CN106010742A - Rust-proof cutting fluid for numerically-controlled machine tool metal processing and preparation method thereof - Google Patents

Rust-proof cutting fluid for numerically-controlled machine tool metal processing and preparation method thereof Download PDF

Info

Publication number
CN106010742A
CN106010742A CN201610347340.0A CN201610347340A CN106010742A CN 106010742 A CN106010742 A CN 106010742A CN 201610347340 A CN201610347340 A CN 201610347340A CN 106010742 A CN106010742 A CN 106010742A
Authority
CN
China
Prior art keywords
cutting fluid
machine tool
parts
control machine
digit control
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610347340.0A
Other languages
Chinese (zh)
Inventor
董德宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIZHENG WANGHAI CNC EQUIPMENT TECHNOLOGY Co Ltd
Original Assignee
YIZHENG WANGHAI CNC EQUIPMENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIZHENG WANGHAI CNC EQUIPMENT TECHNOLOGY Co Ltd filed Critical YIZHENG WANGHAI CNC EQUIPMENT TECHNOLOGY Co Ltd
Priority to CN201610347340.0A priority Critical patent/CN106010742A/en
Publication of CN106010742A publication Critical patent/CN106010742A/en
Pending legal-status Critical Current

Abstract

The invention relates to cutting fluid and a preparation method thereof, in particular to rust-proof cutting fluid for numerically-controlled machine tool metal processing and a preparation method thereof. The rust-proof cutting fluid for numerically-controlled machine tool metal processing is prepared from the following ingredients in parts by weight: 10 to 15 parts of compound antirusting agents, 3 to 5 parts of pH regulating agents, 0.5 to 1 part of antifoaming agents, 15 to 20 parts of compound lubricants, 1 to 5 parts of hard water resisting agents, 3 to 5 parts of extreme pressure agents, 1 to 3 parts of compound anticorrosion and bactericidal agents, 5 to 10 parts of Tween-80, 1 to 5 parts of nano-silica and the balance deionized water. The prepared cutting fluid has the advantages that excellent antisepsis performance, lubricating performance and rust-proof performance are realized; no foreign odor exists; the cutting fluid is friendly to the human body and has no harm; no stimulation exists; no pollution is caused on ambient environment. In addition, the process used by the preparation method is simple; the cost is low; the preparation method is suitable for scale production.

Description

A kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid and preparation method thereof
Technical field
The present invention relates to a kind of cutting fluid and preparation method thereof, be specifically related to a kind of Digit Control Machine Tool intermetallic composite coating and use Rust preventive cutting fluid and preparation method thereof.
Background technology
Cutting fluid is the important supplementary material of metal cutting process, uses the purpose of metalworking fluid to drop exactly Friction between low cutting force and cutter and workpiece, the heat produced in taking away cutting region in time is to reduce cutting Temperature, reduces tool wear, improves tool life, thus improves production efficiency, improves surface of the work thick Rugosity, it is ensured that Workpiece Machining Accuracy, thus reach economic optimum.
At present, the cutting fluid that equipment manufacture uses has cutting oil and emulsion two class.Cutting oil is at high-temperature machining Cut and production can produce substantial amounts of oil smoke, both polluted environment, and affected again safety in production；And cut oil needs Stock solution is cut, and production cost is high；Being that antirust ability is poor again, after even 1-2h, part gets final product corrosion.Emulsion It is a kind of mixed aqueous solution, the animal and plant oils and fats contained in emulsion, the most rotten, poor stability；? Easily there is breakdown of emulsion during use, not only use the cycle short, and waste liquid environmental pollution is serious.
Digit Control Machine Tool industry is the tap of equipment manufacture, is related to national economy and national defence tip is built Basic industry and strategic industry, along with Digit Control Machine Tool is towards specialization, miniaturization, precise treatment and high speed The development changed, Digit Control Machine Tool is the machine of precision as complexity, uses diversified actuating device, according to The requirement of the kind of equipment, working environment and precision has different requirements to the correlated performance of cutting fluid, Present the Digit Control Machine Tool proprietary feature to cutting fluid.By the use of cutting fluid, can be greatly reduced and cut Cut energy consumption, reduce cutting temperature, improve cutting-tool's used life, it is ensured that Workpiece Machining Accuracy and surface quality, Improve working (machining) efficiency, reach optimal economic effect.Chinese patent CN 105296126A discloses a kind of green Color environment-friendly type aqueous rustproof cutting fluid and preparation side thereof, the cutting fluid prepared has excellent rustless property And greasy property；Chinese patent CN102311864A discloses a kind of cutting fluid special for NC machine tools and system thereof Preparation Method, it is long that its cutting fluid prepared has service life, cleaning performance, rust-preventing characteristic, lubricity, cooling Property the advantage such as good.But the organic bactericide that above-mentioned two patent uses has aggressive, abnormal smells from the patient is pungent, Operator are had potentially hazardous.
Summary of the invention
For solving the problems referred to above, the present invention provide a kind of have excellent anti-microbial property, greasy property, Rustless property, free from extraneous odour, to human body close friend's fanout free region, non-stimulated and surrounding is not polluted A kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid and preparation method thereof.
A kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid, counts by weight, is made up of following component:
Composite antirust agent 10-15 part, pH adjusting agent 3-5 part, defoamer 0.5-1 part, compounded lubricant 15-20 Part, hard water resistance dose of 1-5 part, extreme pressure agent 3-5 part, composite anti-corrosive antibacterial 1-3 part, tween 80 5-10 part, Nano silicon 1-5 part, deionized water surplus,
Specifically, described composite antirust agent is prepared as follows: (1) is by 20-30 part triethylamine, 10-15 Part isopropanolamine, 20-30 part oleic acid join in closed reactor, and liter high-temperature is to 60-70 DEG C, and mixing is stirred Mix 20-30min；
(2) being slowly added dropwise in the system of step (1) into 10-15 part heterocycle polybasic carboxylic acid, about 1h drips off, Rise high-temperature to 100-150 DEG C, insulation reaction 3-5h, be down to 50-60 DEG C；
(3) in the system of step (2), 10-15 part BTA and 20-40 part triethanolamine are added, Stirring mixing 1-2h, is cooled to room temperature, obtains composite antirust agent.
Specifically, described pH adjusting agent is by sodium tetraborate and salicylic acid (4-7) in mass ratio: 1 forms.
Specifically, described defoamer is dimethicone.
Specifically, described compounded lubricant is pressed quality by diisopropanol amide, Polyethylene Glycol, polyvinyl alcohol Ratio is 1:(1-1.5): (0.5-1) forms.
Specifically, described hard water resistance dose is the one or two in ethylenediaminetetraacetic acid, N-caprylyl glutamic acid Kind.
Specifically, described extreme pressure agent by sodium molybdate and sodium tetraborate in mass ratio for 1:(4-6) form.
Specifically, described composite anti-corrosive antibacterial is pressed with dodecyl dimethyl benzyl ammonium chloride by silver nitrate Mass ratio (0.5-1): 1 composition.
The invention also discloses the preparation method of a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid, including such as Lower step:
(1) by deionized water, surfactant, compounded lubricant, hard water resistance dose of mixing, 400～600r/min Stir under rotating speed, be heated to 50-70 DEG C, after raw material is completely dissolved, is cooled to 30-40 DEG C；
(2) composite antirust agent, pH adjusting agent, defoamer, composite anti-corrosive antibacterial 1-3 part it are sequentially added into, Nano silicon, under 800～1000r/min speed conditions, is cooled to room temperature after stirring mixing 0.5-1h, ?.
Beneficial effects of the present invention:
(1) the compound composite antirust agent that the present invention uses, its heterocycle polybasic carboxylic acid has good with BTA Good synergistic function, not only increases the rustless property of metal, it is also possible to make the metal surface of processing Glossiness strengthens.
(2) present invention uses silver nitrate and dodecyl dimethyl benzyl ammonium chloride as preservative, has nothing Stimulation, corrosion-free, bactericidal effect and the advantage of good stability, effectively avoid other organic anti-corrosive agent strong Penetrating odor and the strong shortcoming of corrosivity, and to human body close friend's nonhazardous, can effective guarantee operator Health and safety, will not pollute surrounding.
(3) nano silicon that the present invention adds not only can play certain lubricity, reduce cutting force, Friction and power consumption, it is also possible to Adsorption For Ag ion, improve the slow release bactericidal effect of cutting fluid.
(4) compounded lubricant that the present invention uses and nano silicon have preferable synergism, significantly Improve the lubricity of cutting fluid, make the fineness of workpiece improve, improve production processing to greatest extent Efficiency, can effectively extend the service life of cutter and lathe.
(5) cutting fluid low cost, the method that prepared by the present invention are simple, economic and environment-friendly, it is adaptable to various metals Cutting and grinding.
Detailed description of the invention
In order to make the object of the invention, technical scheme and advantage clearer, below in conjunction with example, to this Invention is described in further detail.
Embodiment 1
(1) 20 parts of triethylamines, 10 parts of isopropanolamines, 25 parts of oleic acid are joined in closed reactor, rise High-temperature to 65 DEG C, mix and blend 20-30min；
(2) being slowly added dropwise in the system of step (1) into 10 parts of heterocycle polybasic carboxylic acids, about 1h drips off, Rise high-temperature to 100 DEG C, insulation reaction 3-5h, be down to 55 DEG C；
(3) in the system of step (2), 10 parts of BTAs and 25 parts of triethanolamine, stirring are added Mixing 1-2h, is cooled to room temperature, obtains composite antirust agent.
A kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid, counts by weight, is made up of following component:
Composite antirust agent 10 parts, the pH adjusting agent 3 parts that sodium tetraborate forms with salicylic acid 4:1 in mass ratio, Dimethicone 0.5 part, diisopropanol amide, Polyethylene Glycol, polyvinyl alcohol are 1:1:0.5 group in mass ratio The compounded lubricant 15 parts become, ethylenediaminetetraacetic acid 1 part, sodium molybdate and sodium tetraborate are 1:4 in mass ratio The extreme pressure agent 3 parts of composition, silver nitrate and dodecyl dimethyl benzyl ammonium chloride (0.5-1) in mass ratio: 1 composition Composite anti-corrosive antibacterial 1 part, tween 80 5 parts, nano silicon 1 part, deionized water surplus.
(1) by the deionized water of said ratio, surfactant, compounded lubricant, hard water resistance dose of mixing, Stir under 400～600r/min rotating speeds, be heated to 50-70 DEG C, after raw material is completely dissolved, is cooled to 30-40 DEG C；
(2) composite antirust agent, pH adjusting agent, defoamer, composite anti-corrosive antibacterial 1-3 part it are sequentially added into, Nano silicon, under 800～1000r/min speed conditions, is cooled to room temperature after stirring mixing 0.5-1h, ?.
Embodiment 2-6 is substantially the same manner as Example 1, and difference is table 1.
Table 1
By above-mentioned formula gained cutting fluid performance such as table 2
Table 2
With the above-mentioned desirable embodiment according to the present invention for enlightenment, by above-mentioned description, related work Personnel can carry out various change and amendment completely in the range of without departing from this invention technological thought. The content that the technical scope of this invention is not limited in description, it is necessary to according to right Determine its technical scope.

Claims (9)

1. a Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid, counts by weight, is made up of following component:
Composite antirust agent 10-15 part, pH adjusting agent 3-5 part, defoamer 0.5-1 part, compounded lubricant 15-20 part, hard water resistance dose of 1-5 part, extreme pressure agent 3-5 part, composite anti-corrosive antibacterial 1-3 part, tween 80 5-10 part, nano silicon 1-5 part, deionized water surplus.
2. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterized in that, described composite antirust agent is prepared as follows: 20-30 part triethylamine, 10-15 part isopropanolamine, 20-30 part oleic acid are joined in closed reactor by (1), rise high-temperature to 60-70 DEG C, mix and blend 20-30 min；
(2) being slowly added dropwise in the system of step (1) into 10-15 part heterocycle polybasic carboxylic acid, about 1h drips off, rise high-temperature to 100-150 DEG C, insulation reaction 3-5h, be down to 50-60 DEG C；
(3) in the system of step (2), 10-15 part BTA and 20-40 part triethanolamine are added, stirring mixing 1-2h, it is cooled to room temperature, obtains composite antirust agent.
3. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterised in that described pH adjusting agent is by sodium tetraborate and salicylic acid (4-7) in mass ratio: 1 forms.
4. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterised in that described defoamer is dimethicone.
5. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterized in that, described compounded lubricant is 1:(1-1.5 in mass ratio by diisopropanol amide, Polyethylene Glycol, polyvinyl alcohol): (0.5-1) forms.
6. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterised in that described anti-hard agent is one or both in ethylenediaminetetraacetic acid, N-caprylyl glutamic acid.
7. Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1 a kind of, it is characterised in that described extreme pressure agent is 1:(4-6 by sodium molybdate with sodium tetraborate in mass ratio) form.
8. a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterised in that described composite anti-corrosive antibacterial is by silver nitrate and dodecyl dimethyl benzyl ammonium chloride (0.5-1) in mass ratio: 1 forms.
9. the preparation method of an a kind of Digit Control Machine Tool intermetallic composite coating rust preventive cutting fluid as claimed in claim 1, it is characterised in that comprise the steps:
(1) by deionized water, surfactant, compounded lubricant, hard water resistance dose of mixing, stir under 400 ~ 600r/min rotating speed, be heated to 50-70 DEG C, after raw material is completely dissolved, is cooled to 30-40 DEG C；
(2) being sequentially added into composite antirust agent, pH adjusting agent, defoamer, composite anti-corrosive antibacterial 1-3 part, nano silicon, under 800 ~ 1000r/min speed conditions, stirring mixes Room temperature it is cooled to after 0.5-1h,.
CN201610347340.0A 2016-05-24 2016-05-24 Rust-proof cutting fluid for numerically-controlled machine tool metal processing and preparation method thereof Pending CN106010742A (en)