CN107673746A - 一种高强度陶瓷 - Google Patents
一种高强度陶瓷 Download PDFInfo
- Publication number
- CN107673746A CN107673746A CN201711043485.2A CN201711043485A CN107673746A CN 107673746 A CN107673746 A CN 107673746A CN 201711043485 A CN201711043485 A CN 201711043485A CN 107673746 A CN107673746 A CN 107673746A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- raw material
- barite
- zircon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种高强度陶瓷,包括重量份的原料:黄砂70‑90重量份、重晶石10‑15重量份、白云石13‑18重量份、火山岩8‑17重量份、锆英石35‑55重量份、硅粉24‑26重量份、磷酸三钙1‑3重量份、碳酸钡2.5‑3.6重量份、纳米碳化硅0.9‑2.7重量份、纳米氧化铝8‑11重量份。本发明的有益效果是,在现有技术的基础上,提供一种高强度陶瓷。
Description
技术领域
本发明涉及材料领域,具体的说,涉及一种高强度陶瓷。
背景技术
陶瓷是由粘土、石英砂以及其他无机非金属原料,经配料、球磨、制粉、成型、烧结等工艺生产的板状或块状制品,广泛应用于装饰与保护建筑物、构筑物的墙面和地面。随着房地产业的迅速发展,使得瓷砖的生产和消费都获得了较大的发展,同时对陶瓷的性能要求也越来越高。然而目前市场上的陶瓷大多强度低,不够坚硬,易碎,使用性差,无法满足市场需求。
由此,如何得到一种高强度陶瓷是目前陶瓷产业急需解决的问题。
发明内容
本发明所要解决的技术问题是提供一种高强度陶瓷。
本发明解决上述技术问题的技术方案如下:
一种高强度陶瓷,包括重量份的原料:黄砂70-90重量份、重晶石10-15重量份、白云石13-18重量份、火山岩8-17重量份、锆英石35-55重量份、硅粉24-26重量份、磷酸三钙1-3重量份、碳酸钡2.5-3.6重量份、纳米碳化硅0.9-2.7重量份、纳米氧化铝8-11重量份。
本发明的有益效果是:在现有技术的基础上,提供一种高强度陶瓷。
在上述技术方案的基础上,本发明还可以做如下改进:
进一步,其包括重量份的原料:黄砂70重量份、重晶石10重量份、白云石13重量份、火山岩8重量份、锆英石35重量份、硅粉24重量份、磷酸三钙1重量份、碳酸钡2.5重量份、纳米碳化硅0.9重量份、纳米氧化铝8重量份。
进一步,其包括重量份的原料:黄砂90重量份、重晶石15重量份、白云石18重量份、火山岩17重量份、锆英石55重量份、硅粉26重量份、磷酸三钙3重量份、碳酸钡3.6重量份、纳米碳化硅2.7重量份、纳米氧化铝11重量份。
进一步,其包括重量份的原料:黄砂80重量份、重晶石12重量份、白云石15重量份、火山岩13重量份、锆英石42重量份、硅粉25重量份、磷酸三钙2.3重量份、碳酸钡3.2重量份、纳米碳化硅1.9重量份、纳米氧化铝9重量份。
进一步,其制作方法包括:
(1)按质量比称取原料,混合均匀,粉碎,湿法球磨5-10h,烘干后过150-200目筛,待用;
(2)将上述步骤(1)制得的粉料中加入质量为混合料重量2-4%的水玻璃混合20-30min,静置10-15h,所述水玻璃的固含量为35%;
(3)将步骤(2)混合均匀的粉料送到成型机在60-80MPa下压制成型,然后将压制好的砖坯送至干燥窑中干燥至含水量为3-5%的干坯;
(4)将干坯以5-10℃/min的速率升温至1160-1220℃,保温2-3h,再以10-15℃/min的速率降温至750-850℃,保温0.5-1h,冷却至常温,经磨边、包装即得成品。
具体实施方式
以下结合实施例对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
一种高强度陶瓷,包括重量份的原料:黄砂70重量份、重晶石10重量份、白云石13重量份、火山岩8重量份、锆英石35重量份、硅粉24重量份、磷酸三钙1重量份、碳酸钡2.5重量份、纳米碳化硅0.9重量份、纳米氧化铝8重量份。
其制作方法包括:
(1)按质量比称取原料,混合均匀,粉碎,湿法球磨5h,烘干后过150目筛,待用;
(2)将上述步骤(1)制得的粉料中加入质量为混合料重量2%的水玻璃混合20min,静置10h,所述水玻璃的固含量为35%;
(3)将步骤(2)混合均匀的粉料送到成型机在60MPa下压制成型,然后将压制好的砖坯送至干燥窑中干燥至含水量为3%的干坯;
(4)将干坯以5℃/min的速率升温至1160℃,保温3h,再以10℃/min的速率降温至750℃,保温0.5h,冷却至常温,经磨边、包装即得成品。
实施例2
一种高强度陶瓷,包括重量份的原料:黄砂90重量份、重晶石15重量份、白云石18重量份、火山岩17重量份、锆英石55重量份、硅粉26重量份、磷酸三钙3重量份、碳酸钡3.6重量份、纳米碳化硅2.7重量份、纳米氧化铝11重量份。
其制作方法包括:
(1)按质量比称取原料,混合均匀,粉碎,湿法球磨10h,烘干后过200目筛,待用;
(2)将上述步骤(1)制得的粉料中加入质量为混合料重量4%的水玻璃混合30min,静置15h,所述水玻璃的固含量为35%;
(3)将步骤(2)混合均匀的粉料送到成型机在80MPa下压制成型,然后将压制好的砖坯送至干燥窑中干燥至含水量为5%的干坯;
(4)将干坯以10℃/min的速率升温至1220℃,保温3h,再以15℃/min的速率降温至850℃,保温1h,冷却至常温,经磨边、包装即得成品。
实施例3
一种高强度陶瓷,包括重量份的原料:黄砂80重量份、重晶石12重量份、白云石15重量份、火山岩13重量份、锆英石42重量份、硅粉25重量份、磷酸三钙2.3重量份、碳酸钡3.2重量份、纳米碳化硅1.9重量份、纳米氧化铝9重量份。
其制作方法包括:
(1)按质量比称取原料,混合均匀,粉碎,湿法球磨10h,烘干后过200目筛,待用;
(2)将上述步骤(1)制得的粉料中加入质量为混合料重量4%的水玻璃混合30min,静置15h,所述水玻璃的固含量为35%;
(3)将步骤(2)混合均匀的粉料送到成型机在80MPa下压制成型,然后将压制好的砖坯送至干燥窑中干燥至含水量为5%的干坯;
(4)将干坯以10℃/min的速率升温至1220℃,保温3h,再以15℃/min的速率降温至850℃,保温1h,冷却至常温,经磨边、包装即得成品。
对比例1
市售普通陶瓷材料。
分别将实施例1-3中得到的样品1-3和对比例中的对比样品1进行性能的测试,测试其破坏强度、断裂模数和吸水率,结果如下表所示。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (5)
1.一种高强度陶瓷,其特征在于,包括重量份的原料:黄砂70-90重量份、重晶石10-15重量份、白云石13-18重量份、火山岩8-17重量份、锆英石35-55重量份、硅粉24-26重量份、磷酸三钙1-3重量份、碳酸钡2.5-3.6重量份、纳米碳化硅0.9-2.7重量份、纳米氧化铝8-11重量份。
2.根据权利要求1所述一种高强度陶瓷,其特征在于,包括重量份的原料:黄砂70重量份、重晶石10重量份、白云石13重量份、火山岩8重量份、锆英石35重量份、硅粉24重量份、磷酸三钙1重量份、碳酸钡2.5重量份、纳米碳化硅0.9重量份、纳米氧化铝8重量份。
3.根据权利要求1所述一种高强度陶瓷,其特征在于,包括重量份的原料:黄砂90重量份、重晶石15重量份、白云石18重量份、火山岩17重量份、锆英石55重量份、硅粉26重量份、磷酸三钙3重量份、碳酸钡3.6重量份、纳米碳化硅2.7重量份、纳米氧化铝11重量份。
4.根据权利要求1所述一种高强度陶瓷,其特征在于,包括重量份的原料:黄砂80重量份、重晶石12重量份、白云石15重量份、火山岩13重量份、锆英石42重量份、硅粉25重量份、磷酸三钙2.3重量份、碳酸钡3.2重量份、纳米碳化硅1.9重量份、纳米氧化铝9重量份。
5.根据权利要求1-4任一所述一种高强度陶瓷,其特征在于,其制作方法包括:
(1)按质量比称取原料,混合均匀,粉碎,湿法球磨5-10h,烘干后过150-200目筛,待用;
(2)将上述步骤(1)制得的粉料中加入质量为混合料重量2-4%的水玻璃混合20-30min,静置10-15h,所述水玻璃的固含量为35%;
(3)将步骤(2)混合均匀的粉料送到成型机在60-80MPa下压制成型,然后将压制好的砖坯送至干燥窑中干燥至含水量为3-5%的干坯;
(4)将干坯以5-10℃/min的速率升温至1160-1220℃,保温2-3h,再以10-15℃/min的速率降温至750-850℃,保温0.5-1h,冷却至常温,经磨边、包装即得成品。