CN107573994A - A kind of metal-cutting oil with rust-proof effect - Google Patents
A kind of metal-cutting oil with rust-proof effect Download PDFInfo
- Publication number
- CN107573994A CN107573994A CN201710793914.1A CN201710793914A CN107573994A CN 107573994 A CN107573994 A CN 107573994A CN 201710793914 A CN201710793914 A CN 201710793914A CN 107573994 A CN107573994 A CN 107573994A
- Authority
- CN
- China
- Prior art keywords
- rust
- metal
- cutting oil
- proof effect
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of metal-cutting oil with rust-proof effect and preparation method thereof, the component of the metal-cutting oil includes base oil, extreme pressure agent, oiliness additive, antistatic additive, a methyl cinnamic acid, procyclidine hydrochloride, antioxidant, said components are by mixing, heating, filtering etc. after technique is prepared into product, while the basic effects such as reduction friction are played in intermetallic composite coating, in the case where not adding antirust agent, rust-proof effect can also be played by the synergy between itself component, possess excellent application prospect.
Description
Technical field
The invention belongs to metal working technical area, and in particular to a kind of metal-cutting oil and its system with rust-proof effect
Preparation Method.
Background technology
Cutting oil is by extreme-pressure wear-resistant additive, lubricant, antistatic additive, the antimycotic antiseptic of base oil compounding different proportion
Agent, the additives such as cryogen are urged to synthesize.As a rule, cutting oil can be roughly divided into using lubrication as the non-aqueous of main purpose
Property cutting oil and the Water-soluble cutting oil using cooling effect as main purpose.Water-soluble cutting oil is according to shape when being mixed with water
State, emulsion, microemulsion, solution can be categorized as.Solution is the state that the oily stoste of cutting is dissolved in water, on the other hand, emulsion, micro-
Emulsion is to form the state of O/W types emulsion that the oily stoste of cutting is disperseed in the water of continuous phase, so-called.
Cutting oil have it is splendid to Digit Control Machine Tool in itself, the thorough protective value of cutlery, workpiece and emulsion.To steel
Iron or non-ferrous metal material implement turning, flat when the machining such as cutting, drill, milling, and can use cutting oil.Use cutting oil
Purpose be friction between reduction instrument and machined material and/or chip, the generation that removes chip, prevent built-up edge,
Suppress heating and cooling etc., it is possible thereby to seek the raising of life tools, operating accuracy.With contemporary metal secondary industry pair
In the continuous improvement of extraordinary oily effect requirements, in order to prevent the corrosion of metal, research staff adds often through in cutting oil
Antirust agent realizes this purpose, has also reached certain effect.
The content of the invention
It is an object of the present invention to develop a kind of metal-cutting oil with rust-proof effect, the component of the metal-cutting oil
Including base oil, extreme pressure agent, oiliness additive, antistatic additive, a methyl cinnamic acid, procyclidine hydrochloride, antioxidant.It is above-mentioned
Component plays in intermetallic composite coating by mixing, heating, filtering etc. after technique is prepared into product and reduces the basic effects such as friction
Meanwhile rust-proof effect can be played by the synergy between itself component, possessed excellent in the case where not adding antirust agent
Application prospect.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of metal-cutting oil with rust-proof effect, including following component and weight percentage：
Base oil 60-70%；
Extreme pressure agent 8-20%；
Oiliness additive 6-10%；
Antistatic additive 5-8%；
Between methyl cinnamic acid 4-7%;
Procyclidine hydrochloride 4-5%;
Antioxidant 2-6%,
Above-mentioned each component percentage composition sum is 100%.
Especially, the extreme pressure agent is triphen thiophosphate, chloroethanes, the mixture of sulfide isobutene, and proportioning is preferred
For triphen thiophosphate 65%, chloroethanes 30%, sulfide isobutene 5%.
Especially, the oiliness additive is olefine sulfide copolymer.
Meanwhile the invention also discloses the metal-cutting oil with rust-proof effect preparation method, by following steps group
Into：
（1）Base oil, oiliness additive are mixed, and be heated to 70 DEG C；
（2）Extreme pressure agent, antistatic additive, antioxidant are added in the mixed phase of step 1 while hot, stirring is extremely in homogeneous transparent
Shape, maintain more than 60 DEG C of the h of temperature 1;
（3）The mixed phase of step 2 is cooled to room temperature, methyl cinnamic acid, procyclidine hydrochloride between adding while stirring are completely mixed
Filtered after even, obtain finished product.
Compared with prior art, its advantage is the present invention：
（1）The metal-cutting oil of the present invention can play the basic effects such as reduction friction in intermetallic composite coating；
（2）The metal-cutting oil of the present invention is not in the case where adding antirust agent, by the synergy between itself component also
Good rust-proof effect can be played.
Embodiment
The technical scheme of invention is described in detail with reference to specific embodiment.
Embodiment
（1）Prepare following components according to weight percentage：
Linseed oil 60%；
Chloroethanes 15%；
Olefine sulfide copolymer 1 0%；
The fatty acid ester compounded thing 5% of higher alcohols；
Between methyl cinnamic acid 4%;
Procyclidine hydrochloride 4%;
Irgasfos 168 2%；
（2）Linseed oil, olefine sulfide copolymer are mixed, and be heated to 70 DEG C；
（3）Chloroethanes, the fatty acid ester compounded thing of higher alcohols, irgasfos 168 are added in the mixed phase of step 2 while hot, stirred
To being in homogeneous transparent shape, more than 60 DEG C of the h of temperature 1 is maintained;
（4）The mixed phase of step 3 is cooled to room temperature, methyl cinnamic acid, procyclidine hydrochloride between adding while stirring are completely mixed
Filtered after even, obtain finished product.
Comparative example
Formula according to the antirust extreme pressure sulfurized oil disclosed in Chinese patent CN105296082A prepares corresponding cutting oil,
Specific composition proportion is as follows：100 parts of rosin, 70 parts of cottonseed oil, 25 parts of oleic acid of vulcanization, 6.5 parts of sulphur, 2.5 parts of triethanolamine, hydrogen
0.6 part of sodium oxide molybdena.Preparation method used is to be simply mixed.
Oil will be cut made from embodiment（A）With comparative example made from cut oil（B）And purchase enjoys lubrication material from Guangdong wound
Expect that the model S300 of Co., Ltd anti-rust and lubrication cutting oil together carries out performance test.It is satisfied by cutting in above-mentioned three kinds of products
In the case of cutting oily base attribute, for decay resistance, content of impurities tested obtained by test result be shown in Table 1.
It can be seen that the cutting oil prepared by the present invention is compared with similar products, quality better, and there is excellent rustless property.
Table 1
| Corrosion test（T3 copper sheets, 50 DEG C, 15 d） | Mechanical admixture（%） | |
| Cut oily A | It is corrosion-free | Nothing |
| Cut oily B | Slight erosion | 0.01 |
| S300 anti-rust and lubrications cutting oil | Corrosion | 0.02 |
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to be said using the present invention
The equivalent flow conversion that bright book content is made, or other related technical areas are directly or indirectly used in, it is included in this hair
In bright scope of patent protection.
Claims (4)
1. a kind of metal-cutting oil with rust-proof effect, it is characterised in that including following component and weight percentage：
Base oil 60-70%；
Extreme pressure agent 8-20%；
Oiliness additive 6-10%；
Antistatic additive 5-8%；
Between methyl cinnamic acid 4-7%;
Procyclidine hydrochloride 4-5%;
Antioxidant 2-6%,
Above-mentioned each component percentage composition sum is 100%.
2. the metal-cutting oil according to claim 1 with rust-proof effect, it is characterised in that the extreme pressure agent is triphen
Thiophosphate, chloroethanes, the mixture of sulfide isobutene, proportioning are preferably triphen thiophosphate 65%, chloroethanes 30%, sulphur
Change isobutene 5%.
3. the metal-cutting oil according to claim 1 with rust-proof effect, it is characterised in that the oiliness additive is
Olefine sulfide copolymer.
4. the preparation method of the metal-cutting oil with rust-proof effect as described in claims 1 to 3 is any, it is characterised in that
Comprise the steps of：
（1）Base oil, oiliness additive are mixed, and be heated to 70 DEG C；
（2）Extreme pressure agent, antistatic additive, antioxidant are added in the mixed phase of step 1 while hot, stirring is extremely in homogeneous transparent
Shape, maintain more than 60 DEG C of the h of temperature 1;
（3）The mixed phase of step 2 is cooled to room temperature, methyl cinnamic acid, procyclidine hydrochloride between adding while stirring are completely mixed
Filtered after even, obtain finished product.