CN107700212A - A kind of material treatment anti-ultraviolet radiation treatment liquid - Google Patents
A kind of material treatment anti-ultraviolet radiation treatment liquid Download PDFInfo
- Publication number
- CN107700212A CN107700212A CN201710911679.3A CN201710911679A CN107700212A CN 107700212 A CN107700212 A CN 107700212A CN 201710911679 A CN201710911679 A CN 201710911679A CN 107700212 A CN107700212 A CN 107700212A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- ultraviolet radiation
- treatment liquid
- radiation treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to fabric technical field, and in particular to a kind of ultraviolet-resistant fabric, the fabric include bottom compound successively, intermediate layer, upper strata；The bottom is woven from by warp thread, weft yarn, and warp thread is bamboo-carbon fibre, sweet potato fiber blend forms；The intermediate layer is blending yarn fabric, polyvinyl chloride graft maleic anhydride, dibenzothiazyl disulfide, polyarylene hydrocarbon, the respective copolyesters of tetra-benzyl thiram disulfide are well mixed with graphite powder and carry out spinning hollow fibre filament jointly, the hollow fibre filament carries out blending and obtains blending yarn fabric；The upper strata is formed by cotton fiber, flax fiber blending；Fabric drying ultraviolet-resistant fabric again after anti-ultraviolet radiation treatment liquid immersion treatment.Fabric of the present invention has extraordinary anti-uv-ray by specially treated, and anti-uv-ray is lasting, and has used specifically developed anti-ultraviolet radiation treatment liquid energy to be obviously improved anti-uv-ray.
Description
Technical field：
The present invention relates to fabric technical field, and in particular to a kind of material treatment anti-ultraviolet radiation treatment liquid.
Background technology：
It is also higher for the requirement of wearing quality as people's living standard gradually rises, do not only require comfortable, also need
Have concurrently multi-functional, according to different lifestyles, the function of being worn clothes is also different, when climbing the mountain such as, in response to the low of environment
The ultraviolet of warm, rainy and high mountain exposure, the then clothes worn must then possess the functions such as insulation, waterproof and uvioresistant；When
When carrying out outdoor exercises, then light and handy, moisture absorbing and sweat releasing, rapid-curing cutback and the fabric of the function such as ventilative are needed, and tradition applies to kinetic system
The knitting fabric of row mostly uses common circular-section terylene low stretch yarn raw material, using manufacture craft after original dyeing, water
It is more poor with light shine fastness to wash loose colour, color becomes to wither secretly after long-term outdoor moves dressing, and feel is hardened and sweat is led in moisture absorption
Poor performance, dress is sultry airtight, and comfort is poor；In the case that even if common people do not carry out any activity, still require that and worn
Clothes must possess the quality of high quality, in addition, as context pollutes getting worse, ciril disease also occurs in succession, such as
Too coarse cloth textile can cause some people skin to produce allergy, or to the easy body for producing allergy of external environment
Matter, modern is caused also gradually to pay attention to for the idea of antibacterial, in the past the antibacterial clothing and antibacterial utensil only needed for medical personnel,
Also the articles for use of daily life are gradually used in.
For human body, appropriate ultraviolet radiation has bactericidal action and can promote the synthesis of vitamin D, is advantageous to people
Body health.But under burning sun prolonged exposure, human body skin can lose defensive ability/resistance ability, easily burn, and erythema or bubble occur.Cross
The ultraviolet irradiation of amount can also induce skin disease (such as dermatitis, pigment asteatosis cutis), or even cutaneum carcinoma, promote the generation of cataract simultaneously
Reduce the immunologic function of human body.
From optical principle, ultraviolet radiation to fabric, partly reflected on surface, partly absorbed by fabric, its
Remaining then passes through fabric.Generally, transmitance+reflectivity+absorptivity=100% of ultraviolet.Therefore, fabric pair is improved
The absorptivity and reflectivity can of ultraviolet reduce the transmitance of ultraviolet.Although current existing anti-ultraviolet radiation treatment liquid meeting
Assign fabric certain ultraviolet reflection rate and absorptivity, but after long-time is cleaned, anti-ultraviolet property can gradually subtract
It is weak until disappear.
And the antistatic behaviour of fabric is also particularly important, especially in special occasions, electrostatic often produces cause caused by fabric
The harm of life, therefore, the research to the antistatic behaviour of fabric are also particularly important.
The content of the invention：
The technical problems to be solved by the invention are to overcome existing technological deficiency, there is provided a kind of anti-purple of material treatment
Outside line treatment fluid.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of material treatment anti-ultraviolet radiation treatment liquid, the anti-ultraviolet radiation treatment liquid are made up of following raw material：
4 parts of 4 parts of water soluble chitosan, acidum nalidixicum and orfloxacin, 2.2 parts of different glycol monobutyl ether, 0.3 part of sodium cumene sulfonate, punching
1.3 parts of lotus lactones, 3.6 parts of selfheal extract solution, 1.5 parts of auxiliary agent, 100 parts of purified water, 0.2 part of nano material.
Further, the auxiliary agent is that methionine, pearly-lustre resin acid, melissic acid, nano-graphene powder, medical White Mineral Oil are pressed
The mixture of equal proportion mixing.
Further, the nano material is made including following raw material：Part, nanometer two of nano-graphene 0.1
0.2 part of titanium oxide, 0.1 part of nano aluminium oxide, each raw material are well mixed.
A kind of ultraviolet-resistant fabric, fabric include bottom compound successively, intermediate layer, upper strata；
Bottom is woven from by warp thread, weft yarn, and warp thread is bamboo-carbon fibre, sweet potato fiber blend forms；
Intermediate layer is blending yarn fabric, by polyvinyl chloride graft maleic anhydride, dibenzothiazyl disulfide, polyarylene hydrocarbon,
The respective copolyesters of tetra-benzyl thiram disulfide is well mixed with graphite powder jointly carries out spinning hollow fibre filament, the doughnut
Silk carries out blending and obtains blending yarn fabric；
Upper strata is formed by cotton fiber, flax fiber blending；
Fabric drying ultraviolet-resistant fabric again after anti-ultraviolet radiation treatment liquid immersion treatment.
Beneficial effects of the present invention are：Fabric of the present invention has extraordinary anti-uv-ray by specially treated, and
And anti-uv-ray is lasting, and specifically developed anti-ultraviolet radiation treatment liquid energy has been used to be obviously improved anti-uv-ray.
Brief description of the drawings：
Fig. 1 is the structural representation of fabric of the present invention；
Fig. 2 is the structural representation of fabric basal plane of the present invention and viscose.
Embodiment：
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
, it is necessary to explanation in description of the invention, the orientation of instruction such as term " vertical ", " on ", " under ", " level " or
Person's position relationship is based on orientation shown in the drawings or position relationship, is for only for ease of and describes this practicality and simplify to describe,
Rather than instruction either implies that signified device or element must have specific orientation, with specific azimuth configuration and behaviour
Make, therefore be not considered as limiting the invention.In addition, " first ", " second ", " the 3rd ", " the 4th " are only used for describing mesh
, and it is not intended that instruction or hint relative importance.
In description of the invention, it is also necessary to explanation, unless otherwise clear and definite regulation and limitation, term " setting ", " peace
Dress ", " connected ", " connection " should be interpreted broadly, for example, it may be fixedly connected or be detachably connected, or integratedly
Connection, can be mechanical connection or electrical connection, can be directly connected to or be connected by intermediary, can
To be the connection of two element internals.For the ordinary skill in the art, can understand as the case may be above-mentioned
The concrete meaning of term in the present invention.
Embodiment one
As shown in accompanying drawing 1,2, a kind of material treatment anti-ultraviolet radiation treatment liquid, anti-ultraviolet radiation treatment liquid is by following parts by weight
Raw material is made：4 parts of 4 parts of water soluble chitosan, acidum nalidixicum and orfloxacin, 2.2 parts of different glycol monobutyl ether, sodium cumene sulfonate
0.3 part, 1.3 parts of creat lactone, 3.6 parts of selfheal extract solution, 100 parts of purified water, 0.2 part of nano material.
Nano material is made including following raw material：0.1 part of nano-graphene, nano titanium oxide 0.2 part, nanometer
0.1 part of aluminum oxide, each raw material are well mixed.
A kind of ultraviolet-resistant fabric, fabric include bottom 1 compound successively, intermediate layer 2, upper strata 3；
Bottom 1 is woven from by warp thread, weft yarn, and warp thread is bamboo-carbon fibre, sweet potato fiber blend forms；
Intermediate layer 2 is blending yarn fabric, by polyvinyl chloride graft maleic anhydride, dibenzothiazyl disulfide, polyarylene hydrocarbon,
The respective copolyesters of tetra-benzyl thiram disulfide is well mixed with graphite powder jointly carries out spinning hollow fibre filament, the doughnut
Silk carries out blending and obtains blending yarn fabric；
Upper strata 3 is formed by cotton fiber, flax fiber blending；
Fabric drying ultraviolet-resistant fabric again after anti-ultraviolet radiation treatment liquid immersion treatment.
Embodiment two
As shown in accompanying drawing 1,2, a kind of ultraviolet-resistant fabric, fabric includes bottom 1 compound successively, intermediate layer 2, upper strata 3；
Bottom 1 is woven from by warp thread, weft yarn, and warp thread is bamboo-carbon fibre, sweet potato fiber blend forms；
Intermediate layer 2 is blending yarn fabric, by polyvinyl chloride graft maleic anhydride, dibenzothiazyl disulfide, polyarylene hydrocarbon,
The respective copolyesters of tetra-benzyl thiram disulfide is well mixed with graphite powder jointly carries out spinning hollow fibre filament, the doughnut
Silk carries out blending and obtains blending yarn fabric；
Upper strata 3 is formed by cotton fiber, flax fiber blending；
Fabric drying ultraviolet-resistant fabric again after anti-ultraviolet radiation treatment liquid immersion treatment.
Bottom 1, intermediate layer 2, upper strata 3 are combined with each other by viscose 4.Viscose thickness is 0.1mm, and viscose is that hydrophobicity is more
Hole viscose.
A kind of material treatment anti-ultraviolet radiation treatment liquid, anti-ultraviolet radiation treatment liquid are made up of following raw material：It is water-soluble
Property 4 parts of 4 parts of chitosan, acidum nalidixicum and orfloxacin, 2.2 parts of different glycol monobutyl ether, 0.3 part of sodium cumene sulfonate, in Herba Andrographitis
1.3 parts of fat, 3.6 parts of selfheal extract solution, 1.5 parts of auxiliary agent, 100 parts of purified water, 0.2 part of nano material.
Auxiliary agent is methionine, pearly-lustre resin acid, melissic acid, nano-graphene powder, medical White Mineral Oil are mixed by equal proportion mixing
Compound.
Nano material is made including following raw material：0.1 part of nano-graphene, nano titanium oxide 0.2 part, nanometer
0.1 part of aluminum oxide, each raw material are well mixed.
Embodiment three
As shown in accompanying drawing 1,2, a kind of ultraviolet-resistant fabric, fabric includes bottom 1 compound successively, intermediate layer 2, upper strata 3；
Bottom 1 is woven from by warp thread, weft yarn, and warp thread is bamboo-carbon fibre, sweet potato fiber blend forms；
Intermediate layer 2 is blending yarn fabric, by polyvinyl chloride graft maleic anhydride, dibenzothiazyl disulfide, polyarylene hydrocarbon,
The respective copolyesters of tetra-benzyl thiram disulfide is well mixed with graphite powder jointly carries out spinning hollow fibre filament, the doughnut
Silk carries out blending and obtains blending yarn fabric；
Upper strata 3 is formed by cotton fiber, flax fiber blending；
Fabric drying ultraviolet-resistant fabric again after anti-ultraviolet radiation treatment liquid immersion treatment.
Bottom 1, intermediate layer 2, upper strata 3 are combined with each other by viscose 4.Viscose thickness is 0.1mm, and viscose is that hydrophobicity is more
Hole viscose.
A kind of material treatment anti-ultraviolet radiation treatment liquid, anti-ultraviolet radiation treatment liquid are made up of following raw material：It is water-soluble
Property 4 parts of 4 parts of chitosan, acidum nalidixicum and orfloxacin, 2.2 parts of different glycol monobutyl ether, 0.3 part of sodium cumene sulfonate, in Herba Andrographitis
1.3 parts of fat, 3.6 parts of selfheal extract solution, 1.5 parts of auxiliary agent, 100 parts of purified water, 0.2 part of nano material.
Auxiliary agent is methionine, pearly-lustre resin acid, melissic acid, nano-graphene powder, medical White Mineral Oil are mixed by equal proportion mixing
Compound.
Nano material is made including following raw material：0.1 part of nano-graphene, nano titanium oxide 0.2 part, nanometer
0.1 part of aluminum oxide, each raw material are well mixed.
The preparation method of anti-ultraviolet radiation treatment liquid is as follows：
(1) each raw material of composition anti-ultraviolet radiation treatment liquid is weighed by weight；
(2) surplus stock that purified water is removed in above-mentioned raw materials is proportionally added into high-pressure bottle and enters horizontal high voltage batch mixing,
Pressure is 2~3 times of atmospheric pressure, and the temperature of high pressure batch mixing is 155-180 DEG C, and the time of high pressure batch mixing is 8-10 minutes；
(3) take out above-mentioned batch mixing and then stirred after being mixed together with purified water and produce anti-ultraviolet radiation treatment liquid.
Fabric is dipped into 10-20 minutes in anti-ultraviolet radiation treatment liquid during use, then pulls out and dries.
Experiment
Uvioresistant and antistatic property detection are carried out to the gained uvioresistant of embodiment 1 to 3 Antistatic Fabric, wherein,
Anti-ultraviolet property tests fabric to the transmitance of ultraviolet (especially wavelength 290-400nm ultraviolet), antistatic property with
The ratio resistance Rs (resistance between per square unit sample corresponding sides) of web surface represents, meanwhile, it is washed 20 times in fabric
Afterwards again test fabric antistatic property and anti-ultraviolet property, and with Chinese invention patent application publication No.：CN
105088750 A, data of publication of application：2015.11.25 embodiment 1 be compared, it is as a result as follows：
It can be seen that ultraviolet-resistant fabric superior performance of the present invention, ultraviolet ray transmissivity is low, and it is anti-after repeatedly washing
UV resistance is still very strong, and antistatic property is also relatively stable, and the ultraviolet ray transmissivity detail of embodiment 2,3 is than embodiment 1
It is low, exactly because methionine, pearly-lustre resin acid, melissic acid, nano-graphene powder, medical white ore deposit are added in anti-ultraviolet radiation treatment liquid
Oil.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of material treatment anti-ultraviolet radiation treatment liquid, it is characterised in that the anti-ultraviolet radiation treatment liquid is by following parts by weight
Raw material is made：4 parts of 4 parts of water soluble chitosan, acidum nalidixicum and orfloxacin, 2.2 parts of different glycol monobutyl ether, sodium cumene sulfonate
0.3 part, 1.3 parts of creat lactone, 3.6 parts of selfheal extract solution, 1.5 parts of auxiliary agent, 100 parts of purified water, 0.2 part of nano material.
2. a kind of material treatment anti-ultraviolet radiation treatment liquid according to claim 1, it is characterised in that the auxiliary agent is egg
Propylhomoserin, pearly-lustre resin acid, melissic acid, nano-graphene powder, medical White Mineral Oil press the mixture of equal proportion mixing.
A kind of 3. material treatment anti-ultraviolet radiation treatment liquid according to claim 1, it is characterised in that the nano material
It is made including following raw material：0.1 part of nano-graphene, 0.2 part of nano titanium oxide, 0.1 part of nano aluminium oxide, each original
Material is well mixed.