CN107641432A - One kind is used for new rub resistance non-skid coating in ships deck and preparation method thereof - Google Patents
One kind is used for new rub resistance non-skid coating in ships deck and preparation method thereof Download PDFInfo
- Publication number
- CN107641432A CN107641432A CN201711082303.2A CN201711082303A CN107641432A CN 107641432 A CN107641432 A CN 107641432A CN 201711082303 A CN201711082303 A CN 201711082303A CN 107641432 A CN107641432 A CN 107641432A
- Authority
- CN
- China
- Prior art keywords
- parts
- rub resistance
- skid coating
- resistance non
- ships deck
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides one kind and is used for the new rub resistance non-skid coating in ships deck, is made up of following components by mass fraction：30 45 parts of epoxy resin；10 15 parts of titanium dioxide；Anti-skidding 10 20 parts of filler；10 15 parts of metal zinc metal sheet；13 parts of aluminium powder；0.2 1 parts of Ricinate；0.2 0.5 parts of defoamer；5 10 parts of bentonite；10 15 parts of talcum powder；5 10 parts of kaolin；0.2 0.5 parts of diluent；0.5 1 parts of emulsifying agent；0.2 0.5 parts of coupling agent；Epoxy resin：EP curing agent=5:1.5‑2；60 90 parts of absolute ethyl alcohol.Beneficial effects of the present invention are：This is used for the new rub resistance non-skid coating in ships deck, and wherein metal zinc metal sheet, aluminium powder have in use forms galvanic couple pair with deck, preferential corrosion, prevents deck from corroding so as to play.
Description
Technical field
The present invention is a kind of high-performance coating for military field, is mainly concerned with a kind of new resistance to for ships deck
Rub non-skid coating and preparation method thereof.
Background technology
Due to all personnel, aircraft, vehicle and the equipment operation all on clamping plate on aircraft carrier, so all being applied on its each laminated plank
There is Wear-resistant skid-proof coating.Compared with traditional non-skid coating, increasing can be reached by changing the coefficient of friction on substrate to be coated surface
Big frictional force, the purpose for improving skid resistance, so as to effectively prevent other articles such as personnel, vehicle and aircraft from sliding above deck
It is dynamic.Conventional inorganic matter antilubricant has silica sand, diamond dust, haydite etc., although coefficient of friction can reach requirement, the later stage holds
Easy to wear to come off, service life is short.Conventional also has rubber particles, although with good consistency and elasticity, crocking resistance
Preferably, but price is higher, is not suitable for a large amount of productions.The non-skid coating suitable for ships deck is not only existed including attachment at present
Power and the problems such as weatherability is poor, work progress pollution environment, and traditional coating use layered coating, it is necessary to priming paint parch after
Finish paint can be coated, not only man-hour is longer, and increases the weight of aircraft carrier.
The content of the invention
The purpose of the present invention is to be directed to traditional non-skid coating, there is provided one kind is used for the anti-skidding painting of the new rub resistance in ships deck
Material, solves the problems such as traditional coating adhesive force and weatherability are poor, work progress pollutes environment.
The present invention is achieved by the following technical solutions：
One kind is used for the new rub resistance non-skid coating in ships deck, is made up of following components by mass fraction：Epoxy resin 30-45
Part；Titanium dioxide 10-15 parts；Anti-skidding filler 10-20 parts；Metal zinc metal sheet 10-15 parts；Aluminium powder 1-3 parts；Ricinate 0.2-1 parts；
Defoamer 0.2-0.5 parts；Bentonite 5-10 parts；Talcum powder 10-15 parts；Kaolin 5-10 parts；Diluent 0.2-0.5 parts；Emulsification
Agent 0.5-1 parts；Coupling agent 0.2-0.5 parts；Epoxy resin：EP curing agent 5:1.5-2；Absolute ethyl alcohol 60-90 parts.
Wherein, described anti-skidding filler is 170 mesh aluminum oxide and titanium dioxide powdery mixture, and aluminum oxide:Titanium dioxide
Titanium=1:1.
Wherein, described bentonite is 1000 mesh.
Wherein, described talcum powder is 3000 mesh.
Wherein, described diluent is epoxy active diluent.
A kind of preparation method for the new rub resistance non-skid coating in ships deck, comprise the following steps：By above-mentioned each group
Weigh respectively, epoxy resin and absolute ethyl alcohol are mixed at a certain temperature, stirred, the solution until becoming transparence,
Then anti-skidding filler, titanium dioxide, talcum powder, bentonite, kaolin, metal zinc metal sheet, aluminium powder are sequentially added, then adds emulsification
Agent, defoamer, diluent, using magnetic stirrer 15-20 minutes, mixing speed is 400-500 revs/min, is eventually adding
Curing agent, 3-10 minutes are again stirring for using 300-500 revs/min of mixing speed, obtain being used for the new rub resistance in ships deck
Non-skid coating.
Wherein, solidification temperature is 15oC-45oC during described coating roller coat, and the rear curing time of roller coat is 3-5h.
Compared with prior art, beneficial effects of the present invention are：This is used for the new rub resistance non-skid coating in ships deck, its
Middle metal zinc metal sheet, aluminium powder have in use forms galvanic couple pair with deck, preferential corrosion, prevents that deck is rotten so as to play
Erosion.The corrosion product zinc oxide and the granular corrosion product of aluminium oxide granule formed simultaneously has anti-skidding function.The present invention has well
Wearability and skid resistance, impact resistance, adhesive force it is relatively good.
Embodiment
Below by embodiment, the present invention is further described.
Embodiment 1
One kind is used for the new rub resistance non-skid coating in ships deck, is made up of lower component by mass fraction：30 parts of epoxy resin；Titanium
10 parts of white powder；Anti-skidding 10 parts of filler；10 parts of metal zinc metal sheet；1 part of aluminium powder；0.2 part of Ricinate；0.2 part of defoamer；Bentonite
5 parts；10 parts of talcum powder；5 parts of kaolin；0.2 part of diluent；0.5 part of emulsifying agent；0.2 part of coupling agent；Epoxy resin：EP solidifies
Agent is 5:1.5；60 parts of absolute ethyl alcohol.The anti-skidding filler of the present invention is 170 mesh aluminum oxide and the compound composition of titanium dioxide.
A kind of preparation method for the new rub resistance non-skid coating in ships deck, comprise the following steps：By above-mentioned each group
Divide and weigh respectively, epoxy resin and absolute ethyl alcohol are mixed at a certain temperature, stirred, until becoming the molten of transparence
Liquid, anti-skidding filler, titanium dioxide, talcum powder, bentonite, kaolin, metal zinc metal sheet, aluminium powder are then sequentially added, then add breast
Agent, defoamer, diluent, using magnetic stirrer 15 minutes, mixing speed was 400 revs/min, finally according to asphalt mixtures modified by epoxy resin
Fat:EP curing agent=5:1.5 mass ratio adds curing agent, is stirred 3 minutes with 300 revs/min, using roller coat above deck
Brushed, be fully cured after 3 hours, now solidification temperature is 15 DEG C.
Table 1 is a kind of main performance index for the new rub resistance non-skid coating in ships deck in embodiment 1.
The performance indications of the non-skid coating of table 1.
| Sequence number | Project | Index | Measured value |
| 1 | Adhesive force | 2.0 | 2.5 |
| 2 | Pliability | 2 | 2.3 |
| 3 | Impact strength | 50 | 54 |
| 4 | Resistance to salt water（3%Nacl solution）24h | It is unchanged | It is unchanged |
| 5 | Under coefficient of friction static state | 0.5 | 0.67 |
| 6 | Pencil hardness | 2H | 3H |
| 7 | Salt-fog resistant test（14d is carried out in salt fog cabinet） | It is unchanged | It is unchanged |
Embodiment 2
One kind is used for the new rub resistance non-skid coating in ships deck, and following components is formed by mass fraction：45 parts of epoxy resin；Titanium
15 parts of white powder；Anti-skidding 20 parts of filler；15 parts of metal zinc metal sheet；3 parts of aluminium powder；1 part of Ricinate；0.5 part of defoamer；Bentonite 10
Part；15 parts of talcum powder；10 parts of kaolin；0.5 part of diluent；1 part of emulsifying agent；0.5 part of coupling agent；Epoxy resin：EP curing agent
For=5:2；90 parts of absolute ethyl alcohol.
A kind of preparation method for the new rub resistance non-skid coating in ships deck, comprise the following steps：By above-mentioned each group
Divide and weigh respectively, epoxy resin and absolute ethyl alcohol are mixed at a certain temperature, stirred, until becoming the molten of transparence
Liquid, anti-skidding filler, titanium dioxide, talcum powder, bentonite, kaolin, metal zinc metal sheet, aluminium powder are then sequentially added, then add breast
Agent, defoamer, diluent, using magnetic stirrer 20 minutes, mixing speed was 500 revs/min, finally according to asphalt mixtures modified by epoxy resin
Fat：EP curing agent=5:2 mass ratio adds curing agent, is stirred 10 minutes with 500 revs/min, is entered above deck using roller coat
Row is brushed, and is fully cured after 5 hours, and solidification temperature is 45 DEG C.
Table 2 is a kind of main performance index for the new rub resistance non-skid coating in ships deck in embodiment 2.
The main performance index of the non-skid coating of table 2.
| Sequence number | Project | Index | Measured value |
| 1 | Adhesive force | 2.0 | 2.5 |
| 2 | Pliability | 2 | 2.3 |
| 3 | Impact strength | 50 | 54 |
| 4 | Resistance to salt water（3%Nacl solution）24h | It is unchanged | It is unchanged |
| 5 | Under coefficient of friction static state | 0.5 | 0.71 |
| 6 | Pencil hardness | 2H | 3H |
| 7 | Salt-fog resistant test（14d is carried out in salt fog cabinet） | It is unchanged | It is unchanged |
Embodiment 3
One kind is used for the new rub resistance non-skid coating in ships deck, is made up of following component by mass fraction：35 parts of epoxy resin；
13 parts of titanium dioxide；Anti-skidding 15 parts of filler；13 parts of metal zinc metal sheet；2 parts of aluminium powder；0.5 part of Ricinate；0.3 part of defoamer；Swelling
8 parts of soil；12 parts of talcum powder；8 parts of kaolin；0.3 part of diluent；0.7 part of emulsifying agent；0.3 part of coupling agent；Epoxy resin：EP consolidates
Agent is=5:1.7；75 parts of absolute ethyl alcohol.
A kind of preparation method for the new rub resistance non-skid coating in ships deck, comprise the following steps：By above-mentioned each group
Divide and weigh respectively, epoxy resin and absolute ethyl alcohol are mixed at a certain temperature, stirred, until becoming the molten of transparence
Liquid, anti-skidding filler, titanium dioxide, talcum powder, bentonite, kaolin, metal zinc metal sheet, aluminium powder are then sequentially added, then add breast
Agent, defoamer, diluent, using magnetic stirrer 18 minutes, mixing speed was 450 revs/min, finally according to asphalt mixtures modified by epoxy resin
Fat：EP curing agent=5:1.7 mass ratio adds curing agent, is stirred 7 minutes with 400 revs/min, using roller coat above deck
Brushed, be fully cured after 4 hours, solidification temperature is 30 DEG C.
Table 3 is a kind of main performance index for the new rub resistance non-skid coating in ships deck in embodiment 3.
The main performance index of the non-skid coating of table 3.
| Sequence number | Project | Index | Measured value |
| 1 | Adhesive force | 2.0 | 2.5 |
| 2 | Pliability | 2 | 2.3 |
| 3 | Impact strength | 50 | 54 |
| 4 | Resistance to salt water（3%Nacl solution）24h | It is unchanged | It is unchanged |
| 5 | Under coefficient of friction static state | 0.5 | 0.69 |
| 6 | Pencil hardness | 2H | 3H |
| 7 | Salt-fog resistant test（14d is carried out in salt fog cabinet） | It is unchanged | It is unchanged |
In formulation for coating material described above, its experimental result meets the requirement of ships deck composition wear-resisting antiskid, any technology people
Experiment content of the member to more than is changed or is changed to the equivalent examples of equivalent variations, if with this programme inventive technique one
Cause, or without departing from technical scheme content, still fall within the protection domain of technical solution of the present invention.
Claims (7)
1. one kind is used for the new rub resistance non-skid coating in ships deck, it is characterised in that is made up of following components by mass fraction：
Epoxy resin 30-45 parts；Titanium dioxide 10-15 parts；Anti-skidding filler 10-20 parts；Metal zinc metal sheet 10-15 parts；Aluminium powder 1-3 parts；Moistening
Dispersant 0.2-1 parts；Defoamer 0.2-0.5 parts；Bentonite 5-10 parts；Talcum powder 10-15 parts；Kaolin 5-10 parts；Diluent
0.2-0.5 parts；Emulsifying agent 0.5-1 parts；Coupling agent 0.2-0.5 parts；Epoxy resin：EP curing agent 5：1.5-2；Absolute ethyl alcohol 60-
90 parts.
2. one kind according to claim 1 is used for the new rub resistance non-skid coating in ships deck, it is characterised in that described
Anti-skidding filler is 170 mesh aluminum oxide and titanium dioxide powdery mixture, and aluminum oxide：Titanium dioxide=1：1.
3. one kind according to claim 1 is used for the new rub resistance non-skid coating in ships deck, it is characterised in that described
Bentonite is 1000 mesh.
4. one kind according to claim 1 is used for the new rub resistance non-skid coating in ships deck, it is characterised in that described
Talcum powder is 3000 mesh.
5. one kind according to claim 1 is used for the new rub resistance non-skid coating in ships deck, it is characterised in that described
Diluent is epoxy active diluent.
6. a kind of preparation method for the new rub resistance non-skid coating in ships deck, it is characterised in that comprise the following steps：Will
Above-mentioned each component is weighed respectively, and epoxy resin and absolute ethyl alcohol are mixed at a certain temperature, stirred, until becoming transparent
The solution of shape, anti-skidding filler, titanium dioxide, talcum powder, bentonite, kaolin, metal zinc metal sheet, aluminium powder are then sequentially added, then
Emulsifying agent, defoamer, diluent are added, using magnetic stirrer 15-20 minutes, mixing speed is 400-500 revs/min,
Curing agent is eventually adding, 3-10 minutes are again stirring for using 300-500 revs/min of mixing speed, is obtained new for ships deck
Type rub resistance non-skid coating.
7. a kind of preparation method for the new rub resistance non-skid coating in ships deck according to claim 6, its feature
It is, solidification temperature is 15oC-45oC during described coating roller coat, and roller coat rear curing time is 3-5h.