CN107619677A - 一种富含多种功能基团破乳剂及其制备方法 - Google Patents
一种富含多种功能基团破乳剂及其制备方法 Download PDFInfo
- Publication number
- CN107619677A CN107619677A CN201710895445.4A CN201710895445A CN107619677A CN 107619677 A CN107619677 A CN 107619677A CN 201710895445 A CN201710895445 A CN 201710895445A CN 107619677 A CN107619677 A CN 107619677A
- Authority
- CN
- China
- Prior art keywords
- demulsifier
- parts
- multiple functions
- rich
- functions group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种富含多种功能基团破乳剂及其制备方法,包括以下按重量百分数计的组份:含氢硅油15~40份,烯丙基聚醚10~40份,丙烯酸10~35份,丙烯酸酯15~30份,催化剂0.5~4份、引发剂0.5~6份,链转移剂1~2份,链终止剂1~2份,表面活性剂3~5份,促进剂1~2份以及去离子水10~25份。本发明破乳剂为单组分,HLB可通过合成原料进行调节,具有良好的两亲性,所制备的破乳剂分子结构中同时存在醚键、酯键、羧酸根和引入了硅多种功能基团,能够更好的作用于原油乳状液。所得破乳剂具有用量少、脱水效果好、破乳温度低、脱出水质清、使用范围宽等特点。
Description
技术领域
本发明涉及一种破乳剂,具体涉及一种富含多种功能基团破乳剂及其制备方法。
背景技术
破乳剂是所有油田不可缺少的化学助剂,目前国内使用的以聚醚类破乳剂为主,该类破乳剂大都是以含活泼氢化合物为起始剂,在碱金属催化剂作用下与氧化烯烃进行阴离子开环聚合反应,制得聚氧乙烯聚氧丙烯醚类破乳剂。而许多油田采出的原油中含水率逐年增加,污水回注后原油中的多种残存化学药剂使得乳化原油破乳脱水更为复杂和困难,普通的聚醚类破乳剂脱水效果不理想,不断增加用量仍难以解决问题,导致原油乳状液脱水成本的提高和脱水效果的降低,对原油输送过程和炼油厂进行石油炼制也造成很多不利影响。
发明内容
发明目的:本发明所要解决的技术问题是针对现有技术的不足,提供一种富含多种功能基团破乳剂及其合成方法,该破乳剂为单组分,HLB可通过合成原料进行调节,具有良好的两亲性,所制备的破乳剂分子结构中同时存在醚键、酯键、羧酸根和引入了硅多种功能基团,能够更好的作用于原油乳状液。
为了解决上述技术问题,本发明公开了一种富含多种功能基团破乳剂,包括以下按重量百分数计的组份:含氢硅油15~40份,烯丙基聚醚10~40份,丙烯酸10~35份,丙烯酸酯15~30份,催化剂0.5~4份、引发剂0.5~6份,链转移剂1~2份,链终止剂1~2份,表面活性剂3~5份,促进剂1~2份以及去离子水10~25份。
其中,所述含氢硅油为202高含氢硅油。
其中,所述烯丙基聚醚分子量为800~4000。
其中,所述丙烯酸酯为丙烯酸乙酯和或丙烯酸丁酯。
其中,所述催化剂为氯铂酸。
其中,所述引发剂为过硫酸铵、过硫酸钾中的的一种或它们的混合物。
其中,所述链转移剂为十二烷基硫醇,所述链终止剂为对苯二酚。
其中,所述表面活性剂为十二烷基硫酸钠,增加反应物的接触时间,使反应物能够充分反应;所述促进剂为对甲苯磺酸。
本发明还提供上述富含多种功能基团破乳剂的制备方法,包括如下步骤:
步骤一:将含氢硅油、烯丙基聚醚和催化剂混合,在40~85℃搅拌条件下反应1~4小时得到初产物A。
步骤二:将去离子水、引发剂和表面活性剂混合,通过恒压漏斗依次滴入丙烯酸和丙烯酸酯,在40~95℃搅拌条件下反应1~2.5小时,加入链转移剂和链终止剂同样条件下反应0.5~2小时得到初产物B。
步骤三:将步骤一得到的产物A、步骤二得到的产物B和促进剂混合,在100~145℃搅拌条件下反应2~6小时即得破乳剂。
有益效果:
1、本申请破乳剂为单组分,HLB可通过合成原料进行调节,具有良好的两亲性,所制备的破乳剂分子结构中同时存在醚键、酯键、羧酸根和引入了硅多种功能基团,能够更好的作用于原油乳状液。
2、本申请所制得的破乳剂具有具有用量少、出水速率快、脱出水色清、使用范围宽等特点,在使用量15mg/L时,破乳效果明显优于现有聚醚型破乳剂,脱水率达到95%以上。
具体实施方式
根据下述实施例,可以更好地理解本发明。实施例所描述的内容仅用于说明本发明,而不应当也不会限制权利要求书中所详细描述的本发明。
实施例1
1)将202高含氢硅油15份、烯丙基聚醚10份和氯铂酸0.5份加入带有搅拌和滴加装置的反应器中,在40℃搅拌条件下反应4小时得到初产物A。
2)将去离子水10份、过硫酸钾0.5份和十二烷基硫酸钠3份加入带有搅拌、滴加装置和冷凝管的反应器中,通过恒压漏斗滴加丙烯酸10份和丙烯酸酯类15份,在40℃搅拌条件下反应2.5小时,加入十二烷基硫醇1份和对苯二酚1份,同样条件下反应2小时得到初产物B。
3)将初产物A、初产物B和对甲苯磺酸1份加入带有搅拌和分水回流装置的反应器中,在100℃搅拌条件下反应6小时得到目标产物。
实施例2
1)将202高含氢硅油25份、烯丙基聚醚20份和氯铂酸2份加入带有搅拌和滴加装置的反应器中,在75℃搅拌条件下反应3小时得到初产物A。
2)将去离子水15份、过硫酸钾1份和十二烷基硫酸钠4份加入带有搅拌、滴加装置和冷凝管的反应器中,通过恒压漏斗滴加丙烯酸25份和丙烯酸酯类20份,在60℃搅拌条件下反应2小时,加入十二烷基硫醇1份和对苯二酚1份,同样条件下反应1小时得到初产物B。
3)将初产物A、初产物B和对甲苯磺酸2份加入带有搅拌和分水回流装置的反应器中,在130℃搅拌条件下反应4小时得到目标产物。
实施例3
1)将202高含氢硅油40份、烯丙基聚醚40份和氯铂酸4份加入带有搅拌和滴加装置的反应器中,在85℃搅拌条件下反应1小时得到初产物A。
2)将去离子水25份、过硫酸钾6份和十二烷基硫酸钠5份加入带有搅拌、滴加装置和冷凝管的反应器中,通过恒压漏斗滴加丙烯酸35份和丙烯酸酯类30份,在95℃搅拌条件下反应1小时,加入十二烷基硫醇2份和对苯二酚2份,同样条件下反应0.5小时得到初产物B。
3)将初产物A、初产物B和对甲苯磺酸1份加入带有搅拌和分水回流装置的反应器中,在145℃搅拌条件下反应2小时得到目标产物。
以上实施例制备得到的破乳剂在使用量15mg/L时,破乳效果明显优于现有聚醚型破乳剂,脱水率达到95%以上。
本发明提供了一种富含多种功能基团破乳剂及其制备方法的思路及方法,具体实现该技术方案的方法和途径很多,以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。本实施例中未明确的各组成部分均可用现有技术加以实现。
Claims (9)
1.一种富含多种功能基团破乳剂,其特征在于,包括以下按重量百分数计的组份:含氢硅油15~40份,烯丙基聚醚10~40份,丙烯酸10~35份,丙烯酸酯15~30份,催化剂0.5~4份、引发剂0.5~6份,链转移剂1~2份,链终止剂1~2份,表面活性剂3~5份,促进剂1~2份以及去离子水10~25份。
2.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述含氢硅油为202高含氢硅油。
3.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述烯丙基聚醚分子量为800~4000。
4.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述丙烯酸酯为丙烯酸乙酯和或丙烯酸丁酯。
5.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述催化剂为氯铂酸。
6.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述引发剂为过硫酸铵、过硫酸钾中的一种或它们的混合物。
7.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述链转移剂为十二烷基硫醇,所述链终止剂为对苯二酚。
8.根据权利要求1所述的一种富含多种功能基团破乳剂,其特征在于,所述表面活性剂为十二烷基硫酸钠;所述促进剂为对甲苯磺酸。
9.权利要求1~8任意一项所述的富含多种功能基团破乳剂的制备方法,其特征在于,包括如下步骤:
步骤一:将含氢硅油、烯丙基聚醚和催化剂混合,在40~85℃搅拌条件下反应1~4小时得到初产物A。
步骤二:将去离子水、引发剂和表面活性剂混合,依次滴入丙烯酸和丙烯酸酯,在40~95℃搅拌条件下反应1~2.5小时,加入链转移剂和链终止剂同样条件下反应0.5~2小时得到初产物B。
步骤三:将步骤一得到的产物A、步骤二得到的产物B和促进剂混合,在100~145℃搅拌条件下反应2~6小时即得破乳剂。