CN107602012A - 一种速干型混凝土 - Google Patents
一种速干型混凝土 Download PDFInfo
- Publication number
- CN107602012A CN107602012A CN201710823641.0A CN201710823641A CN107602012A CN 107602012 A CN107602012 A CN 107602012A CN 201710823641 A CN201710823641 A CN 201710823641A CN 107602012 A CN107602012 A CN 107602012A
- Authority
- CN
- China
- Prior art keywords
- parts
- fast
- concrete
- waterglass
- drying type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种速干型混凝土,包括天然乳胶液、碎石、竹炭、硫酸铜、硅酸盐水泥熟料、水玻璃、麦饭石、地开石和磁铁矿,其原料各组分按重量计,所述天然乳胶液15‑19份、碎石30‑47份、竹炭20‑24份、硫酸铜10‑14份、硅酸盐水泥熟料5‑8份、水玻璃3‑8份、麦饭石15‑19份、地开石18‑22份和磁铁矿18‑25份。本发明可以有效实现混凝土的速干,同时提高混凝土抗折强度和韧性,限制的裂缝宽度,抵抗混凝土表面龟裂和抗爆防火能力,可以广泛应用于土木、水利、市政交通、海洋军工等领域的混凝土结构。
Description
技术领域
本发明属于建筑领域,涉及一种速干型混凝土。
背景技术
随着近年来房地产行业的兴起,民用或商用房屋在每个城市都越来越多,但是房屋质量也同时成为人们注意的焦点,如房屋漏水、房屋霉变等诸多问题,即使有些房屋顶部、侧墙做过防水层处理,但是仍会因天气或其他因素受潮霉变。
发明内容
本发明要解决的技术问题是:克服现有技术中房屋墙壁易受潮霉变的技术问题,提供一种防水、防霉变、质轻的速干型混凝土。
本发明解决其技术问题所采用的技术方案是:提供一种速干型混凝土,包括天然乳胶液、碎石、竹炭、硫酸铜、硅酸盐水泥熟料、水玻璃、麦饭石、地开石和磁铁矿,其原料各组分按重量计,所述天然乳胶液15-19份、碎石30-47份、竹炭20-24份、硫酸铜10-14份、硅酸盐水泥熟料5-8份、水玻璃3-8份、麦饭石15-19份、地开石18-22份和磁铁矿18-25份。
作为优选,所述的速干型混凝土,其特征是:其原料各组分按重量计,天然乳胶液15份、碎石30份、竹炭20份、硫酸铜10份、硅酸盐水泥熟料5份、水玻璃3份、麦饭石15份、地开石18份和磁铁矿18份。
作为优选,所述的速干型混凝土,其特征是具有如下步骤:
(1) 按重量份配比配置好各种原料 ;
(2) 将配置好的各种原料一一加入搅拌反应器中,在转速为 60rpm 的条件下搅拌2h,即可制得。
本发明可以有效实现混凝土的速干,同时提高混凝土抗折强度和韧性,限制的裂缝宽度,抵抗混凝土表面龟裂和抗爆防火能力,可以广泛应用于土木、水利、市政交通、海洋军工等领域的混凝土结构。
具体实施方式
本发明所述的一种速干型混凝土,其原料各组分按重量计,包括天然乳胶液、碎石、竹炭、硫酸铜、硅酸盐水泥熟料、水玻璃、麦饭石、地开石和磁铁矿,其原料各组分按重量计,所述天然乳胶液15-19份、碎石30-47份、竹炭20-24份、硫酸铜10-14份、硅酸盐水泥熟料5-8份、水玻璃3-8份、麦饭石15-19份、地开石18-22份和磁铁矿18-25份。
作为优选,所述的速干型混凝土,其特征是:其原料各组分按重量计,天然乳胶液15份、碎石30份、竹炭20份、硫酸铜10份、硅酸盐水泥熟料5份、水玻璃3份、麦饭石15份、地开石18份和磁铁矿18份。
作为优选,所述的速干型混凝土,其特征是具有如下步骤:
(1) 按重量份配比配置好各种原料 ;
(2) 将配置好的各种原料一一加入搅拌反应器中,在转速为 60rpm 的条件下搅拌2h,即可制得。
以上所述仅是本发明的优选实施方式,并不用于限制本发明,应当指出, 对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和变型,这些改进和变型也应视为本发明的保护范围。
Claims (3)
1.一种速干型混凝土,其特征是:包括天然乳胶液、碎石、竹炭、硫酸铜、硅酸盐水泥熟料、水玻璃、麦饭石、地开石和磁铁矿,其原料各组分按重量计,所述天然乳胶液15-19份、碎石30-47份、竹炭20-24份、硫酸铜10-14份、硅酸盐水泥熟料5-8份、水玻璃3-8份、麦饭石15-19份、地开石18-22份和磁铁矿18-25份。
2.如权利要求1所述的速干型混凝土,其特征是:其原料各组分按重量计,天然乳胶液15份、碎石30份、竹炭20份、硫酸铜10份、硅酸盐水泥熟料5份、水玻璃3份、麦饭石15份、地开石18份和磁铁矿18份。
3.如权利要求1-2所述的速干型混凝土,其特征是具有如下步骤:
(1) 按重量份配比配置好各种原料 ;
(2) 将配置好的各种原料一一加入搅拌反应器中,在转速为 60rpm 的条件下搅拌2h,即可制得。