CN107604512A - A kind of blending has the fabric of graphene fiber - Google Patents
A kind of blending has the fabric of graphene fiber Download PDFInfo
- Publication number
- CN107604512A CN107604512A CN201711051316.3A CN201711051316A CN107604512A CN 107604512 A CN107604512 A CN 107604512A CN 201711051316 A CN201711051316 A CN 201711051316A CN 107604512 A CN107604512 A CN 107604512A
- Authority
- CN
- China
- Prior art keywords
- fiber
- cotton
- graphene fiber
- fabric
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the fabric that a kind of blending has graphene fiber, including：Interweave with forming the fabric by warp and weft transverse and longitudinal, warp is purified cotton yarns, the yarn that the parallel is cotton fiber and graphene fiber blending forms, and the weight ratio of cotton fiber and graphene fiber in the parallel is 58:1；Before spinning the parallel, the graphene fiber outer surface is coated with paraffin layer, and the average length of the graphene fiber for spinning parallel is 30 50mm.By being waxed in advance on graphene fiber surface, its spinnability can be improved to a certain extent, make itself and cotton fiber blending, and cotton thread be account for weight than most amounts when, by the auxiliary of the cotton fiber largely easily spun, the yarn containing a certain amount of graphene fiber can be formed.Together with having the blending relatively low with one structural strength of the of a relatively high pure cotton single thread of one structural strength the cotton single-yarn of graphene fiber twisted, make two strands of single thread are twisted to improve bulk strength.
Description
Technical field
The present invention relates to a kind of function fabric, more particularly to a kind of blending the fabric of graphene fiber.
Background technology
There is the textile of the functions such as electromagnetic protection, UV resistance, conductive intelligence mainly by adding work(in existing textile
For energy auxiliary agent to realize above-mentioned simple function, usual function additive addition is big, influences the wearability and endurance quality of textile,
And above-mentioned multi-functional characteristic can not be realized simultaneously.Graphene due to its unique texture and with above-mentioned characteristic (it is antistatic, lead
Electricity, UV resistance, electromagnetic protection, flame-proof heat-resistant, anti-corrosion are ageing-resistant, far infrared health care), and the addition of appropriate graphene and it is equipped with conjunction
The weaving process of reason, you can above-mentioned multiple-effect functional characteristic is realized in fiber and textile, meanwhile, make product cost height.Institute
The development of graphene modified fibre and new function textile project, can be formed in multifunctional textile product field certain
Market scale and good economic benefit., can by the research and development and industrialization of graphene modified fibre and new function textile
The concept of " wide spectrum function textile " is proposed, releases multi-functional series function fiber and textile, prediction there can be consumption
The widespread demand of person.
And the spinnability of graphene fiber is too poor, it is necessary to other fiber blends into yarn, yarn at instant blending, it is tied
Structure intensity is not also high, it is necessary to take the spinnability and weavability of certain measure raising graphene fiber.
The content of the invention
Instant invention overcomes the deficiencies in the prior art, there is provided a kind of blending has the fabric of graphene fiber.
To reach above-mentioned purpose, the technical solution adopted by the present invention is：A kind of blending has the fabric of graphene fiber, bag
Include：Interweave with forming the fabric by warp and weft transverse and longitudinal, it is characterised in that the warp is purified cotton yarns, the parallel
The yarn formed for cotton fiber and graphene fiber blending, the weight ratio of cotton fiber and graphene fiber in the parallel is 5-
8:1；Before spinning the parallel, the graphene fiber outer surface is coated with paraffin layer, for spinning the graphene of parallel
The average length of fiber is 30-50mm.
In a preferred embodiment of the present invention, the parallel, which is that bifilar single thread is twisted, to be formed, and wherein one single thread is pure cotton
Single thread, the single thread that another strand of single thread is cotton fiber and graphene fiber blending forms.
In a preferred embodiment of the present invention, after graphene fiber and paraffin powder are sufficiently mixed, paraffin powder is screened out
Produce the graphene fiber that outer surface is coated with paraffin layer.
In a preferred embodiment of the present invention, the fabric is plain cloth.
In a preferred embodiment of the present invention, the weight ratio of cotton fiber and graphene fiber in the parallel is 6:1.
In a preferred embodiment of the present invention, cotton fiber is long-staple cotton or medium staple cotton.
The present invention solves defect present in background technology, and the present invention possesses following beneficial effect：
(1) by being waxed in advance on graphene fiber surface, its spinnability can be improved to a certain extent, makes it fine with cotton
Tie up blending, and cotton thread be account for weight than most amount when, by the auxiliary of the cotton fiber largely easily spun, can be formed and contained
There is the yarn of a certain amount of graphene fiber.
(2) by the way that the of a relatively high pure cotton single thread of one structural strength and the relatively low blending of one structural strength are had into graphite
The cotton single-yarn of alkene fiber is twisted together, makes two strands of single thread are twisted to improve bulk strength.
(3) during Woven fabric, by regarding the yarn for containing graphene fiber as parallel, structural strength can be avoided not
The high yarn containing graphene fiber makes weaving process not as warp (structural strength of warp requirement is higher with respect to parallel)
More smooth, weaving process is not easy weft-broken occur.
Brief description of the drawings
The present invention is further described with reference to the accompanying drawings and examples；
Fig. 1 is the structural representation one of the preferred embodiments of the present invention fabric；
Fig. 2 is the structural representation two of the preferred embodiments of the present invention fabric；
In figure：1st, warp；2nd, parallel.
Embodiment
Presently in connection with drawings and examples, the present invention is further detailed explanation, and these accompanying drawings are simplified signal
Figure, only illustrate the basic structure of the present invention in a schematic way, therefore it only shows the composition relevant with the present invention.
As shown in Figure 1 and Figure 2, a kind of blending has the fabric of graphene fiber, including：Handed over by warp 1 and the transverse and longitudinal of parallel 2
Knit to form fabric, and fabric is plain cloth.Warp 1 is purified cotton yarns, and parallel 2 is that cotton fiber and graphene fiber blending form
Yarn, during Woven fabric, by regarding the yarn for containing graphene fiber as parallel 2, structural strength can be avoided not high
The yarn containing graphene fiber not as warp 1 (warp 1 requirement structural strength with respect to parallel 2 it is higher), make to weave
Cheng Gengwei is smooth, and weaving process is not easy weft-broken occur.
The average length of graphene fiber for spinning parallel 2 is 30-50mm, and its average length is more than the length of long-staple cotton
Degree, improve the spinnability of the composite fibre for being mixed with graphene fiber in blending process.
Parallel 2, which is that bifilar single thread is twisted, to be formed, and wherein one single thread is pure cotton single thread, and another strand of single thread is cotton fiber and stone
The single thread that black alkene fiber blend forms.By the way that the of a relatively high pure cotton single thread of one structural strength and one structural strength is relatively low
Blending have the cotton single-yarn of graphene fiber twisted together, make two strands of single thread are twisted to improve bulk strength.
Before spinning parallel 2, graphene fiber outer surface is coated with paraffin layer, by the way that graphene fiber and paraffin powder is abundant
After mixing, screen out paraffin powder and produce the graphene fiber that outer surface is coated with paraffin layer.After in advance on graphene fiber surface
Wax, its spinnability can be improved to a certain extent, make itself and cotton fiber blending, and cotton thread be account for weight than most amounts
When, by the auxiliary of the cotton fiber largely easily spun, the yarn containing a certain amount of graphene fiber can be formed.
The weight ratio of cotton fiber and graphene fiber in parallel 2 is 5-8:1, the preferably cotton fiber and graphite in parallel 2
The weight ratio of alkene fiber is 6:1.
Cotton fiber is long-staple cotton or medium staple cotton.
The present invention makes graphene fiber using the conventional technical means of wet spinning, and graphene oxide water solution is stirred
Obtain graphene oxide spinning solution.The manufacture craft of graphene fiber is made for the wet spinning process of comparative maturity：By spinning
Liquid is filled into syringe, and spinning speed is controlled with flow pump, is spinned in the coagulating bath that pH value is 2.35.Fiber is slowly drawn
Go out, drying system, on bobbin is wound up into, and spontaneously dry.By the graphene oxide fiber of preparation, reduced through hydroiodic acid,
And obtained graphene fiber is dried after being washed with absolute ethyl alcohol and deionized water.
The desirable embodiment according to the present invention is enlightenment above, and by above-mentioned description, related personnel completely can be with
Without departing from the scope of the technological thought of the present invention', various changes and amendments are carried out.The technical scope of this invention
The content being not limited on specification, it is necessary to determine the technical scope according to the scope of the claims.
Claims (6)
1. a kind of blending has the fabric of graphene fiber, including：Interweave with forming the fabric by warp and weft transverse and longitudinal, it is special
Sign is, the warp is purified cotton yarns, the yarn that the parallel is cotton fiber and graphene fiber blending forms, the parallel
In cotton fiber and the weight ratio of graphene fiber be 5-8:1；Before spinning the parallel, the graphene fiber outer surface is smeared
There is paraffin layer, the average length of the graphene fiber for spinning parallel is 30-50mm.
2. a kind of blending according to claim 1 has the fabric of graphene fiber, it is characterised in that：The parallel is bifilar
Single thread is twisted to be formed, and wherein one single thread is pure cotton single thread, and another strand of single thread is that cotton fiber and graphene fiber blending form
Single thread.
3. a kind of blending according to claim 1 has the fabric of graphene fiber, it is characterised in that：By the way that graphene is fine
After dimension is sufficiently mixed with paraffin powder, screens out paraffin powder and produce the graphene fiber that outer surface is coated with paraffin layer.
4. a kind of blending according to claim 1 has the fabric of graphene fiber, it is characterised in that：The fabric is plain weave
Fabric.
5. a kind of blending according to claim 1 has the fabric of graphene fiber, it is characterised in that：Cotton in the parallel
The weight of fiber and graphene fiber ratio is 6:1.
6. a kind of blending according to claim 1 has the fabric of graphene fiber, it is characterised in that：Cotton fiber is long-staple cotton
Or medium staple cotton.