CN107675291A - A kind of cloth breathed freely with antiultraviolet moisture absorption and preparation method thereof - Google Patents
A kind of cloth breathed freely with antiultraviolet moisture absorption and preparation method thereof Download PDFInfo
- Publication number
- CN107675291A CN107675291A CN201710843810.7A CN201710843810A CN107675291A CN 107675291 A CN107675291 A CN 107675291A CN 201710843810 A CN201710843810 A CN 201710843810A CN 107675291 A CN107675291 A CN 107675291A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- fibre
- cloth
- antiultraviolet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cloth production field, more particularly to a kind of cloth breathed freely with antiultraviolet moisture absorption and preparation method thereof, the cloth includes being formed by bamboo-carbon fibre, sugarcane fibre, wood-fibred, smart cotton fiber and imperial glycan fiber blend.Fabric fibre made of the present invention has excellent anti-ultraviolet function, nontoxic to human body, tenacity of fibre is good, intensity is high, it is non-aging and due to the fabric fibre to coloring agent have stronger adsorption capacity without fugitive color.
Description
Technical field
The present invention relates to cloth production field, more particularly to a kind of cloth breathed freely with antiultraviolet moisture absorption and its preparation
Method.
Background technology
In general, appropriate ultraviolet is beneficial that it can promote the synthesis of vitamin D, have to rickets to human body
Inhibitory action, and there is sterilization.But in recent years, due to human being's production and the substantial amounts of discharge freon of life etc
Chlorofluorination hydrogen compound, the umbrella i.e. atmosphere of the earth is increasingly destroyed, it is particularly blue or green in terrestrial pole and China
Hide plateau overhead and ozone hole occur, increase the amount of ultraviolet irradiation on arrival ground, because excessive ultraviolet irradiation
Caused disease is more and more.Generally, human body skin can receive the safe amount of radiation of ultraviolet daily should be in 20kJ/
m2Within, two ultraviolets reach ground the amount of radiation cloudy day when be about 40-60kJ/m2, it is about 80-100kJ/m during fine day2, it is hot
Summer can reach 100-200kJ/m2, common cloth, typically 50% or so, do not reach much anti-to the screening rate of ultraviolet
The effect of shield, and the airtight not absorbing sweat of cloth of common antiultraviolet, dress are uncomfortable.
Also, long-term ultraviolet irradiates the colour fading and aging of also textile caused by meeting.Therefore, it is necessary to textile
Carry out anti-ultraviolet finishing.
The content of the invention
It is an object of the invention to provide a kind of cloth breathed freely with antiultraviolet moisture absorption and preparation method thereof, to realize cloth
Material is with the ventilative technique effect of excellent antiultraviolet, moisture absorption.
In order to realize above-mentioned technical problem, the invention provides technical scheme to be：There is one kind antiultraviolet moisture absorption to breathe freely
Cloth, the cloth forms by bamboo-carbon fibre, sugarcane fibre, wood-fibred, smart cotton fiber and imperial glycan fiber blend.
Further, the cloth includes the raw material of following component：Bamboo-carbon fibre 15-26 parts, sugarcane fibre 15-20 parts,
Wood-fibred 16-23 parts, smart cotton fiber 14-24 parts and imperial glycan fiber 17-30 parts；And
Talcum powder 16-20 parts, zinc oxide 22-30 parts, clay 17-28 parts, calcium carbonate 10-16 parts and water 20-28 parts.
Further, the cloth includes the raw material of following component：Bamboo-carbon fibre 16-28 parts, sugarcane fibre 14-18
Part, wood-fibred 15-22 parts, smart cotton fiber 15-25 parts and imperial glycan fiber 16-29 parts；And
Talcum powder 15-19 parts, zinc oxide 20-28 parts, clay 19-30 parts, calcium carbonate 11-18 parts and water 18-26 parts.
Another aspect, the present invention also provide it is a kind of with antiultraviolet moisture absorption breathe freely cloth preparation method, including with
Lower step：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan is extracted using fiber extractor
Fibrous raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200
After mesh sieve, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：The product that step S5 is obtained forms cloth fibre after carrying out dewatered drying, section, spinning, winding, stretching
Tie up, stretch a diameter of 45-55 μm of fiber.
Further, in the step S3：Bamboo-carbon fibre 15-26 parts, sugarcane fibre 15-20 parts, wood-fibred 16-23 parts,
Smart cotton fiber 14-24 parts and imperial glycan fiber 17-30 parts；And
In the step S4：Talcum powder 16-20 parts, zinc oxide 22-30 parts, clay 17-28 parts, calcium carbonate 10-16 parts and
Water 20-28 parts.
Further, in the step S3：Bamboo-carbon fibre 16-28 parts, sugarcane fibre 14-18 parts, wood-fibred 15-22 parts,
Smart cotton fiber 15-25 parts and imperial glycan fiber 16-29 parts；And
In the step S4：Talcum powder 15-19 parts, zinc oxide 20-28 parts, clay 19-30 parts, calcium carbonate 11-18 parts and
Water 18-26 parts.
Further, the sieving subnumber in the step S3 is 200 mesh.
Further, the drying temperature in the step S4 is 120 DEG C.
Further, the step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min.
Further, the stretching fibre diameter in the step S6 is 50 μm.
Fabric fibre made of the present invention has excellent anti-ultraviolet function, nontoxic to human body, tenacity of fibre is good,
Intensity is high, non-aging and because the fabric fibre has stronger adsorption capacity without fugitive color to coloring agent.
Further, the imperial glycan fiber of use, makes cloth have good moisture absorption absorption of perspiration, gas permeability, and have
The characteristic of antistatic, makes cloth cloth cover good luster, and cloth is solid.
Embodiment
The present invention is further detailed explanation now.
Embodiment 1：
The invention provides a kind of cloth breathed freely with antiultraviolet moisture absorption, the cloth is fine by bamboo-carbon fibre, sugarcane
Dimension, wood-fibred, smart cotton fiber and imperial glycan fiber blend form.
Specifically, the cloth includes the raw material of following component：15 parts of bamboo-carbon fibre, 15 parts of sugarcane fibre, wood-fibred 20
Part, 20 parts of smart cotton fiber and imperial 30 parts of glycan fiber；And
20 parts of 16 parts of talcum powder, 22 parts of zinc oxide, 28 parts of clay, 14 parts of calcium carbonate and water.
Using imperial glycan fiber and bamboo-carbon fibre, make cloth that there is ventilative moisture absorption, bacteriostasis antibiosis, cool in summer and warm in winter, green ring
Protect.
The preparation method with the ventilative cloth of antiultraviolet moisture absorption of the present embodiment, comprises the following steps：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan is extracted using fiber extractor
Fibrous raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200
After mesh sieve, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：The product that step S5 is obtained forms cloth fibre after carrying out dewatered drying, section, spinning, winding, stretching
Tie up, stretch a diameter of 45-55 μm of fiber.
Wherein, in the step S3：15 parts of bamboo-carbon fibre, 15 parts of sugarcane fibre, 20 parts of wood-fibred, 20 parts of smart cotton fiber and
Imperial 30 parts of glycan fiber；And
In the step S4：20 parts of 16 parts of talcum powder, 22 parts of zinc oxide, 28 parts of clay, 14 parts of calcium carbonate and water.
Optionally, the sieving subnumber in the step S3 is 200 mesh, is advantageous in manufacturing process below, the mixing of composition
Fully, stock utilization is improved.
Drying temperature in the step S4 is 120 DEG C, is advantageous to flash baking and does not influence the architecture quality of clay.
The step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min, are advantageous to the mixed of each composition
Close abundant so that stirring evenly, can also improve the utilization rate of material to a certain extent.
Stretching fibre diameter in the step S6 is 50 μm, is advantageous to the toughness of fiber reaching highest, and UV resistance
The effect of line is best.
Spinning is carried out to the fabric fibre after section using weaving loom in the step S6.
Winding in the step S6 uses the multi-functional cloth roll inspectings of EL-181LS-3.
Embodiment 2：
A kind of cloth breathed freely with antiultraviolet moisture absorption, the cloth is by bamboo-carbon fibre, sugarcane fibre, wood-fibred, essence
Cotton fiber and imperial glycan fiber blend form.
Specifically, the cloth includes the raw material of following component：20 parts of bamboo-carbon fibre, 17 parts of sugarcane fibre, wood-fibred 23
Part, 15 parts of smart cotton fiber and imperial 25 parts of glycan fiber；And
28 parts of 17 parts of talcum powder, 23 parts of zinc oxide, 22 parts of clay, 10 parts of calcium carbonate and water.
Using imperial glycan fiber and bamboo-carbon fibre, make cloth that there is ventilative moisture absorption, bacteriostasis antibiosis, cool in summer and warm in winter, green ring
Protect.
The preparation method with the ventilative cloth of antiultraviolet moisture absorption of the present embodiment, comprises the following steps：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan is extracted using fiber extractor
Fibrous raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200
After mesh sieve, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：The product that step S5 is obtained forms cloth fibre after carrying out dewatered drying, section, spinning, winding, stretching
Tie up, stretch a diameter of 45-55 μm of fiber.
20 parts of bamboo-carbon fibre in the step S3,17 parts of sugarcane fibre, 23 parts of wood-fibred, smart 15 parts of cotton fiber are fragrant with dragon
25 parts of taro fiber；And
28 parts of 17 parts of talcum powder, 23 parts of zinc oxide, 22 parts of clay, 10 parts of calcium carbonate and water.
Optionally, the sieving subnumber in the step S3 is 200 mesh, is advantageous in manufacturing process below, the mixing of composition
Fully, stock utilization is improved.
Drying temperature in the step S4 is 120 DEG C, is advantageous to flash baking and does not influence the architecture quality of clay.
The step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min, are advantageous to the mixed of each composition
Close abundant so that stirring evenly, can also improve the utilization rate of material to a certain extent.
Stretching fibre diameter in the step S6 is 50 μm, is advantageous to the toughness of fiber reaching highest, and UV resistance
The effect of line is best.
Spinning is carried out to the fabric fibre after section using weaving loom in the step S6.
Winding in the step S6 uses the multi-functional cloth roll inspectings of EL-181LS-3.
Embodiment 3：
A kind of cloth breathed freely with antiultraviolet moisture absorption, the cloth is by bamboo-carbon fibre, sugarcane fibre, wood-fibred, essence
Cotton fiber and imperial glycan fiber blend form.
The cloth includes the raw material of following component：21 parts of bamboo-carbon fibre, 20 parts of sugarcane fibre, 18 parts of wood-fibred, smart cotton
24 parts of fiber and imperial 17 parts of glycan fiber；And
25 parts of 17 parts of talcum powder, 23 parts of zinc oxide, 20 parts of clay, 15 parts of calcium carbonate and water.
Using imperial glycan fiber and bamboo-carbon fibre, make cloth that there is ventilative moisture absorption, bacteriostasis antibiosis, cool in summer and warm in winter, green ring
Protect.
The preparation method with the ventilative cloth of antiultraviolet moisture absorption of the present embodiment, comprises the following steps：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan is extracted using fiber extractor
Fibrous raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200
After mesh sieve, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：The product that step S5 is obtained forms cloth fibre after carrying out dewatered drying, section, spinning, winding, stretching
Tie up, stretch a diameter of 45-55 μm of fiber.
In the step S3：21 parts of bamboo-carbon fibre, 20 parts of sugarcane fibre, 18 parts of wood-fibred, smart 24 parts of cotton fiber are fragrant with dragon
17 parts of taro fiber；And
In the step S4：25 parts of 17 parts of talcum powder, 23 parts of zinc oxide, 20 parts of clay, 15 parts of calcium carbonate and water.
Optionally, the sieving subnumber in the step S3 is 200 mesh, is advantageous in manufacturing process below, the mixing of composition
Fully, stock utilization is improved.
Drying temperature in the step S4 is 120 DEG C, is advantageous to flash baking and does not influence the architecture quality of clay.
The step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min, are advantageous to the mixed of each composition
Close abundant so that stirring evenly, can also improve the utilization rate of material to a certain extent.
Stretching fibre diameter in the step S6 is 50 μm, is advantageous to the toughness of fiber reaching highest, and UV resistance
The effect of line is best.
Spinning is carried out to the fabric fibre after section using weaving loom in the step S6.
Winding in the step S6 uses the multi-functional cloth roll inspectings of EL-181LS-3.
Embodiment 4：
A kind of cloth breathed freely with antiultraviolet moisture absorption, the cloth is by bamboo-carbon fibre, sugarcane fibre, wood-fibred, essence
Cotton fiber and imperial glycan fiber blend form.
The cloth includes the raw material of following component：28 parts of bamboo-carbon fibre, 14 parts of sugarcane fibre, 20 parts of wood-fibred, smart cotton
18 parts of fiber and imperial 20 parts of glycan fiber；And
In the step S4：20 parts of 15 parts of talcum powder, 25 parts of zinc oxide, 26 parts of clay, 14 parts of calcium carbonate and water.
Using imperial glycan fiber and bamboo-carbon fibre, make cloth that there is ventilative moisture absorption, bacteriostasis antibiosis, cool in summer and warm in winter, green ring
Protect.
The preparation method with the ventilative cloth of antiultraviolet moisture absorption of the present embodiment, comprises the following steps：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan is extracted using fiber extractor
Fibrous raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200
After mesh sieve, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：The product that step S5 is obtained forms cloth fibre after carrying out dewatered drying, section, spinning, winding, stretching
Tie up, stretch a diameter of 45-55 μm of fiber.
In the step S3：28 parts of bamboo-carbon fibre, 14 parts of sugarcane fibre, 20 parts of wood-fibred, smart 18 parts of cotton fiber are fragrant with dragon
20 parts of taro fiber；And
In the step S4：20 parts of 15 parts of talcum powder, 25 parts of zinc oxide, 26 parts of clay, 14 parts of calcium carbonate and water.
Optionally, the sieving subnumber in the step S3 is 200 mesh, is advantageous in manufacturing process below, the mixing of composition
Fully, stock utilization is improved.
Drying temperature in the step S4 is 120 DEG C, is advantageous to flash baking and does not influence the architecture quality of clay.
The step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min, are advantageous to the mixed of each composition
Close abundant so that stirring evenly, can also improve the utilization rate of material to a certain extent.
Stretching fibre diameter in the step S6 is 50 μm, is advantageous to the toughness of fiber reaching highest, and UV resistance
The effect of line is best.
Spinning is carried out to the fabric fibre after section using weaving loom in the step S6.
Winding in the step S6 uses the multi-functional cloth roll inspectings of EL-181LS-3.
It is complete by above-mentioned description, relevant staff using the above-mentioned desirable embodiment according to the present invention as enlightenment
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property scope is not limited to the content on specification, it is necessary to determines its technical scope according to right.
Claims (10)
1. it is a kind of with antiultraviolet moisture absorption breathe freely cloth, it is characterised in that the cloth by bamboo-carbon fibre, sugarcane fibre,
Wood-fibred, smart cotton fiber and imperial glycan fiber blend form.
2. the cloth according to claim 1 breathed freely with antiultraviolet moisture absorption, it is characterised in that the cloth is included such as
The raw material of lower component：Bamboo-carbon fibre 15-26 parts, sugarcane fibre 15-20 parts, wood-fibred 16-23 parts, smart cotton fiber 14-24 parts and
Imperial glycan fiber 17-30 parts；And
Talcum powder 16-20 parts, zinc oxide 22-30 parts, clay 17-28 parts, calcium carbonate 10-16 parts and water 20-28 parts.
3. the cloth according to claim 1 breathed freely with antiultraviolet moisture absorption, it is characterised in that the cloth is included such as
The raw material of lower component：Bamboo-carbon fibre 16-28 parts, sugarcane fibre 14-18 parts, wood-fibred 15-22 parts, smart cotton fiber 15-25 parts and
Imperial glycan fiber 16-29 parts；And
Talcum powder 15-19 parts, zinc oxide 20-28 parts, clay 19-30 parts, calcium carbonate 11-18 parts and water 18-26 parts.
4. a kind of preparation method for the cloth breathed freely with antiultraviolet moisture absorption, it is characterised in that comprise the following steps：
Step S1；After imperial glycan is cleaned at a temperature of temperature is 30-40 DEG C, imperial glycan fiber is extracted using fiber extractor
Raw material, it is standby；
Step S2：Remote mountains mao bamboon, white silk is standby into bamboo-carbon fibre；
Step S3：Woodwork, bamboo-carbon fibre, sugarcane fibre, smart cotton fiber and imperial glycan fiber were crushed to 150-200 mesh sieves
Afterwards, it is well mixed；
Step S4：Zinc oxide and calcium carbonate are crushed to form Zinc oxide powder and calcium carbonate powder respectively；
Crushed after clay is dried at 120-150 DEG C to form powder；
Zinc oxide powder, calcium carbonate powder, clay powder and water are mixed, stirred；
Step S5：The product respectively obtained in step S3 and step S4 is mixed, and stirred；
Step S6：Fabric fibre is formed after the product that step S5 is obtained is carried out into dewatered drying, section, spinning, winding, stretching,
Stretch a diameter of 45-55 μm of fiber.
5. the preparation method of the cloth according to claim 4 breathed freely with antiultraviolet moisture absorption, it is characterised in that described
In step S3：Bamboo-carbon fibre 15-26 parts, sugarcane fibre 15-20 parts, wood-fibred 16-23 parts, smart cotton fiber 14-24 parts and dragon are fragrant
Taro fiber 17-30 parts；And
In the step S4：Talcum powder 16-20 parts, zinc oxide 22-30 parts, clay 17-28 parts, calcium carbonate 10-16 parts and water 20-
28 parts.
6. the preparation method of the cloth according to claim 4 breathed freely with antiultraviolet moisture absorption, it is characterised in that described
In step S3：Bamboo-carbon fibre 16-28 parts, sugarcane fibre 14-18 parts, wood-fibred 15-22 parts, smart cotton fiber 15-25 parts and dragon are fragrant
Taro fiber 16-29 parts；And
In the step S4：Talcum powder 15-19 parts, zinc oxide 20-28 parts, clay 19-30 parts, calcium carbonate 11-18 parts and water 18-
26 parts.
7. the preparation method of the cloth according to claim 6 breathed freely with antiultraviolet moisture absorption, it is characterised in that described
Sieving subnumber in step S3 is 200 mesh.
8. the preparation method of the cloth according to claim 4 breathed freely with antiultraviolet moisture absorption, it is characterised in that described
Drying temperature in step S4 is 120 DEG C.
9. the preparation method of the cloth according to claim 4 breathed freely with antiultraviolet moisture absorption, it is characterised in that described
Step S3, step S4 and step S5 stir speed (S.S.) are 1200-1500r/min.
10. the preparation method of the cloth according to claim 4 breathed freely with antiultraviolet moisture absorption, it is characterised in that institute
It is 50 μm to state the stretching fibre diameter in step S6.