CN107557799A - Copper alloy antirust agent - Google Patents
Copper alloy antirust agent Download PDFInfo
- Publication number
- CN107557799A CN107557799A CN201610521058.XA CN201610521058A CN107557799A CN 107557799 A CN107557799 A CN 107557799A CN 201610521058 A CN201610521058 A CN 201610521058A CN 107557799 A CN107557799 A CN 107557799A
- Authority
- CN
- China
- Prior art keywords
- parts
- copper alloy
- acid
- antirust agent
- pure water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides copper alloy antirust agent, include the component of following parts by weight：9 15 parts of watery hydrochloric acid, 13 parts of tetradecyl trimethyl ammonium chloride, 37 parts of sodium metasilicate, 15 parts of AEO, 0.5 1.5 parts of diethanol amine, 0.5 1.5 parts of tartaric acid, 0.2 0.8 parts of sulfamic acid, 5 15 parts of acrylic acid, 0.2 0.5 parts of sodium alkyl sulfonate, 24 parts of glycol propyl ether, 40 60 parts of pure water.The present invention meets the requirement of environmental protection, harmless.And chemical change does not occur with metal surface matrix, smooth metal surface, lubrication, smooth, good antirust property can be kept, especially suitable for the antirust of inter process, metal rust preventing is more than 1 year.
Description
Technical field
The present invention relates to antirust agent technical field, and in particular to a kind of copper alloy antirust agent.
Background technology
Copper alloy antirust agent can be effectively protected the materials such as steel, iron, prevent from getting rusty.Copper alloy antirust agent kind on the market
A lot, but copper alloy antirust agent contains heavy metal and carcinogen mostly, and human body can be damaged in industrial application.And
And the requirement of environmental protection is not met.
The content of the invention
It is an object of the invention to open copper alloy antirust agent, solves one in above-mentioned prior art problem or more
It is individual.
To achieve the above object, the invention provides copper alloy antirust agent, the component of following parts by weight is included：Watery hydrochloric acid 9-
15 parts, tetradecyl trimethyl ammonium chloride 1-3 parts, sodium metasilicate 3-7 parts, AEO 1-5 parts, diethanol amine 0.5-
1.5 parts, tartaric acid 0.5-1.5 parts, sulfamic acid 0.2-0.8 parts, acrylic acid 5-15 parts, sodium alkyl sulfonate 0.2-0.5 parts, second two
Alcohol propyl ether 2-4 parts, pure water 40-60 parts.
Beneficial effect：Copper alloy antirust agent provided by the invention, meet the requirement of environmental protection, it is harmless.And not with
Chemical change occurs for metal surface matrix, smooth metal surface, lubrication, smooth, good antirust property can be kept, especially suitable for work
Antirust between sequence, metal rust preventing is more than 1 year.
Embodiment
With reference to each embodiment, the present invention is described in detail, but it should explanation, these embodiments are simultaneously
Non- limitation of the present invention, those of ordinary skill in the art are according in these embodiment institute work energy, method or structures
Equivalent transformation or replacement, belong within protection scope of the present invention.
Embodiment 1
Copper alloy antirust agent, include the component of following parts by weight：9 parts of watery hydrochloric acid, 1 part of tetradecyl trimethyl ammonium chloride,
3 parts of sodium metasilicate, 1 part of AEO, 0.5 part of diethanol amine, 0.5 part of tartaric acid, 0.2 part of sulfamic acid, acrylic acid 5
Part, 0.2 part of sodium alkyl sulfonate, 2 parts of glycol propyl ether, 40 parts of pure water.
Above-mentioned other components are separately added into pure water, finished product is can obtain after being sufficiently mixed.
Application method：Rust remover is heated to 50 DEG C, the metal to be cleaned is dipped in 5min in this flourish liquid, taking-up is
Can.When after soaking 5min can not cleared greasy dirt rusty stain completely when, can be according to solution actual concentrations, proper extension soak time, directly
Untill cleared.
Embodiment 2
Copper alloy antirust agent, include the component of following parts by weight：12 parts of watery hydrochloric acid, 2 parts of tetradecyl trimethyl ammonium chloride,
5 parts of sodium metasilicate, 3 parts of AEO, 1 part of diethanol amine, 1 part of tartaric acid, 0.5 part of sulfamic acid, 10 parts of acrylic acid,
0.3 part of sodium alkyl sulfonate, 3 parts of glycol propyl ether, 50 parts of pure water.
Above-mentioned other components are separately added into pure water, finished product is can obtain after being sufficiently mixed.
Application method：Rust remover is heated to 50 DEG C, the metal to be cleaned is dipped in 5min in this flourish liquid, taking-up is
Can.When after soaking 5min can not cleared greasy dirt rusty stain completely when, can be according to solution actual concentrations, proper extension soak time, directly
Untill cleared.
Embodiment 3
Copper alloy antirust agent, include the component of following parts by weight：15 parts of watery hydrochloric acid, 3 parts of tetradecyl trimethyl ammonium chloride,
7 parts of sodium metasilicate, 5 parts of AEO, 1.5 parts of diethanol amine, 1.5 parts of tartaric acid, 0.8 part of sulfamic acid, acrylic acid
15 parts, 0.5 part of sodium alkyl sulfonate, 4 parts of glycol propyl ether, 60 parts of pure water.
Above-mentioned other components are separately added into pure water, finished product is can obtain after being sufficiently mixed.
Application method：Rust remover is heated to 50 DEG C, the metal to be cleaned is dipped in 5min in this flourish liquid, taking-up is
Can.When after soaking 5min can not cleared greasy dirt rusty stain completely when, can be according to solution actual concentrations, proper extension soak time, directly
Untill cleared.
Those listed above is a series of to be described in detail only for feasibility embodiment of the invention specifically
Bright, they simultaneously are not used to limit the scope of the invention, all equivalent implementations made without departing from skill spirit of the present invention
Or change should be included in the scope of the protection.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (1)
1. copper alloy antirust agent, it is characterised in that include the component of following parts by weight：Watery hydrochloric acid 9-15 parts, CPC
Ammonium chloride 1-3 parts, sodium metasilicate 3-7 parts, AEO 1-5 parts, diethanol amine 0.5-1.5 parts, tartaric acid 0.5-
1.5 parts, sulfamic acid 0.2-0.8 parts, acrylic acid 5-15 parts, sodium alkyl sulfonate 0.2-0.5 parts, glycol propyl ether 2-4 parts, pure water
40-60 parts.