 is carried out being dried to 50 DEG C of its surface temperature；
S7：Fire；The step S6 base substrates prepared are positioned in kiln, 18h is fired at a temperature of 1250 DEG C, it is naturally cold
But to normal temperature, kiln discharge, polishing, which is formed, receives tea sand device.
Embodiment 2
One kind receives tea sand device, includes each component of following parts by weight：
Blue or green earthenware 30-80 parts, bentonite 3-10 parts, sand cash 20-35 parts, feldspar 7-20 parts and quartzy 2-9 parts.
The present invention also provides a kind of method for cooking for receiving tea sand device, comprises the following steps：
S1：Dispensing；Blue or green 50 parts of earthenware is chosen, 5 parts of bentonite, 5 parts of 30 parts of sand cash, 10 parts of feldspar and quartz are stand-by；
S2：Grinding；Each raw material that step S1 is chosen insert in ball mill be ground it is standby to 200 targeted fine powders；
S3：Mud processed；The fine powder that step S2 is ground is 1 according to weight ratio with water:4.5 proportioning is placed in clear mud sump rotten
Change 3 months, dried in the shade after mud-water separation, obtain the base mud that water content is 55%；
S4：Rub mud；Base mud prepared by step S3 is kneaded to form walk repeatedly, it is desirable to the surface of walk and inner homogeneous and
Free from admixture and stomata；
S5：Shaping；By the walk that step S4 is formed, the base substrate for receiving tea sand device is made in throwing on mud platform；
S6：Drying；The base substrate that tea sand device is received made of step S5 is carried out being dried to 62 DEG C of its surface temperature；
S7：Fire；The step S6 base substrates prepared are positioned in kiln, 21h is fired at a temperature of 1270 DEG C, it is naturally cold
But to normal temperature, kiln discharge, polishing, which is formed, receives tea sand device.
Embodiment 3
One kind receives tea sand device, includes each component of following parts by weight：
Blue or green 80 parts of earthenware, 10 parts of bentonite, 9 parts of 35 parts of sand cash, 20 parts of feldspar and quartz.
The present invention also provides a kind of method for cooking for receiving tea sand device, comprises the following steps：
S1：Dispensing；Blue or green 80 parts of earthenware is chosen, 10 parts of bentonite, 9 parts of 35 parts of sand cash, 20 parts of feldspar and quartz are stand-by；
S2：Grinding；Each raw material that step S1 is chosen insert in ball mill be ground it is standby to 200 targeted fine powders；
S3：Mud processed；The fine powder that step S2 is ground is 1 according to weight ratio with water:6 proportioning, which is placed in clear mud sump, degenerates
To half a year, dried in the shade after mud-water separation, obtain the base mud that water content is 70%；
S4：Rub mud；Base mud prepared by step S3 is kneaded to form walk repeatedly, it is desirable to the surface of walk and inner homogeneous and
Free from admixture and stomata；
S5：Shaping；By the walk that step S4 is formed, the base substrate for receiving tea sand device is made in throwing on mud platform；
S6：Drying；The base substrate that tea sand device is received made of step S5 is carried out being dried to 70 DEG C of its surface temperature；
S7：Fire；The step S6 base substrates prepared are positioned in kiln, 25h is fired at a temperature of 1300 DEG C, it is naturally cold
But to normal temperature, kiln discharge, polishing, which is formed, receives tea sand device.
The core that the present invention receives tea sand device is to be used as raw material from blue or green earthenware, bentonite, sand cash, feldspar and quartz, arranged in pairs or groups
Using dispensing, grinding, mud processed, rub mud, be molded, drying, the technological process of firing, and the rational proportion of preferred pair above-mentioned raw materials and
Firing temperature, produce the receipts tea sand device that heat transfer is uniform, good permeability and heat endurance are high.Because sand utensil has good breathe freely
Property, brewing rear remaining tealeaves will not go bad for a long time, and keep the business composition of original tealeaves, through to remaining tealeaves
It after collection, can again recycle, such as beauty, such as be used as pillow, be alternatively arranged as deodorant for refregerator and use etc..
Claims (2)
1. one kind receives tea sand device, it is characterised in that includes each component of following parts by weight：
Blue or green earthenware 30-80 parts, bentonite 3-10 parts, sand cash 20-35 parts, feldspar 7-20 parts and quartzy 2-9 parts.
2. a kind of method for cooking for receiving tea sand device, it is characterised in that comprise the following steps：
S1：Dispensing；Blue or green earthenware 30-80 parts, bentonite 3-10 parts are chosen, sand cash 20-35 parts, feldspar 7-20 parts and quartzy 2-9 parts are treated
With；
S2：Grinding；Each raw material that step S1 is chosen insert in ball mill be ground it is standby to 200 targeted fine powders；
S3：Mud processed；The fine powder that step S2 is ground is 1 according to weight ratio with water:3-6 proportioning, which is placed in clear mud sump, degenerates 2
To half a year, dried in the shade after mud-water separation within individual month, obtain the base mud that water content is 50-70%；
S4：Rub mud；Base mud prepared by step S3 is kneaded to form walk repeatedly, it is desirable to the surface of walk and inner homogeneous and without miscellaneous
Matter and stomata；
S5：Shaping；By the walk that step S4 is formed, the base substrate for receiving tea sand device is made in throwing on mud platform；
S6：Drying；To the base substrate for receiving tea sand device made of step S5 be dried to its surface temperature as 50-70 DEG C；
S7：Fire；The step S6 base substrates prepared are positioned in kiln, 18-25h is fired at a temperature of 1250-1300 DEG C, from
Normal temperature, kiln discharge are so cooled to, polishing, which is formed, receives tea sand device.