CN107674743A - A kind of composite solid lubricant material and its preparation technology - Google Patents
A kind of composite solid lubricant material and its preparation technology Download PDFInfo
- Publication number
- CN107674743A CN107674743A CN201710970996.2A CN201710970996A CN107674743A CN 107674743 A CN107674743 A CN 107674743A CN 201710970996 A CN201710970996 A CN 201710970996A CN 107674743 A CN107674743 A CN 107674743A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- solid lubricant
- fluorographite
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite solid lubricant material and its preparation technology, lubriation material component includes 20 40 parts of liquid paraffin, 10 20 parts of fluorographite, 5 15 parts of palmitoleic acid, 4 12 parts of lignin carbonate, 10 20 parts of dimethicone, 4 10 parts of isopropanol, 10 20 parts of SIMMONDSIA CHINENSIS SEED OIL, 49 parts of graphene, 39 parts of coconut oil alkanolamide, three red 4 12 parts of oil in parts by weight, preparation technology of the present invention is simple, obtained lubriation material greasy property is good, improve the service life of plant equipment, production cost is reduced, is economized on resources.
Description
Technical field
The present invention relates to lubriation material preparing technical field, specially a kind of composite solid lubricant material and its preparation work
Skill.
Background technology
Fretting wear is that plant equipment, space flight and aviation etc. have generally existing between the object of relative motion or relative motion trend
Natural phenomena, according to the preliminary statistics, China every year caused by abrasion loss account for the 1% of gross national product, therefore, how
Solve anti-attrition lubrication, the service life of prolonged mechanical part, reduce production cost, be current and significant period of time in future urgently
Need to solve the problems, such as.
The content of the invention
It is an object of the invention to provide a kind of composite solid lubricant material and its preparation technology, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme:A kind of composite solid lubricant material, lubriation material group
Divide includes liquid paraffin 20-40 parts, fluorographite 10-20 parts, palmitoleic acid 5-15 parts, lignin carbonate 4- in parts by weight
12 parts, dimethicone 10-20 parts, isopropanol 4-10 parts, SIMMONDSIA CHINENSIS SEED OIL 10-20 parts, graphene 4-9 parts, coconut oil alkanol acyl
Amine 3-9 parts, three red oily 4-12 parts.
Preferably, the preferable composition proportion of lubriation material component includes 30 parts of liquid paraffin, 15 parts of fluorographite, palm oil
10 parts of acid, 8 parts of lignin carbonate, 15 parts of dimethicone, 7 parts of isopropanol, 15 parts of SIMMONDSIA CHINENSIS SEED OIL, 7 parts of graphene, coconut oil
6 parts of alkanolamide, three red 8 parts of oil.
Preferably, its preparation technology comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Compared with prior art, the beneficial effects of the invention are as follows:Preparation technology of the present invention is simple, obtained lubriation material profit
Slip can be good, improves the service life of plant equipment, reduces production cost, economizes on resources;Wherein, the lotus lotus added in the present invention
Bar oil, three red oil can increase lubricant effect;The fluorographite of addition can increase the abrasion resistance of lubriation material;The two of addition
Methyl-silicone oil, it can prevent lubriation material from occurring oxidative phenomena.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme:A kind of composite solid lubricant material, lubriation material component are wrapped in parts by weight
Include liquid paraffin 20-40 parts, fluorographite 10-20 parts, palmitoleic acid 5-15 parts, lignin carbonate 4-12 parts, dimethyl-silicon
Oily 10-20 parts, isopropanol 4-10 parts, SIMMONDSIA CHINENSIS SEED OIL 10-20 parts, graphene 4-9 parts, coconut oil alkanolamide 3-9 parts, three red oil
4-12 parts.
Embodiment one:
Lubriation material component includes 20 parts of liquid paraffin, 10 parts of fluorographite, 5 parts of palmitoleic acid, lignin carbon in parts by weight
4 parts of hydrochlorate, 10 parts of dimethicone, 4 parts of isopropanol, 10 parts of SIMMONDSIA CHINENSIS SEED OIL, 4 parts of graphene, 3 parts of coconut oil alkanolamide, three
Red 4 parts of oil.
The preparation technology of the present embodiment comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Embodiment two:
Lubriation material component includes 40 parts of liquid paraffin, 20 parts of fluorographite, 15 parts of palmitoleic acid, lignin carbon in parts by weight
12 parts of hydrochlorate, 20 parts of dimethicone, 10 parts of isopropanol, 20 parts of SIMMONDSIA CHINENSIS SEED OIL, 9 parts of graphene, 9 parts of coconut oil alkanolamide,
Three red 12 parts of oil.
The preparation technology of the present embodiment comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Embodiment three:
Lubriation material component includes 25 parts of liquid paraffin, 12 parts of fluorographite, 7 parts of palmitoleic acid, lignin carbon in parts by weight
6 parts of hydrochlorate, 12 parts of dimethicone, 5 parts of isopropanol, 12 parts of SIMMONDSIA CHINENSIS SEED OIL, 5 parts of graphene, 4 parts of coconut oil alkanolamide, three
Red 6 parts of oil.
The preparation technology of the present embodiment comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Example IV:
Lubriation material component includes 35 parts of liquid paraffin, 18 parts of fluorographite, 13 parts of palmitoleic acid, lignin carbon in parts by weight
11 parts of hydrochlorate, 18 parts of dimethicone, 9 parts of isopropanol, 18 parts of SIMMONDSIA CHINENSIS SEED OIL, 8 parts of graphene, 8 parts of coconut oil alkanolamide, three
Red 10 parts of oil.
The preparation technology of the present embodiment comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Embodiment five:
Lubriation material component includes 30 parts of liquid paraffin, 15 parts of fluorographite, 10 parts of palmitoleic acid, lignin carbon in parts by weight
8 parts of hydrochlorate, 15 parts of dimethicone, 7 parts of isopropanol, 15 parts of SIMMONDSIA CHINENSIS SEED OIL, 7 parts of graphene, 6 parts of coconut oil alkanolamide, three
Red 8 parts of oil.
The preparation technology of the present embodiment comprises the following steps:
A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl
Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;
B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;
C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.
Preparation technology of the present invention is simple, and obtained lubriation material greasy property is good, improves the service life of plant equipment, drop
Low production cost, economize on resources;Wherein, SIMMONDSIA CHINENSIS SEED OIL, the three red oil added in the present invention can increase lubricant effect;Addition
Fluorographite can increase the abrasion resistance of lubriation material;The dimethicone of addition, it can prevent lubriation material from aoxidizing
Phenomenon.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. composite solid lubricant material, it is characterised in that:Lubriation material component includes liquid paraffin 20-40 in parts by weight Part, fluorographite 10-20 parts, palmitoleic acid 5-15 parts, lignin carbonate 4-12 parts, dimethicone 10-20 parts, isopropanol 4-10 parts, SIMMONDSIA CHINENSIS SEED OIL 10-20 parts, graphene 4-9 parts, coconut oil alkanolamide 3-9 parts, three red oily 4-12 parts.
- A kind of 2. composite solid lubricant material according to claim 1, it is characterised in that:Lubriation material component preferably into Distribution ratio includes 30 parts of liquid paraffin, 15 parts of fluorographite, 10 parts of palmitoleic acid, 8 parts of lignin carbonate, dimethicone 15 Part, 7 parts of isopropanol, 15 parts of SIMMONDSIA CHINENSIS SEED OIL, 7 parts of graphene, 6 parts of coconut oil alkanolamide, three red 8 parts of oil.
- 3. realize a kind of preparation technology of composite solid lubricant material described in claim 1, it is characterised in that:Its preparation technology Comprise the following steps:A, by palmitoleic acid, lignin carbonate, dimethicone, isopropanol, SIMMONDSIA CHINENSIS SEED OIL, graphene, coconut oil alkanol acyl Add in kneading machine and be kneaded after amine, three red oil mixing, melting temperature is 60 DEG C, time 10min, obtains mixture A;B, liquid paraffin, fluorographite are added in mixture A, 20min is stirred after mixing at normal temperatures, obtains mixture B;C, mixture B is stood into 7h at normal temperatures, that is, obtains solid lubricant.