CN107556827A - 一种飞机空速管涂层材料及其制备方法 - Google Patents
一种飞机空速管涂层材料及其制备方法 Download PDFInfo
- Publication number
- CN107556827A CN107556827A CN201710752150.1A CN201710752150A CN107556827A CN 107556827 A CN107556827 A CN 107556827A CN 201710752150 A CN201710752150 A CN 201710752150A CN 107556827 A CN107556827 A CN 107556827A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating material
- pipe coating
- aircraft airspeed
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种飞机空速管涂层涂层材料及其制备方法,按照质量份数包括以下成分:铝粉10‑15份、防腐料6‑10份、聚乙烯5‑9份、酚醛树脂5‑8份、增塑剂1‑3份、有机硅树脂1‑3份、润滑剂1‑3份、触变剂6‑10份、分散剂0.5‑0.7份、溶剂20‑40份,本发明一种飞机空速管涂层材料,提供一种硬度高、硬度高、可提高安全性的飞机空速管涂层。
Description
技术领域
本发明涉及一种复合材料,具体而言涉及一种飞机空速管涂层材料及其制备方法。
背景技术
在飞机的机头或机翼上一般都会有一根细长的方向朝着飞机的正前方管子。这就是空速管,空速管测量飞机速度的原理是这样的,当飞机向前飞行时,气流便冲进空速管,在管子末端的感应器会感受到气流的冲击力量,飞机飞得越快,动压就越大,如果将空气静止时的压力即静压和动压相比就可以知道冲进来的空气有多快,也就是飞机飞得有多快,飞机空速管涂层很容易被腐蚀,选择好的涂层材料至关重要,目前没有防腐性好,耐热性好的飞机空速管涂层材料,因此研发一种防腐性好,耐热性好的飞机空速管涂层材料成为目前急需解决的问题。
发明内容
本发明提供了一种飞机空速管涂层材料及其制备方法。
为实现上述目的,本发明提供如下技术方案:
一种飞机空速管涂层材料,按照质量份数包括以下成分:
铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份、润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份。
进一步、按照质量份数包括如下成分:
铝粉10份、防腐料6份、聚乙烯5份、酚醛树脂5份、增塑剂1份、有机硅树脂1份、润滑剂1份、触变剂6份、分散剂0.5份、溶剂20份。
进一步、按照质量份数包括如下成分:
铝粉12份、防腐料8份、聚乙烯7份、酚醛树脂6份、增塑剂2份、有机硅树脂2份、润滑剂2份、触变剂8份、分散剂0.6份、溶剂30份。
进一步、按照质量份数包括如下成分:
铝粉15份、防腐料10份、聚乙烯9份、酚醛树脂8份、增塑剂3份、有机硅树脂3份、润滑剂3份、触变剂10份、分散剂0.7份、溶剂40份。
进一步、飞机空速管涂层材料的制备方法,包含如下步骤:
1)将铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份,充分混合搅拌制得混合物A;
2)将步骤一制得的混合物A,添加润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份,继续加热至120-210度充分混合,制得混合物B,将混合物B急速冷却即可。
本发明的有益效果是:
1、耐热性好。
2、防腐性更好。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例,仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例一:
一种飞机空速管涂层材料及其制备方法,按照质量份数包括以下成分:
铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份、润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份。
上述配方的制备方法:
1)将铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份,充分混合搅拌制得混合物A;
2)将步骤一制得的混合物A,添加润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份,继续加热至120-210度充分混合,制得混合物B,将混合物B急速冷却即可。
实施例二:
一种飞机空速管涂层材料按照质量份数包括以下成分:
铝粉10份、防腐料6份、聚乙烯5份、酚醛树脂5份、增塑剂1份、有机硅树脂1份、润滑剂1份、触变剂6份、分散剂0.5份、溶剂20份。
实施例三:
一种飞机空速管涂层材料及其制备方法,按照质量份数包括如下成分:
铝粉12份、防腐料8份、聚乙烯7份、酚醛树脂6份、增塑剂2份、有机硅树脂2份、润滑剂2份、触变剂8份、分散剂0.6份、溶剂30份。
实施例四:
一种飞机空速管涂层材料及其制备方法,按照质量份数包括如下成分:
铝粉15份、防腐料10份、聚乙烯9份、酚醛树脂8份、增塑剂3份、有机硅树脂3份、润滑剂3份、触变剂10份、分散剂0.7份、溶剂40份。
此外,应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施例中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种飞机空速管涂层材料,按照质量份数包括以下成分:
铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份、润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份。
2.根据权利要求1所述的一种飞机空速管涂层材料,按照质量份数包括如下成分:
铝粉10份、防腐料6份、聚乙烯5份、酚醛树脂5份、增塑剂1份、有机硅树脂1份、润滑剂1份、触变剂6份、分散剂0.5份、溶剂20份。
3.根据权利要求1所述的一种飞机空速管涂层材料,按照质量份数包括如下成分:
铝粉12份、防腐料8份、聚乙烯7份、酚醛树脂6份、增塑剂2份、有机硅树脂2份、润滑剂2份、触变剂8份、分散剂0.6份、溶剂30份。
4.根据权利要求1所述的一种飞机空速管涂层材料,按照质量份数包括如下成分:
铝粉15份、防腐料10份、聚乙烯9份、酚醛树脂8份、增塑剂3份、有机硅树脂3份、润滑剂3份、触变剂10份、分散剂0.7份、溶剂40份。
5.一种如权利要求1-4任一所述的飞机空速管涂层材料的制备方法,包含如下步骤:
1)将铝粉10-15份、防腐料6-10份、聚乙烯5-9份、酚醛树脂5-8份、增塑剂1-3份、有机硅树脂1-3份,充分混合搅拌制得混合物A;
2)将步骤一制得的混合物A,添加润滑剂1-3份、触变剂6-10份、分散剂0.5-0.7份、溶剂20-40份,继续加热至120-210度充分混合,制得混合物B,将混合物B急速冷却即可。