CN107574708A - A kind of auxiliary material of corrugated paper and preparation method thereof - Google Patents
A kind of auxiliary material of corrugated paper and preparation method thereof Download PDFInfo
- Publication number
- CN107574708A CN107574708A CN201710746012.2A CN201710746012A CN107574708A CN 107574708 A CN107574708 A CN 107574708A CN 201710746012 A CN201710746012 A CN 201710746012A CN 107574708 A CN107574708 A CN 107574708A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrugated paper
- auxiliary material
- resin
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of auxiliary material of corrugated paper, it is related to corrugated paper processing technical field, it is characterised in that：It is made up of the material of following parts by weight, 13 17 parts of resin, 6 10 parts of defoamer, 58 parts of coupling agent, 48 parts of calcium sulfate, 14 parts of tertiary carbonic acid glycidyl ester, 8 13 parts of smectite powder, 14 parts of talcum powder, 25 parts of isocyanates, 25 parts of parachlorometaxylenol, 25 parts of phenyl glycidyl ether, 27 32 parts of clear water.The inventive method is reasonable, easy to operate, product caking property is good.
Description
Technical field
The present invention relates to corrugated paper to process technical field, and in particular to a kind of auxiliary material of corrugated paper and its preparation
Method.
Background technology
Corrugated paper is to process the plate object being bonded and the corrugated paper of the waveform formed by sheet lining and by corrugated roller,
Single wall corrugated board and the class of double-layer corrugated cardboard two are generally divided into, is divided into according to the size of corrugation：A, the type of B, C, E, F five.Corrugation
The invention and application of paper have more than 100 years history history, have low cost, light weight, processing is easy, intensity is big, printing adaptability sample is excellent
It is good, storage convenient in carrying the advantages that, more than 80% corrugated paper can be by reclaiming, and corrugated paper can be used as food or number
The packaging of code product, relatively environment-friendly, use is relatively broad.
A types corrugation and Type B corrugation are typically used as transporting extranal packing box, and beer case is typically made of B is stupefied.E is stupefied to be used as having more
Certain aesthetic and the packed single case for being put into appropriate weight content, F types corrugation and G type corrugations are referred to as minitype corrugation,
It is a kind of very thin corrugation, the disposable packaging container as food such as hamburger, eclair cakes, or as digital phase
The packaging of micro- electric product such as machine, Portable combination audio device and refrigerated product.
And fracture, the situation of cracking often occurs in corrugated paper during processing, and some corrugated papers are using
A period of time after various problems occur because the reason for the environment or weather on periphery and caused by, thus can
All made troubles to sale, production.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side
Just a kind of, good auxiliary material of corrugated paper of product caking property and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of auxiliary material of corrugated paper, it is characterised in that：It is made up of the material of following parts by weight,
Resin 13-17 parts, defoamer 6-10 parts, coupling agent 5-8 parts, calcium sulfate 4-8 parts, tertiary carbonic acid glycidyl ester 1-4
Part, smectite powder 8-13 parts, talcum powder 1-4 parts, isocyanates 2-5 parts, parachlorometaxylenol 2-5 parts, phenyl glycidyl
Glycerin ether 2-5 parts, clear water 27-32 parts；
The resin is organic siliconresin, polyisocyanate resin, phenolic resin, bisphenol A epoxide resin, 191 unsaturations
One kind in polyester resin；
The defoamer is one kind in organosiloxane, higher alcohols, GP types defoamer, GPE type defoamers；
The coupling agent is silane coupler KH-580；
The preparation method of the smectite powder is：Montmorillonite is ground and crosses 500-600 mesh sieves, is added and its weight
Identical pure water, it is stirred at room temperature after 1.5 hours of mixing, continuously adds aluminum nitride powder, continues to be stirred 2 small
When, then dry, grind, obtain smectite powder；
The mass ratio of the aluminum nitride powder and montmorillonite is 1：4；
A kind of preparation method of the auxiliary material of corrugated paper is,
Resin, defoamer, coupling agent, tertiary carbonic acid glycidyl ester and clear water are put into reactor and stirred at room temperature by I
Mix mixing 50 minutes；
II by the material left 10 minutes after stirring, then adds smectite powder, talcum powder, isocyanates, heating
To 40-45 DEG C, stir 40 minutes；
5 minutes are stood after III stirring to add to chlor-alkali dimethylbenzene, phenyl glycidyl ether, calcium sulfate, and are warming up to 50-55
DEG C, it is stirred for 2.5 hours；
The speed of the stirring is 2000-2500r/min.
Beneficial effects of the present invention are：Product is made in material under a series of hybrid mode, and product mixes so with paper pulp
After processed, product has good adhesive property, additionally it is possible to ensure production after product have good suppleness,
Compressive property and anti-wear performance.The inventive method is reasonable, easy to operate, product caking property is good.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of auxiliary material of corrugated paper, it is characterised in that：It is made up of the material of following parts by weight,
It is 13 parts of resin, 6 parts of defoamer, 5 parts of coupling agent, 4 parts of calcium sulfate, 1 part of tertiary carbonic acid glycidyl ester, modified montmorillonite used
8 parts of powder, 1 part of talcum powder, 2 parts of isocyanates, 2 parts of parachlorometaxylenol, 2 parts of phenyl glycidyl ether, 27 parts of clear water；
The resin is organic siliconresin, polyisocyanate resin, phenolic resin, bisphenol A epoxide resin, 191 unsaturations
One kind in polyester resin；
The defoamer is one kind in organosiloxane, higher alcohols, GP types defoamer, GPE type defoamers；
The coupling agent is silane coupler KH-580；
The preparation method of the smectite powder is：Montmorillonite is ground and crosses 500-600 mesh sieves, is added and its weight
Identical pure water, it is stirred at room temperature after 1.5 hours of mixing, continuously adds aluminum nitride powder, continues to be stirred 2 small
When, then dry, grind, obtain smectite powder；
The mass ratio of the aluminum nitride powder and montmorillonite is 1：4；
A kind of preparation method of the auxiliary material of corrugated paper is,
Resin, defoamer, coupling agent, tertiary carbonic acid glycidyl ester and clear water are put into reactor and stirred at room temperature by I
Mix mixing 50 minutes；
II by the material left 10 minutes after stirring, then adds smectite powder, talcum powder, isocyanates, heating
To 40-45 DEG C, stir 40 minutes；
5 minutes are stood after III stirring to add to chlor-alkali dimethylbenzene, phenyl glycidyl ether, calcium sulfate, and are warming up to 50-55
DEG C, it is stirred for 2.5 hours；
The speed of the stirring is 2000-2500r/min.
Embodiment 2
A kind of auxiliary material of corrugated paper, it is characterised in that：It is made up of the material of following parts by weight,
17 parts of resin, 10 parts of defoamer, 8 parts of coupling agent, 8 parts of calcium sulfate, 4 parts of tertiary carbonic acid glycidyl ester, modified cover take off
13 parts of stone flour, 4 parts of talcum powder, 5 parts of isocyanates, 5 parts of parachlorometaxylenol, 5 parts of phenyl glycidyl ether, 32 parts of clear water；
The resin is organic siliconresin, polyisocyanate resin, phenolic resin, bisphenol A epoxide resin, 191 unsaturations
One kind in polyester resin；
The defoamer is one kind in organosiloxane, higher alcohols, GP types defoamer, GPE type defoamers；
The coupling agent is silane coupler KH-580；
The preparation method of the smectite powder is：Montmorillonite is ground and crosses 500-600 mesh sieves, is added and its weight
Identical pure water, it is stirred at room temperature after 1.5 hours of mixing, continuously adds aluminum nitride powder, continues to be stirred 2 small
When, then dry, grind, obtain smectite powder；
The mass ratio of the aluminum nitride powder and montmorillonite is 1：4；
A kind of preparation method of the auxiliary material of corrugated paper is,
Resin, defoamer, coupling agent, tertiary carbonic acid glycidyl ester and clear water are put into reactor and stirred at room temperature by I
Mix mixing 50 minutes；
II by the material left 10 minutes after stirring, then adds smectite powder, talcum powder, isocyanates, heating
To 40-45 DEG C, stir 40 minutes；
5 minutes are stood after III stirring to add to chlor-alkali dimethylbenzene, phenyl glycidyl ether, calcium sulfate, and are warming up to 50-55
DEG C, it is stirred for 2.5 hours；
The speed of the stirring is 2000-2500r/min.
Embodiment 3
A kind of auxiliary material of corrugated paper, it is characterised in that：It is made up of the material of following parts by weight,
It is 15 parts of resin, 8 parts of defoamer, 6 parts of coupling agent, 6 parts of calcium sulfate, 3 parts of tertiary carbonic acid glycidyl ester, modified montmorillonite used
11 parts of powder, 2 parts of talcum powder, 4 parts of isocyanates, 3 parts of parachlorometaxylenol, 4 parts of phenyl glycidyl ether, 30 parts of clear water；
The resin is organic siliconresin, polyisocyanate resin, phenolic resin, bisphenol A epoxide resin, 191 unsaturations
One kind in polyester resin；
The defoamer is one kind in organosiloxane, higher alcohols, GP types defoamer, GPE type defoamers；
The coupling agent is silane coupler KH-580；
The preparation method of the smectite powder is：Montmorillonite is ground and crosses 500-600 mesh sieves, is added and its weight
Identical pure water, it is stirred at room temperature after 1.5 hours of mixing, continuously adds aluminum nitride powder, continues to be stirred 2 small
When, then dry, grind, obtain smectite powder；
The mass ratio of the aluminum nitride powder and montmorillonite is 1：4；
A kind of preparation method of the auxiliary material of corrugated paper is,
Resin, defoamer, coupling agent, tertiary carbonic acid glycidyl ester and clear water are put into reactor and stirred at room temperature by I
Mix mixing 50 minutes；
II by the material left 10 minutes after stirring, then adds smectite powder, talcum powder, isocyanates, heating
To 40-45 DEG C, stir 40 minutes；
5 minutes are stood after III stirring to add to chlor-alkali dimethylbenzene, phenyl glycidyl ether, calcium sulfate, and are warming up to 50-55
DEG C, it is stirred for 2.5 hours；
The speed of the stirring is 2000-2500r/min.
By the measuring embodiment of the present invention 1-3 performance and effect, such as table 1 below：
Remarks：Performance in table 1 is divided into high, medium and low three levels.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
- A kind of 1. auxiliary material of corrugated paper, it is characterised in that：It is made up of the material of following parts by weight,Resin 13-17 parts, defoamer 6-10 parts, coupling agent 5-8 parts, calcium sulfate 4-8 parts, tertiary carbonic acid glycidyl ester 1-4 parts, change Property montmorillonite powder 8-13 parts, talcum powder 1-4 parts, isocyanates 2-5 parts, parachlorometaxylenol 2-5 parts, phenyl glycidyl ether 2-5 parts, clear water 27-32 parts.
- A kind of 2. auxiliary material of corrugated paper according to claim 1, it is characterised in that：The resin is organosilicon tree One kind in fat, polyisocyanate resin, phenolic resin, bisphenol A epoxide resin, 191 unsaturated polyester resins.
- A kind of 3. auxiliary material of corrugated paper according to claim 1, it is characterised in that：The defoamer is organic silica One kind in alkane, higher alcohols, GP types defoamer, GPE type defoamers.
- A kind of 4. auxiliary material of corrugated paper according to claim 1, it is characterised in that：The coupling agent is silane coupled Agent KH-580.
- A kind of 5. auxiliary material of corrugated paper according to claim 1, it is characterised in that：The system of the smectite powder It is for mode：Montmorillonite is ground and crosses 500-600 mesh sieves, addition and its weight identical pure water, is stirred at room temperature mixed After closing 1.5 hours, aluminum nitride powder is continuously added, continues to be stirred 2 hours, then dried, grind, it is de- that illiteracy must be modified Stone flour.
- A kind of 6. auxiliary material of corrugated paper according to claim 5, it is characterised in that：The aluminum nitride powder and montmorillonite Mass ratio be 1：4.
- A kind of 7. auxiliary material of corrugated paper according to claim 1, it is characterised in that：A kind of auxiliary of the corrugated paper The preparation method of material is,I resin, defoamer, coupling agent, tertiary carbonic acid glycidyl ester and clear water are put into reactor be stirred at room temperature it is mixed Close 50 minutes；II by the material left 10 minutes after stirring, then adds smectite powder, talcum powder, isocyanates, is warming up to 40- 45 DEG C, stir 40 minutes；5 minutes are stood after III stirring to add to chlor-alkali dimethylbenzene, phenyl glycidyl ether, calcium sulfate, and are warming up to 50-55 DEG C, It is stirred for 2.5 hours.
- A kind of 8. auxiliary material of corrugated paper according to claim 7, it is characterised in that：The speed of the stirring is 2000-2500r/min。