CN107718183A - Multiple-plate production method and product are spliced in regeneration - Google Patents
Multiple-plate production method and product are spliced in regeneration Download PDFInfo
- Publication number
- CN107718183A CN107718183A CN201710986661.XA CN201710986661A CN107718183A CN 107718183 A CN107718183 A CN 107718183A CN 201710986661 A CN201710986661 A CN 201710986661A CN 107718183 A CN107718183 A CN 107718183A
- Authority
- CN
- China
- Prior art keywords
- layer sheet
- thickness
- product
- template
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind regeneration to splice multiple-plate production method, it is characterised in that：Follow these steps to carry out,（a）The discarded construction multi-layer sheet of purchase, and go to follow closely, remove surface impurity；（b）With right angle bead cutter crop；（c）Multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；（d）The wide strip of different size will be sawed into piece by the sorted similar multi-layer sheet of thickness；（e）It is template that template will be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；（f）Using jigsaw hot press by multi-layer sheet strip bed board and hot forming；（g）Sand flat after cooling with sander, plain plate is obtained after sanding；（h）The difference of product thickness is required according to user, it is overlapping to be put into cold press cold moudling together after several plain plates are glued by automatic double-sided gluing machine；（i）Using four product is obtained in bead cutter cutting four.
Description
Technical field
The present invention relates to a kind of production method of sheet material and product, more particularly to a kind of regeneration to splice multiple-plate producer
Method and product.
Background technology
It is well known that at present China furniture, dress is drilled, decorated, timber industry uses raw material usually using solid wood board, refer to
Fishplate bar, glued board etc., and high-end sheet material such as solid wood board, splice plate, finger-jointed plate is sufficiently expensive, at present between solid wood and composite plate
Although high-quality glued board between material is pure wood products, because using conventional art, process and structure fabrication, product quality
The needs of people can not be met, and be present many discarded multi-layer sheet and be not recycled utilization in existing building woodworking, have
Direct burning, on the one hand cause air environmental pollution, on the other hand bring the significant wastage of timber resources again, now at present to useless
Abandon in the multi-layer sheet board material splice process of reproduction, due to early stage, the discarded multi-layer sheet sheet metal thickness difference of recovery is big, manual sort
Limitation, cause classifying quality bad, for each discarded raw sheet uneven thickness of splicing, cause raw material in process
A large amount of wastes, dust pollution it is also more serious, so the splice plate produced is of low quality, and because production technology is owed
It is good, cause that the human resources that production line is long, spends are big, cost is higher.
The content of the invention
It is an object of the invention to provided for overcome the deficiencies in the prior art one kind can be effectively reduced product into
Sheet, the multiple-plate production method of a kind of regeneration splicing for economizing on resources, improving product quality and efficiency.Its concrete technical scheme
For：Multiple-plate production method is spliced in one kind regeneration, follows these steps to carry out,
A, discarded construction multi-layer sheet is purchased, and goes to follow closely, remove surface impurity；
B, with right angle bead cutter crop；
C, multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；
D, the wide strip of different size will be sawed into piece by the sorted similar multi-layer sheet of thickness；
E, it is template template will to be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；
F, using jigsaw hot press by multi-layer sheet strip bed board and hot forming；
G, sand flat after cooling down with sander, plain plate is obtained after sanding；
H, the difference of product thickness is required according to user, after several plain plates are glued by automatic double-sided gluing machine, overlapping one
Rise and be put into cold press cold moudling；
I, product is obtained in bead cutter cutting four using four.
Described hot forming is in four sides side pressure hot press synchronization hot pressing, side pressure, and its side pressure pressure is 6-16MPa, just
Pressure pressure is 6-16MPa, temperature is 80-100 DEG C, the time is 4-15 minutes.
From technical scheme as can be seen that this technique in process of production, has more used integrative-structure
Production of machinery, substantial amounts of human resources can be saved, due to multiple-plate thickness is carried out into exact classification in advance, multiple blade saw is to more
Resource is not only make use of to greatest extent while laminate classification cutting, and facilitates jigsaw, with cutting in the production line of saving over
The process links such as skin in the fixed thick plus solid wood of side machine.During actual production, this technique not only greatly reduces the row of dust
Put and be beneficial to environmentally friendly, effectively save more than the % of electricity 40, also greatly reduce province consumption of the multi-layer sheet when cutting is fixed thick.Fully achieve
The goal of the invention that the present invention can be effectively reduced product cost, economize on resources, improve product quality and efficiency.
Embodiment
Multiple-plate production method is spliced in embodiment 1, a kind of regeneration, follows these steps to carry out,
A, discarded construction multi-layer sheet is purchased, and goes to follow closely, remove surface impurity；
B, with right angle bead cutter crop；
C, multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；
D, the wide length of tri- kinds of specifications of 12.6cm, 7.6cm, 3.7cm will be sawed into piece by the sorted similar multi-layer sheet of thickness
Bar；
E, it is template template will to be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；
F, using jigsaw hot press by multi-layer sheet strip bed board and hot forming；
G, sand flat after cooling down with sander, plain plate is obtained after sanding；
H, the difference of product thickness is required according to user, after several plain plates are glued by automatic double-sided gluing machine, overlapping one
Rise and be put into cold press cold moudling；
I, product is obtained in bead cutter cutting four using four.
Described hot forming is in four sides side pressure hot press synchronization hot pressing, side pressure, and its side pressure pressure is 6MPa, malleation pressure
Power is 6MPa, temperature is 80 DEG C, the time is 15 minutes.
Multiple-plate production method is spliced in embodiment 2, a kind of regeneration, follows these steps to carry out,
A, discarded construction multi-layer sheet is purchased, and goes to follow closely, remove surface impurity；
B, with right angle bead cutter crop；
C, multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；
D, the wide length of tri- kinds of specifications of 12.6cm, 7.6cm, 3.7cm will be sawed into piece by the sorted similar multi-layer sheet of thickness
Bar；
E, it is template template will to be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；
F, using jigsaw hot press by multi-layer sheet strip bed board and hot forming；
G, sand flat after cooling down with sander, plain plate is obtained after sanding；
H, the difference of product thickness is required according to user, after several plain plates are glued by automatic double-sided gluing machine, overlapping one
Rise and be put into cold press cold moudling；
I, product is obtained in bead cutter cutting four using four.
Described hot forming is in four sides side pressure hot press synchronization hot pressing, side pressure, and its side pressure pressure is 11MPa, malleation
Pressure is 11MPa, temperature is 90 DEG C, the time is 10 minutes.
Multiple-plate production method is spliced in embodiment 3, a kind of regeneration, follows these steps to carry out,
A, discarded construction multi-layer sheet is purchased, and goes to follow closely, remove surface impurity；
B, with right angle bead cutter crop；
C, multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；
D, the wide length of tri- kinds of specifications of 12.6cm, 7.6cm, 3.7cm will be sawed into piece by the sorted similar multi-layer sheet of thickness
Bar；
E, it is template template will to be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；
F, using jigsaw hot press by multi-layer sheet strip bed board and hot forming；
G, sand flat after cooling down with sander, plain plate is obtained after sanding；
H, the difference of product thickness is required according to user, after several plain plates are glued by automatic double-sided gluing machine, overlapping one
Rise and be put into cold press cold moudling；
I, product is obtained in bead cutter cutting four using four.
Described hot forming is in four sides side pressure hot press synchronization hot pressing, side pressure, and its side pressure pressure is 16MPa, malleation
Pressure is 16MPa, temperature is 100 DEG C, the time is 4 minutes.
Claims (3)
1. multiple-plate production method is spliced in one kind regeneration, it is characterised in that：Follow these steps to carry out,
（a）The discarded construction multi-layer sheet of purchase, and go to follow closely, remove surface impurity；
（b）With right angle bead cutter crop；
（c）Multi-layer sheet is subjected to exact classification stacking by thickness using lumber thickness classifier；
（d）The wide strip of different size will be sawed into piece by the sorted similar multi-layer sheet of thickness；
（e）It is template that template will be put into after the gluing of multi-layer sheet length direction both sides and is just spelled with automatic glue spreaders；
（f）Using jigsaw hot press by multi-layer sheet strip bed board and hot forming；
（g）Sand flat after cooling with sander, plain plate is obtained after sanding；
（h）The difference of product thickness is required according to user, after several plain plates are glued by automatic double-sided gluing machine, overlapping one
Rise and be put into cold press cold moudling；
（i）Using four product is obtained in bead cutter cutting four.
2. multiple-plate production method is spliced in a kind of regeneration according to claim 1, it is characterised in that：Described is hot pressed into
Shape is that its side pressure pressure is 6-16MPa, positive pressure pressure 6-16MPa, temperature in four sides side pressure hot press synchronization hot pressing, side pressure
It it is 4-15 minutes for 80-100 DEG C, time.
A kind of 3. product for regenerating splicing multilayer laminin plate, it is characterised in that：Obtained by the method according to claim 11
Product.