CN107641879A - Sheet fabric and preparation method thereof - Google Patents
Sheet fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107641879A CN107641879A CN201710907833.XA CN201710907833A CN107641879A CN 107641879 A CN107641879 A CN 107641879A CN 201710907833 A CN201710907833 A CN 201710907833A CN 107641879 A CN107641879 A CN 107641879A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- cotton
- fibre
- sheet fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of sheet fabric and preparation method thereof, the parts by weight proportioning of each raw material of the sheet fabric is：2 16 parts of regenerated fiber, 3 15 parts of linen-cotton, 4 10 parts of synthetic fibers, 38 parts of bamboo fibre, 47 parts of cotton fiber, 38 parts of wool fiber, 36 parts of flax fiber, 28 parts of silk, 28 parts of polyacrylonitrile fibre, 2 16 parts of polyvinyl chloride fibre, 37 parts of tencel fiber, 48 parts of polyfluoroolefin fibre.Service life length of the present invention, has excellent color fastness, it is not easy to fade, cost is low.
Description
Technical field
The present invention relates to a kind of fabric and preparation method thereof, in particular it relates to a kind of sheet fabric and preparation method thereof.
Background technology
Sheet fabric is classified largely into pure cotton, terylene, blending in current market, and these three are more commonplace.These three
In sheet cloth fabric, sheet the most comfortable of pure cotton is also most ventilative, so most of families are when sheeting is selected, mostly all
The sheet of pure cotton can be selected.Pure cotton sheet belongs to most economical economical.The service life of existing pure cotton sheet fabric is short, easily takes off
Color.
The content of the invention
For in the prior art the defects of, the technical problem to be solved in the present invention is to provide a kind of sheet fabric and its preparation
Method, its service life length, has excellent color fastness, it is not easy to fade, cost is low.
According to an aspect of the present invention, there is provided a kind of sheet fabric, it is characterised in that each raw material of the sheet fabric
Parts by weight proportioning be：Regenerated fiber 2-16 parts, linen-cotton 3-15 parts, synthetic fibers 4-10 parts, bamboo fibre 3-8 parts, cotton fiber
4-7 parts, wool fiber 3-8 parts, flax fiber 3-6 parts, silk 2-8 parts, polyacrylonitrile fibre 2-8 parts, polyvinyl chloride fibre 2-
16 parts, tencel fiber 3-7 parts, polyfluoroolefin fibre 4-8 parts.
Preferably, the synthetic fibers are terylene or spandex.
Preferably, the bamboo fibre fabric has warp and weft intertexture blending to form.
The present invention also provides a kind of preparation method of sheet fabric, it is characterised in that comprises the following steps：Will regeneration fibre
Dimension, linen-cotton, synthetic fibers, bamboo fibre, cotton fiber, wool fiber, flax fiber, silk, polyacrylonitrile fibre, polyvinyl chloride are fine
Dimension, tencel fiber, polyfluoroolefin fibre mixing, then form sliver, finally by network by scutching cotton, cotton carding, combing, drafting
Cylinder, warping, sizing, pass, weave, being wound into yardage roll, finally cut and shape for forming sheet.
Compared with prior art, the present invention has following beneficial effect：Service life length of the present invention, has excellent color
Fastness, it is not easy to fade, cost is low, and elasticity is good.
Embodiment
With reference to specific embodiment, the present invention is described in detail.Following examples will be helpful to the technology of this area
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this area
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection domain.
The parts by weight of each raw material of sheet fabric of the present invention match：Regenerated fiber 2-16 parts, linen-cotton 3-15 parts, synthesis
Fiber 4-10 parts, bamboo fibre 3-8 parts, cotton fiber 4-7 parts, wool fiber 3-8 parts, flax fiber 3-6 parts, silk 2-8 parts, poly- third
Alkene nitrile fiber 2-8 parts, polyvinyl chloride fibre 2-16 parts, tencel fiber 3-7 parts, polyfluoroolefin fibre 4-8 parts.
Synthetic fibers can be terylene or spandex, so reduce cost.
The bamboo fibre fabric has warp and weft intertexture blending to form, and so increases intensity.
Regenerated fiber is soft, good luster, hygroscopicity, good air permeability, has environmental-protecting performance, in addition in regenerated fiber
Containing protein, thus it is good with skin affinity, there is certain anti-microbial property.The convenient dyeing of linen-cotton and raising intensity.Synthesis is fine
It is high to tie up intensity, light, quick-drying washable, elasticity is good, is not afraid of mould moth.Bamboo fiber have good gas permeability, instant water absorption, compared with
The characteristic such as strong wearability and good dyeability, there is natural antibacterial, antibacterial, except mite, deodorization and anti-ultraviolet function.Cotton is fine
The intensity of dimension is high, and wrinkle resistance is good.Wool fiber improves warmth retention property.Flax fiber has temperature adjustment, antiallergy, antistatic, antibacterial
Function.Silk is frivolous, reduces weight.Polyacrylonitrile fibre has soft, bulk, easy dye, bright in colour, fast light, antibacterial, is not afraid of
The advantages that damaging by worms.Polyvinyl chloride fibre is fire retardant, warming, sun-proof, wear-resisting, anti-corrosion and moth-resistant, and elasticity is also fine, and warmth retention property is good.My god
Silk fiber has good hygroscopicity, comfortableness, drapability and a stiffness, and dyeability is good.Polyfluoroolefin fibre can improve anti-
Combustion ability.
The preparation method of sheet fabric of the present invention comprises the following steps：By regenerated fiber, linen-cotton, synthetic fibers, bamboo fibre,
Cotton fiber, wool fiber, flax fiber, silk, polyacrylonitrile fibre, polyvinyl chloride fibre, tencel fiber, polyfluoroolefin fibre
Mixing, sliver is then formed by scutching cotton, cotton carding, combing, drafting, finally by winder, warping, sizing, pass, weave, roll up
Yardage roll is coiled into, finally cuts and shapes for forming sheet.
Embodiment one
The parts by weight of each raw material of sheet fabric of the present invention match：2 parts of regenerated fiber, 3 parts of linen-cotton, 4 parts of synthetic fibers, bamboo
3 parts of fiber, 4 parts of cotton fiber, 8 parts of wool fiber, 6 parts of flax fiber, 8 parts of silk, 8 parts of polyacrylonitrile fibre, polyvinyl chloride are fine
16 parts of dimension, 7 parts of tencel fiber, 8 parts of polyfluoroolefin fibre.
Embodiment two
The parts by weight of each raw material of sheet fabric of the present invention match：16 parts of regenerated fiber, 15 parts of linen-cotton, synthetic fibers 10
Part, 8 parts of bamboo fibre, 7 parts of cotton fiber, 3 parts of wool fiber, 3 parts of flax fiber, 2 parts of silk, 2 parts of polyacrylonitrile fibre, polychlorostyrene second
2 parts of alkene fiber, 3 parts of tencel fiber, 4 parts of polyfluoroolefin fibre.
Embodiment three
The parts by weight of each raw material of sheet fabric of the present invention match：10 parts of regenerated fiber, 9 parts of linen-cotton, 7 parts of synthetic fibers,
6 parts of bamboo fibre, 5 parts of cotton fiber, 5 parts of wool fiber, 4 parts of flax fiber, 5 parts of silk, 5 parts of polyacrylonitrile fibre, polyvinyl chloride
11 parts of fiber, 5 parts of tencel fiber, 6 parts of polyfluoroolefin fibre.
In summary, service life length of the present invention, has excellent color fastness, it is not easy to fades, cost is low, and elasticity is good.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (4)
1. a kind of sheet fabric, it is characterised in that the parts by weight of each raw material of the sheet fabric, which match, is：Regenerated fiber 2-
16 parts, linen-cotton 3-15 parts, synthetic fibers 4-10 parts, bamboo fibre 3-8 parts, cotton fiber 4-7 parts, wool fiber 3-8 parts, flax fiber
3-6 parts, silk 2-8 parts, polyacrylonitrile fibre 2-8 parts, polyvinyl chloride fibre 2-16 parts, tencel fiber 3-7 parts, poly- fluoroolefins are fine
Tie up 4-8 parts.
2. sheet fabric according to claim 1, it is characterised in that the synthetic fibers are terylene or spandex.
3. sheet fabric according to claim 1, it is characterised in that it is mixed that the bamboo fibre fabric has warp and weft to interweave
Spinning forms.
4. a kind of preparation method of sheet fabric, it is characterised in that comprise the following steps：Regenerated fiber, linen-cotton, synthesis is fine
It is dimension, bamboo fibre, cotton fiber, wool fiber, flax fiber, silk, polyacrylonitrile fibre, polyvinyl chloride fibre, tencel fiber, poly-
Fluoroolefins fiber mixes, and then forms sliver by scutching cotton, cotton carding, combing, drafting, finally by winder, warping, sizing, wears
Through, weaving, be wound into yardage roll, finally cut and shape for forming sheet.