CN107555849A - A kind of environment-friendly architecture ornament sheet material and preparation method thereof - Google Patents
A kind of environment-friendly architecture ornament sheet material and preparation method thereof Download PDFInfo
- Publication number
- CN107555849A CN107555849A CN201710902107.9A CN201710902107A CN107555849A CN 107555849 A CN107555849 A CN 107555849A CN 201710902107 A CN201710902107 A CN 201710902107A CN 107555849 A CN107555849 A CN 107555849A
- Authority
- CN
- China
- Prior art keywords
- parts
- sheet material
- powder
- preparation
- xanthans
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendly architecture ornament sheet material and preparation method thereof, the ratio of weight and number of sheet material raw material is 10 30 parts of epoxy resin, 8 18 parts of polyvinyl resin, 26 parts of glass fibre, 20 30 parts of powder of straw, 5 16 parts of magnesium silicate fiber, 16 parts of nano silicon micronization, 14 parts of polyvinyl alcohol 28 part, nanometer material, 26 parts of nano titanium dioxide powder, 6 12 parts of xanthans, preparation method of the present invention is simple, preparation process is environment friendly and pollution-free, and obtained dalle has the advantages of resistance to compression, wear-resisting, fire resisting, sound insulation.
Description
Technical field
The present invention relates to dalle preparing technical field, specially a kind of environment-friendly architecture ornament sheet material and its preparation side
Method.
Background technology
Dalle suffers from very extensive application in building trade, and current existing building board soundproof effect is not
Ideal, easy aging, and be incubated, waterproof, fireproof ability, using effect is bad, is not received by people.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly architecture ornament sheet material and preparation method thereof, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme：A kind of environment-friendly architecture ornament sheet material, sheet material raw material
Ratio of weight and number is epoxy resin 10-30 parts, polyvinyl resin 8-18 parts, glass fibre 2-6 parts, powder of straw 20-30 parts, silicic acid
Magnesium fiber 5-16 parts, nano silicon micronization 1-6 parts, polyvinyl alcohol 2-8 parts, nanometer material 1-4 parts, nano titanium dioxide powder 2-6 parts,
Xanthans 6-12 parts.
Preferably, the preferable composition proportion of sheet material raw material is 20 parts of epoxy resin, 13 parts of polyvinyl resin, glass fibre 4
Part, 25 parts of powder of straw, 11 parts of magnesium silicate fiber, 4 parts of nano silicon micronization, polyvinyl alcohol 5 part, nanometer expect 3 parts, nano titanium oxide
4 parts of powder, 9 parts of xanthans.
Preferably, its preparation method comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Compared with prior art, the beneficial effects of the invention are as follows：Preparation method of the present invention is simple, and preparation process environmental protection is without dirt
Dye, obtained dalle have the advantages of resistance to compression, wear-resisting, fire resisting, sound insulation；Wherein, the magnesium silicate fiber of addition, nano-silicon are micro-
Powder, nano titanium dioxide powder can improve the resistance to elevated temperatures of dalle；The xanthans of addition can improve each raw material it
Between bond effect, in addition, the preparation method that uses of the present invention can be sufficiently mixed each material, reduce the system of dalle
Make cost, obtained through overtesting, dalle compression strength produced by the present invention reaches 40MPA, and high temperature resistant reaches 130 DEG C.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme：A kind of environment-friendly architecture ornament sheet material, the ratio of weight and number of sheet material raw material is ring
Oxygen tree fat 10-30 parts, polyvinyl resin 8-18 parts, glass fibre 2-6 parts, powder of straw 20-30 parts, magnesium silicate fiber 5-16 parts,
Nano silicon micronization 1-6 parts, polyvinyl alcohol 2-8 parts, nanometer material 1-4 parts, nano titanium dioxide powder 2-6 parts, xanthans 6-12 parts.
Embodiment one：
The ratio of weight and number of sheet material raw material be 10 parts of epoxy resin, 8 parts of polyvinyl resin, 2 parts of glass fibre, 20 parts of powder of straw,
5 parts of magnesium silicate fiber, 1 part of nano silicon micronization, 1 part of polyvinyl alcohol 2 part, nanometer material, 2 parts of nano titanium dioxide powder, xanthans 6
Part.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Embodiment two：
The ratio of weight and number of sheet material raw material be 30 parts of epoxy resin, 18 parts of polyvinyl resin, 6 parts of glass fibre, 30 parts of powder of straw,
16 parts of magnesium silicate fiber, 6 parts of nano silicon micronization, 4 parts of polyvinyl alcohol 8 part, nanometer material, 6 parts of nano titanium dioxide powder, xanthans
12 parts.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Embodiment three：
The ratio of weight and number of sheet material raw material be 12 parts of epoxy resin, 9 parts of polyvinyl resin, 3 parts of glass fibre, 22 parts of powder of straw,
7 parts of magnesium silicate fiber, 2 parts of nano silicon micronization, 2 parts of polyvinyl alcohol 3 part, nanometer material, 3 parts of nano titanium dioxide powder, xanthans 7
Part.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Example IV：
The ratio of weight and number of sheet material raw material be 28 parts of epoxy resin, 16 parts of polyvinyl resin, 5 parts of glass fibre, 28 parts of powder of straw,
Magnesium silicate is fine 14 parts, 5 parts of nano silicon micronization, 3 parts of polyvinyl alcohol 7 part, nanometer material, 5 parts of nano titanium dioxide powder, xanthans 11
Part.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Embodiment five：
The ratio of weight and number of sheet material raw material be 22 parts of epoxy resin, 15 parts of polyvinyl resin, 4 parts of glass fibre, 26 parts of powder of straw,
14 parts of magnesium silicate fiber, 5 parts of nano silicon micronization, 4 parts of polyvinyl alcohol 6 part, nanometer material, 5 parts of nano titanium dioxide powder, xanthans
10 parts.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Embodiment six：
The ratio of weight and number of sheet material raw material be 20 parts of epoxy resin, 13 parts of polyvinyl resin, 4 parts of glass fibre, 25 parts of powder of straw,
11 parts of magnesium silicate fiber, 4 parts of nano silicon micronization, 3 parts of polyvinyl alcohol 5 part, nanometer material, 4 parts of nano titanium dioxide powder, xanthans
9 parts.
The preparation method of the present embodiment comprises the following steps：
A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder
Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；
B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans
Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；
C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced
To dalle.
Preparation method of the present invention is simple, and preparation process is environment friendly and pollution-free, and obtained dalle has resistance to compression, wear-resisting, resistance to
The advantages of fire, sound insulation；Wherein, the magnesium silicate fiber of addition, nano silicon micronization, nano titanium dioxide powder can improve decorative panel
The resistance to elevated temperatures of material；The xanthans of addition can improve the bond effect between each raw material, in addition, the preparation that the present invention uses
Method can be sufficiently mixed each material, reduce the cost of manufacture of dalle, obtained through overtesting, dress produced by the present invention
Decoratice board compression strength reaches 40MPA, and high temperature resistant reaches 130 DEG C.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. environment-friendly architecture ornament sheet material, it is characterised in that：The ratio of weight and number of sheet material raw material be epoxy resin 10-30 parts, Polyvinyl resin 8-18 parts, glass fibre 2-6 parts, powder of straw 20-30 parts, magnesium silicate fiber 5-16 parts, nano silicon micronization 1-6 Part, polyvinyl alcohol 2-8 parts, nanometer material 1-4 parts, nano titanium dioxide powder 2-6 parts, xanthans 6-12 parts.
- A kind of 2. environment-friendly architecture ornament sheet material according to claim 1, it is characterised in that：The preferable composition of sheet material raw material is matched somebody with somebody Than for 20 parts of epoxy resin, 13 parts of polyvinyl resin, 4 parts of glass fibre, 25 parts of powder of straw, 11 parts of magnesium silicate fiber, nano-silicon 4 parts of micro mist, 3 parts of polyvinyl alcohol 5 part, nanometer material, 4 parts of nano titanium dioxide powder, 9 parts of xanthans.
- 3. realize a kind of preparation method of environment-friendly architecture ornament sheet material described in claim 1, it is characterised in that：Its preparation method Comprise the following steps：A, add after mixing glass fibre, powder of straw, magnesium silicate fiber, nano silicon micronization, nanometer material, nano titanium dioxide powder Enter in stirred tank and stir, speed is 400 revs/min, time 25min, obtains mixture A；B, heating stirring in agitator tank, stirring speed are added after mixing epoxy resin, polyvinyl resin, polyvinyl alcohol, xanthans Rate is 1000 revs/min, time 10min, and heating-up temperature is 80 DEG C, obtains mixture B；C, mixture B is added in mixture A, be sufficiently mixed in rear injection moulding mould, compressing rear demoulding is dried, and is produced To dalle.