CN107653532A - A kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance and preparation method thereof - Google Patents
A kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance and preparation method thereof Download PDFInfo
- Publication number
- CN107653532A CN107653532A CN201610590548.5A CN201610590548A CN107653532A CN 107653532 A CN107653532 A CN 107653532A CN 201610590548 A CN201610590548 A CN 201610590548A CN 107653532 A CN107653532 A CN 107653532A
- Authority
- CN
- China
- Prior art keywords
- spinning
- environment
- sportswear
- shell
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance and preparation method thereof, the fabric will be modified Profile Polyester Fibre and tencel fiber, Coolplus fiber blends, the moisture permeability of three kinds of fibers is very good, and the performance such as the sucting wet air permeability of the fabric after blending, wrinkle resistance is very good；The environmentally friendly and degradable tencel fiber using preparation process, the environmental-protecting performance of fabric are high；It is a kind of environmentally friendly tencel preparation method using mineral antiseptic；Using special modified polyester fibre processing method, antiseptic is attached to fiber surface, and usage amount substantially reduces；Antiseptic is in fabric preparation process, adhesion-tight；Antiseptic effect is lasting, can play long-term antibacterial, deodorization effect.
Description
Technical field
The present invention relates to functional form garment material field, is moved more particularly to a kind of environment-friendly type of highly hygroscopic perspiration discharging performance
Take fabric and preparation method thereof.
Background technology
For polyester fiber as most widely used chemical fibre, it has good fibre-forming performance and mechanical performance, intensity
High, fast light, heat-resisting and resistance to acids and bases is good, has good processability and Yi Fangxing, pure can spin, blending and intertexture.Polyester fabric
Washable and wearable, ironing and anti-crease, clothes, home textile, decoration and product with etc. field be widely used.However, polyester fiber is also deposited
Hygroscopicity is poor, absorbing sweat, dress do not have the shortcomings that feeling of oppression and heat, anti-static ability difference and easily stain dust fabric, therefore make significantly
The about application and development of polyester fiber.To improve the snugness of fit of polyester fiber, the application added value of polyester fiber is improved,
The improvement of chemically or physically aspect, and then the moisture absorbing and sweat releasing property that endowing terylene fiber is higher are typically carried out to polyester fiber, is carried
High dacron wearing comfort.
With requirement more and more higher of the people to fabric, the other performance of polyester fiber is also gradually valued by people,
Especially possess the chemical fibre product of antibacterial, deodorization performance, there are good market prospects.
The content of the invention
In view of this, it is an object of the invention to provide a kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance and its system
Preparation Method.
A kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, including following main component：
Modified polyester fibre 40-60%
Tencel fiber 25-45%
Coolplus fibers 10-20%.
Preferably, described modified polyester fibre is modified Profile Polyester Fibre.
Preferably, described modification Profile Polyester Fibre is trefoil fiber.
A kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, is carried out as steps described below：
A, shell raw material is placed in immersion 12-16 hours in 10% sodium hydrate aqueous solution, rinsed after taking-up with water to neutrality,
Then plus slurry is made in the water stirring equivalent to the shell weight 40-80% of exfoliating, and carries out wet grinding to gained slurry,
Sea shell micropowder slurry is made；
B, the silver-colored presoma that will be equivalent to the shell weight 0.1-0.3% of exfoliating is added in step A sea shell micropowder slurry,
8-12 hours are stirred at a temperature of 50-70 DEG C, obtain being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：Spinning temperature 320-340
DEG C, spinning speed 1000-1100m/min；Described spinning is sprayed at spinning nozzle, will carry silver-colored oyster shell whiting antiseptic spray
It is coated in spinning surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3-4 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance.
Preferably, the particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm.
Shell is the biogenic mineral material that a kind of biomineralization is formed, and calcium carbonate accounts for 95% in its chemical composition,
Remaining about 5% is the organic substrate such as protein, chitin.Because calcium carbonate crystal deposits in shell pearl layer in order, formed more
The orderly nanometer ultra microstructure of level, the nano composite material that shell is made up of calcium carbonate and large biological molecule, through appropriate alkali
Liquid processing and Mechanosensitive channels, are destroyed some original keys of large biological molecule interchain and group, surface exposes greatly
Various active function groups such as amino, amide groups, carboxyl, hydroxyl etc. of amount.These active function groups there is provided silver ion load
Place, meanwhile, the swelling degraded of few fibers albumen, chitin is converted into chitosan, and chitosan itself has anti-microbial property.
Coolplus fibers, fiber surface carry numerous micropores and micro-grooves, can produce capillary effect, can be by people
The sweat and moisture of body skin surface, outer fabric layer, Quick diffusing moisture and sweat are absorbed to quickly, human body surface is kept dry
It is refreshing, refrigerant, comfortable, have the function that to adjust body temperature.Fibre section is "+" type, and surface is micro-grooves, at the same add it is special
Condensate utilizes the deliquescent difference of the material, assigns fiber countless trickle cavities.Pass through capillary caused by these micro-grooves
Phenomenon, the moisture of skin surface discharge is excreted with sweat via effect, moments such as wicking diffusion, transmission.Coolplus
Fiber applications are extensive, can pure spinning, also can with cotton, hair, silk, fiber crops and all kinds of chemical fibre blending or intertexture, can tatting, be also knitted.Both
Possess such as cotton, fiber crops, silk, the sense of touch of wool natural fiber, and surmounted natural fiber, no matter Coolplus fabrics are in rapid-curing cutback
Natural cotton is superior in property, gas permeability, preventing sheding tintability, shrink resistance and wrinkle resistance.
For the pulp that tencel fiber is formed after being smashed to pieces using reproducible bamboo and wood etc. as raw material, advanced technique causes its solvent
The rate of recovery is up to 99.7%, not only energy-saving and environmental protection, and sustainable development.Made of this fiber clothing not only gloss from
So, slippery feel, intensity are high, substantially shrink-proof, and penetrability, good permeability, good with wool blended fabric effects.My god
Silk fiber is a hundred per cent natural material, plus the manufacturing process of environmental protection, allows life style using conservation of nature environment as this, complete
The full demand for catering to modern consumer, and it is green, it can be rated as the green fiber of 21 century.
Silver-colored oyster shell whiting antiseptic is carried in the present invention to reference in Zhejiang University invention disclosed patent CN 102939958A
Preparation method, and therefrom preferably go out suitable silver ion addition.
In the preparation process of the whole antibiotic polyester fiber of the present invention, silver-colored oyster shell whiting antiseptic will be carried and be added to polyester fiber
Method and traditional method it is entirely different, traditional method is that additive is added into congruent melting in polyester slice, but this method
The addition of additive is larger, and antiseptic is painted on into fiber surface in the present invention, with the rapid drop of fiber temperature
Low, antiseptic is firmly attached to fiber surface；The main component for carrying silver-colored oyster shell whiting antiseptic is calcium carbonate, and calcium carbonate is a kind of
Acid is soluble in, is not readily dissolved in the compound of alkali, and under terylene is in neutral and alkalescence condition during the follow-up weaving, therefore
Antiseptic adhesion effect is lasting；Only under conditions of consumer puts on clothes and perspires, oyster shell whiting of the sweat to fiber surface
Dissolved, the antibacterial action of silver ion just can significantly be brought into play, play good antibacterial, deodorization effect.
If additive is added into congruent melting technique in polyester slice using traditional, resist inside polyester fiber containing substantial amounts of
Microbial inoculum, these antiseptics will waste completely, can not play practical function.
A kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance provided by the present invention, have as follows
Advantage：
1st, Profile Polyester Fibre will be modified and tencel fiber, Coolplus fiber blends, the moisture permeability of three kinds of fibers is equal
Very good, the performance such as the gas permeability of the fabric after blending, wrinkle resistance is very good；
2nd, the tencel fiber environmentally friendly and degradable using preparation process, the environmental-protecting performance of fabric are high；
3rd, it is a kind of environmentally friendly tencel preparation method using mineral antiseptic；
4th, fiber surface is attached to using special modified polyester fibre processing method, antiseptic, usage amount substantially reduces；Antibacterial
Agent is in fabric preparation process, adhesion-tight；Antiseptic effect is lasting, can play long-term antibacterial, deodorization effect.
Embodiment
Embodiment 1
A kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, is carried out as steps described below：
A, shell raw material is placed in 10% sodium hydrate aqueous solution and soaked 14 hours, rinsed after taking-up with water to neutrality, then
Add the water of the shell weight 60% equivalent to exfoliating to stir and slurry is made, and wet grinding is carried out to gained slurry, shellfish is made
Shell micro mist slurry；
B, the silver-colored presoma that will be equivalent to the shell weight 0.2% of exfoliating is added in step A sea shell micropowder slurry, 65
It is stirred at a temperature of DEG C 10 hours, obtains being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：330 DEG C of spinning temperature,
Spinning speed is 1050m/min；Described spinning is sprayed at spinning nozzle, will be carried silver-colored oyster shell whiting antiseptic and is sprayed on spinning
Surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance.
The particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm.
In the environment-friendly type fabric for sportswear of described highly hygroscopic perspiration discharging performance, the addition of modified polyester fibre is 80%,
The addition of coolplus fibers is 20%.
Embodiment 2
A kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, is carried out as steps described below：
A, shell raw material is placed in 10% sodium hydrate aqueous solution and soaked 16 hours, rinsed after taking-up with water to neutrality, then
Add the water of the shell weight 40% equivalent to exfoliating to stir and slurry is made, and wet grinding is carried out to gained slurry, shellfish is made
Shell micro mist slurry；
B, the silver-colored presoma that will be equivalent to the shell weight 0.3% of exfoliating is added in step A sea shell micropowder slurry, 50
It is stirred at a temperature of DEG C 12 hours, obtains being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：320 DEG C of spinning temperature,
Spinning speed is 1100m/min；Described spinning is sprayed at spinning nozzle, will be carried silver-colored oyster shell whiting antiseptic and is sprayed on spinning
Surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance.
The particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm.
Described modified polyester fibre is modified dacron trefoil fiber；
In the environment-friendly type fabric for sportswear of described highly hygroscopic perspiration discharging performance, the addition of modified polyester fibre is 60%, and tencel is fine
The addition of dimension is that the addition of 25%, coolplus fibers is 15%.
Embodiment 3
A kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, is carried out as steps described below：
A, shell raw material is placed in 10% sodium hydrate aqueous solution and soaked 12 hours, rinsed after taking-up with water to neutrality, then
Add the water of the shell weight 80% equivalent to exfoliating to stir and slurry is made, and wet grinding is carried out to gained slurry, shellfish is made
Shell micro mist slurry；
B, the silver-colored presoma that will be equivalent to the shell weight 0.1% of exfoliating is added in step A sea shell micropowder slurry, 70
It is stirred at a temperature of DEG C 8 hours, obtains being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：340 DEG C of spinning temperature,
Spinning speed is 1000m/min；Described spinning is sprayed at spinning nozzle, will be carried silver-colored oyster shell whiting antiseptic and is sprayed on spinning
Surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 4 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance.
The particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm.
Described modified polyester fibre is modified dacron trefoil fiber；
In the environment-friendly type fabric for sportswear of described highly hygroscopic perspiration discharging performance, the addition of modified polyester fibre is 40%, and tencel is fine
The addition of dimension is that the addition of 40%, coolplus fibers is 20%.
Embodiment 1-3 fabric is subjected to anti-microbial property and takes performance test, obtains following data.
Table 1：The bacteriostasis property (%) of fabric:
| Staphylococcus aureus | Candida albicans | Escherichia coli | |
| Embodiment 1 | 99 | 99 | 98 |
| Embodiment 2 | 99 | 98 | 97 |
| Embodiment 3 | 99 | 97 | 98 |
Table 2：The wearability of fabric：
| Dampness RET RET ㎡ K/W | Thermal resistance RCT RCT ㎡ K/W | Static drape degree % | Dynamic pendency degree % | |
| Embodiment 1 | 7.2 | 0.07 | 43 | 44 |
| Embodiment 2 | 7.1 | 0.07 | 44 | 44 |
| Embodiment 3 | 7.3 | 0.07 | 43 | 45 |
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto, it is any
Those familiar with the art the invention discloses technical scope in, technique according to the invention scheme and its invention
Design is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, it is characterised in that including following main component：
Modified polyester fibre 40-60%
Tencel fiber 25-45%
Coolplus fibers 10-20%.
2. the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance as claimed in claim 1, it is characterised in that described modification
Polyester fiber is modified Profile Polyester Fibre.
3. the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance as claimed in claim 2, it is characterised in that described modification
Profile Polyester Fibre is trefoil fiber.
4. a kind of preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance, it is characterised in that as steps described below
Carry out：
A, shell raw material is placed in immersion 12-16 hours in 10% sodium hydrate aqueous solution, rinsed after taking-up with water to neutrality,
Then plus slurry is made in the water stirring equivalent to the shell weight 40-80% of exfoliating, and carries out wet grinding to gained slurry,
Sea shell micropowder slurry is made；
B, the silver-colored presoma that will be equivalent to the shell weight 0.1-0.3% of exfoliating is added in step A sea shell micropowder slurry,
8-12 hours are stirred at a temperature of 50-70 DEG C, obtain being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：Spinning temperature 320-340
DEG C, spinning speed 1000-1100m/min；Described spinning is sprayed at spinning nozzle, will carry silver-colored oyster shell whiting antiseptic spray
It is coated in spinning surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3-4 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance.
5. the preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance as claimed in claim 1, it is characterised in that
The particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm.
6. the preparation method of the environment-friendly type fabric for sportswear of highly hygroscopic perspiration discharging performance as claimed in claim 1, it is characterised in that
Carry out as steps described below：
A, shell raw material is placed in 10% sodium hydrate aqueous solution and soaked 14 hours, rinsed after taking-up with water to neutrality, then
Add the water of the shell weight 60% equivalent to exfoliating to stir and slurry is made, and wet grinding is carried out to gained slurry, shellfish is made
Shell micro mist slurry；
B, the silver-colored presoma that will be equivalent to the shell weight 0.2% of exfoliating is added in step A sea shell micropowder slurry, 65
It is stirred at a temperature of DEG C 10 hours, obtains being loaded with the sea shell micropowder slurry of silver ion；
C, the sea shell micropowder slurry for being loaded with silver ion is subjected to press filtration, drying and crushing and is filtrated to get the silver-colored oyster shell whiting antibacterial of load
Agent；
D, by polyester slice, as-spun fibre is made in high speed spinning on spinning-drawing machine, and concrete technology condition is：330 DEG C of spinning temperature,
Spinning speed is 1050m/min；Described spinning is sprayed at spinning nozzle, will be carried silver-colored oyster shell whiting antiseptic and is sprayed on spinning
Surface；
E, as-spun fibre is shaped using parallel drafting machine, you can obtain modified polyester fibre, drafting multiple is 3 times；
F, modified polyester fibre, tencel fiber and coolplus fibers are subjected to blending, dyeing and arrangement, obtain described high suction
The environment-friendly type fabric for sportswear of wet perspiration discharging performance；
The particle diameter of the described silver-colored oyster shell whiting antiseptic of load is 50-200nm；
Described modified polyester fibre is modified dacron trefoil fiber；The environment-friendly type gym suit of described highly hygroscopic perspiration discharging performance
In fabric, the addition of modified polyester fibre is 50%, and the addition of tencel fiber is for the addition of 30%, coolplus fibers
20%。