CN107718265A - A kind of sound-absorbing integrated board and preparation method thereof - Google Patents

A kind of sound-absorbing integrated board and preparation method thereof Download PDF

Info

Publication number
CN107718265A
CN107718265A CN201610653445.9A CN201610653445A CN107718265A CN 107718265 A CN107718265 A CN 107718265A CN 201610653445 A CN201610653445 A CN 201610653445A CN 107718265 A CN107718265 A CN 107718265A
Authority
CN
China
Prior art keywords
sound
integrated board
absorbing integrated
board
components
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610653445.9A
Other languages
Chinese (zh)
Inventor
蔡晓波
周风雷
葛高将
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong King's Energy Saving Building Material Difficult To Understand Development In Science And Technology Co Ltd
Original Assignee
Nantong King's Energy Saving Building Material Difficult To Understand Development In Science And Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong King's Energy Saving Building Material Difficult To Understand Development In Science And Technology Co Ltd filed Critical Nantong King's Energy Saving Building Material Difficult To Understand Development In Science And Technology Co Ltd
Priority to CN201610653445.9A priority Critical patent/CN107718265A/en
Publication of CN107718265A publication Critical patent/CN107718265A/en
Pending legal-status Critical Current

Abstract

The present invention discloses a kind of sound-absorbing integrated board and preparation method thereof, including wood wool board and other components, and other components account for the 20 30% of sound-absorbing integrated board total amount；It is made up of following raw material by weight percentage：Ceramsite sand 20% 30%, white cement 8% 12%, alumina cement 11% 17%, quartz sand 26% 32%, calcium carbonate 16% 28%, vinyl acetate ethylene copolymer latices powder 1.8% 3%, lignocellulosic 0.25% 0.29%, methyl cellulose ether 0.2% 0.25%, organosilicon hydrophobic powder 0.1% 0.15% and iron oxide series inorganic pigment 1% 5%, wood wool board 70% 80%.The sound-absorbing integrated board of the present invention has sound insulation, heat-insulated, noise reduction and fireproof function.

Description

A kind of sound-absorbing integrated board and preparation method thereof
Technical field
The present invention relates to a kind of sound-absorbing integrated board and preparation method thereof.
Background technology
The surface texture of wood-wool acoustic board shows graceful texture and sampled with unique, can fully the intention of deductive design teacher with Theory.The product combines the advantages of timber and cement：It is light such as timber, it is firm such as cement, have sound-absorbing, shock resistance, Moistureproof, mildew preventing functions, can be widely applied to stadiums, arenas, movie theatre, meeting room, church, factory, school, books Shop, natatorium etc..
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of sound-absorbing integrated board, has sound insulation, heat-insulated, noise reduction and fireproof Function.
In order to solve the above technical problems, the technical solution adopted by the present invention is：Sound-absorbing integrated board, including wood wool board and other Component, other components account for the 20-30% of sound-absorbing integrated board total amount；Described other components are by following original by weight percentage Material composition：Ceramsite sand 20%-30%, white cement 8%-12%, alumina cement 11%-17%, quartz sand 26%-32%, carbonic acid Calcium 16%-28%, vinyl acetate-ethylene copolymer latex powder 1.8%-3%, lignocellulosic 0.25%-0.29%, methyl are fine Tie up plain ether 0.2%-0.25%, organosilicon hydrophobic powder 0.1%-0.15% and iron oxide series inorganic pigment 1%-5%, wood wool board 70%-80%.
The present invention also provides a kind of preparation method of sound-absorbing integrated board, comprises the following steps：
(1) by ceramsite sand 20%-30%, white cement 8%-12%, alumina cement 11%-17%, quartz sand 26%- 32%, calcium carbonate 16%-28%, vinyl acetate-ethylene copolymer latex powder 1.8%-3%, lignocellulosic 0.25%- 0.29%, methyl cellulose ether 0.2%-0.25%, organosilicon hydrophobic powder 0.1%-0.15% and iron oxide series inorganic pigment 1%-5%, various raw material are sufficiently stirred；
(2) step (1) passes through bottoming with wood wool board, puts down and criticizes, roller coating process；
(3) step (2) is passed through to the drying of more than 20 hours；
The product that step (3) is obtained is using surface layer special-purpose protecting agent roller coating more than 2 times, and 24 is small after protective agent completion When more than can case.
Further, the temperature of step 3 is maintained between 15 ° -35 °.
Beneficial effects of the present invention：The sound-absorbing integrated board of the present invention has sound insulation, heat-insulated, noise reduction and fireproof function, makes Standby technique is simple.
Embodiment
Embodiment 1
Sound-absorbing integrated board, including wood wool board and other components, other components account for the 20% of sound-absorbing integrated board total amount；Other groups Divide and be made up of following raw material by weight percentage：Ceramsite sand 20%, white cement 10%, alumina cement 11%, quartz sand 30%, calcium carbonate 23.56%, vinyl acetate-ethylene copolymer latex powder 1.8%, lignocellulosic 0.29%, methylcellulose Ether 0.25%, organosilicon hydrophobic powder 0.1% and iron oxide series inorganic pigment 2%.
Embodiment 2
Sound-absorbing integrated board, including wood wool board and other components, other components account for the 25% of sound-absorbing integrated board total amount；Other groups Divide and be made up of following raw material by weight percentage：Ceramsite sand 30%, white cement 8%, alumina cement 11%, quartz sand 26%, calcium carbonate 18%, vinyl acetate-ethylene copolymer latex powder 3%, lignocellulosic 1.25%, methyl cellulose ether 0.25%, organosilicon hydrophobic powder 0.1% and iron oxide series inorganic pigment 2.4%.
Embodiment 3
(1) preparation method of sound-absorbing integrated board, by ceramsite sand 20%-35%, white cement 8%-12%, alumina cement 11%-17%, quartz sand 26%-32%, calcium carbonate 16%-28%, vinyl acetate-ethylene copolymer latex powder 1.8%-3%, Lignocellulosic 0.25%-0.29%, methyl cellulose ether 0.2%-0.25%, organosilicon hydrophobic powder 0.1%-0.15% and oxygen Change iron series inorganic pigment 1%-5%, various raw material are sufficiently stirred；
(2) step (1) passes through bottoming with wood wool board, puts down and criticizes, roller coating process；
(3) step (2) is passed through to the drying of more than 20 hours；
(4) product for obtaining step (3) is using surface layer special-purpose protecting agent roller coating more than 2 times, after protective agent completion It can case within more than 24 hours.
Step 1-3 temperature is held between 15 ° -35 °.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to the design of the present invention It is defined with scope, on the premise of design concept of the present invention is not departed from, ordinary skill technical staff is to this hair in this area The all variations and modifications that bright technical scheme is made all should fall into protection scope of the present invention, claimed skill of the invention Art content, all it is documented in technical requirements book.

Claims (3)

1. sound-absorbing integrated board, it is characterised in that：Including wood wool board and other components, other components account for sound-absorbing integrated board total amount 20-30%；Described other components are made up of following raw material by weight percentage：Ceramsite sand 20%-30%, white cement 8%-12%, alumina cement 11%-17%, quartz sand 26%-32%, calcium carbonate 16%-28%, vinyl acetate-ethylene copolymerization Thing latex powder 1.8%-3%, lignocellulosic 0.25%-0.29%, methyl cellulose ether 0.2%-0.25%, organosilicon hydrophobic Powder 0.1%-0.15% and iron oxide series inorganic pigment 1%-5%.
2. the preparation method of sound-absorbing integrated board, it is characterised in that：Comprise the following steps：
(1) by ceramsite sand 20%-30%, white cement 8%-12%, alumina cement 11%-17%, quartz sand 26%-32%, carbon Sour calcium 16%-28%, vinyl acetate-ethylene copolymer latex powder 1.8%-3%, lignocellulosic 0.25%-0.29%, methyl Cellulose ether 0.2%-0.25%, organosilicon hydrophobic powder 0.1%-0.15% and iron oxide series inorganic pigment 1%-5%, will be each Kind raw material are sufficiently stirred；
(2) step (1) passes through bottoming with wood wool board, puts down and criticizes, roller coating process；
(3) step (2) is passed through to the drying of more than 20 hours；
(4) product for obtaining step (3) is using surface layer special-purpose protecting agent roller coating more than 2 times, and 24 is small after protective agent completion When more than can case.
3. the preparation method of sound-absorbing integrated board according to claim 2, it is characterised in that：The temperature of the drying steps is protected Hold between 15 ° -35 °.
CN201610653445.9A 2016-08-11 2016-08-11 A kind of sound-absorbing integrated board and preparation method thereof Pending CN107718265A (en)