CN101519777A - Antirusting agent - Google Patents
Antirusting agent Download PDFInfo
- Publication number
- CN101519777A CN101519777A CN200910136079A CN200910136079A CN101519777A CN 101519777 A CN101519777 A CN 101519777A CN 200910136079 A CN200910136079 A CN 200910136079A CN 200910136079 A CN200910136079 A CN 200910136079A CN 101519777 A CN101519777 A CN 101519777A
- Authority
- CN
- China
- Prior art keywords
- rust
- preventive agent
- corrosion
- agent
- antirusting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an antirusting agent which is characterized by comprising the following components by weight percent: 1.5 to 2 of calcined soda, 0.5 to 1 of trisodium phosphate, 0.3 to 1 of sodium propionate, 0.5 to 0.7 of trimeric sodium phosphate, and the balance of water. The antirusting agent has the advantages of integration of rust resistance, sterilization, mildew resistance and cleanness, as well as good antirusting effect, wide sterilization spectrum, good sterilization effect, long antirusting and bacteriostasis control period, innocuity, insipidity, no simulation to skin, no corrosion to base metal, no pollution to part surface, no bond, convenient operation, economy, practicality, no environment pollution, stable property, no easy metamorphism, easy storage, no flammability, and the like.
Description
Technical field
The present invention is a kind of rust-preventive agent, is applicable to the antirust processing of metallic surface.
Background technology
Existing rust-preventive agent adopts slushing oil mostly, and often contains harmful, inflammable material such as dimethylbenzene, gasoline in the slushing oil.In addition metallic substance is carried out antirust processing, adopt oiliness class rust-preventive agent, be applied to material surface, before welding, paint, electroplating, must oil removing clean, make operation various, lose time and raw material.In addition, rust-preventive agent effect in the market is single, and antirust function is only arranged, and does not have fungus and mildew resistance and cleaning function; But also exist some other problem: perhaps human body skin there is hormesis or very pungent smell is arranged or toxic or rust-proof effect is poor or cost height or character instability or be difficult for preservation, at room temperature apt to deteriorate behind the Kaifeng.These rust-preventive agent all bring some influences and harm to the mankind, animal, environment to some extent.
Summary of the invention
The purpose of this invention is to provide that a kind of to collect antirust, sterilization, mildew-resistant and cleaning be the rust-preventive agent of one, and favorable rust preventing effect, fungicidal spectrum is wide, sterilization effect good, antirust long rust-preventive agent of antibacterial preventive effect phase.
Another object of the present invention provides a kind of nonpoisonous and tasteless, rust-preventive agent of skin irritation not, does not contain any harmful oxygenant, SYNTHETIC OPTICAL WHITNER, heavy metal etc.
Another object of the present invention provides does not a kind ofly have to matrix metal that burn into does not pollute piece surface, do not cohere, easy to operate, economical and practical rust-preventive agent.
Another object of the present invention provides a kind of to non-environmental-pollution, non-harmful environment-friendly type rust-preventive agent, and absolutely biological degradation can not produce secondary pollution, washes back sewage and can directly discharge.
Another object of the present invention provides a kind of stable in properties, is not easy to go bad, is easy to preservation, nonflammable rust-preventive agent.
Based on above-mentioned purpose, the present invention is achieved in that
A kind of rust-preventive agent includes soda ash, tertiary sodium phosphate, Sodium Propionate, tripoly phosphate sodium STPP.
A kind of rust-preventive agent is characterized in that, by weight percentage, comprises following component: soda ash 1.5%-2%, tertiary sodium phosphate 0.5%-1%, Sodium Propionate 0.3%-1%, tripoly phosphate sodium STPP 0.5%-0.7%, water surplus.
Further, soda ash can be 1.5 or 1.6% or 1.7% or 1.8% or 1.9% or 2%.
Tertiary sodium phosphate can be 0.5% or 0.6% or 0.7% or 0.8% or 0.9% or 1%.
Sodium Propionate can be 0.3% or 0.4% or 0.5% or 0.6% or 0.7% or 0.8% or 0.9% or 1%.
Tripoly phosphate sodium STPP can be 0.5% or 0.6% or 0.7%.
The synthetic method that the invention has the advantages that compound is simple, all is stable compound, and long-term storage does not have denaturalization phenomenon; Adopt pure natural raw material, high-tech means, special formulation, form through the special process flow process is refining, through acute toxicity test and carcinogenicity test, show that this rust-preventive agent belongs to the non-toxic type compound, toxicological harmless, do not have carinogenicity and a teratogenecity fully, and human body skin is not had any hormesis; Collecting antirust, sterilization, mildew-resistant and cleaning is one, fungicidal spectrum is wide, yeast, bacterium etc. had bactericidal effect widely, also can kill all protokaryons and eukaryotic microorganisms, common mould genus examination bacterium such as Penicillium, Aspergillus, Rhizopus, Mucor, fusarium, the mould genus of interlinkage, Trichoderma all there is the obvious sterilization effect, thoroughly protects user's Biosafety; Antirust sterilization effect speed is fast, efficacy stability, long action time.
Embodiment
A kind of rust-preventive agent is characterized in that, by weight percentage, comprises following component: soda ash 1.5%-2%, tertiary sodium phosphate 0.5%-1%, Sodium Propionate 0.3%-1%, tripoly phosphate sodium STPP 0.5%-0.7%, water surplus.
Embodiment 1) rust-preventive agent, by weight percentage, comprise following component: soda ash 1.5%, tertiary sodium phosphate 0.5%, Sodium Propionate 0.3%, tripoly phosphate sodium STPP 0.5%, water surplus.
Embodiment 2) rust-preventive agent, by weight percentage, comprise following component: soda ash 2%, tertiary sodium phosphate 1%, Sodium Propionate 1%, tripoly phosphate sodium STPP 0.7%, water surplus.
Embodiment 3) rust-preventive agent, by weight percentage, comprise following component: soda ash 1.7%, tertiary sodium phosphate 0.8%, Sodium Propionate 0.6%, tripoly phosphate sodium STPP 0.6%, water surplus.
Embodiment 4) rust-preventive agent, by weight percentage, comprise following component: soda ash 1.8%, tertiary sodium phosphate 0.7%, Sodium Propionate 0.5%, tripoly phosphate sodium STPP 0.5%, water surplus.
Embodiment 5) rust-preventive agent, by weight percentage, comprise following component: soda ash 1.6%, tertiary sodium phosphate 0.9%, Sodium Propionate 0.8%, tripoly phosphate sodium STPP 0.6%, water surplus.
The present invention kills the mould on surface simultaneously by in metal surface extruding and discharge the aftereffect thing and reach antirust and anti-mold effect to metal.Metal spray with this product and drying after, the solid protective layer of surface formation one deck nano thickness, this protective layer not only can suppress corrosion, the growth of mould fungus inhibition effectively, and cleaning subsequently is more prone to.In addition, this product stores and is easy to carry.
The present invention can be used as the maintaniing agent of special-purpose gun, cannon.It is different from the general rifle bore cleaning oil of selling on the market, is the special-purpose gun maintaniing agent that unique in the world employing is natural, 100% safety non-toxic raw material is configured to.This product is nonpoisonous and tasteless, does not pollute worktable, uniform, holster etc., very is convenient to cleaning, problems such as the solvent that does not have other gun maintaniing agent fully and brought, the skin irritation that machine oil causes, contaminate environment.In addition, use this product can reduce the weapon handling time and efforts.Especially the weapon that used this product to handle before, the number of times of repeated treatments can significantly reduce, and this is because of superpower effect of this product and the outstanding long-acting mould antirust function that kills.
The using method of the present invention during as the antirust mildew-resistant sanitising agent of gun:
1, each parts of gun is disassembled.
2, because of this product is a group water solution, should guarantee that each parts is in the exsiccant situation before using, wait to do otherwise should place to place under the room temperature.
3, carefully this product evenly is sprayed at each parts surface of having dismantled.
4, available dried brush or clean cloth carry out wiping to unclean position.
5, place under the room temperature to place and wait to do, guarantee each parts complete drying before the assembling.
6, if necessary, can after drying, drip high-quality lubricating oil and further increase lubricant effect.
7, this product and other gun maintaniing agent please don't be used with.
The present invention is during as the antirust mildew-resistant sanitising agent of gun and the result of use comparison sheet of common rifle bore cleaning oil:
| The antirust mildew-resistant sanitising agent of gun | Other gun maintaniing agent | |
| Raw material | With the pure natural article is raw material | With Chemicals is raw material |
| Rust-proof effect | Outstanding rust-proof effect | Limited rust-proof effect |
| Kill mould anti-mold effect | Kill mould fully | Do not have and kill mould antimildew function |
| Heavy metal | Do not contain any heavy metal, reach the quality standard requirement " ROHS " of EU member country from implementation on July 1 in 2006 ' requirement of instruction quality standard | Contain the heterogeneity heavy metal, do not reach European Union " ROHS " ' requirement of instruction quality standard |
| Poison and corrosion | Nontoxic nothing corrosion | Poisonous and harmful has corrosion in various degree |
| Secondary pollution | Do not produce secondary pollution, be not infected with implements | Produce secondary pollution, not easy cleaning |
| Biological degradation | 100% biological degradation | Not biodegradable |
| Safeguard timeliness | Long | Short |
The experiment of the antirust mildew-resistant cleaning effect of the antirust mildew-resistant sanitising agent of test this product gun:
With hacksaw the shotgun gun barrel is sawn into 12 joints, long 10 centimetres of every joint grinds off the blueing agent on gun barrel surface with sand paper, and 12 joint gun barrels are divided into four groups, every group of total A, B, C three joints, and wherein the A joint does not promptly spray any reagent for contrast; The B joint sprays common machine oil class gun sanitising agent; The C joint sprays the antirust mildew-resistant sanitising agent of gun.Every group three joint gun are placed an airtight container (but and blow-by secluding air), and the condition of storage of each group is:
First group: place indoor environment.
Second group: the wet environment under the state of saturation, promptly in an airtight container (but and in blow-by secluding air), annotate
Go into the tap water of suitable height, gun barrel places the top of the water surface, and dried up about 5 centimetres.
The 3rd group: be placed in the rainwater.
The 4th group: be placed in the salt solution.
Temperature all is controlled at 37 ℃ under above-mentioned each group situation, and be five days storage period.
Experimental result:
1, places after 24 hours, have only the gun barrel (being gun barrel C) that has sprayed the antirust mildew-resistant sanitising agents of gun not get rusty.
2, place after 5 days, gun barrel C has only a small amount of corrosion in the surface, and gun barrel A and B rusting rate are serious.
3, at the 5th day, dip in the wiping of this sanitising agent with cotton and respectively save gun barrel, found that and have only gun barrel C surface not have rust staining.Tangible rust staining is all arranged on gun barrel A, the B.
Following table is the summary of this experiment:
1, after 24 hour
| Gun barrel A | Gun barrel B | Gun barrel C | |
| Indoor environment | Bright and clean | Bright and clean | Bright and clean |
| Saturated wet environment | Corrosion | Corrosion | Bright and clean |
| Rainwater | Corrosion | Corrosion | Bright and clean |
| Salt solution | Corrosion | Corrosion | Bright and clean |
2, after five days
| Gun barrel A | Gun barrel B | Gun barrel C | |
| Indoor environment | Bright and clean | Bright and clean | Bright and clean |
| Saturated wet environment | Corrosion +++ | Corrosion ++ | Corrosion+ |
| Rainwater | Corrosion +++ | Corrosion ++ | Corrosion+ |
| Salt solution | Corrosion +++ | Corrosion ++ | Corrosion+ |
Annotate: "+" represents a small amount of corrosion; The corrosion of " ++ " expression moderate; " +++" represents serious corrosion
3, the 5th day, after the cotton wiping, observe cleaning and rust cleaning effect:
| Gun barrel A | Gun barrel B | Gun barrel C | |
| Indoor environment | Bright and clean | Bright and clean | Bright and clean |
| Saturated wet environment | Rust staining is arranged | A small amount of corrosion | Bright and clean |
| Rainwater | Rust staining is arranged | A small amount of corrosion | Bright and clean |
| Salt solution | Rust staining is arranged | A small amount of corrosion | Bright and clean |
Though disclosed the preferred embodiments of the present invention for explanation; but those of ordinary skill in the art understands; under the situation that does not break away from claims institute's restricted portion of the present invention and spirit, various improvement, to increase and substitute all be possible, all within protection scope of the present invention.
Claims (9)
1. a rust-preventive agent is characterized in that, by weight percentage, comprises following component: soda ash 1.5%-2%, tertiary sodium phosphate 0.5%-1%, Sodium Propionate 0.3%-1%, tripoly phosphate sodium STPP 0.5%-0.7%, water surplus.
2. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 1.5%.
3. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 1.6%.
4. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 1.7%.
5. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 1.8%.
6. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 1.9%.
7. rust-preventive agent as claimed in claim 1 is characterized in that soda ash is 2%.
8. rust-preventive agent as claimed in claim 1 is characterized in that tertiary sodium phosphate is 0.5%.
9. rust-preventive agent as claimed in claim 1 is characterized in that tertiary sodium phosphate is 0.6%.