CN107619667A - A kind of greenery patches restoration of the ecosystem composition and its production method - Google Patents
A kind of greenery patches restoration of the ecosystem composition and its production method Download PDFInfo
- Publication number
- CN107619667A CN107619667A CN201710773692.7A CN201710773692A CN107619667A CN 107619667 A CN107619667 A CN 107619667A CN 201710773692 A CN201710773692 A CN 201710773692A CN 107619667 A CN107619667 A CN 107619667A
- Authority
- CN
- China
- Prior art keywords
- parts
- restoration
- greenery patches
- ecosystem
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of greenery patches restoration of the ecosystem composition, including the polynary base-material of iron calcium, organic steady matter agent, crystallite polymerization sulfur-coated urea, modification dolomite composite titanium dioxide, ammonium sulfate, xanthans, flue berry extract, hydrophily colloidal particle and synergist, iron calcium polynary base-material lanthanum rich mischmetal, calcium ferrous substrate and the potassium humate, mass ratio 7:55‑60:11；The preparation method of the restoration of the ecosystem composition, include the preparation of the polynary base-material of iron calcium, be crushed to 90 mesh fine powders, add ammonium hydrogen carbonate, potassium humate and water, mass ratio 80:10:14.5‑16:1000, after fermentation is mixed, adds lanthanum rich mischmetal, stir speed (S.S.) is 1000 1800rad/min, stirs 30min；The composition, repairing effect is notable, and topsoil aerobic microbiological content is 851 927 grams 1, and the stable aggregate amounts of the soil water are up to 51.43 61.54%.
Description
Technical field
The invention belongs to technical field of land improvement, is related to a kind of lawn soil restoration of the ecosystem composition, and in particular to one
Kind greenery patches restoration of the ecosystem composition and its production method.
Background technology
Greening lawn is and the pruned artificial pasture with perennial short and small draft plant dense planting, in 18th century, Britain from
There is large area lawn in right landscape garden.Also occurs lawn in China modern gardens, principal item has Hawaii platinum grass, Lin Ke
This grass seeds, Bermuda grass, Manila, annual bluegrass, Festuca Arundinacea, evergreen all the year round, cold-season type lawn, mixed turf etc..
Sports turf, it is the basis of sports, is the stage of athletic competition, it is made using itself excellent buffering
With Protection of the sportsman body preserves from, and good frictional force and preferably elasticity is provided for match, to sports equipment（Football,
Tennis, golf etc.）Also there is certain protective effect；Motion lawn also has certain ecological functions, can conserve water and soil,
Stir up a cloud of dust always, purify air, reduce noise, the certain humidity of space is kept, to moving the sportsman's on
Eyes have protective effect, give the pleasure of body and mind.
Existing most motion lawn is artificial lawn, belongs to chinampa made of artificial plastics, due to nature
The foundation cost on lawn, maintenance and management etc., the particularly maintenance management after planting so that the cost on natural lawn increases
Add, in summary, research and develop a kind of greenery patches restoration of the ecosystem composition for athletic ground lawn and urgently solved as modern service industry
Certainly the problem of.
Following major defect be present in existing restoration of the ecosystem composition：
（1）Existing greenery patches remediation composition, formula is complicated, and function is single；
（2）Existing greenery patches remediation composition, special quality soil remediation effect this to athletic ground lawn and unobvious.
The content of the invention
Present invention deficiency for more than, the technical problems to be solved by the invention are to provide a kind of greenery patches restoration of the ecosystem combination
Thing and preparation method thereof.The present invention is especially suitable for athletic ground lawn, repairing effect is obvious, improves athletic ground lawn soil
The guarantor of earth stores performance, and water conservation, water holding, nutrient preserving capability greatly increase, and effectively slows down moisture evaporation speed, lawn long lifespan up to 10 years with
On, quick into level ground, lawn coverage rate is more than 95%, and Stability Analysis of Structures, weeds are few, the resistance to trample of weatherable, and floor space and maintenance
Technical costs is cheap, and the present invention can realize following goal of the invention：
（1）A kind of greenery patches restoration of the ecosystem composition, formula is reasonable, and effect is obvious, Synergistic；
（2）A kind of greenery patches restoration of the ecosystem composition, special quality soil remediation significant effect this to athletic ground lawn, is carried
High protect stores performance, to heavy rain and other with the environmental attack of water, there is good durability；Effectively extend nature lawn
The greenweed phase.
In order to solve the above technical problems, using following technical scheme：
A kind of greenery patches restoration of the ecosystem composition, it is characterised in that the restoration of the ecosystem composition, including the polynary base-material of iron calcium, institute
State the polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate.
As currently preferred technical scheme, the restoration of the ecosystem composition, in addition to organic steady matter agent, crystallite polymerization
Sulfur-coated urea, modification dolomite composite titanium dioxide, ammonium sulfate, xanthans, flue berry extract, hydrophily colloidal particle and increasing
Imitate agent.
As currently preferred technical scheme, iron calcium polynary base-material lanthanum rich mischmetal, calcium ferrous substrate and the humic
The mass ratio of sour potassium is 7:55-60: 11.
As currently preferred technical scheme, the weight/mass percentage composition of the polynary base-material of iron calcium is 1-90%.
As currently preferred technical scheme, the weight/mass percentage composition of the polynary base-material of iron calcium is 40%.
As currently preferred technical scheme, organic steady matter agent, crystallite polymerization sulfur-coated urea, modification dolomite
Composite titanium dioxide, ammonium sulfate, xanthans, flue berry extract, hydrophily colloidal particle and synergist, by weight, to have
The steady matter agent 65-90 parts of machine, crystallite polymerization sulfur-coated urea 12-20 parts, modification dolomite composite titanium dioxide 2-9 parts, ammonium sulfate 20-
40 parts, xanthans 3-30 parts, flue berry extract 10-20 parts, hydrophily colloidal particle 10-25 parts and synergist 5-10 parts.
As currently preferred technical scheme, by weight, for organic steady 75 parts of matter agent, crystallite polymerised sulphur coating urine
18 parts of element, 7 parts of modification dolomite composite titanium dioxide, 32 parts of ammonium sulfate, 15 parts of xanthans, 11 parts of flue berry extract, hydrophily
8 parts of 20 parts of colloidal particle and synergist.
As currently preferred technical scheme, the hydrophily colloidal particle is selected from asphalt emulsion, algae essence, land plaster
End and Sodium Polyacrylate mass ratio are 5:8:7:11.
As currently preferred technical scheme, described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts
CaSO4 is formed.
A kind of preparation method of greenery patches restoration of the ecosystem composition, it is characterised in that include the preparation of the polynary base-material of iron calcium, will
Calcium ferrous substrate is crushed to fine powder, crosses 90 mesh sieves, adds ammonium hydrogen carbonate, potassium humate and water, the calcium ferrous substrate, ammonium hydrogen carbonate,
The mass ratio of potassium humate and water is 80:10:14.5-16:1000, after being sufficiently mixed, add in fermentation vat and be sealed by fermentation,
Room temperature is stood after fermentation 75-80 hours, adds lanthanum rich mischmetal, high-speed stirred, speed 1000-1800rad/min, stirring
30min；
The greenery patches restoration of the ecosystem composition, topsoil aerobic micro- life notable to the Effect of Ecological Restoration on athletic ground nature lawn
Thing content is 851-927 grams -1, the stable aggregate of the soil water（>0.25mm）Content is up to 51.43-61.54%.
The present invention uses above technical scheme, compared with prior art, have advantages below：
（1）Using a kind of greenery patches restoration of the ecosystem composition of the present invention, formula is reasonable, and collaboration is produced between the polynary base-material of iron calcium and is increased
Effect acts on；Remediation composition formula is reasonable, environmental protection, does not produce any toxic action to nature, surrounding environment is not produced residual
Stay；
（2）It is notable to the repairing effect on athletic ground nature lawn using a kind of greenery patches restoration of the ecosystem composition of the present invention, grass
Level ground soil regime be improved significantly, topsoil aerobic microbiological content be 851-927 grams-1, the stable aggregate of the soil water（>
0.25mm）Content is up to 51.43-61.54%；On the premise of the certain permeability in nature lawn and elasticity is ensured, fortune is improved
The guarantor on dynamic place nature lawn stores performance, and water conservation, water holding, nutrient preserving capability greatly increase, to heavy rain and other invaded with the environment of water
Erosion, has good durability, effectively slows down moisture evaporation speed, lawn long lifespan was up to more than 10 years；
（3）Using a kind of greenery patches restoration of the ecosystem composition of the present invention, the greenweed phase on nature lawn is effectively extended, is extended to
300-330 days, extended 35-45 days than the common natural lawn greenweed phase；
（4）Using a kind of greenery patches restoration of the ecosystem composition of the present invention, repairing effect is obvious, improves the reunion of Lawn soil
Stability, Stability Analysis of Structures, turf speed is fast, and weeds are few, the resistance to trample of weatherable, and floor space and maintenance technology cost are cheap；
（5）Using a kind of greenery patches restoration of the ecosystem composition of the present invention, green cover is uniform, and convex spot area is reduced, and increases greenery patches
Coverage rate, green grassland coverage rate is more than 95%.
Embodiment
A kind of greenery patches restoration of the ecosystem composition of embodiment 1
By weight, including：
Organic steady 65 parts of matter agent, 20 parts of sulfur-coated urea of crystallite polymerization, 2 parts of modification dolomite composite titanium dioxide, 40 parts of ammonium sulfate,
10 parts of 3 parts of xanthans, 20 parts of flue berry extract, 10 parts of hydrophily colloidal particle and synergist；
The greenery patches restoration of the ecosystem composition also includes the polynary base-material of iron calcium, the polynary base-material of iron calcium, in greenery patches ecology
Quality accounting in remediation composition is 1-90%；
The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate, mass ratio 7:55-60: 11；
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Organic steady matter agent, by the rice bran fermentate of 70-90 parts, 15 parts of inositol dregs, the residue of monosodium glutamate of 40-45 parts, 20-25 parts
Vinasse slag and 10-15 parts amino acid sludge composition；
The modification dolomite composite titanium dioxide, fineness are 200 mesh, by 2-5 parts titanium dioxide, 15-30 parts dolomite, 3-7 parts grass
The parts by weight ingredient composition of acid；
The flue berry extract, fresh dragon fruit is removed the peel, pulp is put into refiner and is beaten, according to flue parchment and
The mass ratio of 90% ethanol is 2:11 ratio mixing, soaks 3-4 hours, then at a temperature of 45 DEG C at a temperature of 40-45 DEG C
Concentrated with Rotary Evaporators, collect cut, obtain flue berry extract；
It is 5 that the hydrophily colloidal particle, which is selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio,:8:7:
11；
The crystallite polymerize sulfur-coated urea, purchased from Shandong Hanfeng Slow Release Fertilizer Co., Ltd.
A kind of greenery patches restoration of the ecosystem composition of embodiment 2
Organic steady 90 parts of matter agent, 12 parts of sulfur-coated urea of crystallite polymerization, 9 parts of modification dolomite composite titanium dioxide, 20 parts of ammonium sulfate,
5 parts of 30 parts of xanthans, 10 parts of flue berry extract, 25 parts of hydrophily colloidal particle and synergist；
The greenery patches restoration of the ecosystem composition also includes the polynary base-material of iron calcium, the polynary base-material of iron calcium, in greenery patches ecology
Quality accounting in remediation composition is 1-90%；
The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate, mass ratio 7:55-60: 11；
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Organic steady matter agent, by the rice bran fermentate of 70-90 parts, 15 parts of inositol dregs, the residue of monosodium glutamate of 40-45 parts, 20-25 parts
Vinasse slag and 10-15 parts amino acid sludge composition；
The modification dolomite composite titanium dioxide, fineness are 200 mesh, by 2-5 parts titanium dioxide, 15-30 parts dolomite, 3-7 parts grass
The parts by weight ingredient composition of acid；
The flue berry extract, fresh dragon fruit is removed the peel, pulp is put into refiner and is beaten, according to flue parchment and
The mass ratio of 90% ethanol is 2:11 ratio mixing, soaks 3-4 hours, then at a temperature of 45 DEG C at a temperature of 40-45 DEG C
Concentrated with Rotary Evaporators, collect cut, obtain flue berry extract；
It is 5 that the hydrophily colloidal particle, which is selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio,:8:7:
11；
The crystallite polymerize sulfur-coated urea, purchased from Shandong Hanfeng Slow Release Fertilizer Co., Ltd.
A kind of greenery patches restoration of the ecosystem composition of embodiment 3
Organic steady 75 parts of matter agent, 18 parts of sulfur-coated urea of crystallite polymerization, 7 parts of modification dolomite composite titanium dioxide, 32 parts of ammonium sulfate,
8 parts of 15 parts of xanthans, 11 parts of flue berry extract, 20 parts of hydrophily colloidal particle and synergist；
The greenery patches restoration of the ecosystem composition also includes the polynary base-material of iron calcium, the polynary base-material of iron calcium, in greenery patches ecology
Quality accounting in remediation composition is 1-90%；
The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate, mass ratio 7:55-60: 11；
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Organic steady matter agent, by the rice bran fermentate of 70-90 parts, 15 parts of inositol dregs, the residue of monosodium glutamate of 40-45 parts, 20-25 parts
Vinasse slag and 10-15 parts amino acid sludge composition；
The modification dolomite composite titanium dioxide, fineness are 200 mesh, by 2-5 parts titanium dioxide, 15-30 parts dolomite, 3-7 parts grass
The parts by weight ingredient composition of acid；
The flue berry extract, fresh dragon fruit is removed the peel, pulp is put into refiner and is beaten, according to flue parchment and
The mass ratio of 90% ethanol is 2:11 ratio mixing, soaks 3-4 hours, then at a temperature of 45 DEG C at a temperature of 40-45 DEG C
Concentrated with Rotary Evaporators, collect cut, obtain flue berry extract；
It is 5 that the hydrophily colloidal particle, which is selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio,:8:7:
11；
The crystallite polymerize sulfur-coated urea, purchased from Shandong Hanfeng Slow Release Fertilizer Co., Ltd.
A kind of greenery patches restoration of the ecosystem composition of embodiment 4
Organic steady 70 parts of matter agent, 13 parts of sulfur-coated urea of crystallite polymerization, 4 parts of modification dolomite composite titanium dioxide, 24 parts of ammonium sulfate,
6 parts of 32 parts of xanthans, 13 parts of flue berry extract, 14 parts of hydrophily colloidal particle and synergist；
The greenery patches restoration of the ecosystem composition also includes the polynary base-material of iron calcium, the polynary base-material of iron calcium, in greenery patches ecology
Quality accounting in remediation composition is 1-90%；
The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate, mass ratio 7:55-60: 11；
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Organic steady matter agent, by the rice bran fermentate of 70-90 parts, 15 parts of inositol dregs, the residue of monosodium glutamate of 40-45 parts, 20-25 parts
Vinasse slag and 10-15 parts amino acid sludge composition；
The modification dolomite composite titanium dioxide, fineness are 200 mesh, by 2-5 parts titanium dioxide, 15-30 parts dolomite, 3-7 parts grass
The parts by weight ingredient composition of acid；
The flue berry extract, fresh dragon fruit is removed the peel, pulp is put into refiner and is beaten, according to flue parchment and
The mass ratio of 90% ethanol is 2:11 ratio mixing, soaks 3-4 hours, then at a temperature of 45 DEG C at a temperature of 40-45 DEG C
Concentrated with Rotary Evaporators, collect cut, obtain flue berry extract；
It is 5 that the hydrophily colloidal particle, which is selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio,:8:7:
11；
The crystallite polymerize sulfur-coated urea, purchased from Shandong Hanfeng Slow Release Fertilizer Co., Ltd.
A kind of greenery patches restoration of the ecosystem composition of embodiment 5
Organic steady 85 parts of matter agent, 18 parts of sulfur-coated urea of crystallite polymerization, 8 parts of modification dolomite composite titanium dioxide, 35 parts of ammonium sulfate,
8 parts of 38 parts of xanthans, 18 parts of flue berry extract, 24 parts of hydrophily colloidal particle and synergist；
The greenery patches restoration of the ecosystem composition also includes the polynary base-material of iron calcium, the polynary base-material of iron calcium, in greenery patches ecology
Quality accounting in remediation composition is 1-90%；
The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate, mass ratio 7:55-60: 11；
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Organic steady matter agent, by the rice bran fermentate of 70-90 parts, 15 parts of inositol dregs, the residue of monosodium glutamate of 40-45 parts, 20-25 parts
Vinasse slag and 10-15 parts amino acid sludge composition；
The modification dolomite composite titanium dioxide, fineness are 200 mesh, by 2-5 parts titanium dioxide, 15-30 parts dolomite, 3-7 parts grass
The parts by weight ingredient composition of acid；
The flue berry extract, fresh dragon fruit is removed the peel, pulp is put into refiner and is beaten, according to flue parchment and
The mass ratio of 90% ethanol is 2:11 ratio mixing, soaks 3-4 hours, then at a temperature of 45 DEG C at a temperature of 40-45 DEG C
Concentrated with Rotary Evaporators, collect cut, obtain flue berry extract；
It is 5 that the hydrophily colloidal particle, which is selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio,:8:7:
11；
The crystallite polymerize sulfur-coated urea, purchased from Shandong Hanfeng Slow Release Fertilizer Co., Ltd.
A kind of preparation method of greenery patches restoration of the ecosystem composition of embodiment 6
The preparation method, comprises the following steps：
A, the preparation of the polynary base-material of iron calcium：
Described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition；
Lanthanum rich mischmetal, calcium ferrous substrate and potassium humate are weighed by formula rate, calcium ferrous substrate is crushed to fine powder, crosses 90 mesh
Sieve, add ammonium hydrogen carbonate, potassium humate and water（Calcium ferrous substrate, ammonium hydrogen carbonate, the mass ratio of potassium humate and water are 80:10:
14.5-16:1000）After being sufficiently mixed, add in fermentation vat and be sealed by fermentation, room temperature, Xiang Qi are stood after 75-80 hours of fermenting
Middle addition lanthanum rich mischmetal, high-speed stirred, speed 1000-1800rad/min, 30min is stirred, it is polynary to obtain the iron calcium
Base-material.
B, blend：
By formula rate weigh organic steady matter agent, crystallite polymerization sulfur-coated urea, modification dolomite composite titanium dioxide, ammonium sulfate,
Xanthans, flue berry extract, hydrophily colloidal particle and synergist, it is added sequentially to stir in reactor, stirs 30-
The polynary base-material of iron calcium described in step A is added after 40min, continues insulated and stirred, until uniformly；Add gross mass 2-3% paddy
The sweet peptide of Guang, continues to stir and evenly mix；Described glutathione is purchased from Shandong Jincheng Pharmaceutical ＆ Chemicals Co., Ltd..
C, it is granulated：
Step B blend is granulated, collects pellet；By the pellet lost pressure cooling of collection, screened；After screening
Pellet carries out coating, packs shipment, and the greenery patches restoration of the ecosystem composition of the present invention is made.
Application process：
Greening lawn can be directly carried out after restoration of the ecosystem composition of the present invention is applied into the soil on athletic ground lawn
Laying, saturation is carried out after and is irrigated；Or by the restoration of the ecosystem composition of the present invention according to 1:1000 ratio is molten
Yu Shui, is made solvent, and direct heap lawn is sprayed or irrigated；Athletic ground lawn at least six moon can be ensured needs water to need
Fertilizer requires；Every mu of 4-6 ton of amount of application amount of application, it is annual 1-3 times.
A kind of application of the greenery patches restoration of the ecosystem composition of embodiment 7 in golf course Lawn
In Weifang City of Shandong Province Kuiwen District Bao Tong streets golf course, the area selects 36 mu of area to be used as experimental plot at random, respectively
A-I cells are divided into, per 3 mu of plot area；Wherein, A-E cells：Using the restoration of the ecosystem group described in 1-5 of the embodiment of the present invention
Compound；F cells：Using commercially available（Randomly select brand）Greenery patches remediation composition fertilizer；G cells：Using with the embodiment of the present invention 5
The similar formula of described restoration of the ecosystem composition, is differed only in, and the content of the polynary base-material of iron calcium is 0.5%；H cells：Using
The formula similar to the restoration of the ecosystem composition described in the embodiment of the present invention 5, is differed only in, and the content of the polynary base-material of iron calcium is
91%；I cells：As check plot, do not apply.
Multiple sampling experiment, by soil-column test, the experimental result such as table 1 of each character of soil are carried out to the cell applied
It is shown：
Table 1：
Topsoil of the present invention, refer to the soil horizon of 0-15cm depth.
From table 1, the general effect of A-E cells is better than F-I cells effect, and the soil plough horizon of C cells is good in A-E cells
Oxygen animalcule content highest, the stable aggregate of water（>0.25mm）Content is high, and aerobic microbiological survival condition therein is good, raw
Reason activity is active.
The restoration of the ecosystem composite formula of the present invention is reasonable, environmental protection, any toxic action is not produced to nature, to surrounding
Environment does not produce residual；On the premise of the certain permeability in nature lawn and elasticity is ensured, it is naturally careless to improve athletic ground
The guarantor on level ground stores performance, and water conservation, water holding, nutrient preserving capability greatly increase, to heavy rain and other with the environmental attack of water, have good
Durability, effectively slowing down moisture evaporation speed, improve the stability reunion of Lawn soil, Stability Analysis of Structures, turf speed is fast,
Weeds are few, the resistance to trample of weatherable, and floor space and maintenance technology cost are cheap；Green cover is uniform, and convex spot area is reduced, increase
Forest coverage rate, green grassland coverage rate is more than 95%；It is corresponding, restoration of the ecosystem composite formula described in embodiment 3 compared with
It is excellent.
The present inventor has been surprisingly found that the polynary base-material of iron calcium of the invention accounts for the ecology in actual mechanical process
The percentage composition of remediation composition gross mass has significant impact to whole restoration of the ecosystem composition, has carried out a series of related realities
Example experiment is applied, following examples 8-12 is the percentage accounting for only changing the polynary base-material of iron calcium on the basis of embodiment 3, specifically
Such as table 2 below：
Table 2：
Embodiment 8-12 is tested as described in Example 7, cell corresponding to the embodiment 8-12 difference is that J-N is small
Area, experimental result table 3：
Table 3：
From table 3, the general effect of J-N cells is good, the stable aggregate of the soil water of L cells in J-N cells（>0.25mm）Contain
Amount is high, soil plough horizon aerobic microbiological content highest, corresponding, life embodiment 10 described in obvious to the repairing effect in the area
State remediation composition formula is more excellent, i.e., iron calcium polynary base-material accounting 40% when the effect that is obtained it is best.
To area's turf plant：J-N cells lawn is grown fine, and careless color depth is green, comes along fine, and lawn long lifespan was up to 10 years
More than；The greenweed phase on nature lawn is effectively extended, the lawn greenweed phase of J-N cells extends than the lawn of control group I cells
Nearly 3 months, 300-330 days are extended to, than common natural lawn（G and H cells）The greenweed phase extends 35-45 days.
The formula of the present invention is reasonable, particularly the polynary base-material of iron calcium, is learnt by a series of experiment of unicity, described iron
Improved effect caused by the polynary base-material of calcium（12 points）More than the independent caused effect sum of single dose material（1 point, 3 points and 5 points）, this
Synergistic function is produced between each single dose of the polynary base-material of iron calcium of invention, will not enumerate herein.
The present inventor operates through repeatedly practice, finds the restoration of the ecosystem composition improved effect prepared by the present invention
Effectively extend, effect is lasting, and compared with commercially available common ecological remediation composition, the effect time after applying every time averagely extends
15-20 days.
Unless otherwise indicated, percentage of the present invention is percetage by weight, ratio of the present invention, is
Mass ratio.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still can be with
Technical scheme described in foregoing embodiments is modified, or equivalent substitution is carried out to which part technical characteristic.It is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc., it should be included in the guarantor of the present invention
Within the scope of shield.
Claims (10)
- A kind of 1. greenery patches restoration of the ecosystem composition, it is characterised in that the restoration of the ecosystem composition, including the polynary base-material of iron calcium, The polynary base-material of iron calcium, including lanthanum rich mischmetal, calcium ferrous substrate and potassium humate.
- A kind of 2. greenery patches restoration of the ecosystem composition according to claim 1, it is characterised in that the restoration of the ecosystem combination Thing, in addition to organic steady matter agent, crystallite polymerization sulfur-coated urea, modification dolomite composite titanium dioxide, ammonium sulfate, xanthans, fire Imperial berry extract, hydrophily colloidal particle and synergist.
- 3. a kind of greenery patches restoration of the ecosystem composition according to claim 1, it is characterised in that the polynary base-material of iron calcium is rich The mass ratio of La mixed rare earth, calcium ferrous substrate and potassium humate is 7:55-60: 11.
- 4. a kind of greenery patches restoration of the ecosystem composition according to claim 1, it is characterised in that the polynary base-material of iron calcium Weight/mass percentage composition is 1-90%.
- 5. a kind of greenery patches restoration of the ecosystem composition according to claim 1, it is characterised in that the polynary base-material of iron calcium Weight/mass percentage composition is 40%.
- 6. a kind of greenery patches restoration of the ecosystem composition according to claim 1, it is characterised in that organic steady matter agent, micro- Crystalline substance polymerization sulfur-coated urea, modification dolomite composite titanium dioxide, ammonium sulfate, xanthans, flue berry extract, hydrophilic gel plasmid Son and synergist, by weight, it polymerize sulfur-coated urea 12-20 parts, modified white clouds for organic steady matter agent 65-90 parts, crystallite Stone composite titanium dioxide 2-9 parts, ammonium sulfate 20-40 parts, xanthans 3-30 parts, flue berry extract 10-20 parts, hydrophilic gel plasmid Sub- 10-25 parts and synergist 5-10 parts.
- 7. a kind of greenery patches restoration of the ecosystem composition according to claim 2 or 6, it is characterised in that by weight, to have 75 parts of the steady matter agent of machine, 18 parts of sulfur-coated urea of crystallite polymerization, 7 parts of modification dolomite composite titanium dioxide, 32 parts of ammonium sulfate, xanthans 8 parts of 15 parts, 11 parts of flue berry extract, 20 parts of hydrophily colloidal particle and synergist.
- A kind of 8. greenery patches restoration of the ecosystem composition according to claim 2, it is characterised in that the hydrophily colloidal particle It is 5 selected from asphalt emulsion, algae essence, gypsum powder and Sodium Polyacrylate mass ratio:8:7:11.
- A kind of 9. greenery patches restoration of the ecosystem composition according to claim 2, it is characterised in that described calcium ferrous substrate, by 55-80 part Fe, 20-30 part Mo, 3-10 parts CaSO4Composition.
- A kind of 10. preparation method of greenery patches restoration of the ecosystem composition, it is characterised in that include the preparation of the polynary base-material of iron calcium, will Calcium ferrous substrate is crushed to fine powder, crosses 90 mesh sieves, adds ammonium hydrogen carbonate, potassium humate and water, the calcium ferrous substrate, ammonium hydrogen carbonate, The mass ratio of potassium humate and water is 80:10:14.5-16:1000, after being sufficiently mixed, add in fermentation vat and be sealed by fermentation, Room temperature is stood after fermentation 75-80 hours, adds lanthanum rich mischmetal, high-speed stirred, speed 1000-1800rad/min, stirring 30min；The greenery patches restoration of the ecosystem composition, topsoil aerobic micro- life notable to the Effect of Ecological Restoration on athletic ground nature lawn Thing content is 851-927 grams-1, the stable aggregate of the soil water（>0.25mm）Content is up to 51.43-61.54%.