CN107619545A - A kind of radiation hardness plastic floor and preparation method thereof - Google Patents
A kind of radiation hardness plastic floor and preparation method thereof Download PDFInfo
- Publication number
- CN107619545A CN107619545A CN201610547115.1A CN201610547115A CN107619545A CN 107619545 A CN107619545 A CN 107619545A CN 201610547115 A CN201610547115 A CN 201610547115A CN 107619545 A CN107619545 A CN 107619545A
- Authority
- CN
- China
- Prior art keywords
- plastic floor
- roller
- corvic
- poly
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of radiation hardness plastic floor and preparation method thereof, it is made up of the raw material of following parts by weight：Corvic 46 59, polyether sulfone 31 42, poly 22 35, witherite powder 22 28, the monooctyl ester 16 22 of trimellitic acid three, ricinoleic acid amide 6 11, blanc fixe 18 24, two (dodecylthio) dibutyl tin 47, tricresyl phosphate 14 22, high temperature active bamboo charcoal powder 10 15, lead hydroxide 5 10.The present invention is using Corvic, polyether sulfone, poly compounding, and add the raw materials such as witherite powder, blanc fixe, tricresyl phosphate, high temperature active bamboo charcoal powder, lead hydroxide, the radiation resistance of plastic floor can be not only significantly improved, heat resistance, resistance to ag(e)ing, wearability and the anti-flammability of plastic floor can also be improved.
Description
Background technology
The present invention relates to a kind of plastic floor and preparation method thereof, and in particular to a kind of radiation hardness plastic floor and its preparation
Method.
Background technology
In modern society, the kind of floor decorative material is more and more, from traditional cement mortar surface to generally slaughtering light
Terrazzo floor, then emerged in an endless stream to floor tile, granite, timber floor, new material.Wherein plastic floor is because with deadweight
The advantages that small, speed of application is fast, and impression quality is good, and color is various, and walking is comfortable, anti-skidding, is widely used in kindergarten, guest
Many fields such as shop, hospital, office buildings, house, airport, gymnasium, railway station.In recent years, it is quick with industrial technology
Development and people's living standards continue to improve, to the performance requirement more and more higher of plastic floor.But traditional plastic floor
There are still the shortcomings that radiation resistance difference, can not meet the needs of market.
The content of the invention
For above shortcomings in the prior art, the technical problems to be solved by the invention are to provide a kind of radiation hardness
Plastic floor and preparation method thereof.
The technical problems to be solved by the invention are achieved by the following technical solution：
A kind of radiation hardness plastic floor, is made up of the raw material of following parts by weight：Corvic 46-59, polyether sulfone 31-42,
Poly 22-35, witherite powder 22-28, the monooctyl ester 16-22 of trimellitic acid three, ricinoleic acid amide 6-
11st, blanc fixe 18-24, two (dodecylthio) dibutyl tin 4-7, tricresyl phosphate 14-22, high temperature active bamboo charcoal powder
10-15, lead hydroxide 5-10.
A kind of preparation method of radiation hardness plastic floor, comprises the following steps：
（1）By Corvic, polyether sulfone, poly, ricinoleic acid amide, two (dodecylthios)
Dibutyl tin is in high-speed mixer, the mixed at high speed 7-11min at 75-85 DEG C, sequentially add witherite, blanc fixe,
The raw materials such as high temperature active bamboo charcoal powder, lead hydroxide, the monooctyl ester of trimellitic acid three, tricresyl phosphate, at 105-120 DEG C at a high speed
6-9min is stirred, is then transferred in cooling and stirring machine, when stirring material temperature is down to 40-50 DEG C, discharging；
（2）Compound obtained above is added in plasticator, beating, triangle bag is thin logical 7-10 times, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
195-215 DEG C, 210-235 DEG C, 200-220 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.07-1.14, third roll
The speed ratio of second roller is in 1.03-1.06；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.
Beneficial effects of the present invention：
The present invention adds witherite powder, again using Corvic, polyether sulfone, poly compounding
The raw materials such as spar powder, tricresyl phosphate, high temperature active bamboo charcoal powder, lead hydroxide, can not only significantly improve plastic floor
Radiation resistance, heat resistance, resistance to ag(e)ing, wearability and the anti-flammability of plastic floor can also be improved.
Embodiment
Embodiment 1
A kind of radiation hardness plastic floor, by following weight（kg）Raw material be made：Corvic 46, polyether sulfone 31, it is poly- between
Phenyl-diformyl m-phenylene diamine (MPD) 22, witherite powder 22, the monooctyl ester 16 of trimellitic acid three, ricinoleic acid amide 6, blanc fixe 18, two
(dodecylthio) dibutyl tin 4, tricresyl phosphate 14, high temperature active bamboo charcoal powder 10, lead hydroxide 5.
A kind of preparation method of radiation hardness plastic floor, comprises the following steps：
（1）By Corvic, polyether sulfone, poly, ricinoleic acid amide, two (dodecylthios)
Dibutyl tin is in high-speed mixer, the mixed at high speed 7-11min at 75-85 DEG C, sequentially add witherite, blanc fixe,
The raw materials such as high temperature active bamboo charcoal powder, lead hydroxide, the monooctyl ester of trimellitic acid three, tricresyl phosphate, at 105-120 DEG C at a high speed
6-9min is stirred, is then transferred in cooling and stirring machine, when stirring material temperature is down to 40-50 DEG C, discharging；
（2）Compound obtained above is added in plasticator, beating, triangle bag is thin logical 7-10 times, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
195-215 DEG C, 210-235 DEG C, 200-220 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.07-1.14, third roll
The speed ratio of second roller is in 1.03-1.06；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.
Embodiment 2
A kind of radiation hardness plastic floor, by following weight（kg）Raw material be made：Corvic 51, polyether sulfone 36, it is poly- between
Phenyl-diformyl m-phenylene diamine (MPD) 29, witherite powder 25, the monooctyl ester 19 of trimellitic acid three, ricinoleic acid amide 8, blanc fixe 20, two
(dodecylthio) dibutyl tin 6, tricresyl phosphate 18, high temperature active bamboo charcoal powder 12, lead hydroxide 7.
Preparation method is the same as embodiment 1.
Embodiment 3
A kind of radiation hardness plastic floor, by following weight（kg）Raw material be made：Corvic 59, polyether sulfone 42, it is poly- between
Phenyl-diformyl m-phenylene diamine (MPD) 35, witherite powder 28, the monooctyl ester 22 of trimellitic acid three, ricinoleic acid amide 11, blanc fixe 24, two
(dodecylthio) dibutyl tin 7, tricresyl phosphate 22, high temperature active bamboo charcoal powder 15, lead hydroxide 10.
Preparation method is the same as embodiment 1.
The performance test results of plastic floor are as shown in the table made from above-described embodiment 1-3：
Claims (2)
1. a kind of radiation hardness plastic floor, it is characterised in that be made up of the raw material of following parts by weight：Corvic 46-59,
Polyether sulfone 31-42, poly 22-35, witherite powder 22-28, the monooctyl ester 16-22 of trimellitic acid three, castor
Numb alkyd acid amides 6-11, blanc fixe 18-24, two (dodecylthio) dibutyl tin 4-7, tricresyl phosphate 14-22, high temperature
Active bamboo powdered carbon 10-15, lead hydroxide 5-10.
2. the preparation method of radiation hardness plastic floor according to claim 1, it is characterised in that comprise the following steps：
（1）By Corvic, polyether sulfone, poly, ricinoleic acid amide, two (dodecylthios)
Dibutyl tin is in high-speed mixer, the mixed at high speed 7-11min at 75-85 DEG C, sequentially add witherite, blanc fixe,
The raw materials such as high temperature active bamboo charcoal powder, lead hydroxide, the monooctyl ester of trimellitic acid three, tricresyl phosphate, at 105-120 DEG C at a high speed
6-9min is stirred, is then transferred in cooling and stirring machine, when stirring material temperature is down to 40-50 DEG C, discharging；
（2）Compound obtained above is added in plasticator, beating, triangle bag is thin logical 7-10 times, pulling-on piece；
（3）The sheet material for post-tensioning of plasticating is transported on tri-roll press machine and rolled, the roller temperature of three rollers is respectively from top to bottom
195-215 DEG C, 210-235 DEG C, 200-220 DEG C, the speed ratio of the second roller and the first roller is controlled in 1.07-1.14, third roll
The speed ratio of second roller is in 1.03-1.06；
（4）The trimming after the sheet material rolled is cooled to normal temperature, it is finished product to examine qualified.