CN107571355A - The processing method of timber - Google Patents
The processing method of timber Download PDFInfo
- Publication number
- CN107571355A CN107571355A CN201710981791.4A CN201710981791A CN107571355A CN 107571355 A CN107571355 A CN 107571355A CN 201710981791 A CN201710981791 A CN 201710981791A CN 107571355 A CN107571355 A CN 107571355A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- processing method
- humidity
- curing agent
- timber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing method of timber, comprise the following steps：Step 1: choosing finished product sheet material, sheet metal thickness is 0.3 3.0mm；Humidified Step 2: the plate surface of step 1 is sprayed water so that humidity is consistent inside and outside sheet material, and humidity reaches 40 65%；Step 3: in the plate surface brush curing agent of step 2, and at a warm condition, hot pressing thickness is 0.2 0.5mm melamine sheet material；Step 4: by the sheet material of step 3, in 1.5 atmospheric pressure, humidity cools down under the conditions of being 45 60%；Step 5: by the sheet material of step 4, brush thickness is 1 3mm curing agent in dust-free room, is packed after solidification.Its technique is simple, and strength of wood is high, is unlikely to deform；Not cracky, its service life is extended, meets the market demand, is advantageous to product promotion.
Description
Technical field
The invention belongs to wood processing technique field, and in particular to a kind of processing method of timber.
Background technology
In recent years, people have been paid close attention to for by wood compression and making it be configured to intended shape and processing the skill of timber
Art.Due to a variety of grain patterns, Wood products are according to the position for cutting out specific Wood products of log made of timber
Put and show personal feature.This personal feature of each Wood products makes it have the quality of uniqueness.It is further, since long-term
The unique texture for easily causing the warm and known sensation of user is generated using caused surface damage and discoloration.
The content of the invention
The purpose of the present invention is to propose to a kind of processing method of timber, its technique is simple, and strength of wood is high, is unlikely to deform；
Not cracky, its service life is extended, meets the market demand, is advantageous to product promotion.
In order to reach above-mentioned purpose of design, under the technical solution adopted by the present invention：
A kind of processing method of timber, comprises the following steps：
Step 1: choose finished product sheet material, sheet metal thickness 0.3-3.0mm；
Humidified Step 2: the plate surface of step 1 is sprayed water so that humidity is consistent inside and outside sheet material, and humidity reaches 40-
65%；
Step 3: in the plate surface brush curing agent of step 2, and at a warm condition, hot pressing thickness is 0.2-0.5mm
Melamine sheet material；
Step 4: by the sheet material of step 3, in 1.5 atmospheric pressure, humidity cools down under the conditions of being 45-60%；
Step 5: by the sheet material of step 4, brush thickness is 1-3mm curing agent in dust-free room, is packed after solidification.
In above-mentioned steps three, when being bonded melamine sheet material, temperature is 150-350 degrees Celsius, and hot pressing pressure is 1-3 air
Pressure.
In above-mentioned steps three, curing agent is 35% isocyanates.
In above-mentioned steps five, curing agent is AB glue, and hardening time is 8-24 hours, and solidification humidity is less than 50%.
Sheet material made from the above method, above-mentioned melamine sheet material are provided with pattern.
Sheet material made from the above method, the pattern on above-mentioned melamine sheet material is using silk-screen printing.
Sheet material made from the above method, the pattern on above-mentioned melamine sheet material are carved using laser engraving machine.
The beneficial effect of the processing method of timber of the present invention is：Its technique is simple, and strength of wood is high, not variable
Shape；Not cracky, its service life is extended, meets the market demand, is advantageous to product promotion.
Embodiment
Preferred embodiment of the invention is described in further detail below.
The processing method of the timber, comprises the following steps：
Step 1: choose finished product sheet material, sheet metal thickness 0.3-3.0mm；
Humidified Step 2: the plate surface of step 1 is sprayed water so that humidity is consistent inside and outside sheet material, and humidity reaches 40-
65%；
Step 3: in the plate surface brush curing agent of step 2, and at a warm condition, hot pressing thickness is 0.2-0.5mm
Melamine sheet material；
Step 4: by the sheet material of step 3, in 1.5 atmospheric pressure, humidity cools down under the conditions of being 45-60%；
Step 5: by the sheet material of step 4, brush thickness is 1-3mm curing agent in dust-free room, is packed after solidification.
Preferably technical scheme is in specific implementation, in above-mentioned steps three, when being bonded melamine sheet material, and temperature 150-
350 degrees Celsius, hot pressing pressure is 1-3 atmospheric pressure.
Preferably technical scheme is in specific implementation, and in above-mentioned steps three, curing agent is 35% isocyanates.
Preferably technical scheme is in specific implementation, and in above-mentioned steps five, curing agent is AB glue, and hardening time is that 8-24 is small
When, solidification humidity is less than 50%.
Preferably technical scheme is in specific implementation, and above-mentioned melamine sheet material is provided with pattern.
Preferably technical scheme is in specific implementation, and the pattern on above-mentioned melamine sheet material is using silk-screen printing.
Preferably technical scheme is in specific implementation, and the pattern on above-mentioned melamine sheet material is carved using laser engraving machine
Carve.
Above content is to combine the further description that specific preferred embodiment is done to the present invention, is easy to the skill
The technical staff in art field is understood that and using the present invention, it is impossible to assert that the specific implementation of the present invention is confined to these explanations.
For general technical staff of the technical field of the invention, it can also make without departing from the inventive concept of the premise
Some simple deduction or replace, without by performing creative labour.Therefore, those skilled in the art's taking off according to the present invention
Show, the simple modifications made to the present invention all should be within protection scope of the present invention.
Claims (7)
- A kind of 1. processing method of timber, it is characterised in that：Comprise the following steps：Step 1: comprise the following steps：Step 1: choose finished product sheet material, sheet metal thickness 0.3-3.0mm；Humidified Step 2: the plate surface of step 1 is sprayed water so that humidity is consistent inside and outside sheet material, and humidity reaches 40-65%；Step 3: in the plate surface brush curing agent of step 2, and at a warm condition, hot pressing thickness is the three of 0.2-0.5mm Poly cyanamid sheet material；Step 4: by the sheet material of step 3, in 1.5 atmospheric pressure, humidity cools down under the conditions of being 45-60%；Step 5: by the sheet material of step 4, brush thickness is 1-3mm curing agent in dust-free room, is packed after solidification.
- 2. the processing method of timber according to claim 1, it is characterised in that：In above-mentioned steps three, melamine is bonded During sheet material, temperature is 150-350 degrees Celsius, and hot pressing pressure is 1-3 atmospheric pressure.
- 3. the processing method of timber according to claim 2, it is characterised in that：In above-mentioned steps three, curing agent 35% Isocyanates.
- 4. the processing method of timber according to claim 2, it is characterised in that：In above-mentioned steps five, curing agent is AB glue, Hardening time is 8-24 hours, and solidification humidity is less than 50%.
- 5. the processing method of the timber according to claim 2-4, it is characterised in that：Sheet material made from the above method, it is above-mentioned Melamine sheet material is provided with pattern.
- 6. the processing method of timber according to claim 5, it is characterised in that：Sheet material made from the above method, above-mentioned three Pattern on poly cyanamid sheet material is using silk-screen printing.
- 7. the processing method of timber according to claim 5, it is characterised in that：Sheet material made from the above method, above-mentioned three Pattern on poly cyanamid sheet material is carved using laser engraving machine.