CN107584606A - A kind of braiding basket of batten - Google Patents
A kind of braiding basket of batten Download PDFInfo
- Publication number
- CN107584606A CN107584606A CN201710874620.1A CN201710874620A CN107584606A CN 107584606 A CN107584606 A CN 107584606A CN 201710874620 A CN201710874620 A CN 201710874620A CN 107584606 A CN107584606 A CN 107584606A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- basket
- timber
- batten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of braiding basket of batten, it is related to woodwork processing technical field, it is characterised in that：Including following preparation process, chosen material, immersion timber, baking timber, again soak timber, toast again, be fabricated to basket, cleaning basket, immersion basket, take out it is stand-by.The inventive method is reasonable, it is easy to operate, being capable of anti-insect bite.
Description
Technical field
The present invention relates to woodwork to process technical field, and in particular to a kind of braiding basket of batten.
Background technology
Woodwork be with wood raw material, by processing and fabricating, the product formed.
Woodwork is broadly divided into following a few major classes：Furniture woodwork, office woodwork, technique woodwork, gardening woodwork,
Life woodwork, there is present high-tech woodwork.Woodcarving is an offspring of technique woodwork.
Knitting refers to people or the product that machine is woven, and generally has the material of excellent toughness with wicker, reed etc..
Timber is the plant for being capable of secondary growth, such as tree and shrubs, the lignified tissue formed.These plants are first
After raw growth terminates, the vascular cambium in rhizome comes into play, and outwards develops bast, inwardly develops timber.
Timber is the inside general designation for developing plant tissue of vascular cambium, including xylem and thin-walled ray.Timber
Very big supporting function is played for human lives.According to the different nature and characteristic of timber, they are used for different approaches by people.
And be not wooden in the general of production and application now, it is more to be all that wicker plaiting article or reed etc. are compared, but use
Wood weaves just fewer, and tends to make moist after braiding, rots, and appearance is also without the attractive in appearance of wicker plaiting article.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side
Just, it is capable of a kind of braiding basket of batten of anti-insect bite.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of braiding basket of batten, it is characterised in that：Including following preparation process,
Step 1: chosen material：Healthy conventional wood in selective cutting 5-9 days, no lesion, without insect pest, according to volume
Knitting needs that strip is made, and is then rinsed well with clear water, then is placed on and dries, divulges information, stands 3-5 in the environment of direct sunlight
Individual hour；
Step 2: immersion timber：Timber after standing is blown 3 minutes repeatedly with hair-dryer, is then placed in hydrogen peroxide and soaks
10-15 minutes are steeped, liquid level lid is crossed timber upper surface, then taken out, rinsed with clear water, then dry surface moisture again；
Step 3: baking timber：Timber after immersion is put into 95-110 DEG C of drying baker and toasted, is operated altogether
20-25 minutes；
Step 4: timber is soaked again：Timber after baking is taken out, it is quiet at room temperature to be placed on dry, ventilation place
Put 30 minutes, be then placed in 2-3 hour of immersion in soak；
Step 5: toast again：Timber after immersion is taken out, is then directly placed into 85-100 DEG C of drying baker and toasts
35-45 minutes；
Step 6: it is fabricated to basket：Batten is woven into basket by the weaving manner according to routine, in batten before batten is penetrated
One layer of lubricant of surface smear；
Step 7: cleaning basket：Basket after braiding is cleaned in suds or in liquid detergent, then rinsed with clear water dry
Naturally dry after net；
Step 8: immersion basket：A soak is remake, then basket is put into soak and soaks 40 minutes, then
Taking-up, which is put into 75-90 DEG C of baking oven, is toasted 25 minutes, and 5 minutes are stood after taking-up；The step of repeating immersion, baking, standing one
Totally 3 times；
Step 9: take out stand-by：Basket after standing is taken out be placed on dry, the place of ventilation, wait to finish or directly
Use；
The soak is made up of the material of following parts by weight,
Barium sulfate powder 3-6 parts, active powdered carbon 5-8 parts, smectite powder 11-17 parts, calcium carbonate powder 4-9 parts, vinegar
Acid butyl ester 1-3 parts, ethanol 9-14 parts, age resistor 4-10 parts, adjuvant 10-15 parts；
Preparation method is：Ethanol is put into mixing plant, then sequentially added butyl acetate, calcium carbonate every two minutes
Powder, smectite powder, active powdered carbon, barium sulfate, age resistor, are stirred while adding, and material leaching is added after treating 20 minutes
70-80 DEG C of pure water of 0.5 times of liquid raw material is steeped, adjuvant is added after then proceeding to stirring 10 minutes, is further continued for stirring 30
Minute；
The barium sulfate powder, active powdered carbon, calcium carbonate powder are the particle that particle diameter made of grinding is 20-40mm；
The preparation method of the smectite powder is：By montmorillonite grind and cross 300-400 mesh sieves, then add and its
The clear water of homogenous quantities, mixing 50 minutes is stirred at room temperature, then adds tributoxyethyl phosphate, is warming up to 50-60 DEG C,
Then proceed to be stirred 2 hours, then dry, re-grind, produce smectite powder；
The mass ratio 1 of the tributoxyethyl phosphate and montmorillonite：2.8；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A；
The adjuvant is made up of the material of following parts by weight,
1 part of peppermint, 2 parts of tripterygium wilfordii, 3 parts of caulis piperis futokadsurae, 4 parts of wrinkled giant hyssop, 5 parts of ginger, 6 parts of pseudo-ginseng, 1 part of corydalis tuber, myrrh 2
Part, 3 parts of radix aconiti agrestis, 4 parts of rascal, 5 parts of the bark of official magnolia, 6 parts of betel nut；
Preparation method：I is put into above-mentioned material in marmite, adds the pure water and then with high heat of 2 times of material gross weight
Boil 50 minutes, then boiled 45 minutes with slow fire；
II separates the dregs of a decoction and medical filtration, and the pure water that the dregs of a decoction are further continued for the weight such as addition boils 30 minutes with high heat,
Then filter residue stays decoction；
III by I and the medicinal liquid agitating mixing 3-5 minutes in II.
Beneficial effects of the present invention are：Soak is that chemical materials is mixed with biomaterial, can not only prevent always,
Protection against the tide, also with anti-insect bite, increase the effect of brightness, by immersion repeatedly, heating baking can by internal unnecessary impurity,
Moisture retains various other material such as required soak, composition, and can also ensure that the good suction of material to dispelling
Receive, ensure that quality, toughness of batten etc., by increasing capacitance it is possible to increase the service life of batten.The inventive method is reasonable, easy to operate, energy
Enough anti-insect bites.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of braiding basket of batten, it is characterised in that：Including following preparation process,
Step 1: chosen material：Healthy conventional wood in selective cutting 5-9 days, no lesion, without insect pest, according to volume
Knitting needs that strip is made, and is then rinsed well with clear water, then is placed on and dries, divulges information, stands 3-5 in the environment of direct sunlight
Individual hour；
Step 2: immersion timber：Timber after standing is blown 3 minutes repeatedly with hair-dryer, is then placed in hydrogen peroxide and soaks
10-15 minutes are steeped, liquid level lid is crossed timber upper surface, then taken out, rinsed with clear water, then dry surface moisture again；
Step 3: baking timber：Timber after immersion is put into 95-110 DEG C of drying baker and toasted, is operated altogether
20-25 minutes；
Step 4: timber is soaked again：Timber after baking is taken out, it is quiet at room temperature to be placed on dry, ventilation place
Put 30 minutes, be then placed in 2-3 hour of immersion in soak；
Step 5: toast again：Timber after immersion is taken out, is then directly placed into 85-100 DEG C of drying baker and toasts
35-45 minutes；
Step 6: it is fabricated to basket：Batten is woven into basket by the weaving manner according to routine, in batten before batten is penetrated
One layer of lubricant of surface smear；
Step 7: cleaning basket：Basket after braiding is cleaned in suds or in liquid detergent, then rinsed with clear water dry
Naturally dry after net；
Step 8: immersion basket：A soak is remake, then basket is put into soak and soaks 40 minutes, then
Taking-up, which is put into 75-90 DEG C of baking oven, is toasted 25 minutes, and 5 minutes are stood after taking-up；The step of repeating immersion, baking, standing one
Totally 3 times；
Step 9: take out stand-by：Basket after standing is taken out be placed on dry, the place of ventilation, wait to finish or directly
Use；
The soak is made up of the material of following parts by weight,
3 parts of barium sulfate powder, 5 parts of active powdered carbon, 11 parts of smectite powder, 4 parts of calcium carbonate powder, 1 part of butyl acetate,
9 parts of ethanol, 4 parts of age resistor, 10 parts of adjuvant；
Preparation method is：Ethanol is put into mixing plant, then sequentially added butyl acetate, calcium carbonate every two minutes
Powder, smectite powder, active powdered carbon, barium sulfate, age resistor, are stirred while adding, and material leaching is added after treating 20 minutes
70-80 DEG C of pure water of 0.5 times of liquid raw material is steeped, adjuvant is added after then proceeding to stirring 10 minutes, is further continued for stirring 30
Minute；
The barium sulfate powder, active powdered carbon, calcium carbonate powder are the particle that particle diameter made of grinding is 20-40mm；
The preparation method of the smectite powder is：By montmorillonite grind and cross 300-400 mesh sieves, then add and its
The clear water of homogenous quantities, mixing 50 minutes is stirred at room temperature, then adds tributoxyethyl phosphate, is warming up to 50-60 DEG C,
Then proceed to be stirred 2 hours, then dry, re-grind, produce smectite powder；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A；
The adjuvant is made up of the material of following parts by weight,
1 part of peppermint, 2 parts of tripterygium wilfordii, 3 parts of caulis piperis futokadsurae, 4 parts of wrinkled giant hyssop, 5 parts of ginger, 6 parts of pseudo-ginseng, 1 part of corydalis tuber, myrrh 2
Part, 3 parts of radix aconiti agrestis, 4 parts of rascal, 5 parts of the bark of official magnolia, 6 parts of betel nut；
Preparation method：I is put into above-mentioned material in marmite, adds the pure water and then with high heat of 2 times of material gross weight
Boil 50 minutes, then boiled 45 minutes with slow fire；
II separates the dregs of a decoction and medical filtration, and the pure water that the dregs of a decoction are further continued for the weight such as addition boils 30 minutes with high heat,
Then filter residue stays decoction；
III by I and the medicinal liquid agitating mixing 3-5 minutes in II.
Embodiment 2
A kind of braiding basket of batten, it is characterised in that：Including following preparation process,
Step 1: chosen material：Healthy conventional wood in selective cutting 5-9 days, no lesion, without insect pest, according to volume
Knitting needs that strip is made, and is then rinsed well with clear water, then is placed on and dries, divulges information, stands 3-5 in the environment of direct sunlight
Individual hour；
Step 2: immersion timber：Timber after standing is blown 3 minutes repeatedly with hair-dryer, is then placed in hydrogen peroxide and soaks
10-15 minutes are steeped, liquid level lid is crossed timber upper surface, then taken out, rinsed with clear water, then dry surface moisture again；
Step 3: baking timber：Timber after immersion is put into 95-110 DEG C of drying baker and toasted, is operated altogether
20-25 minutes；
Step 4: timber is soaked again：Timber after baking is taken out, it is quiet at room temperature to be placed on dry, ventilation place
Put 30 minutes, be then placed in 2-3 hour of immersion in soak；
Step 5: toast again：Timber after immersion is taken out, is then directly placed into 85-100 DEG C of drying baker and toasts
35-45 minutes；
Step 6: it is fabricated to basket：Batten is woven into basket by the weaving manner according to routine, in batten before batten is penetrated
One layer of lubricant of surface smear；
Step 7: cleaning basket：Basket after braiding is cleaned in suds or in liquid detergent, then rinsed with clear water dry
Naturally dry after net；
Step 8: immersion basket：A soak is remake, then basket is put into soak and soaks 40 minutes, then
Taking-up, which is put into 75-90 DEG C of baking oven, is toasted 25 minutes, and 5 minutes are stood after taking-up；The step of repeating immersion, baking, standing one
Totally 3 times；
Step 9: take out stand-by：Basket after standing is taken out be placed on dry, the place of ventilation, wait to finish or directly
Use；
The soak is made up of the material of following parts by weight,
6 parts of barium sulfate powder, active powdered carbon part, 17 parts of smectite powder, 9 parts of calcium carbonate powder, 3 parts of butyl acetate,
14 parts of ethanol, 10 parts of age resistor, 15 parts of adjuvant；
Preparation method is：Ethanol is put into mixing plant, then sequentially added butyl acetate, calcium carbonate every two minutes
Powder, smectite powder, active powdered carbon, barium sulfate, age resistor, are stirred while adding, and material leaching is added after treating 20 minutes
70-80 DEG C of pure water of 0.5 times of liquid raw material is steeped, adjuvant is added after then proceeding to stirring 10 minutes, is further continued for stirring 30
Minute；
The barium sulfate powder, active powdered carbon, calcium carbonate powder are the particle that particle diameter made of grinding is 20-40mm；
The preparation method of the smectite powder is：By montmorillonite grind and cross 300-400 mesh sieves, then add and its
The clear water of homogenous quantities, mixing 50 minutes is stirred at room temperature, then adds tributoxyethyl phosphate, is warming up to 50-60 DEG C,
Then proceed to be stirred 2 hours, then dry, re-grind, produce smectite powder；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A；
The adjuvant is made up of the material of following parts by weight,
1 part of peppermint, 2 parts of tripterygium wilfordii, 3 parts of caulis piperis futokadsurae, 4 parts of wrinkled giant hyssop, 5 parts of ginger, 6 parts of pseudo-ginseng, 1 part of corydalis tuber, myrrh 2
Part, 3 parts of radix aconiti agrestis, 4 parts of rascal, 5 parts of the bark of official magnolia, 6 parts of betel nut；
Preparation method：I is put into above-mentioned material in marmite, adds the pure water and then with high heat of 2 times of material gross weight
Boil 50 minutes, then boiled 45 minutes with slow fire；
II separates the dregs of a decoction and medical filtration, and the pure water that the dregs of a decoction are further continued for the weight such as addition boils 30 minutes with high heat,
Then filter residue stays decoction；
III by I and the medicinal liquid agitating mixing 3-5 minutes in II.
Embodiment 3
A kind of braiding basket of batten, it is characterised in that：Including following preparation process,
Step 1: chosen material：Healthy conventional wood in selective cutting 5-9 days, no lesion, without insect pest, according to volume
Knitting needs that strip is made, and is then rinsed well with clear water, then is placed on and dries, divulges information, stands 3-5 in the environment of direct sunlight
Individual hour；
Step 2: immersion timber：Timber after standing is blown 3 minutes repeatedly with hair-dryer, is then placed in hydrogen peroxide and soaks
10-15 minutes are steeped, liquid level lid is crossed timber upper surface, then taken out, rinsed with clear water, then dry surface moisture again；
Step 3: baking timber：Timber after immersion is put into 95-110 DEG C of drying baker and toasted, is operated altogether
20-25 minutes；
Step 4: timber is soaked again：Timber after baking is taken out, it is quiet at room temperature to be placed on dry, ventilation place
Put 30 minutes, be then placed in 2-3 hour of immersion in soak；
Step 5: toast again：Timber after immersion is taken out, is then directly placed into 85-100 DEG C of drying baker and toasts
35-45 minutes；
Step 6: it is fabricated to basket：Batten is woven into basket by the weaving manner according to routine, in batten before batten is penetrated
One layer of lubricant of surface smear；
Step 7: cleaning basket：Basket after braiding is cleaned in suds or in liquid detergent, then rinsed with clear water dry
Naturally dry after net；
Step 8: immersion basket：A soak is remake, then basket is put into soak and soaks 40 minutes, then
Taking-up, which is put into 75-90 DEG C of baking oven, is toasted 25 minutes, and 5 minutes are stood after taking-up；The step of repeating immersion, baking, standing one
Totally 3 times；
Step 9: take out stand-by：Basket after standing is taken out be placed on dry, the place of ventilation, wait to finish or directly
Use；
The soak is made up of the material of following parts by weight,
4 parts of barium sulfate powder, 7 parts of active powdered carbon, 15 parts of smectite powder, 6 parts of calcium carbonate powder, 2 parts of butyl acetate,
12 parts of ethanol, 8 parts of age resistor, 14 parts of adjuvant；
Preparation method is：Ethanol is put into mixing plant, then sequentially added butyl acetate, calcium carbonate every two minutes
Powder, smectite powder, active powdered carbon, barium sulfate, age resistor, are stirred while adding, and material leaching is added after treating 20 minutes
70-80 DEG C of pure water of 0.5 times of liquid raw material is steeped, adjuvant is added after then proceeding to stirring 10 minutes, is further continued for stirring 30
Minute；
The barium sulfate powder, active powdered carbon, calcium carbonate powder are the particle that particle diameter made of grinding is 20-40mm；
The preparation method of the smectite powder is：By montmorillonite grind and cross 300-400 mesh sieves, then add and its
The clear water of homogenous quantities, mixing 50 minutes is stirred at room temperature, then adds tributoxyethyl phosphate, is warming up to 50-60 DEG C,
Then proceed to be stirred 2 hours, then dry, re-grind, produce smectite powder；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A；
The adjuvant is made up of the material of following parts by weight,
1 part of peppermint, 2 parts of tripterygium wilfordii, 3 parts of caulis piperis futokadsurae, 4 parts of wrinkled giant hyssop, 5 parts of ginger, 6 parts of pseudo-ginseng, 1 part of corydalis tuber, myrrh 2
Part, 3 parts of radix aconiti agrestis, 4 parts of rascal, 5 parts of the bark of official magnolia, 6 parts of betel nut；
Preparation method：I is put into above-mentioned material in marmite, adds the pure water and then with high heat of 2 times of material gross weight
Boil 50 minutes, then boiled 45 minutes with slow fire；
II separates the dregs of a decoction and medical filtration, and the pure water that the dregs of a decoction are further continued for the weight such as addition boils 30 minutes with high heat,
Then filter residue stays decoction；
III by I and the medicinal liquid agitating mixing 3-5 minutes in II.
Determine the experiment number of the wooden basket of this addition embodiments of the invention 1-3 material and the normal wood basket of no added material
According to such as following table：
| Period of storage (time limit) | Water resistance (48h) | Insect prevention performance (time limit) | |
| Embodiment 1 | 5 years | It is without exception | 1 year |
| Embodiment 2 | 5 years | It is without exception | 3 months 1 year |
| Embodiment 3 | 4.5 year | It is without exception | 6 months 1 year |
| Normal wood basket | 1 year | Without water resistance | 2 months |
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
- A kind of 1. braiding basket of batten, it is characterised in that：Including following preparation process,Step 1: chosen material：Healthy conventional wood in selective cutting 5-9 days, no lesion, without insect pest, according to braiding need Strip is made, is then rinsed well with clear water, then be placed on and dry, ventilation, direct sunlight environment in stand 3-5 small When；Step 2: immersion timber：Timber after standing is blown 3 minutes repeatedly with hair-dryer, is then placed in hydrogen peroxide and soaks 10- 15 minutes, liquid level lid crossed timber upper surface, then takes out, and is rinsed with clear water, then dries surface moisture again；Step 3: baking timber：Timber after immersion is put into 95-110 DEG C of drying baker and toasted, operates 20- altogether 25 minutes；Step 4: timber is soaked again：Timber after baking is taken out, dry, ventilation place is placed on and stands 30 at room temperature Minute, it is then placed in 2-3 hour of immersion in soak；Step 5: toast again：Timber after immersion is taken out, is then directly placed into 85-100 DEG C of drying baker and toasts 35- 45 minutes；Step 6: it is fabricated to basket：Batten is woven into basket by the weaving manner according to routine, on batten surface before batten is penetrated Smear one layer of lubricant；Step 7: cleaning basket：Basket after braiding is cleaned in suds or in liquid detergent, after then being rinsed well with clear water Naturally dry；Step 8: immersion basket：A soak is remake, then basket is put into soak and soaked 40 minutes, is then taken out It is put into 75-90 DEG C of baking oven and toasts 25 minutes, 5 minutes is stood after taking-up；The step of repeating immersion, baking, standing has 3 altogether It is secondary；Step 9: take out stand-by：Basket after standing is taken out to the place for being placed on and drying, divulging information, waits to finish or directly uses.
- A kind of 2. braiding basket of batten according to claim 1, it is characterised in that：The soak is by following parts by weight Material be made,Barium sulfate powder 3-6 parts, active powdered carbon 5-8 parts, smectite powder 11-17 parts, calcium carbonate powder 4-9 parts, acetic acid fourth Ester 1-3 parts, ethanol 9-14 parts, age resistor 4-10 parts, adjuvant 10-15 parts；Preparation method is：Ethanol is put into mixing plant, then sequentially added butyl acetate, Paris white every two minutes End, smectite powder, active powdered carbon, barium sulfate, age resistor, are stirred while adding, and material immersion is added after treating 20 minutes 70-80 DEG C of pure water of 0.5 times of liquid raw material, adjuvant is added after then proceeding to stirring 10 minutes, be further continued for 30 points of stirring Clock.
- A kind of 3. braiding basket of batten according to claim 2, it is characterised in that：The barium sulfate powder, activated carbon Powder, calcium carbonate powder are the particle that particle diameter made of grinding is 20-40mm.
- A kind of 4. braiding basket of batten according to claim 2, it is characterised in that：The preparation of the smectite powder Mode is：Montmorillonite is ground and crosses 300-400 mesh sieves, the clear water with its homogenous quantities is then added, mixing is stirred at room temperature 50 minutes, tributoxyethyl phosphate is then added, is warming up to 50-60 DEG C, then proceedes to be stirred 2 hours, then Dry, re-grind, produce smectite powder.
- A kind of 5. braiding basket of batten according to claim 2, it is characterised in that：The age resistor be antioxidant A W, One kind in anti-aging agent RD, antioxidant A.
- A kind of 6. braiding basket of batten according to claim 2, it is characterised in that：The adjuvant is by following parts by weight Material be made,1 part of peppermint, 2 parts of tripterygium wilfordii, 3 parts of caulis piperis futokadsurae, 4 parts of wrinkled giant hyssop, 5 parts of ginger, 6 parts of pseudo-ginseng, 1 part of corydalis tuber, 2 parts of myrrh, grass 3 parts of crow, 4 parts of rascal, 5 parts of the bark of official magnolia, 6 parts of betel nut；Preparation method：I is put into above-mentioned material in marmite, adds the pure water of 2 times of material gross weight and then boils with high heat 50 minutes, then boiled 45 minutes with slow fire；II separates the dregs of a decoction and medical filtration, and the pure water for the weight such as the dregs of a decoction are further continued for adding boils 30 minutes with high heat, then Filter residue stays decoction；III by I and the medicinal liquid agitating mixing 3-5 minutes in II.