CN107629861A - A kind of Hard-alloy Grinding Fluid - Google Patents
A kind of Hard-alloy Grinding Fluid Download PDFInfo
- Publication number
- CN107629861A CN107629861A CN201610575489.4A CN201610575489A CN107629861A CN 107629861 A CN107629861 A CN 107629861A CN 201610575489 A CN201610575489 A CN 201610575489A CN 107629861 A CN107629861 A CN 107629861A
- Authority
- CN
- China
- Prior art keywords
- hard
- grinding fluid
- alloy grinding
- mixed
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of Hard-alloy Grinding Fluid, based formulas composition is：Formula composition:Special amine 6-18%, inorganic base 2-5%, boric acid 2-7%, decanedioic acid 2-5%, SL-AH 2-4%, polyethers 15-25%, CU250 non-ferrous metal inhibitor 0.2-1.0%, glycerine 5-15%, sedimentation agent 0.3-2.0% and excess water etc..Hard-alloy Grinding Fluid provided by the invention, for the grinding of the high line production wolfram steel rod ring of steel mill, ALP 810 is mainly characterized by extending the service life of skive so that emery wheel loss is reduced to 6 point/ton steel；Effectively suppress cobalt to separate out, long-term use of grinding fluid is non-discolouring, and environmental protection is free from environmental pollution, substantially reduces high line steel production loss.
Description
Technical field
The invention belongs to chemical products field, more particularly to a kind of Hard-alloy Grinding Fluid.
Background technology
The carbon tungsten roller ring of high-speed rod (special steel such as stainless steel, cold-forging steel) production line is repaiied with skive
Whole, in general grinding fluid easily causes cobalt to separate out, and not only pollutes environment, and causes wheel life to shorten, and often repairs emery wheel,
So that emery wheel loss is up to 3 yuan/ton of steel, 1,000,000 tons of the yield of justing think, single one, emery wheel increases 2,940,000；Cobalt is separated out and also led
Cause often to change liquid, added liquid waste processing expense.
The content of the invention
It is an object of the invention in place of overcome the deficiencies in the prior art, there is provided it is a kind of reduce pollution, be unlikely to deteriorate it is hard
The preparation method of matter alloy grinding fluid.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of hard-alloy grinding cuts liquid, and its raw material components and its percentage by weight are respectively：
Moreover, described special amine is diglycolamine.
Moreover, described CU250 non-ferrous metals inhibitor is methyl benzotriazole.
Moreover, described polyethers is polyethers L61.
Moreover, described sedimentation agent is the Staradd MF403 of Shanghai Hong Ze chemical industry.
The preparation method of above-mentioned Hard-alloy Grinding Fluid, its step are：
(1) prepared by alkali：Special amine, inorganic base are mixed, obtain aqueous slkali；
(2) prepared by acid：Boric acid, decanedioic acid are mixed, obtain acid solution；
(3) prepared by emulsion：CU250 non-ferrous metals inhibitor, glycerine, sedimentation agent are put into water and mixed, is stirred,
Obtain emulsion；
(4) acid solution and aqueous slkali are mixed, after reaction to be neutralized terminates, are cooled to water temperature and add emulsion, stirring is equal
It is even, 20 minutes are stood, produces product.
The advantages and positive effects of the present invention are：
Hard-alloy Grinding Fluid provided by the invention, for the grinding of the high line production wolfram steel rod ring of steel mill, ALP-810
It is mainly characterized by extending the service life of skive so that emery wheel loss is reduced to 6 point/ton steel；Effectively suppress cobalt
Separate out, long-term use of grinding fluid is non-discolouring, and environmental protection is free from environmental pollution, substantially reduces high line steel production loss.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not limit
Qualitatively, it is impossible to which protection scope of the present invention is limited with this.
Embodiment 1：
A kind of Hard-alloy Grinding Fluid, its component and weight are respectively：
The preparation method of above-mentioned Hard-alloy Grinding Fluid, its step are：
(1) prepared by alkali：Special amine, inorganic base are mixed, obtain aqueous slkali；
(2) prepared by acid：Boric acid, decanedioic acid are mixed, obtain acid solution；
(3) prepared by emulsion：CU250 non-ferrous metals inhibitor, glycerine, sedimentation agent are put into water and mixed, is stirred,
Obtain emulsion；
(4) acid solution and aqueous slkali are mixed, after reaction to be neutralized terminates, are cooled to water temperature and add emulsion, stirring is equal
It is even, 20 minutes are stood, produces product.
Embodiment 2：
A kind of Hard-alloy Grinding Fluid, its component and weight/mass percentage composition are：
The preparation method of above-mentioned Hard-alloy Grinding Fluid is the same as embodiment 1.
Embodiment 3：
A kind of Hard-alloy Grinding Fluid, its component and weight/mass percentage composition are：
The preparation method of above-mentioned Hard-alloy Grinding Fluid is the same as embodiment 1.
Above-described is only the preferred embodiment of the present invention, it is noted that for one of ordinary skill in the art
For, on the premise of inventive concept is not departed from, various modifications and improvements can be made, these belong to the protection of the present invention
Scope.
Claims (6)
- A kind of 1. Hard-alloy Grinding Fluid, it is characterised in that：Its raw material components and its percentage by weight are respectively：
- 2. Hard-alloy Grinding Fluid according to claim 1, it is characterised in that：Described special amine is diglycolamine.
- 3. Hard-alloy Grinding Fluid according to claim 1, it is characterised in that：Described CU250 non-ferrous metal inhibitor is Methyl benzotriazole.
- 4. Hard-alloy Grinding Fluid according to claim 1, it is characterised in that：Described polyethers is polyethers L61.
- 5. Hard-alloy Grinding Fluid according to claim 1, it is characterised in that：Described sedimentation agent is Shanghai Hong Ze chemical industry Staradd MF403。
- A kind of 6. preparation method of Hard-alloy Grinding Fluid, it is characterised in that：Its step is：(1) prepared by alkali：Special amine, inorganic base are mixed, obtain aqueous slkali；(2) prepared by acid：Boric acid, decanedioic acid are mixed, obtain acid solution；(3) prepared by emulsion：CU250 non-ferrous metals inhibitor, glycerine, sedimentation agent are put into water and mixed, stirs, obtains Emulsion；(4) acid solution and aqueous slkali are mixed, after reaction to be neutralized terminates, are cooled to water temperature and add emulsion, stir, it is quiet Put 20 minutes, produce product.